The primary objective of this research was to examine the strength degradation of Glass Fiber Reinforced Polymer (GFRP) bars at high temperature and alkalinity and determine if an Arrhenius type relationship can be used as a means of projecting life. The work done includes a thorough literature review, experiments and development of strength prediction models. The experimental work involves exposure of GFRP bars incased in cement mortar to lime-water solution at 30, 45 and 57°C. Overall 100 specimens were included in the experimental program. The tensile strength and modulus of elasticity retention after 180 days of exposure at 57°C was 57% and 82% respectively. The secondary objective was to determine the moisture absorption properties of GFRP bars. The moisture absorption data available is till 80 days from the immersion of the specimens in the tank. The collected data was used in the development of strength retention models. Two strength prediction models, Time Shift Method and Fickian Model for moisture absorption are formulated. Using the Fickian Model, strength is predicted for GFRP bars, if used in bridge decks in Roanoke, Virginia. The strength loss predicted was 45% after 50 years of exposure in real life environment. A linear relationship was observed when the moisture content and strength retention were plotted. The study estimates a strength loss higher than the ACI-440H recommended environmental degradation factor of 0.7 to calculate the design ultimate tensile strength. / Master of Science

Yes / The flexural performance of geopolymer concrete (GPC) T-beams reinforced longitudinally with GFRP bars under a four-point static bending test was investigated. Six full-scale simply supported T-beams were cast and tested; one control specimen was made with ordinary Portland cement concrete (OPCC), while the other five beams were made of geopolymer concrete. The G-GPC2 was designed to attain the same theoretical moment capacity as the G-OPCC6 control beam. The main parameters investigated were the reinforcement ratio of ρ_f/ρ_b= 0.75, 1.05, 1.12, 1.34 and 1.34 for G-GPC1, G-GPC2, G-GPC3, G-GPC4, and G-GPC5, respectively, and compressive strength of geopolymer concrete. Based on the results of the experiments, the ultimate strain of GPC did not show the same behaviour as that of OPCC, which affects the mode of failure. The beam capacity and deflection were, respectively, overestimated and underestimated using the ACI 440 2R-17 predictive equations.

Yes / The results of testing two simply and three continuously supported concrete beams reinforced with glass fiber-reinforced polymer (GFRP) bars are presented. The amount of GFRP reinforcement was the main parameter investigated. Over and under GFRP reinforcements were applied for the simply supported concrete beams. Three different GFRP reinforcement combinations of over and under reinforcement ratios were used for the top and bottom layers of the continuous concrete beams tested. A concrete continuous beam reinforced with steel bars was also tested for comparison purposes. The experimental results revealed that over-reinforcing the bottom layer of either the simply or continuously supported GFRP beams is a key factor in controlling the width and propagation of cracks, enhancing the load capacity, and reducing the deflection of such beams. Comparisons between experimental results and those obtained from simplified methods proposed by the ACI 440 Committee show that ACI 440.1R-06 equations can reasonably predict the load capacity and deflection of the simply and continuously supported GFRP reinforced concrete beams tested.