Orientador: Wolney Luiz Stolf / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-21T23:40:05Z (GMT). No. of bitstreams: 1 Maia_HamiltonPires_D.pdf: 3805288 bytes, checksum: 07f3aee967f501e0780138540fb87554 (MD5) Previous issue date: 1996 / Resumo: Determinou-se o percentual volumétrico de fase y2 em 768 corpos de prova obtidos de seis ligas para amálgama dentário, através do teste colorimétrico quantitativo desenvolvido por KROpp33. As seis ligas selecionadas apresentavam conteúdo de cobre variando entre 12 e 24% e partículas dos tipos esferoidal, limalha ou mistura. Oito amostras de liga/mercúrio, proporcionadas por pesagem, foram, individualmente, trituradas mecanicamente durante 10, 15, 20 ou 25 segundos constituindo-se nos corpos de prova que, posteriormente, foram armazenados a 37°C :t 1 durante 1 hora, 24 horas, 1 semana ou 2 semanas. Após a armazenagem mediase o comprimento do corpo de prova que, em seguida, era imerso em uma solução de 5 ml de ácido cítrico a 5% e 1 ml de ácido fosfomolíbdico a 1%. Decorridos 10 minutos, sob agitação mecânica, o líquido era transferido para um tubo de ensaio e levado ao espectrofotômetro, regulado em 578 nanômetros, para leitura da densidade óptica. Através deste teste colorimétrico quantitativo verificou-se o aparecimento de uma coloração azul, na solução para leitura da densidade óptica, relacionada diretamente à quantidade de fase y2 do corpo de prova visto que 'o estanho liberado pela ação do ácido cítrico sobre a fase y2 reduz o ácido fosfomolíbdico em molibdênio azul. Os percentuais volumétricos de y2 foram determinados utilizando-se a fórmula proposta por KROpp33. A análise de variância indicou que os resultados foram estatisticamente significantes (p < 0,01). O teste de TUK.EY para as variações entre os percentuais de y2 da mesma variável apresentou significância estatística. O conteúdo de y2 das ligas Kerrtyn, Dispersalloy, Alpha-E, Alpha-M, DFL Alloy e Alpha-L aumentou nesta ordem. Os percentuais de y2 aumentaram do menor para o maior tempo de trituração enquanto que, para os períodos de armazenagem, diminuíram do menor para o maior período / Abstract: Using the quantitative colorimetric test developed by KROpp35, the volume percentage ofthe y2 phase was deternrined for 768 test specimens obtained from six dental amalgam alloys. The selected alloys, of which 3 were commercial and 3 experimental, presented a copper content varying between 12 and 24%, and particles of the spheroid, lathe-cut, or mixture types. Eight samples of mercury/alloy, apportioned per weight, were individually ground for 10, 15, 20 or 25 seconds. The lest specimens, obtained by mechanical grinding, were stored ar 37°C :t 1°C for 1 hour, 24. hours, 1 week or 2 weeks. After storage, the test specimen had its lenght measured, was immersed in 5 ml of a 5% citric acid and 1 ml of a 1% phosphomolybdic acid solution. The liquid, after 10 minutes under mechanical agitation, was transfered to a test tube and taken to the spectrophotometer set at 578 n, to give an optic density reading. The quantitative colorimetric test was based on the appearance of a blue coloring in the optical density reading solution directly related to the amount of y2 phase in the test specimen. Tin liberated through the action of citric acid in the y2 phase reduces the phosphomolibdic acid to bluer molybdenum. Volume percentuals of y2 were determined using KROPP's formule33. Variance analysis showed results to be statistically significant (p < 0.01). TUKEY's test for the variation between y2 percentages of the same variable presented statistic significance. The Kerrtyn, Dispersalloy, Alpha-E, Alpha-M, DFL Alloy, and Alpha-L alloys showed, in this order, an increase in the y2 contents. Percentages of y2 increased from shorter to longer grinding time, whereas for storage periods the percentages were reduced from the shorter to the longer period / Doutorado / Materiais Dentarios / Doutor em Ciências

Made available in DSpace on 2016-12-08T17:19:16Z (GMT). No. of bitstreams: 1 Randolfo Christiano Koster.pdf: 64402 bytes, checksum: baaccbce80d028291d827fb8d22873f8 (MD5) Previous issue date: 1998-07-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / A metalurgia do pó tem vindo de encontro as necessidades de redução de processos de manufatura convencionais. Em muitas circunstancias, no entanto a união de peças produzidas por metalurgia do pó necessitam ser unidas às mesmas ou a materiais manufaturados por processo como parafusamento rebitagem e soldagem. Opresente trabalho é uma investigação experimental da soldabilidade por resistência e brasagem com liga Bag2 de ligas ferrosinterizadas. Os experimentos conduzidos visam traçar um comparativo entre as peças obtidas por processo de manufatura normais que envolvem usinagem e a metalurgia do pó. Para tanto, optou-se por reduzir um componente manufaturado e submete-lo às mesmas condições de soldabilidade e brasagem. Uma matriz de compactação simples efeito foi desenvolvida para obtenção dos componentes sinterizados. Devido à aplicação do componente de estudo na parte estrutural de um compressor hermético, testes de estanqueidade foram desenvolvidos à pressão de 20 bar. Os resultados dos testes de brasagem e soldagem por resistência foram muito satisfatório, estando de acordo com a literatura existente no aspecto da metalurgia do pó, foram insatisfatórios quando aplicada a componentes sem tratamento superficial que pudesse selar as porosidades interconectadas.