Submitted by Nathália Faria da Silva (nathaliafsilva.ufv@gmail.com) on 2017-07-18T12:17:23Z No. of bitstreams: 1 texto completo.PDF: 324092 bytes, checksum: 985515511859d2667ea0585a33475e4c (MD5) / Made available in DSpace on 2017-07-18T12:17:23Z (GMT). No. of bitstreams: 1 texto completo.PDF: 324092 bytes, checksum: 985515511859d2667ea0585a33475e4c (MD5) Previous issue date: 2001-07-28 / Fundação de Amparo à Pesquisa do Estado de Minas Gerais / Este trabalho foi dividido em duas etapas: na primeira, painéis OSB foram fabricados com cinco diferentes proporções de misturas entre as partículas de Eucalyptus grandis (Euc) e Pinus elliottii (Pin). Os tratamentos avaliados foram: A, 100% Euc; B, 75% Euc / 25% Pin; C, 50% Euc / 50% Pin; D, 25% Euc / 75% Pin; E, 100% Pin. Na segunda etapa, a proporção entre as espécies foi fixada em 50% e a estrutura do colchão foi alterada, sendo delineados três tratamentos: C, de camadas indistintas; F, formado exclusivamente por partículas de Eucalyptus grandis na face do colchão; e G, formado unicamente com madeira de Pinus elliottii na face. Outra variável avaliada foi a taxa de adesivo: os tratamentos foram aglutinados com 4%, 6% e 8% de sólidos resinosos sobre o peso seco das partículas de um adesivo fenólico com viscosidade de 350 cps, pH 12,15 e 47,63% de sólidos. Foi utilizada parafina em emulsão, na quantidade de 1% em relação ao peso seco das partículas. Para os sete tratamentos, foram feitas 3 repetições, totalizando 63 chapas. As chapas foram submetidas aos testes de flexão estática, ligação interna, arranque de parafuso, expansão linear, inchamento em espessura e absorção de água, obedecendo aos critérios da norma ASTM D 1037-91. Os melhores resultados foram obtidos para as chapas fabricadas com 6 e com 8% de adesivo; porém, a maioria dos resultados obtidos com painéis produzidos com 4% de adesivo foi superior ao mínimo exigido pela norma CSA O437-93. Os painéis fabricados com 50% de cada espécie alcançaram valores satisfatórios. Nenhum tratamento teve êxito ao ser avaliado para inchamento em espessura; entretanto, todos foram aprovados no teste de expansão linear. Não houve diferença estatística entre as estruturas de colchão avaliadas. / This work has been divided into two steps: in the first one, OSB was produced from five mixtures of Eucalyptus grandis (Euc) and Pinus elliottii (Pin). The treatments evaluated were: A: 100% Euc, B: 75% Euc / 25% Pin, C: 50% Euc / 50% Pin, D: 25% Euc / 75% Pin, E: 100% Pin. In the second step, the parcel of each specie was set in 50% and the mat structure was modified, so that three treatments were designed: C, with indistinct layers; F, with only Eucalyptus grandis in the mat faces; and G, with only Pinus elliottii in the mat faces. A phenolic resin containing 47,63% of total solids, pH of 12,15 and viscosity of 350 cps was used as an adhesive, with three levels of 4%, 6% and 8% of resin solids based on the oven-dry weight of particles. One per cent of wax emulsion was also added. Each treatment was replicated three times. Sixty-three boards were produced. The following properties were determined: static bending (MOR and MOE), internal board, screw withdrawal, thickness swelling, water absorption and linear expansion, following the ASTM D 1037-91 procedures. In general, the best results were observed on boards made with 6 and 8% of resin. But most treatments carried out with 4% of adhesive achieved the mechanic tests requirements of the CSA O437-93 standard. The best results were observed on boards fabricated with 50% of each species. No treatment was successful in thickness swelling. On the other hand, all treatments showed satisfactory results in linear expansion. No statistical difference has been found between the mat structures evaluated.

Submitted by Claudia Rocha (claudia.rocha@udesc.br) on 2017-12-11T13:34:57Z No. of bitstreams: 1 PGEF16MA070.pdf: 2448624 bytes, checksum: 4869319201ca98d0673aaafa7f95a8ce (MD5) / Made available in DSpace on 2017-12-11T13:34:57Z (GMT). No. of bitstreams: 1 PGEF16MA070.pdf: 2448624 bytes, checksum: 4869319201ca98d0673aaafa7f95a8ce (MD5) Previous issue date: 2016-02-26 / UNIEDU / This study aimed to evaluate the potential of Eucalyptus badjensis wood for the production of particleboard, as well as mixing it with the wood of Pinus spp. and further compare the effect of using different amounts of urea-formaldehyde adhesive (UF) on the properties of the produced panels. Thus particles were made using panels of E. badjensis and Pinus spp., As well as the mixture of two species in homogeneous composition and multilayer panels panels in proportions 25%/50%/25% using the levels of 8%, 10% and 12% of the urea formaldehyde adhesive. Were realized the analyzes of compression ratio, thickness swelling and water absorption in 2 and 24 hours of immersion in water, not return rate in thickness, modulus of elasticity (MOE) and modulus of rupture (MOR) , Traction perpendicular to the surface (Internalbond) and screw pullout , aiming to enhance discussion of the results were also conducted chemical analyzes of wood , particle geometry and basic wood density. With this study it was concluded that the Eucalyptus badjensis has the potential for making particleboards, as average values presented statistically better or equal to Pinus spp. all properties examined in the same manner was observed that the increase in adhesive, content causes an improvement in the properties of the panels / O presente estudo teve como objetivo avaliar o potencial da madeira de Eucalyptus badjensis para a produção de painéis de madeira aglomerada, bem como de sua mistura com a madeira de Pinus spp. e ainda comparar o efeito da utilizando diferentes teores do adesivo ureia-formaldeído (UF) nas propriedades dos painéis produzidos. Desse modo foram confeccionados painéis utilizando partículas de E. badjensis e de Pinus spp., bem como com a mistura das duas espécies em painéis de composição homogênea e painéis multicamada nas proporções 25%/50%/25 % utilizando os teores de 8%, 10% e 12% do adesivo ureia-formaldeído. Foram realizadas as análises de densidade aparente, razão de compactação, absorção de água e inchamento em espessura em 2 e 24h de imersão em água, taxa de não retorno em espessura (TNRE), modulo de elasticidade (MOE), modulo de ruptura (MOR), tração perpendicular à superfície (ligação interna) e arrancamento de parafuso com o objetivo de aprimorar a discussão dos resultados também foram realizadas análises químicas da madeira, da geometria de partículas e da densidade básica da madeira. Com o presente trabalho foi possível concluir que a madeira de Eucalyptus badjensis apresenta potencial para a confecção de painéis do tipo aglomerado, uma vez que apresentou valores médios melhores ou iguais ao Pinus spp. em todas as propriedades analisadas, do mesmo modo foi observado que o aumento nos teores de adesivo ocasiona uma melhora nas propriedades dos painéis