Orientador : Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-03T09:08:15Z (GMT). No. of bitstreams: 1 Lopes_MuriloBaena_M.pdf: 3159373 bytes, checksum: ad00b137bd99ef0ce27f90caa4071c10 (MD5) Previous issue date: 2003 / Resumo: O processo de refundição é rotineiramente utilizado por laboratórios protéticos para a confecção de próteses e restaurações fundidas. Este trabalho propõe avaliar os desajustes cervical e interno de coroas totais metálicas fundidas com liga de Pd-Ag (Pors-on 4, Degussa S/A), sob influência da refundição e de diferentes configurações marginais (ombro reto, ombro biselado em 20° e chanfro reto em 45°), com a fonte de calor de fundição gás-oxigênio. Foram confeccionados 30 troquéis de alumínio, sendo 10 para cada tipo de término cervical, sobre os quais foram encerados coroas com auxílio de uma matriz cilíndrica metálica bipartida, com o propósito de padronizar a espessura das paredes. Os padrões de cera foram incluídos em revestimento aglutinado por fosfato (Deguvest) e a fundição realizada após aquecimento em forno (EDG). Posteriormente, as coroas metálicas foram assentadas nos respectivos troquéis, sob carga estática de 9 kgf, e a leitura do desajuste cervical realizada com um microscópio metrológico (Carl Zeiss), provido de um relógio comparador digital (Mitutoyo, série 543 IDF), com precisão de 0,001 mm. Em seguida, as amostras foram incluídas em resina de poliéster e após a polimerização, seccionadas ao meio no sentido longitudinal, para as leituras da adaptação interna, efetuadas da mesma maneira como descrito para a adaptação cervical. Os resultados foram submetidos à análise de variância e ao teste de Tukey (5%) e demonstraram que a liga virgem apresentou melhor adaptação, tanto cervical quanto interna, quando comparada com a liga refundida; o tipo de término não exerceu influência nos desajustes, quando a coroa foi fundida com liga virgem. Para a liga refundida, o término em ombro reto demonstrou valores de adaptação estatisticamente superiores ao ombro biselado em 20°, sendo que o chanfro em 45° não diferiu de ambos / Abstract: The metal recast process is traditionally used by dental laboratories to produce prosthesis and restorations. The aim of this study was to evaluate the cervical and internal fits of total metal crowns, which were casted and recasted with palladium-silver alloy (Pors-on 4, Degussa S/A), with three different marginal configuration: straight shoulder, 20-degree bevel shoulder and 45-degree chamfered. The oxigen-gas heat source was used to melt the alloy. Thirty aluminium dies were made, 10 for each margin configuration. The dies were waxed using a cylindrical metal matrix to standardize the thickness of the walls. The wax patterns were invested in a phosphate investment (Deguvest) and cast after heated in an oven (EDG), according to the manufacturer's instruction. Afterwards, the specimens were seated on the dies, with a static load of 9 kgf. The marginal discrepancy was measured with a metric microscope (Carl Zeiss), using a digital micrometer (Mitutoyo, 543 IDF series), with accuracy of 0,001 mm. The samples were embedding in polyester resin and longitudinally cut for internal discrepancy measurements, measured by the same way made in the marginal discrepancy. The results were submitted to analysis of variance and Tuckey's test (5%) and indicated that the new metal presented better adaptation than the recast one for both marginal and internal discrepancy measurements. The margin designs didn't have any influence when new metal were used. For recast metal, the straight shoulder was better than the 20-degree bevel shoulder and the 45-degree chamfered didn't differ from anyone / Mestrado / Mestre em Materiais Dentários

Devido à grande demanda em se obter materiais magnéticos para aplicação na área de leitura/gravação magnética e armazenamento de dados, filmes finos de ligas magnéticas tem sido extensivamente estudados como materiais promissores. Este trabalho trata do estudo da eletrodeposição galvanostática de ligas magnéticas de CoPd e FePd. Para a obtenção das ligas CoPd foram variados parâmetros como densidade de corrente, pH e concentração dos metais na solução. Dois aditivos foram utilizados nos banhos: para banhos de cloreto e sulfamato a glicina (Gly) e para sulfato o ácido 5-sulfosalicílico (5-ASS). O teor de Co nas ligas obtidas variou de 6,4 a 94,0 %at. e a eficiência de corrente máxima foi de 88,1 % para um banho de cloreto onde a razão molar [Co2