This thesis describes an investigation which was carried out under the Interdisciplinary Higher Degres (IHD) Scheme of The University of Aston in Birmingham. The investigation, which involved joint collaboration between the IHD scheme, the Department of Mechanical Engineering, and G.E.C. Turbine Generators Limited, was concerned with hydrostatic bearing characteristics and of how hydrostatic bearings could be used to enable turbine generator rotor support impedances to be controlled to give an improved rotor dynamic response. Turbine generator rotor critical speeds are determined not only by the mass and flexibility of the rotor itself, which are relatively easily predicted, but also by the dynamic characteristics of the bearing oil film, pedestal, and foundations. It is because of the difficulty in accurately predicting the rotor support characteristics that the designer has a problem in ensuring that a rotor's normal running speed is not close to one of its critical speeds. The consequence of this situation is that some rotors do have critical speeds close to their normal running speed and the resulting high levels of vibration cause noise, high rotor stresses, and a shortening of bearing life. A combined theoretical and experimental investigation of the effects of mounting the normal rotor journal bearing in a hydrostatic bearing was carried out. The purpose of the work was to show that by changing the oil flow resistance offered by capillaries connecting accumulators to the hydrostatic bearing, the overall rotor support characteristics could be tuned to enable rotor critical speeds to be moved at will. Testing of a combined journal and hydrostatic bearing has confirmed the theory of its operation and a theoretical study of a full size machine showed that its critical speed could be moved by over 350 rpm and that its rotor vibration at running speed could be reduced by 80%.

This research initiates a study of the mechanics of four roll plate bending and provides a methodology to investigate the process experimentally. To carry out the research a suitable model bender was designed and constructed. The model bender was comprehensively instrumented with ten load cells, three torquemeters and a tachometer. A rudimentary analysis of the four roll pre-bending mode considered the three critical bending operations. The analysis also gave an assessment of the model bender capacity for the design stage. The analysis indicated that an increase in the coefficient of friction in the contact region of the pinch rolls and the plate would reduce the pinch resultant force required to end a plate to a particular bend radius. The mechanisms involved in the four roll plate bending process were investigated and a mathematical model evolved to determine the mechanics of four roll thin plate bending. A theoretical and experimental investigation was conducted for the bending of HP30 aluminium plates in both single and multipass bending modes. The study indicated that the multipass plate bending mechanics of the process varied according to the number of bending passes executed and the step decrement of the anticipated finished bend radius in any two successive passes (i.e. the bending route). Experimental results for single pass bending indicated that the rollers normally exert a higher bending load for the steady-continous bending with the pre-inactive side roll oper?tive. For the pre-bending mode and the steady-continous bending mode with the pre-active side roll operative, the former exerted the higher loads. The single pass results also indicated that the force on the side roll, the torque and power steadily increased as the anticipated bend radius decreased. Theoretical predictions for the plate internal resistance to accomplish finished bend radii of between 2500mm and 500mm for multipass bending HP30 aluminium plates, suggested that there was a certain bending route which would effectively optimise the bender capacity.

The problem of variation in weld crack susceptibility caused by small variations in alloy and impurity elements for the 70-30 cupro-nickel alloy has been investigated. Both wrought and cast versions of the alloy have been studied, the main techniques employed being the Varestraint test and weld thermal simulation. In the wrought alloys, cracking has been found to occur mainly in the weld metal, whilst in the cast alloys cracking is extensive in both weld metal and heat affected zone. The previously reported effects of certain impurities (P,S,Si) in increasing cracking have been confirmed, and it has also been shown that Ti and Zr may both have a crack promoting effect at levels commonly found in cupro-nickels, whilst C can interact with several of the other elements investigated to produce a beneficial effect. The testing carried out using the weld thermal simulator has shown that a relationship does exist between hot ductility and weld cracking. In particular, the absence of the peak in ductility in the range 1100°C-900°C on cooling from a temperature near to the solidus is indicative of a highly crack susceptible alloy. Principal practical implications of the investigation concern the relationship of weld metal cracking to alloy composition, especially the level of certain impurities. It would appear that the upper limits permitted by the alloy specifications are unrealistically high. The introduction of lower impurity limits would alleviate the current problems of variability in resistance to cracking during welding.

No description available.

