Gasification of biomass has become an area of key interest as it is a reasonably quick and direct way of converting material into a fuel source that works in many industrial systems. The purpose of the present work is to explore biomass gasification and in particular pyrolysis behavior of corn kernels, oat hulls, and paper sludge. For the materials, low temperature gasification behavior was studied. Here, tests were performed with pyrolysis temperatures from 400 - 800°C, at 1 atm and a rapid heating rate. A small concentration of O2 was added to the gasification agent (N2) to enhance CO yields, similar to modern industrial gasifiers. The evolution of CO, CO2, CH4, H2, and O2 were measured throughout the pyrolysis process. Results show a direct correlation between temperature and the composition of the gas byproduct for all biomasses. CO production increases with an increase in temperature while CO2 shows no temperature correlation. O2 depletion mimics the CO evolution and increases with an increase in temperature. CH4 production was observed, however the results were rarely repeatable due to the sensor's sensitivity to moisture and tar in the gas byproduct. No hydrogen was observed, as would be expected for the short experimental residence time (0.2 seconds).

Temas relacionados ao desenvolvimento de novos materiais têm sido cada vez mais abordados e discutidos, num contexto em que questões como meio ambiente, sociedade, economia de energia e aproveitamento de resíduos, vêm se tornando relevantes. Neste cenário, faz-se necessário estudar aplicações de insumos alternativos na produção de pisos de madeira, tanto para reduzir o consumo de essências tropicais quanto para suprir o aumento da demanda de madeira nas indústrias deste segmento. O objetivo deste estudo foi produzir painéis de partículas homogêneos de alta densidade, com resíduos de madeira de Pinus elliottii e casca de aveia (Avena sativa), aderidos sob pressão com dois tipos de adesivo, poliuretano à base de óleo de mamona e melamina formaldeído, nos percentuais de 11 e 13%, e avaliar o desempenho físico-mecânico de tais painéis para aplicação em pisos. O desempenho físico-mecânico dos painéis (Planejamento I - 20 tratamentos) foi avaliado com base nas normas ABNT NBR 14810 (2006 e 2013). Realizou-se análise de variância (ANOVA) para testar a influência dos fatores individuais (percentual de casca de aveia, percentual de adesivo e tipo de adesivo), além das interações entre tais fatores (dois a dois e três a três) nas propriedades físico-mecânicas dos painéis. Também foi avaliado o desempenho para pisos, tanto dos painéis (Planejamento II - 12 tratamentos) quanto de três espécies de madeira tropical (Angelim Vermelho, Dinizia excelsa; Cumaru, Dipteryx odorata e Jatobá, Hymenaea sp.), segundo diversas normas relacionadas a pisos de madeira. Os resultados apontaram propriedades físico-mecânicas dos painéis, em alguns tratamentos superiores aos requisitos estipulados por normas nacionais e internacionais. Quanto ao desempenho para pisos, os painéis apresentaram desempenho semelhante as três espécies de madeira, na maioria das propriedades avaliadas. A análise de porosimetria por intrusão de mercúrio confirmou a similaridade entre os painéis (do Planejamento II) e as três espécies de madeira avaliadas, evidenciando a potencialidade dos painéis produzidos para aplicação na indústria de pisos engenheirados. / Matters related to the development of new materials have been increasingly addressed and discussed in a context where issues such as the environment, society, energy and waste recovery economy, is becoming relevant. In this scenario, it is necessary to study alternative inputs for applications in the production of wood floors, both to reduce the consumption of tropical essences as to meet the increasing demand for wood in industries in this segment. The aim this study was to produce high density homogeneous particleboard with waste wood of Pinus elliottii and oat hulls (Avena sativa), adhered under pressure with two types of adhesive, castor oil-based polyurethane and melamine formaldehyde, the percentage of 11 and 13%, and evaluate the physical and mechanical performance of such panels for use in floors. The physical-mechanical performance of the panels (Planning I - 20 treatments) was evaluated based on the NBR 14810 (2006 and 2013) standards. We conducted an analysis of variance (ANOVA) to evaluate the influence of individual factors (oat hulls percentage, adhesive percentage and type of adhesive), and the interactions between these factors (two by two and three by three) on the physical properties-mechanical panels. It was also evaluated the performance for floors, both panels (Planning II - 12 treatments) as three species of tropical wood (Angelim Vermelho, Dinizia excelsa; Cumaru, Dipteryx odorata e Jatobá, Hymenaea sp.), according to various standards related to wood floors. The results indicated physical and mechanical properties of the panels, in some treatments superior to the requirements stipulated by national and international standards. As for performance flooring, panels statistically equivalent to the three species of wood, most of the evaluated properties. Porosimetry analysis by mercury intrusion confirmed the similarity between the panels (from Planning II) and the three wood species evaluated, demonstrating the potential of the panels produced for use in the flooring industry engineered.

