Objective: The aim of this study was to analyses the relationship between the degree of conversion of double bonds of self-etching adhesives and microshear bond strength on dentin. Materials and methods: For microshear testing twenty third molar caries free were selected. They had their crowns sectioned longitudinally so as to obtain slices that were randomly chosen and divided into four groups according to the adhesive system, Single Bond (SB), Clearfil SEBond (CL) , Adhese (AD) and Gbond (GB). The slices were included into epoxy resin, and then cylindrical restorations were built with an area of 1.0 mm in diameter and 2.0 mm in height, around ten restorations per group, using a starch matrix. After 24 hours the specimens were tested for bond strength. To analyze the degree of conversion of these systems, a drop of adhesive was dispensed on a glass plate and after 20 seconds polymerized, forming a film of adhesive. After 24 hours, these films were pulverized and mixed with potassium bromide, pressed in a hydraulic press to form an insert for analysis with the spectrophotometer - FT-IR. The data of shear bond strength and degree of conversion of each specimen were submitted to ANOVA and Tukey s test (p = 0.05). Results: The SB adhesive system had mean values of bond strength statistically higher than AD and GB, but no statistical difference was found with Cl. Among the self-etching systems, the highest average shear bond strength was achieved with the application of the union CL, followed by GB and AD systems, which were not statistically different. Regarding the degree of conversion, similar statistical results were found for the systems SB and CL, and despite the SB had a higher average it, did not differ from CL. The adhesive system SB and CL showed higher values in AD and GB. The AD, showed values higher than the GB. Conclusion: The degree of conversion is affected by several factors related to the complex mixture of adhesive systems, which somehow contribute to their bond strength. / Objetivo: O objetivo desse estudo foi avaliar o grau de conversão de sistemas adesivos autocondiconantes em dentina e correlacioná-los com a resistência ao teste de microcisalhamento. Materiais e Métodos: Para o ensaio de microcisalhamento foram selecionados vinte terceiros molares livres de cárie, os quais tiveram suas coroas seccionadas longitudinalmente de modo a se obter fatias, que, aleatoriamente, foram divididas em quatro grupos, de acordo com o sistema adesivo uilizado, Single Bond (SB), Clearfil SE Bond (CL), Adhese (AD) e Gbond (GB). As fatias foram incluídas em tubos de PVC com resina acrílica e, em seguida, foram construídas restaurações cilíndricas com uma área de 1,0 mm de diâmetro e 2,0 mm de altura, em torno de dez restaurações por grupo, por meio de uma matriz de amido. Após 24 horas, os corpos de prova foram submetidos ao ensaio de microcisalhamento. Para análise do grau de conversão desses sistemas, uma gota do adesivo foi dispensada sobre uma placa de vidro e, após 20 segundos, foram fotopolimerizadas, formando uma película de adesivo. Após 24h, essas películas foram pulverizadas e misturadas com brometo de potássio, prensadas em prensa hidráulica de modo a formar uma pastilha para análise no espectofotômetro - FT-IR. Os dados obtidos da resistência de união e do grau de conversão foram submetidos à análise de variância e teste de Tukey (p = 0.05). Resultados: O sistema de união SB apresentou valores médios de resistência de união ao microcisalhamento estatisticamente superior AD e GB, mas não apresentou diferença estatística em relação ao sistema Cl. Dentre os sistemas autocondicionantes, as maiores médias no ensaio mecânico foram obtidas com a aplicação do sistema de união CL, seguido pelos sistemas AD e GB, que não foram estatisticamente diferentes entre si. Em relação ao grau de conversão, resultados estatísticos semelhantes foram encontrados para os sistemas SB e CL, que, apesar do SB apresentar uma maior média, não diferiu do CL. O sistema adesivo SB e CL apresentaram valores médios superiores ao AD e GB. O AD, que por sua vez, apresentou valores médios maiores que o GB. Conclusão: O grau de conversão é afetado por diversos fatores relacionados à mistura complexa dos sistemas adesivos, que, de certo modo, repercutirá na sua resistência de união.

