Modificação de processo de fabricação de folha de flandres atraves da inibição de crescimento da camada de liga Fe-SnBertazzoli, Rodnei, 1965- 20 December 1989 (has links)
Orientadores: Ettore Bresciani Filho, Margarita Balester Santos / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Campinas / Made available in DSpace on 2018-07-14T00:17:44Z (GMT). No. of bitstreams: 1
Bertazzoli_Rodnei_D.pdf: 2785661 bytes, checksum: 9afbe74c5fbeb9cf05e27a7157d8085d (MD5)
Previous issue date: 1989 / Resumo: Neste trabalho tomou-se como objetivo a obtenção de uma folha de Flandres modificada através da interposição de uma camada de níquel entre o aço e o estanho. Tomando por base a chapa estanhada convencional foi feita nesta, uma caracterização através de dissolução anódica, difração de Raios-X e espectroscopia Auger para determinar a composição e estrutura do material. Sua resistência à corrosão foi determinada através de polarizações catódicas em meio cítrico. Para produzir depósitos de 10-lOOmg/m² de níquel, 0,3-0,8 g/m² de estanho com confiabilidade foram feitos ensaios voltamétricos nos eletrólitos de deposição. Foram identificados potenciais e correntes de deposição bem como o rendimento dos processos de eletrodeposição. A seguir amostras de folhas de Flandres pré-niqueladas foram produzidas mostrando que teores entre 20-40 mg/m² de níquel não só inibem a formação da liga Fe-Sn como produzem a maior quantidade de estanho livre, medido através de dissolução anódica, após o abrilhantamento do revestimento. As polarizações catódicas mostraram que a chapa mais resistente à corrosão são aqueles que possuem teores entre 10-40 mg/m² de níquel sob o estanho. / Abstract: This work presents the manufacturing process of tinp1ate modified by interposition of a nickel thin lager between the stee1, and tin. The conventiona1 product was characterized by anodic dissolution, X-rays diffraction and Auger spectroscopy in order to investigate the tinplate composition ond structure. The corrosion resistance of tinplate was investigate by cathodic polarizations in citric solutions, pH3. Volumetric measures were done to obtain reproducible nickel coatings of 10-100 mg/m² and tin coatings of 0,3-0,8 g/m². Potentials, currents and efficiences of deposition pocesses were identified. Samp1es of tinplate nickel-preplated were prepared showing that 20-40 mg/m² of nickel inhibited the growth of FeSn2 alloy layer and showed an optimization of the free tin after flow melting. The cathodic polarizations showed that 10-40 mg/m² of nickel had a very favourable effect on the corrosion resistance. / Doutorado / Doutor em Engenharia Mecânica
|
2 |
Filmes híbridos modificados com agentes flexibilizantes para uso como revestimento barreira e como pré-tratamento de folha de flandres para aplicação de tinta UVKunst, Sandra Raquel January 2015 (has links)
Um dos principais problemas da folha de flandres utilizada no setor de embalagens é a adesão dos revestimentos UV sobre o substrato devido à presença de óxidos na superfície. Dessa forma, o emprego de pré-tratamentos superficiais se faz necessário, e o uso de revestimentos híbridos tem sido proposto para melhorar a aderência e a resistência à corrosão. Contudo, esses revestimentos tendem a serem frágeis e não suportam deformação mecânica. No presente trabalho, os filmes híbridos foram depositados sobre a folha de flandres a fim de avaliar o seu desempenho como revestimento protetor e como pré-tratamento para posterior aplicação do revestimento UV. Visando melhorar o efeito barreira, as folhas de flandres foram revestidas com um filme híbrido obtido a partir de um sol constituído pelos precursores: 3-(trimetoxisililpropil)metacrilato (TMSM) e tetraetoxisilano (TEOS) e Ce(NO3)3 0,01M com adição do plastificante di-isodecil adipato (DIDA) em diferentes concentrações: (0,5, 1, 2 e 4%). Utilizou-se o processo de dip-coating com velocidade de retirada de 10 cm.min-1, com aplicação em monocamada e bicamada, e curados por cura térmica empregando-se duas diferentes temperaturas de cura, 60 °C e 90 °C. Com o objetivo de analisar um pré-tratamento para posterior aplicação do