Os painéis à base de madeira vêm sendo amplamente utilizados em todo o mundo, em resposta à redução de oferta de madeira maciça em diversos segmentos da indústria madeireira, como em móveis, painéis, estruturas e outros componentes na construção civil. O grande volume de resíduos gerados pela agroindústria viabiliza o desenvolvimento de materiais alternativos e sustentáveis, destacando-se os painéis de partículas. Este trabalho apresenta um estudo da produção e avaliação de painéis de partículas de Eucalyptus grandis e casca de aveia, aderidas sob pressão com dois tipos de resinas (poliuretana à base de mamona e ureia formaldeído). O desempenho físico-mecânico dos painéis produzidos foi avaliado com base na ABNT NBR 14810:2006. Por meio de análise de variância (ANOVA), avaliou-se a influência dos fatores adotados: madeira de Eucalyptus grandis, com proporções mássicas de 70, 85 e 100%; casca de aveia, nas proporções de 15, 30 e 100%; e adesivos, nas proporções de 10, 12 e 14%, bem como a combinação entre ambos, em cada uma das variáveis respostas (propriedades físico-mecânicas) avaliadas. Os resultados apontaram excelentes propriedades físico-mecânicas, em alguns casos muito superiores aos requisitos estipulados pelas normas nacionais e internacionais. Desta maneira, ficou comprovado o bom desempenho dos painéis de partículas produzidos, além de sua compatibilidade para aplicações em indústrias, como de móveis, painéis, embalagens e na construção civil. / Wood-based panels have been widely used around the world, replacing solid wood in various segments of the industry, such as furniture, panels, structures and other building components. The large volume of waste generated by agro industry enables the development of alternative and sustainable materials, highlighting the particleboard. This paper presents a study about production and evaluation of particleboard of Eucalyptus grandis and oat hulls, bonded under pressure with two types of resins (polyurethane based on castor oil and urea formaldehyde). Physical-mechanical performance of the panels produced was evaluated based on ABNT NBR 14810:2006. A variance analysis (ANOVA) evaluated the factors influence: Eucalyptus grandis, with mass ratios of 70, 85 and 100%; oat hulls, in proportions of 15, 30 and 100%; adhesives, in proportions of 10, 12 and 14%, and the combination of both, in each of the response variables (physical and mechanical properties) evaluated. Results showed excellent physical-mechanical properties, in some cases much higher than national and international codes requirements. Thus, panel particles good performance was proved, in addition to its compatibility with applications in wood industries, such as furniture, panels, packaging and in building construction.

Temas relacionados ao desenvolvimento de novos materiais têm sido cada vez mais abordados e discutidos, num contexto em que questões como meio ambiente, sociedade, economia de energia e aproveitamento de resíduos, vêm se tornando relevantes. Neste cenário, faz-se necessário estudar aplicações de insumos alternativos na produção de pisos de madeira, tanto para reduzir o consumo de essências tropicais quanto para suprir o aumento da demanda de madeira nas indústrias deste segmento. O objetivo deste estudo foi produzir painéis de partículas homogêneos de alta densidade, com resíduos de madeira de Pinus elliottii e casca de aveia (Avena sativa), aderidos sob pressão com dois tipos de adesivo, poliuretano à base de óleo de mamona e melamina formaldeído, nos percentuais de 11 e 13%, e avaliar o desempenho físico-mecânico de tais painéis para aplicação em pisos. O desempenho físico-mecânico dos painéis (Planejamento I - 20 tratamentos) foi avaliado com base nas normas ABNT NBR 14810 (2006 e 2013). Realizou-se análise de variância (ANOVA) para testar a influência dos fatores individuais (percentual de casca de aveia, percentual de adesivo e tipo de adesivo), além das interações entre tais fatores (dois a dois e três a três) nas propriedades físico-mecânicas dos painéis. Também foi avaliado o desempenho para pisos, tanto dos painéis (Planejamento II - 12 tratamentos) quanto de três espécies de madeira tropical (Angelim Vermelho, Dinizia excelsa; Cumaru, Dipteryx odorata e Jatobá, Hymenaea sp.), segundo diversas normas relacionadas a pisos de madeira. Os resultados apontaram propriedades físico-mecânicas dos painéis, em alguns tratamentos superiores aos requisitos estipulados por normas nacionais e internacionais. Quanto ao desempenho para pisos, os painéis apresentaram desempenho semelhante as três espécies de madeira, na maioria das propriedades avaliadas. A análise de porosimetria por intrusão de mercúrio confirmou a similaridade entre os painéis (do Planejamento II) e as três espécies de madeira avaliadas, evidenciando a potencialidade dos painéis produzidos para