Spelling suggestions: "subject:"anitrogen diffusion"" "subject:"initrogen diffusion""
1 |
The properties of nitrogen in siliconAlpass, Charles Rowland January 2008 (has links)
The behaviour of nitrogen in silicon is investigated using the dislocation unlocking technique. Specimens containing well-ordered arrays of dislocations are isothermally annealed for a controlled duration, during which nitrogen segregates to and pins the dislocations. The stress required to unlock the dislocations is then measured by three-point bending at elevated temperature. By analysing the dependence of this unlocking stress on anneal duration and temperature, information about nitrogen's transport and interaction with dislocations can be deduced. Experiments are performed at anneal temperatures of 500 - 1050C using float-zone silicon with [N] = 2x10^15 cm^-3. The results are analysed to give an expression for nitrogen's effective diffusivity of D = 173,000 exp(-3.24eV/kT)cm^2 s^-1 in the 500 - 750C range, showing for the first time that nitrogen transport at low temperatures behaves in the same way as measured at higher temperatures by other groups using secondary ion mass spectrometry. If analysed in terms of monomer-dimer dissociative transport, the results give a nitrogen monomer diffusivity of D_1 = 28 exp(-(1.1 to 1.4 eV)/kT) cm^2 s^-1, which is similar to that found by another analysis in the literature. The measurements also show that nitrogen's dislocation locking strength measured at 550C is dependent on anneal temperature, peaking at 600 - 700C and falling towards zero above 1000C. The dislocation unlocking technique itself is also investigated and characterized. It is found that the measured unlocking stress is dependent on the three-point bend duration, falling with increasing duration. Analysis of these results in terms of the theory of release of dislocations from pinning points indicates that nitrogen dislocation locking is likely to be by an atomic species. This effect also has implications for the results of previous nitrogen dislocation unlocking experiments, and the technique has been modified so that a standardised set of conditions is used for every test. Other measurements show that nitrogen's dislocation locking effect is lessened by the presence of transition metal contamination, and that dislocation velocity in silicon may be affected by the nitrogen present in the material. A modified dislocation unlocking technique is developed to measure dislocation locking from near-surface ion-implanted impurities. Results from heavily N-implanted silicon show that nitrogen implantation can provide additional dislocation locking strength to that already given by the oxygen in the material. The scale of the dislocation locking effect in these experiments may provide evidence that nitrogen's effective diffusivity is reduced at high concentrations, indicating that nitrogen transport may be by a dissociative mechanism.
|
2 |
Nitretação a plasma de um aço inoxidável duplex 2205. / Pasma nitriding of a dupllex stainless steel 2005.Zimmermann, Margarita Rosa Bobadilla 19 November 2014 (has links)
Os aços inoxidáveis duplex se caracterizam por terem boas propriedades mecânicas e de resistência a corrosão, no entanto as suas propriedades de resistência ao desgaste são baixas. Para melhorar as propriedades superficiais desses materiais são utilizados tratamentos termoquímicos como a nitretação a plasma. Este tratamento é feito em temperaturas baixas para evitar a formação de nitretos de cromo, os quais quando são formados empobrecem o teor de cromo da matriz metálica, evitando que se forme a camada passiva, que confere resistência a corrosão a este tipo de material. Também, a nitretação a plasma permite que a dureza superficial atinja até dez vezes o valor da dureza inicial do material, o que melhora notavelmente as propriedades de resistência ao desgaste destes aços. Este estudo tem por objetivo avaliar camadas nitretadas formadas por nitretação a plasma em um aço inoxidável duplex AISI 2205. Para isto foram feitas várias experiências onde se estudou o efeito das variáveis do processo na formação da camada nitretada. Foram feitos tratamentos na temperatura de 400ºC sob pressões de 1,8 e 3,6 Torr por 720 min. Outra série de experimentos foi feita entre 350 e 500º por 240 min, para avaliar o efeito da temperatura nesse tratamento. Além disso, foi estudado o efeito de diferentes porcentagens de ferrita (40 e 64%) incialmente presente na microestrutura do material. Para isto foi feito um tratamento térmico de solubilização com têmpera em água a partir de 1200°C por uma hora, no material como recebido. A caracterização das camadas formadas foi feita por microscopia eletrônica de varredura, microscopia de força atômica, difração de raios x com radiação Cu K e difração de raios x de ângulo rasante a 5º. 7 Obtiveram-se camadas nitretadas com espessuras entre 3 µm e 18 µm. As espessuras das camadas sugerem que as variáveis: temperatura, tempo e pressão se relacionam com a espessura de forma direta, à medida que aumentam cada uma dessas variáveis, há um aumento da espessura da camada. As imagens obtidas por AFM sugerem que a nitretação a plasma induz mudanças na topografia da superfície, mudando com isto os valores de rugosidade. Também, foi observado que a espessura da camada nitretada é maior na amostra com menor percentagem de ferrita (40%). Nos difratogramas foi possível identificar a formação de austenita expandida e nitretos de cromo CrN. / The duplex stainless steels are characterized by their good mechanical properties and corrosion resistance, but their wear resistance is low. To improve the surface properties of these materials plasma nitriding thermochemical treatments are used. This treatment is done at low temperatures to avoid chromium nitrides precipitation. CrN precipitation promotes the depletion of chromium of the metallic matrix preventing the formation of the chromium oxide layer that passivates these kind of materials. In addition, the plasma nitriding treatment allows reaching hardness values up to ten times greater the characteristic values of the untreated material, greatly improving the wear resistance of these steels. The aim of this work is to study nitrided layers formed by plasma nitriding in an AISI 2205 duplex stainless steel. For this, there were made several experiments where it was studied the effect of process variables on the nitrided layer formation. Treatments were performed at temperature of 400 °C under 1.8 and 3.6 Torr pressures during 720 min. Another series of experiments was tested between 350 °C and 500 °C during 240 min, to study the temperature effect. In addition, the effect of different ferrite percentages (40 and 64%) in the microstructure was studied. The ferrite percentage variation was obtained by a heat treatment of quenching in water at 1200 °C for one hour in the material as received. Samples characterization was done by scanning electron microscopy, atomic force microscopy and x-ray diffraction Cu K, glancing angle x-ray diffraction with an incident angle of 5º. There were obtained nitrided layer with a thickness between 3m and 18m. Layer thicknesses suggest that the variables: temperature, pressure and time are related to the thickness directly. AFM images obtained suggest that the plasma nitriding induces changes in surface topography, changing the values of roughness of the surface. In addition, it was observed that the layer thickness is bigger in the sample with less ferrite percentage (40%). X-ray patterns show the presence of expanded austenite and CrN.