revestimento UV, as folhas de flandres foram revestidas com um filme híbrido obtido a partir de um sol com a mesma formulação citada, substituindo o plastificante DIDA pelo flexibilizante polietilenoglicol (PEG) em diferentes concentrações: (20, 40, 60 e 80 g.L-1). Os filmes foram obtidos e curados conforme descrito anteriormente, além disso, após o pré-tratamento com filme híbrido, a folha de flandres foi submetida ao processo de pintura com tinta uretânica alifática acrilada curada por radiação ultravioleta (UV). Foram empregadas como técnicas para caracterização quanto ao comportamento eletroquímico: monitoramento do potencial de circuito aberto, curvas de polarização potenciodinâmicas, medidas de impedância eletroquímica e svet. O comportamento físico-químico dos filmes foi avaliado por ângulo de contato, termogravimetria, espectroscopia de infravermelho e ressonância magnética nuclear. A resistência ao desgaste foi avaliada pela técnica de esfera sobre plano. Os sistemas de pintura curada por radição ultravioleta foram analisados quanto à adesão, flexibilidade e molhabilidade. Os resultados obtidos, mostraram que a adição de 2% do plastificante di-isodecil adipato melhorou a resistência à corrosão e a cura a 90 °C e com aplicação da bicamada otimizou o efeito barreira do filme. Adição de PEG na concentração de 20 g.L-1 contribuiu para melhorar a flexibilidade do filme retardando a cinética da reação de reticulação e consequentemente evitando a formação de fissuras. Nesta concentração, e curado a 60 °C, o filme melhorou a resistência mecânica para os sistemas com pós-tratamento em tinta UV. / One of the main problems of the tinplate for the packaging sector is the coating adherence of UV coatings on the substrate, due to the presence of oxides on the surface. Thus, it makes necessary the use of surface pretreatments, and the use of hybrid coatings has been proposed to improve the adherence and corrosion resistance. However, these hybrid films tend to be fragile and do not hold on mechanical deformation. In this work, the tinplate was coated with hybrid films aiming to evaluate its performance as protective coating and as pre-treatment for further UV coating application. In order to improve the barrier effect, the tinplate were coated with a hybrid film obtained from a sol constituted by the precursors 3-(trimethoxysilyl)propyl methacrylate (TMSM) and tetraethoxysilane (TEOS), 0.01 mol.L-1 cerium nitrate (Ce(NO3)3) and diisodecyl adipate (DIDA) in different concentrations (0.5, 1, 2 and 4%) as plasticizer. Dip-coating was the process for applying the films with removal rate of 10 cm.min-1. The films were applied in one or two layers and, then, thermally cured at 60 °C or 90 °C. As a pretreatment for further UV coating, the tinplate were coated with a hybrid film with the aforementioned formulation, but replacing the plasticizer DIDA for polyethylene glycol (PEG) in different concentrations (20, 40, 60 e 80 g.L-1). The films were obtained and cured through the same dip-coating process and, after, the samples were painted with aliphatic acrylic urethane coating with ultraviolet radiation curing. The characterization techniques for electrochemical behavior were open circuit potential monitoring, potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS) and scanning vibrating electrode technique (SVET). The physicochemical behavior of the films was evaluated by contact angle measurement, thermogravimetric analysis, infrared spectroscopy and nuclear magnetic resonance. Wear resistance was evaluated by using a ball-on-plate test. The systems with UV-radiation-cured ink were analyzed regarding adherence, flexibility and wettability. Results showed that adding 2% of DIDA plasticizer improved the corrosion resistance and that curing a bilayer film at 90 °C optimizes the film barrier effect. Adding PEG in a concentration of 20 g.L-1 improved the flexibility of the film, making the cross-linking reaction kinetics slower and, in consequence, avoided cracks. With this concentration and curing at 60 °C, the film had better mechanical resistance for systems post-treated with UV ink.