aplicação na indústria de pisos engenheirados. / Matters related to the development of new materials have been increasingly addressed and discussed in a context where issues such as the environment, society, energy and waste recovery economy, is becoming relevant. In this scenario, it is necessary to study alternative inputs for applications in the production of wood floors, both to reduce the consumption of tropical essences as to meet the increasing demand for wood in industries in this segment. The aim this study was to produce high density homogeneous particleboard with waste wood of Pinus elliottii and oat hulls (Avena sativa), adhered under pressure with two types of adhesive, castor oil-based polyurethane and melamine formaldehyde, the percentage of 11 and 13%, and evaluate the physical and mechanical performance of such panels for use in floors. The physical-mechanical performance of the panels (Planning I - 20 treatments) was evaluated based on the NBR 14810 (2006 and 2013) standards. We conducted an analysis of variance (ANOVA) to evaluate the influence of individual factors (oat hulls percentage, adhesive percentage and type of adhesive), and the interactions between these factors (two by two and three by three) on the physical properties-mechanical panels. It was also evaluated the performance for floors, both panels (Planning II - 12 treatments) as three species of tropical wood (Angelim Vermelho, Dinizia excelsa; Cumaru, Dipteryx odorata e Jatobá, Hymenaea sp.), according to various standards related to wood floors. The results indicated physical and mechanical properties of the panels, in some treatments superior to the requirements stipulated by national and international standards. As for performance flooring, panels statistically equivalent to the three species of wood, most of the evaluated properties. Porosimetry analysis by mercury intrusion confirmed the similarity between the panels (from Planning II) and the three wood species evaluated, demonstrating the potential of the panels produced for use in the flooring industry engineered.

Os painéis à base de madeira vêm sendo amplamente utilizados em todo o mundo, em resposta à redução de oferta de madeira maciça em diversos segmentos da indústria madeireira, como em móveis, painéis, estruturas e outros componentes na construção civil. O grande volume de resíduos gerados pela agroindústria viabiliza o desenvolvimento de materiais alternativos e sustentáveis, destacando-se os painéis de partículas. Este trabalho apresenta um estudo da produção e avaliação de painéis de partículas de Eucalyptus grandis e casca de aveia, aderidas sob pressão com dois tipos de resinas (poliuretana à base de mamona e ureia formaldeído). O desempenho físico-mecânico dos painéis produzidos foi avaliado com base na ABNT NBR 14810:2006. Por meio de análise de variância (ANOVA), avaliou-se a influência dos fatores adotados: madeira de Eucalyptus grandis, com proporções mássicas de 70, 85 e 100%; casca de aveia, nas proporções de 15, 30 e 100%; e adesivos, nas proporções de 10, 12 e 14%, bem como a combinação entre ambos, em cada uma das variáveis respostas (propriedades físico-mecânicas) avaliadas. Os resultados apontaram excelentes propriedades físico-mecânicas, em alguns casos muito superiores aos requisitos estipulados pelas normas nacionais e internacionais. Desta maneira, ficou comprovado o bom desempenho dos painéis de partículas produzidos, além de sua compatibilidade para aplicações em indústrias, como de móveis, painéis, embalagens e na construção civil. / Wood-based panels have been widely used around the world, replacing solid wood in various segments of the industry, such as furniture, panels, structures and other building components. The large volume of waste generated by agro industry enables the development of alternative and sustainable materials, highlighting the particleboard. This paper presents a study about production and evaluation of particleboard of Eucalyptus grandis and oat hulls, bonded under pressure with two types of resins (polyurethane based on castor oil and urea formaldehyde). Physical-mechanical performance of the panels produced was evaluated based on ABNT NBR 14810:2006. A variance analysis (ANOVA) evaluated the factors influence: Eucalyptus grandis, with mass ratios of 70, 85 and 100%; oat hulls, in proportions of 15, 30 and 100%; adhesives, in proportions of 10, 12 and 14%, and the combination of both, in each of the response variables (physical and mechanical properties) evaluated. Results showed excellent physical-mechanical properties, in some cases much higher than national and international codes requirements. Thus, panel particles good performance was proved, in addition to its compatibility with applications in wood industries, such as furniture, panels, packaging and in building construction.