The aim of this study is focused on the experimental investigation of dynamic wear behavior of carbon black filled rubber compounds comprising pristine styrene butadiene rubber (SBR) together with incorporated SBR ground rubber (rubber powder). We also analyzed and described quantitatively the service conditions of some dynamically loaded rubber products, which are liable to wear (e.g. conveyor belts, tires). Beside the well-known standard test method to characterize wear resistance at steady-state conditions, we used an own developed testing equipment based on gravimetric determination of mass loss of rubber test specimen to investigate the influence of rubber powder content on dynamic wear depending on varying impact energy levels. Incorporation of SBR rubber powder in SBR rubber compounds increases wear. With increasing rubber powder content the wear at steady-state conditions progressively increases. However, the level of wear at dynamic loading conditions increases only once, but stays constant subsequently even with contents of incorporated rubber powder.

The aim of this study is concentrated on the experimental investigation of wear resistance of rubber powder modified rubber blends. Styrene-Butadiene-Rubber (SBR) blends applied for conveying belt top covers have been modified by ground rubber (rubber powder) based on SBR. We theoretically described the rubber wear mechanism due to loading conditions occurring at conveyor belts in the field, to simulate wear behavior of top cover rubber materials. An own developed testing equipment based on gravimetric determination of mass loss of rubber test specimen was used investigating dynamic wear with respect to fracture properties of top cover materials. Furthermore we investigated fatigue crack growth (FCG) data over a broad range of tearing energy by Tear Analyzer to characterize crack propagation behavior of rubber powder modified rubber blends. Thus, we demonstrate the influence of rubber powder on resistance against occurrence of fracture as well as dynamic wear as a function of the rubber powder content in rubber blends applied for conveying belt top covers.