|
3 |
Filmes híbridos modificados com agentes flexibilizantes para uso como revestimento barreira e como pré-tratamento de folha de flandres para aplicação de tinta UVKunst, Sandra Raquel January 2015 (has links)
Um dos principais problemas da folha de flandres utilizada no setor de embalagens é a adesão dos revestimentos UV sobre o substrato devido à presença de óxidos na superfície. Dessa forma, o emprego de pré-tratamentos superficiais se faz necessário, e o uso de revestimentos híbridos tem sido proposto para melhorar a aderência e a resistência à corrosão. Contudo, esses revestimentos tendem a serem frágeis e não suportam deformação mecânica. No presente trabalho, os filmes híbridos foram depositados sobre a folha de flandres a fim de avaliar o seu desempenho como revestimento protetor e como pré-tratamento para posterior aplicação do revestimento UV. Visando melhorar o efeito barreira, as folhas de flandres foram revestidas com um filme híbrido obtido a partir de um sol constituído pelos precursores: 3-(trimetoxisililpropil)metacrilato (TMSM) e tetraetoxisilano (TEOS) e Ce(NO3)3 0,01M com adição do plastificante di-isodecil adipato (DIDA) em diferentes concentrações: (0,5, 1, 2 e 4%). Utilizou-se o processo de dip-coating com velocidade de retirada de 10 cm.min-1, com aplicação em monocamada e bicamada, e curados por cura térmica empregando-se duas diferentes temperaturas de cura, 60 °C e 90 °C. Com o objetivo de analisar um pré-tratamento para posterior aplicação do revestimento UV, as folhas de flandres foram revestidas com um filme híbrido obtido a partir de um sol com a mesma formulação citada, substituindo o plastificante DIDA pelo flexibilizante polietilenoglicol (PEG) em diferentes concentrações: (20, 40, 60 e 80 g.L-1). Os filmes foram obtidos e curados conforme descrito anteriormente, além disso, após o pré-tratamento com filme híbrido, a folha de flandres foi submetida ao processo de pintura com tinta uretânica alifática acrilada curada por radiação ultravioleta (UV). Foram empregadas como técnicas para caracterização quanto ao comportamento eletroquímico: monitoramento do potencial de circuito aberto, curvas de polarização potenciodinâmicas, medidas de impedância eletroquímica e svet. O comportamento físico-químico dos filmes foi avaliado por ângulo de contato, termogravimetria, espectroscopia de infravermelho e ressonância magnética nuclear. A resistência ao desgaste foi avaliada pela técnica de esfera sobre plano. Os sistemas de pintura curada por radição ultravioleta foram analisados quanto à adesão, flexibilidade e molhabilidade. Os resultados obtidos, mostraram que a adição de 2% do plastificante di-isodecil adipato melhorou a resistência à corrosão e a cura a 90 °C e com aplicação da bicamada otimizou o efeito barreira do filme. Adição de PEG na concentração de 20 g.L-1 contribuiu para melhorar a flexibilidade do filme retardando a cinética da reação de reticulação e consequentemente evitando a formação de fissuras. Nesta concentração, e curado a 60 °C, o filme melhorou a resistência mecânica para os sistemas com pós-tratamento em tinta UV. / One of the main problems of the tinplate for the packaging sector is the coating adherence of UV coatings on the substrate, due to the presence of oxides on the surface. Thus, it makes necessary the use of surface pretreatments, and the use of hybrid coatings has been proposed to improve the adherence and corrosion resistance. However, these hybrid films tend to be fragile and do not hold on mechanical deformation. In this work, the tinplate was coated with hybrid films aiming to evaluate its performance as protective coating and as pre-treatment for further UV coating application. In order to improve the barrier effect, the tinplate were coated with a hybrid film obtained from a sol constituted by the precursors 3-(trimethoxysilyl)propyl methacrylate (TMSM) and tetraethoxysilane (TEOS), 0.01 mol.L-1 cerium nitrate (Ce(NO3)3) and diisodecyl adipate (DIDA) in different concentrations (0.5, 1, 2 and 4%) as plasticizer. Dip-coating was the process for applying the films with removal rate of 10 cm.min-1. The films were applied in one or two layers and, then, thermally cured at 60 °C or 90 °C. As a pretreatment for further UV coating, the tinplate were coated with a hybrid film with the aforementioned formulation, but replacing the plasticizer DIDA for polyethylene glycol (PEG) in different concentrations (20, 40, 60 e 80 g.L-1). The films were obtained and cured through the same dip-coating process and, after, the samples were painted with aliphatic acrylic urethane coating with ultraviolet radiation curing. The characterization techniques for electrochemical behavior were open circuit potential monitoring, potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS) and scanning vibrating electrode technique (SVET). The physicochemical behavior of the films was evaluated by contact angle measurement, thermogravimetric analysis, infrared spectroscopy and nuclear magnetic resonance. Wear resistance was evaluated by using a ball-on-plate test. The systems with UV-radiation-cured ink were analyzed regarding adherence, flexibility and wettability. Results showed that adding 2% of DIDA plasticizer improved the corrosion resistance and that curing a bilayer film at 90 °C optimizes the film barrier effect. Adding PEG in a concentration of 20 g.L-1 improved the flexibility of the film, making the cross-linking reaction kinetics slower and, in consequence, avoided cracks. With this concentration and curing at 60 °C, the film had better mechanical resistance for systems post-treated with UV ink.