Made available in DSpace on 2014-06-11T19:31:05Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-03-19Bitstream added on 2014-06-13T18:41:40Z : No. of bitstreams: 1 costa_sxs_dr_arafo.pdf: 852844 bytes, checksum: 8945fe6817e7f7f0051c98cb920416e1 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho, dividido em três estudos, foi avaliar: (1) a influência da utilização de diferentes fontes de luz e métodos de fotoativação sobre o grau de conversão e a contração de polimerização de uma resina composta nanoparticulada; (2) a influência da utilização dos diferentes métodos de fotoativacao, disponibilizados por aparelhos LED de 2a geração, sobre a contração volumétrica das resinas compostas microhíbrida e nanopartículada e (3) as propriedades térmicas e o grau de conversão das resinas compostas microhíbrida e nanopartículada, submetidas aos diferentes métodos de fotoativação disponibilizados por aparelhos LED de 2a geracao. No primeiro estudo, o grau de conversão (GC) foi avaliado pelo metodo da espectroscopia infravermelha transformada de Fourier (FT-IR) e as forças de contração (C) mensuradas em máquina de ensaios universal (EMIC). Os dados obtidos para o GC e C foram analísados estatísticamente pelo teste da análise de variancia (ANOVA), sendo que para as forças de contração, a correção de Welch e o teste Tamhane também foram empregados. No segundo estudo, a contração volumétrica foi avaliada por um mecanismo de vídeo e imagem (AcuvolR/Bisco) e os dados obtidos foram análisados estatísticamente pelos testes ANOVA e Tukey. No terceiro estudo, o método da calorimetria exploratória diferencial foi empregado para avaliar a temperatura de transição vitrea (Tg) e de degradação dos materiais e o GC por FTIR. Os dados relativos ao GC foram análisados estatísticamente pelos testes ANOVA e Tukey. Os resultados demonstraram diferenças na contração de polimerização de acordo com o método de fotoativação empregado. No primeiro e segundo estudos, mesmo empregando diferentes metodologias, o método de fotoativação contínuo apresentou os maiores valores de contração. Por outro lado,o GC não... / The aim of this work, divided into three studies, was evaluate: (1) the influence of different light sources and photo-activation methods on degree of conversion and polymerization shrinkage of a nanocomposite resin; (2) the influence of different photo-activation methods, available by the 2nd generation LED light-curing units, on the volumetric shrinkage of microhybrid and nanocomposite resins and (3) thermal properties and degree of conversion of microhybrid and nanocomposite resins submitted to different photo-activation methods available by 2nd generation LED light-curing units. In the first study, degree of conversion (DC) was evaluated by Fourier transform infrared spectroscopy (FT-IR) and shrinkage forces (S) were measured in a universal testing machine (EMIC). The data obtained for DC and S were analyzed by Analysis of Variance test (ANOVA) and for S Welch’s correction and Tamhane’s tests were also employed. In the second study, volumetric shrinkage was evaluated by video-imaging device (AcuvolR/Bisco) and data were analyzed by ANOVA and Tukey’s test. In the third study, differential scanning calorimetry was used in order to observe glass transition temperature (Tg) and degradation peak of the materials and DC was evaluated for FT-IR. The DC data were analyzed by ANOVA and Tukey’s test. The results showed differences in the polymerization shrinkage according to photo-activation method employed. In the first and second studies, the continuous photo-activation methods presented the highest values for shrinkage even though different methodologies were used to assess. Moreover, DC was not influenced by the photo-activation method but was influenced by light sources. The lowest DC values were observed for halogen light-curing unit. In the second study beyond the influence of the photo-activation... (Complete abstract click electronic access below)

