Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Amorphous glass-coated microwires are materials with soft magnetic properties suitable for various technological applications, mainly magnetic sensors. One of the outstanding properties of microwires with positive magnetostriction is the magnetic bi-stability, that means, the inversion of the magnetization is done by one magnetic domain wall displacement along the wire. In this work it was developed a system to determine the domain wall speed in microwires and studied its dynamic. Particularly, were studied the relation between domain wall speed, magnetic field and magnetoelastic anisotropy in Fe77;5Si7;5B15 microwires. It has been verified that the main source of domain wall damping is the eddy-currents and spin relaxation, both with a strong relation with the magnetoelastic energy. The magnetoelastic energy is changed by the axial applied stress which, by its time, modifies the damping mechanisms. It was also verified that the domain wall damping present different behavior at low (mainly eddy-currents) and high applied stress (spin relaxation). / Microfios amorfos recobertos por vidro são materiais com propriedades magnéticas macias adequadas para várias aplicações tecnológicas, especialmente sensores magnéticos. Uma das propriedades interessantes dos microfios com magnetostricção positiva é a biestabilidade magnética, cuja inversão da magnetização se dá pela propagação de uma parede de domínio ao longo do material. Nesse trabalho foi desenvolvido um sistema para a determinação da velocidade de uma parede de domínio em microfios e estudada a dinâmica dessa parede. Em particular, foram estudadas as relações entre velocidade da parede de domínio, campo magnético e anisotropia magnetoelástica em microfios amorfos com composição nominal de Fe77;5Si7;5B15. Verificouse que os principais mecanismos de amortecimento das paredes de domínio têm origem nas microcorrentes de Foucault (eddy-currents) e na relaxação de spins, ambas com forte dependência da energia magnetoelástica. A energia magnetoelástica varia com a aplicação de uma tensão axial ao fio influenciando os mecanismos de amortecimento. Verificou-se também que a variação do amortecimento efetivo das paredes de domínio com a tensão tem comportamentos distintos a baixas (eddy-currents) e altas tensões aplicadas (relaxação de spin).

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In this work, we have measured the domain wall velocity in the low field regime and studied the domain wall dynamics in Joule-annealed amorphous glass-covered microwires with positive magnetostriction. Such microwires are known to present magnetic bi-stability when axially magnetized. In order to measure of the single domain wall dynamics under different conditions, an electrical current was applied to the wire simultaneously to the mechanical stress and driving magnetic field. We have observed that the applied stress decreases the domain wall mobility. When the dc current is applied to the sample, an increase or a decrease is observed on the axial domain wall mobility, depending on the current direction. When we have treated the orthogonal motion of the domain wall, the current influence is not detected. On the other hand, it was verified a modification on the domain wall length. It was also observed a change in the domain wall shape from conical to parabolic one. These results are explained in terms of the change in the magnetic energy promoted by the additional Oersted field which, by its time, modifies the length and shape of the conical domain wall, in such a way that the orthogonal domain wall velocity is not changed by the applied current. / Nesse trabalho, foi medida a velocidade de paredes de domínios em regime de baixos campos e estudada a dinâmica dessas paredes em microfios amorfos recobertos por vidros com magnetostricção positiva tratados via efeito Joule. Tais microfios são conhecidos por apresentar biestabilidade magnética quando axialmente magnetizados. A fim avaliar a dinâmica de uma única parede de domínio sob diferentes condições, corrente elétrica DC foi aplicada simultaneamente a tensões mecânicas e campo magnético externo. Foi verificado que quando uma tensão mecânica externa é aplicada, a mobilidade da parede de domínio diminui. Já quando a corrente foi aplicada na amostra, um aumento ou decréscimo da mobilidade axial da parede foi observado, dependendo do sentido da corrente aplicada. Quando foi tratado da velocidade ortogonal da parede de domínio, não foi observada influência da corrente. Por outro lado, foi verificado uma modificação no comprimento da parede de domínios. Além disto, foi observado uma mudança na forma da parede de domínio, passando de um formato cônico para parabólico. Os resultados são explicados em termos da mudança na energia magnética promovida pelo campo de Oersted, gerado pela corrente aplicada, que por sua vez modifica o comprimento e a forma da parede de domínio sem que a velocidade ortogonal da parede de domínio seja alterada pela corrente aplicada.