Made available in DSpace on 2015-05-08T14:59:52Z (GMT). No. of bitstreams: 1 parte1.pdf: 2223950 bytes, checksum: 585473348fd57251708f0ba93240c53b (MD5) Previous issue date: 2008-10-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The presented work consists of a study for observation of the martensite kept in the transformation of martensite phase - austenite in a alloy of Ni - Al - V, with memory shape effect, into, a room temperature. We defined that the alloy with composition the 3,5% (in weigh) of nickel, presents better results when happens successive loading and downloading cancel though, 3,0% of deformation into a room temperature, back to austenite phase after retreat the load. Above 3,0% of deformation became evident the appearance of retrain martensite. For her identification it was necessary the development of on equipment to traction, as well as bodies of proofs dimensioned for that. The analyses were done through X rays diffraction of optical microscopy and rehearsal of traction. / O trabalho apresentado consta de um estudo para observação da martensita retida na transformação de fase de martensita austenita em uma liga de Ni Al V, com efeito de memória de forma, a temperatura ambiente. Definimos que a liga com composição 3,5% (em peso) de níquel, apresenta melhor resultado quando submetida a carregamento e descarregamento sucessivos; chegando a 3,0% de deformação a temperatura ambiente, retornando ao estado austenítico depois de retirada a carga. Acima de 3,0% de deformação, evidencia-se o surgimento de martensita retida. Para sua identificação, foi necessária a confecção de um equipamento para tracionar, como também corpos de prova dimensionados para tanto. As observações foram realizadas através de análises de raios X, microscopia ótica e ensaios de tração.