Five linepipe type steels were produced in order to study the effect of calcium and magnesium injection on their final properties. Two of these steels were at the extremes of the sulphide range i.e. 0.003 and 0.017% sulphur with no injection attempted; thereby, providing standards to compare with the injected steels. The oxygen level varied from 21 to 63 p.p.m. The cast ingots were controlled-rolled and isothermally rolled in order to study the deformation characteristics of the residual non-metallic inclusions. The structure and cleanliness of these steels was evaluated metallographically using the light microscope, SEM, and image analysis and the results related to their Charpy toughness and HIC resistance. Increasing sulphur levels decreased final properties of the steel. In the untreated state, with as little as 0.003% sulphur, test orientation was highly influential. Modification of sulphur bearing steels was achieved with low modifying element to sulphur ratios provided that the oxygen content was very low. Injection of calcium into steel caused interaction with oxide and sulphide inclusions which was biased toward oxide reduction relative to sulphur removal. Magnesium again reduced oxides and appeared to be linked with aluminia containing inclusions in the final product. It produced improved toughness values relative to a similar sulphur containing calcium treated steel. The results of this work could be extended to establish the mechanism of inclusion modification with magnesium additions to sulphur bearing steels.

The available literature has been surveyed to determine the parameters affecting fuelling requirements of spark ignition engines and their relation to engine performance and emissions. Theories and experiment relating to two phase and multi-component flows have also been examined and the techniques employed in the measurement of droplet sizes and liquid wall films have been reviewed. Following preliminary steady flow visualisation experiments to examine the trajectories of droplets discharging from the valve port an extensive practical investigation of the spectrum of droplet sizes formed by the break up of the wall film has produced results which have been correlated in terms of the important fuel and airflow parameters. It is concluded that the Sauter mean diameter of droplets formed by the break up of the wall film will vary between 70 and 150 m, depending on the operating conditions of the engine. The spectra of droplet sizes measured show that a significant proportion of the total mass of the wall film breaks into drops which will be too large to burn completely and, by comparison with measurements of unburned hydrocarbon emissions from engines supplied with a homogeneous mixture of air and gaseous hydrocarbons, it is concluded that the droplets from the wall film are likely to increase emissions by 50%.

No description available.

This investigation examined the process of the longitudinal rolling of tubes through a set of three driven grooved rolls. Tubes were rolled with or without internal support i.e. under mandrel rolling or sinking conditions. Knowledge was required of the way in which the roll separating force and rolling torque vary for different conditions of rolling. The objective of this work being to obtain a better understanding and optimization of the mechanics of the process. The design and instrumentation of a complete experimental three-roll mill for the rolling of lead tube as an analogue material for hot steel, with the measurement of the individual roll force and torque is described. A novel type of roll load cell was incorporated and its design and testing discussed. Employing three roll sizes of 170 mm, 255 mm and 340 mm shroud diameter, precise tube specimens of various tube diameter to thickness ratios were rolled under sinking and mandrel rolling conditions. To obtain an indication of the tube-roll contact areas some of the specimens were partially rolled. For comparative purposes the remaining tubes were completely rolled as a single pass. The roll forces, torques and tube parameters e.g. reduction of area, D/t ratio, were collated and compared for each of the three roll diameters considered. The influence of friction, particularly in the mandrel rolling process, was commented upon. Theoretical studies utilising the equilibrium and energy methods were applied to both the sinking and mandrel rolling processes. In general, the energy approach gave better comparison with experiment, especially for mandrel rolling. The influence of the tube deformation zones on the two processes was observed and on the subsequent modification of the tube-roll arc contact length. A rudimentary attempt was made in the theoretical sinking analysis to allow for the deformation zone prior to roll contact; some success was noted. A general survey of the available tube rolling literature, for both the sinking and mandrel processes has been carried out.

The aim of this research was to investigate the integration of computer-aided drafting and finite-element analysis in a linked computer-aided design procedure and to develop the necessary software. The Be'zier surface patch for surface representation was used to bridge the gap between the rather separate fields of drafting and finite-element analysis because the surfaces are defined by analytical functions which allow systematic and controlled variation of the shape and provide continuous derivatives up to any required degree. The objectives of this research were achieved by establishing : (i) A package which interpretes the engineering drawings of plate and shell structures and prepares the Be'zier net necessary for surface representation. (ii) A general purpose stand-alone meshed-surface modelling package for surface representation of plates and shells using the Be'zier surface patch technique. (iii) A translator which adapts the geometric description of plate and shell structures as given by the meshed-surface modeller to the form needed by the finite-element analysis package. The translator was extended to suit fan impellers by taking advantage of their sectorial symmetry. The linking processes were carried out for simple test structures, simplified and actual fan impellers to verify the flexibility and usefulness of the linking technique adopted. Finite-element results for thin plate and shell structures showed excellent agreement with those obtained by other investigators while results for the simplified and actual fan impellers also showed good agreement with those obtained in an earlier investigation where finite-element analysis input data were manually prepared. Some extensions of this work have also been discussed.

No description available.