Made available in DSpace on 2014-06-11T19:31:05Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-08-10Bitstream added on 2014-06-13T19:40:56Z : No. of bitstreams: 1 queiroz_rs_dr_arafo.pdf: 679998 bytes, checksum: 47166f3c2a2f40adf0235d9237b0bd24 (MD5) / Esse estudo se propõe a avaliar as propriedades ópticas (Fluorescência e Absorbância) da resina composta fotoativada (4 SEASONS®) utilizando aparelho fotopolimerizador convencional (luz Halógena Ulttralux - DabiAtlant), e aparelho emissor de Diodo (Radii – SDI e Ultralume Led 5- Ultradent), em função da fonte de luz foto-ativadora, cor, espessura e tempo de armazenamento em saliva artificial. Foram confeccionadas 5 amostras (10,0x1,0 mm) para cada grupo experimental. Para a realização do teste de Absorbância foi utilizado aparelho espectrofotômetro de luz visível (Diode Array Spectrophotometer, HP – Serial Number: 8452-A). Para a obtenção dos valores de fluorescência emitida pelas amostras, foi utilizado espectrofotômetro (SPEX TRIAX FLUOROLOG 3, Jobin Yvon – Serial Number: 0135B-3-99). Os resultados foram julgados estatisticamente conforme a interação entre os fatores de avaliação nos distintos trabalhos. Pode-se concluir que a fonte de luz fotoativadora influenciou apenas a emissão fluorescente da resina de cor TC, não tendo efeito negativo na absorbância; o aumento na espessura da amostra acarretou uma diminuição na emissão fluorescente e na absorbância de todas as cores da resina, independente da fonte de luz; e as diferentes cores da resina exibiram diferentes emissões fluorescentes e absorbância... / The arm of this study is to evaluate optical properties (fluorescence and Absorbance) of a composite resin (4 SEASONS®) using light curing units (LCUs)-(QTH - Ulttralux – DabiAtlant and LEDs Radii – SDI and Ultralume Led 5- Ultradent) in function of LCUs, shade, thickness and storage times. 5 samples were prepared for each experimental group. To perform the Absorbance test, was used of UV-Vis spectrophotometer (Diode Array Spectrophotometer, HP – Serial Number: 8452-A). To obtain the fluorescence emission by samples, we used a spectrophotometer (SPEX TRIAX FLUOROLOG 3, Jobin Yvon – Serial Number: 0135B-3-99). The results were deemed statistically as the interaction between the evaluation factors in the different works. It can be concluded that the LCUs only influenced the fluorescent emission of resin color TC, having no negative effect on the absorbance; the increase in thickness of the sample decrease the fluorescent emission and absorbance for colors of the resin, independent of the LCUs; different colors of resin exhibited different fluorescent emission and absorbance.

Orientador: Sizenando de Toledo Porto Neto / Banca: Alberto Magno Gonçalvez / Banca: Sicknan Soares da Rocha / Banca: José Roberto Cury Saad / Banca: Marcelo Ferrarezi de Andrade / Resumo: Esse estudo se propõe a avaliar as propriedades ópticas (Fluorescência e Absorbância) da resina composta fotoativada (4 SEASONS®) utilizando aparelho fotopolimerizador convencional (luz Halógena Ulttralux - DabiAtlant), e aparelho emissor de Diodo (Radii - SDI e Ultralume Led 5- Ultradent), em função da fonte de luz foto-ativadora, cor, espessura e tempo de armazenamento em saliva artificial. Foram confeccionadas 5 amostras (10,0x1,0 mm) para cada grupo experimental. Para a realização do teste de Absorbância foi utilizado aparelho espectrofotômetro de luz visível (Diode Array Spectrophotometer, HP - Serial Number: 8452-A). Para a obtenção dos valores de fluorescência emitida pelas amostras, foi utilizado espectrofotômetro (SPEX TRIAX FLUOROLOG 3, Jobin Yvon - Serial Number: 0135B-3-99). Os resultados foram julgados estatisticamente conforme a interação entre os fatores de avaliação nos distintos trabalhos. Pode-se concluir que a fonte de luz fotoativadora influenciou apenas a emissão fluorescente da resina de cor TC, não tendo efeito negativo na absorbância; o aumento na espessura da amostra acarretou uma diminuição na emissão fluorescente e na absorbância de todas as cores da resina, independente da fonte de luz; e as diferentes cores da resina exibiram diferentes emissões fluorescentes e absorbância... / Abstract: The arm of this study is to evaluate optical properties (fluorescence and Absorbance) of a composite resin (4 SEASONS®) using light curing units (LCUs)-(QTH - Ulttralux - DabiAtlant and LEDs Radii - SDI and Ultralume Led 5- Ultradent) in function of LCUs, shade, thickness and storage times. 5 samples were prepared for each experimental group. To perform the Absorbance test, was used of UV-Vis spectrophotometer (Diode Array Spectrophotometer, HP - Serial Number: 8452-A). To obtain the fluorescence emission by samples, we used a spectrophotometer (SPEX TRIAX FLUOROLOG 3, Jobin Yvon - Serial Number: 0135B-3-99). The results were deemed statistically as the interaction between the evaluation factors in the different works. It can be concluded that the LCUs only influenced the fluorescent emission of resin color TC, having no negative effect on the absorbance; the increase in thickness of the sample decrease the fluorescent emission and absorbance for colors of the resin, independent of the LCUs; different colors of resin exhibited different fluorescent emission and absorbance. / Doutor

