X-ray diffraction analysis (XRD), infrared (IR) spectroscopy and scanning electron microscopy have been used for the characterization of cobalt-based pigments (Kremer Pigmente) and their lead-based glazes.It was also demonstrated that XRD analysis could be successfully used for the identification of cobalt pigments cobalt violet brilliant light CoNH4PO4•H2O, cobalt blue light, cerulean blue, cobalt green bluish CoO·ZnO in their glazes. However, only non-oxide cobalt pigments cobalt yellow [K3(Co(NO2)6]•3H2O, cobalt violet brilliant light and cobalt violet dark Co3(PO4)2 could be determined in their glazes using IR spectroscopy. The similarity of all SEM images of cobalt-based glazes let us to conclude, that the main morphological features of glazes are not dependent on the nature of cobalt pigment. The single phase cobalt violet light brilliant pigment has been synthesized using a simple co-precipitation approach. The characteristics of the obtained product were compared with those of a commercial sample purchased from Kremer Pigmente. For the first time to our knowledge, it was demonstrated that the characteristic Si-O absorption band at 812 cm-1 could be successfully used as indicator in the evaluation of molar ratio of CoO and SiO2 in their mixture. The novel method for the determination of SiO2 in physical mixtures of CoO ir SiO2 (in the range 9,1-50 %) or blue cobalt smalt pigment (CoO×nSiO2) (in the range 20-50 %) by FTIR spectroscopy is suggested. New cobalt-based... [to full text] / Atlikta istorinių kobalto pigmentų analogų Rentgeno spindulių difrakcinė analizė parodė, kad metodas efektyvus, nustatant kobalto šviesiai violetinį CoNH4PO4•H2O, kobalto mėlynąjį šviesų, ceruleumą ir kobalto žalsvai mėlyną CoO·ZnO, jų švino glazūrose, bet netinka aureolino [K3(Co(NO2)6]•3H2O, kobalto tamsiai violetinio Co3(PO4)2, kobalto mėlynojo tamsus, kobalto melsvai žalio ir smaltos CoO•nSiO2 nustatymui. IR spektroskopiniai tyrimai parodė, kad šis metodas efektyvus, kokybiškai nustatant neoksidinius kobalto pigmentus aureoliną, kobalto šviesiai violetinį, kobalto tamsiai violetinį jų švino glazūrose. Paprastu nusodinimo metodu susintetintas kobalto pigmentas violetinis šviesusis CoNH4PO4, pasižymintis analogiškomis fizikinėmis savybėmis, kaip ir komercinis Kremer Pigmente pigmentas. Sukurtas naujas, patogus ir pakankamai tikslus IR spektroskopinis SiO2 kiekio CoO ir SiO2 mišiniuose (ribose tarp 9,1-50 mol%) ir kobalto pigmente smaltoje CoO×nSiO2 (ribose tarp 20 iki 50 mol%) nustatymo metodas. Zolių-gelių metodu susintetinti ir visapusiškai ištirti nauji kobalto pigmentai: špinelio struktūros kobalto aliuminatas CoAl2O4 ir chromatas CoCr2O4 bei kobalto, aliuminio ir neodimio oksidų mišiniai (CoAl1,75Nd0,25O4, CoAl1,5Nd0,5O4, CoAlNdO4), pasižymintys spalvinėmis keraminių pigmentų savybėmis. Pirmą kartą zolių-gelių metodu susintetinti ir visapusiškai ištirti nauji kobalto pigmentai: vienfazis perovskito struktūros neodimio kobaltatas NdCoO3, mišrūs perovskitiniai neodimio... [toliau žr. visą tekstą]

Atlikta istorinių kobalto pigmentų analogų Rentgeno spindulių difrakcinė analizė parodė, kad metodas efektyvus, nustatant kobalto šviesiai violetinį CoNH4PO4•H2O, kobalto mėlynąjį šviesų, ceruleumą ir kobalto žalsvai mėlyną CoO·ZnO, jų švino glazūrose, bet netinka aureolino [K3(Co(NO2)6]•3H2O, kobalto tamsiai violetinio Co3(PO4)2, kobalto mėlynojo tamsus, kobalto melsvai žalio ir smaltos CoO•nSiO2 nustatymui. IR spektroskopiniai tyrimai parodė, kad šis metodas efektyvus, kokybiškai nustatant neoksidinius kobalto pigmentus aureoliną, kobalto šviesiai violetinį, kobalto tamsiai violetinį jų švino glazūrose. Paprastu nusodinimo metodu susintetintas kobalto pigmentas violetinis šviesusis CoNH4PO4, pasižymintis analogiškomis fizikinėmis savybėmis, kaip ir komercinis Kremer Pigmente pigmentas. Sukurtas naujas, patogus ir pakankamai tikslus IR spektroskopinis SiO2 kiekio CoO ir SiO2 mišiniuose (ribose tarp 9,1-50 mol%) ir kobalto pigmente smaltoje CoO×nSiO2 (ribose tarp 20 iki 50 mol%) nustatymo metodas. Zolių-gelių metodu susintetinti ir visapusiškai ištirti nauji kobalto pigmentai: špinelio struktūros kobalto aliuminatas CoAl2O4 ir chromatas CoCr2O4 bei kobalto, aliuminio ir neodimio oksidų mišiniai (CoAl1,75Nd0,25O4, CoAl1,5Nd0,5O4, CoAlNdO4), pasižymintys spalvinėmis keraminių pigmentų savybėmis. Pirmą kartą zolių-gelių metodu susintetinti ir visapusiškai ištirti nauji kobalto pigmentai: vienfazis perovskito struktūros neodimio kobaltatas NdCoO3, mišrūs perovskitiniai neodimio... [toliau žr. visą tekstą] / X-ray diffraction analysis (XRD), infrared (IR) spectroscopy and scanning electron microscopy have been used for the characterization of cobalt-based pigments (Kremer Pigmente) and their lead-based glazes. It was also demonstrated that XRD analysis could be successfully used for the identification of cobalt pigments cobalt violet brilliant light CoNH4PO4•H2O, cobalt blue light, cerulean blue, cobalt green bluish CoO·ZnO in their glazes. However, only non-oxide cobalt pigments cobalt yellow [K3(Co(NO2)6]•3H2O, cobalt violet brilliant light and cobalt violet dark Co3(PO4)2 could be determined in their glazes using IR spectroscopy. The similarity of all SEM images of cobalt-based glazes let us to conclude, that the main morphological features of glazes are not dependent on the nature of cobalt pigment. The single phase cobalt violet light brilliant pigment has been synthesized using a simple co-precipitation approach. The characteristics of the obtained product were compared with those of a commercial sample purchased from Kremer Pigmente. For the first time to our knowledge, it was demonstrated that the characteristic Si-O absorption band at 812 cm-1 could be successfully used as indicator in the evaluation of molar ratio of CoO and SiO2 in their mixture. The novel method for the determination of SiO2 in physical mixtures of CoO ir SiO2 (in the range 9,1-50 %) or blue cobalt smalt pigment (CoO×nSiO2) (in the range 20-50 %) by FTIR spectroscopy is suggested. New cobalt-based... [to full text]