|
3 |
Nitretação a plasma de um aço inoxidável duplex 2205. / Pasma nitriding of a dupllex stainless steel 2005.Margarita Rosa Bobadilla Zimmermann 19 November 2014 (has links)
Os aços inoxidáveis duplex se caracterizam por terem boas propriedades mecânicas e de resistência a corrosão, no entanto as suas propriedades de resistência ao desgaste são baixas. Para melhorar as propriedades superficiais desses materiais são utilizados tratamentos termoquímicos como a nitretação a plasma. Este tratamento é feito em temperaturas baixas para evitar a formação de nitretos de cromo, os quais quando são formados empobrecem o teor de cromo da matriz metálica, evitando que se forme a camada passiva, que confere resistência a corrosão a este tipo de material. Também, a nitretação a plasma permite que a dureza superficial atinja até dez vezes o valor da dureza inicial do material, o que melhora notavelmente as propriedades de resistência ao desgaste destes aços. Este estudo tem por objetivo avaliar camadas nitretadas formadas por nitretação a plasma em um aço inoxidável duplex AISI 2205. Para isto foram feitas várias experiências onde se estudou o efeito das variáveis do processo na formação da camada nitretada. Foram feitos tratamentos na temperatura de 400ºC sob pressões de 1,8 e 3,6 Torr por 720 min. Outra série de experimentos foi feita entre 350 e 500º por 240 min, para avaliar o efeito da temperatura nesse tratamento. Além disso, foi estudado o efeito de diferentes porcentagens de ferrita (40 e 64%) incialmente presente na microestrutura do material. Para isto foi feito um tratamento térmico de solubilização com têmpera em água a partir de 1200°C por uma hora, no material como recebido. A caracterização das camadas formadas foi feita por microscopia eletrônica de varredura, microscopia de força atômica, difração de raios x com radiação Cu K e difração de raios x de ângulo rasante a 5º. 7 Obtiveram-se camadas nitretadas com espessuras entre 3 µm e 18 µm. As espessuras das camadas sugerem que as variáveis: temperatura, tempo e pressão se relacionam com a espessura de forma direta, à medida que aumentam cada uma dessas variáveis, há um aumento da espessura da camada. As imagens obtidas por AFM sugerem que a nitretação a plasma induz mudanças na topografia da superfície, mudando com isto os valores de rugosidade. Também, foi observado que a espessura da camada nitretada é maior na amostra com menor percentagem de ferrita (40%). Nos difratogramas foi possível identificar a formação de austenita expandida e nitretos de cromo CrN. / The duplex stainless steels are characterized by their good mechanical properties and corrosion resistance, but their wear resistance is low. To improve the surface properties of these materials plasma nitriding thermochemical treatments are used. This treatment is done at low temperatures to avoid chromium nitrides precipitation. CrN precipitation promotes the depletion of chromium of the metallic matrix preventing the formation of the chromium oxide layer that passivates these kind of materials. In addition, the plasma nitriding treatment allows reaching hardness values up to ten times greater the characteristic values of the untreated material, greatly improving the wear resistance of these steels. The aim of this work is to study nitrided layers formed by plasma nitriding in an AISI 2205 duplex stainless steel. For this, there were made several experiments where it was studied the effect of process variables on the nitrided layer formation. Treatments were performed at temperature of 400 °C under 1.8 and 3.6 Torr pressures during 720 min. Another series of experiments was tested between 350 °C and 500 °C during 240 min, to study the temperature effect. In addition, the effect of different ferrite percentages (40 and 64%) in the microstructure was studied. The ferrite percentage variation was obtained by a heat treatment of quenching in water at 1200 °C for one hour in the material as received. Samples characterization was done by scanning electron microscopy, atomic force microscopy and x-ray diffraction Cu K, glancing angle x-ray diffraction with an incident angle of 5º. There were obtained nitrided layer with a thickness between 3m and 18m. Layer thicknesses suggest that the variables: temperature, pressure and time are related to the thickness directly. AFM images obtained suggest that the plasma nitriding induces changes in surface topography, changing the values of roughness of the surface. In addition, it was observed that the layer thickness is bigger in the sample with less ferrite percentage (40%). X-ray patterns show the presence of expanded austenite and CrN.
|
Page generated in 0.0545 seconds