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-08-05Bitstream added on 2014-06-13T18:51:43Z : No. of bitstreams: 1 caldas_mrgr_me_arafo.pdf: 492580 bytes, checksum: 6bbf6b8719f88e58ede102ebb27a6c6c (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho, dividido em dois estudos, foi avaliar: (1) a influência dos tipos de ponteiras (fibra óptica e polímero) utilizadas em um aparelho fotoativador à base de LED (Ultrablue IS - DMC) sobre o grau de conversão e dureza de uma resina composta microhíbrida (FiltekTM Z250) e uma nanoparticulada (FiltekTM Supreme XT); e (2) a influência dos tipos de ponteiras (fibra óptica e polímero) utilizadas em um aparelho fotoativador à base de LED (Ultrablue IS - DMC) sobre a resistência à compressão de uma resina composta microhíbrida (FiltekTM Z250) e uma nanoparticulada (FiltekTM Supreme XT). No primeiro estudo, para os testes de grau de conversão (GC) e dureza, cinco corpos-de-prova com 4 mm de diâmetro e 2 mm de espessura (ISO 4049), foram confeccionados para cada grupo avaliado. O grau de conversão foi analisado pelo Espectrofotômetro Nexus - 470 FT-IR. Para o teste de dureza Vickers, os corpos-de-prova foram levados ao Durômetro Micromet 2100 (Buehler, EUA) onde foi utilizada uma carga de 50 gramas força (gf) e tempo de 30 segundos. Para cada corpo-de-prova oito medidas foram realizadas nas superfícies de topo e base. Os dados obtidos para o GC e dureza foram analisados estatisticamente pelo teste de Análise de Variância (ANOVA) e Tukey. No segundo estudo, para o teste de resistência à compressão foram confeccionados oito corpos-de-prova com 8 mm de altura e 4 mm de diâmetro. O teste foi realizado na máquina de ensaio universal EMIC com célula de carga de 5 kN à velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente pelo teste ANOVA e o teste Tamhane. Os resultados demonstraram que o GC e dureza foram influenciados pelas ponteiras, sendo a dureza também influenciada pelo tipo de resina composta utilizada. A resina composta microhíbrida fotoativada com a ponteira de fibra óptica apresentou maiores valores do GC e dureza... / The aim of this work, divided into two studies, was evaluate: (1) the influence of types of light guide tips (fiber optic and polymer) used in a photo-activation based on LED (Ultrablue IS - DMC) on the degree of conversion and hardness one microhybrid FiltekTM Z250 and one nanofilled FiltekTM Supreme XT composite resins; and (2) the influence of types of light guide tips (fiber optic and polymer) used in a photo-activation based on LED (Ultrablue IS - DMC) on the compressive strength of one microhybrid FiltekTM Z250 and one nanofilled FiltekTM Supreme XT composite resins. In the first study, to test the degree of conversion (GC) and hardness, five samples 4 mm in diameter and 2 mm in thickness (ISO 4049) were made for each group evaluated. The degree of conversion was evaluated by Fourier transform infrared spectroscopy (FT-IR). For the Vickers hardness test, the samples were brought to the durometer Micromet 2100 (Buehler, USA) where was used a load of 50 gram force (gf) and time of 30 seconds. For each sample test measurements were performed eigth measures on the surfaces of top and bottom. The data obtained for the GC and hardness test were statistically analyzed by Analysis of Variance (ANOVA) and Tukey’s test. In the second study to test the compressive strength eight samples (4 mm in diameter and 8 mm in thickness) were made for each group evaluated, and the test was conducted in a universal testing machine EMIC with load cell 5 kN and speed of 0,5 mm/min. The data were statistically analyzed by ANOVA test and Tamhane’s test. The results showed that the GC and hardness were influenced by the light guide tip, and the hardness also influenced by the type of resin used. The microhybrid composite resin photo-activated with the fiber optic light tip had higher values of GC and hardness. The lowest values of GC and hardness were observed with nanofilled composite resin photoactivated... (Complete abstract click electronic access below)