|
4 |
Filmes híbridos modificados com agentes flexibilizantes para uso como revestimento barreira e como pré-tratamento de folha de flandres para aplicação de tinta UVKunst, Sandra Raquel January 2015 (has links)
Um dos principais problemas da folha de flandres utilizada no setor de embalagens é a adesão dos revestimentos UV sobre o substrato devido à presença de óxidos na superfície. Dessa forma, o emprego de pré-tratamentos superficiais se faz necessário, e o uso de revestimentos híbridos tem sido proposto para melhorar a aderência e a resistência à corrosão. Contudo, esses revestimentos tendem a serem frágeis e não suportam deformação mecânica. No presente trabalho, os filmes híbridos foram depositados sobre a folha de flandres a fim de avaliar o seu desempenho como revestimento protetor e como pré-tratamento para posterior aplicação do revestimento UV. Visando melhorar o efeito barreira, as folhas de flandres foram revestidas com um filme híbrido obtido a partir de um sol constituído pelos precursores: 3-(trimetoxisililpropil)metacrilato (TMSM) e tetraetoxisilano (TEOS) e Ce(NO3)3 0,01M com adição do plastificante di-isodecil adipato (DIDA) em diferentes concentrações: (0,5, 1, 2 e 4%). Utilizou-se o processo de dip-coating com velocidade de retirada de 10 cm.min-1, com aplicação em monocamada e bicamada, e curados por cura térmica empregando-se duas diferentes temperaturas de cura, 60 °C e 90 °C. Com o objetivo de analisar um pré-tratamento para posterior aplicação do revestimento UV, as folhas de flandres foram revestidas com um filme híbrido obtido a partir de um sol com a mesma formulação citada, substituindo o plastificante DIDA pelo flexibilizante polietilenoglicol (PEG) em diferentes concentrações: (20, 40, 60 e 80 g.L-1). Os filmes foram obtidos e curados conforme descrito anteriormente, além disso, após o pré-tratamento com filme híbrido, a folha de flandres foi submetida ao processo de pintura com tinta uretânica alifática acrilada curada por radiação ultravioleta (UV). Foram empregadas como técnicas para caracterização quanto ao comportamento eletroquímico: monitoramento do potencial de circuito aberto, curvas de polarização potenciodinâmicas, medidas de impedância eletroquímica e svet. O comportamento físico-químico dos filmes foi avaliado por ângulo de contato, termogravimetria, espectroscopia de infravermelho e ressonância magnética nuclear. A resistência ao desgaste foi avaliada pela técnica de esfera sobre plano. Os sistemas de pintura curada por radição ultravioleta foram analisados quanto à adesão, flexibilidade e molhabilidade. Os resultados obtidos, mostraram que a adição de 2% do plastificante di-isodecil adipato melhorou a resistência à corrosão e a cura a 90 °C e com aplicação da bicamada otimizou o efeito barreira do filme. Adição de PEG na concentração de 20 g.L-1 contribuiu para melhorar a flexibilidade do filme retardando a cinética da reação de reticulação e consequentemente evitando a formação de fissuras. Nesta concentração, e curado a 60 °C, o filme melhorou a resistência mecânica para os sistemas com pós-tratamento em tinta UV. / One of the main problems of the tinplate for the packaging sector is the coating adherence of UV coatings on the substrate, due to the presence of oxides on the surface. Thus, it makes necessary the use of surface pretreatments, and the use of hybrid coatings has been proposed to improve the adherence and corrosion resistance. However, these hybrid films tend to be fragile and do not hold on mechanical deformation. In this work, the tinplate was coated with hybrid films aiming to evaluate its performance as protective coating and as pre-treatment for further UV coating application. In order to improve the barrier effect, the tinplate were coated with a hybrid film obtained from a sol constituted by the precursors 3-(trimethoxysilyl)propyl methacrylate (TMSM) and tetraethoxysilane (TEOS), 0.01 mol.L-1 cerium nitrate (Ce(NO3)3) and diisodecyl adipate (DIDA) in different concentrations (0.5, 1, 2 and 4%) as plasticizer. Dip-coating was the process for applying the films with removal rate of 10 cm.min-1. The films were applied in one or two layers and, then, thermally cured at 60 °C or 90 °C. As a pretreatment for further UV coating, the tinplate were coated with a hybrid film with the aforementioned formulation, but replacing the plasticizer DIDA for polyethylene glycol (PEG) in different concentrations (20, 40, 60 e 80 g.L-1). The films were obtained and cured through the same dip-coating process and, after, the samples were painted with aliphatic acrylic urethane coating with ultraviolet radiation curing. The characterization techniques for electrochemical behavior were open circuit potential monitoring, potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS) and scanning vibrating electrode technique (SVET). The physicochemical behavior of the films was evaluated by contact angle measurement, thermogravimetric analysis, infrared spectroscopy and nuclear magnetic resonance. Wear resistance was evaluated by using a ball-on-plate test. The systems with UV-radiation-cured ink were analyzed regarding adherence, flexibility and wettability. Results showed that adding 2% of DIDA plasticizer improved the corrosion resistance and that curing a bilayer film at 90 °C optimizes the film barrier effect. Adding PEG in a concentration of 20 g.L-1 improved the flexibility of the film, making the cross-linking reaction kinetics slower and, in consequence, avoided cracks. With this concentration and curing at 60 °C, the film had better mechanical resistance for systems post-treated with UV ink.
|
5 |
Análise de simulantes para produtos ácidos acondicionados em embalagens metálicas / Analysis of simulants to acidic products conditioned in meal packagePelici, Bianca de Oliveira, 1985- 21 August 2018 (has links)
Orientador: Célia Marina de Alvarenga Freire / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-21T02:18:10Z (GMT). No. of bitstreams: 1
Pelici_BiancadeOliveira_M.pdf: 3905161 bytes, checksum: 85a5220db551a3df1468acd995cba296 (MD5)
Previous issue date: 2012 / Resumo: As latas em folha-de-flandres representam a maior parte das embalagens metálicas para conservas alimentícias. Como não são inertes, durante o período de estocagem, ocorre interação com o produto e alguma dissolução de metais pode acontecer, principalmente quando se acondiciona alimentos ácidos. Para minimizar essa interação faz-se uso de revestimentos orgânicos, sendo a resina epóxi-fenólica a mais utilizada. Uma vez que os alimentos são sistemas bioquímicos complexos, na maioria dos estudos relacionados à interação produto/embalagem utiliza-se simulantes, que são substâncias orgânicas com propriedades difusivas análogas aos de um alimento e que apresentam composição química mais simples. Essas substâncias são utilizadas nos ensaios em substituição ao alimento, visando facilitar, agilizar e reduzir custos de procedimentos analíticos. A escolha do simulante é feita de acordo com as características físicoquímicas do alimento, que segue a classificação determinada pela legislação. No caso de alimentos aquosos ácidos o simulante proposto é o ácido acético 3% (m/v). Este trabalho teve por objetivo avaliar soluções simulantes alternativas ao ácido acético, realizando análises quanto ao desempenho de latas com camada nominal de estanho 2,0 g/m2 revestidas com verniz do tipo epóxi-fenólico (dupla camada interna) quando em contato com estas soluções. A técnica de espectroscopia de impedância eletroquímica foi utilizada para monitorar a degradação do revestimento orgânico e para caracterizar suas propriedades de barreira ao longo do tempo quanto a resistência à corrosão; a polarização foi aplicada para determinar a taxa de corrosão e a susceptibilidade do material metálico à corrosão. Também foram obtidas imagens da superfície das amostras através da Microscopia Eletrônica de Varredura e da Espectroscopia de Energia Dispersiva (MEV/EDS) após os ensaios eletroquímicos para complementar a caracterização do filme / Abstract: Tin-plate cans represent most of the cans for canned food. Since they are not inert, during the storage period, interaction occurs with the product and metal dissolution can occur, especially when it is acid food. To minimize this interaction it is used organic coatings, and epoxy-phenolic resin is the the most used. As the foods are complex biochemical systems, in most of the studies related to the interaction product / package simulants are used, that are organic substances that are analogous to the diffusive properties of food and have simpler composition. These substances are used in the tests to replace the food, to facilitate, speed up and reduce costs in analytical procedures. The choice of simulating is made according to the physico-chemical properties of the food, which follows the classification determined by the legislation. For acidic aqueous food the proposed simulant is acetic acid 3% (w / v). This work aimed to evaluate alternative solutions to acetic acid simulating, analyzing the performance in cans with nominal layer of tin 2.0 g/m2 coated with lacquer-type epoxy phenolic (double inner layer) when in contact with these solutions . The technique of electrochemical impedance spectroscopy was used to monitor the degradation of organic coating and to characterize their barrier properties over time as corrosion resistance; polarization was applied to determine the corrosion rate and susceptibility to corrosion of metallic material. Also images were also obtained of the sample surfaces by Scanning Electron Microscopy and Energy Dispersive Spectroscopy (SEM / EDS) after the electrochemical tests to complement the characterization of the film / Mestrado / Materiais e Processos de Fabricação / Mestra em Engenharia Mecânica
|