Resumo: O objetivo deste trabalho, dividido em dois estudos, foi avaliar: (1) a influência dos tipos de ponteiras (fibra óptica e polímero) utilizadas em um aparelho fotoativador à base de LED (Ultrablue IS - DMC) sobre o grau de conversão e dureza de uma resina composta microhíbrida (FiltekTM Z250) e uma nanoparticulada (FiltekTM Supreme XT); e (2) a influência dos tipos de ponteiras (fibra óptica e polímero) utilizadas em um aparelho fotoativador à base de LED (Ultrablue IS - DMC) sobre a resistência à compressão de uma resina composta microhíbrida (FiltekTM Z250) e uma nanoparticulada (FiltekTM Supreme XT). No primeiro estudo, para os testes de grau de conversão (GC) e dureza, cinco corpos-de-prova com 4 mm de diâmetro e 2 mm de espessura (ISO 4049), foram confeccionados para cada grupo avaliado. O grau de conversão foi analisado pelo Espectrofotômetro Nexus - 470 FT-IR. Para o teste de dureza Vickers, os corpos-de-prova foram levados ao Durômetro Micromet 2100 (Buehler, EUA) onde foi utilizada uma carga de 50 gramas força (gf) e tempo de 30 segundos. Para cada corpo-de-prova oito medidas foram realizadas nas superfícies de topo e base. Os dados obtidos para o GC e dureza foram analisados estatisticamente pelo teste de Análise de Variância (ANOVA) e Tukey. No segundo estudo, para o teste de resistência à compressão foram confeccionados oito corpos-de-prova com 8 mm de altura e 4 mm de diâmetro. O teste foi realizado na máquina de ensaio universal EMIC com célula de carga de 5 kN à velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente pelo teste ANOVA e o teste Tamhane. Os resultados demonstraram que o GC e dureza foram influenciados pelas ponteiras, sendo a dureza também influenciada pelo tipo de resina composta utilizada. A resina composta microhíbrida fotoativada com a ponteira de fibra óptica apresentou maiores valores do GC e dureza... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this work, divided into two studies, was evaluate: (1) the influence of types of light guide tips (fiber optic and polymer) used in a photo-activation based on LED (Ultrablue IS - DMC) on the degree of conversion and hardness one microhybrid FiltekTM Z250 and one nanofilled FiltekTM Supreme XT composite resins; and (2) the influence of types of light guide tips (fiber optic and polymer) used in a photo-activation based on LED (Ultrablue IS - DMC) on the compressive strength of one microhybrid FiltekTM Z250 and one nanofilled FiltekTM Supreme XT composite resins. In the first study, to test the degree of conversion (GC) and hardness, five samples 4 mm in diameter and 2 mm in thickness (ISO 4049) were made for each group evaluated. The degree of conversion was evaluated by Fourier transform infrared spectroscopy (FT-IR). For the Vickers hardness test, the samples were brought to the durometer Micromet 2100 (Buehler, USA) where was used a load of 50 gram force (gf) and time of 30 seconds. For each sample test measurements were performed eigth measures on the surfaces of top and bottom. The data obtained for the GC and hardness test were statistically analyzed by Analysis of Variance (ANOVA) and Tukey's test. In the second study to test the compressive strength eight samples (4 mm in diameter and 8 mm in thickness) were made for each group evaluated, and the test was conducted in a universal testing machine EMIC with load cell 5 kN and speed of 0,5 mm/min. The data were statistically analyzed by ANOVA test and Tamhane's test. The results showed that the GC and hardness were influenced by the light guide tip, and the hardness also influenced by the type of resin used. The microhybrid composite resin photo-activated with the fiber optic light tip had higher values of GC and hardness. The lowest values of GC and hardness were observed with nanofilled composite resin photoactivated... (Complete abstract click electronic access below) / Orientador: Marcelo Ferrarezi de Andrade / Coorientador: Alessandro Nara de Souza Rastelli / Banca: Silmara Aparecida Milori Corona / Banca: José Roberto Cury Saad / Mestre