Electrical conductivity of segregated network polymer nanocompositesKim, Yeon Seok 02 June 2009 (has links)
A set of experiments was designed and performed to gain a fundamental
understanding of various aspects of the segregated network concept. The electrical and
mechanical properties of composites made from commercial latex and carbon black are
compared with another composite made from a polymer solution. The percolation
threshold of the emulsion-based composite is nearly one order of magnitude lower than
that of the solution-based composite. The segregated network composite also shows
significant improvement in both electrical and mechanical properties with low carbon
black loading, while the solution-based composite achieves its maximum enhancement
at higher carbon black loading (~25wt%). The effect of the particle size ratio between
the polymer particle and the filler was also studied. In order to create a composite with
an extremely large particle size ratio (> 80,000), layer-by-layer assembly was used to
coat large polyethylene particles with the carbon black. Hyper-branched
polyethylenimine was covalently grafted to the surface of polyethylene to promote the
film growth. The resulting composite has a percolation threshold below 0.1 wt%, which
is the lowest percolation threshold ever reported for a carbon-filled composite. Theoretical predictions suggest that the actual percolation threshold may be lower than
0.002 wt%.
Finally, the effect of the emulsion polymer modulus on the segregated network
was studied. Monodispersed emulsions with the different glass transition temperature
were used as the matrix. The composites made using the emulsion with higher modulus
show lower percolation threshold and higher conductivity. Higher modulus causes
tighter packing of carbon black between the polymer particles. When the drying
temperature was increased to 80°C, the percolation thresholds became closer between
some systems because their moduli were very close. This work suggests modulus is a
variable that can be used to tailor percolation threshold and electrical conductivity, along
with polymer particle size.
|
2 |
Geomaterial gradation influences on interface shear behaviorFuggle, Andrew Richard 04 April 2011 (has links)
Particulate materials are ubiquitous in the natural environment and have served throughout human history as one of the basic materials for developing civilizations. In terms of human activity, the handling of particulate materials consumes approximately 10% of all the energy produced on earth. Advances in the study and understanding of particulate materials can thus be expected to have a major impact on society.
Geotechnical engineers have a long history of studying particulate materials since the fundamental building blocks of the profession include sands, silts, clays, gravels and ores, all of which are in one form or another particulates. The interface between particulates and other engineered materials is very important in determining the overall behavior of many geotechnical systems. Laboratory experimental studies into interface shear behavior has until now, been largely confined to systems involving uniformly graded sands comprised of a single particle size.
This study addresses these potential shortcomings by investigating the behavior of binary particle mixtures in contact with surfaces. The binary nature of the mixtures gives rise to a changing fabric state which in turn can affect the shear strength of the mixture. Accordingly, packing limit states and the shear strength of binary mixtures were investigated across a range of mixtures, varying in particle size ratio and the proportion of fine particles to provide a reference.
Binary mixtures in contact with smooth surfaces were investigated from both a global shear response and a contact mechanics perspective. A model was developed that allowed for the prediction of an interface friction coefficient based on fundamental material properties, particle and mixture parameters. Surface roughness changes as a result of shearing were also examined.
The interface shear behavior with rough interfaces was examined in the context of the relative roughness between particles and surface features. The interpretation of traditional measures of relative roughness suffer from the need for a definitive average particle size, which is ambiguous in the case of non-uniform mixtures. Measures of an applicable average particle size for binary mixtures were evaluated.
|
3 |
Analysis of a database of uniaxial geogrid pullout resistance resultsHutcherson, Shawn Curtis 26 April 2013 (has links)
Being able to extrapolate interaction values from a database of pullout resistance testing results may possibly help with narrowing down the most suitable reinforcement/fill material combinations for a Mechanically Stabilized Earth wall, thereby reducing the number of tests needed for a design and maximizing the efficiency of the system.
The objectives of this thesis include the following: collect and organize a broad collection of data in a way that can assist in preliminary selection of interaction properties for uniaxial geogrids; analyze the collection of data for trends related to geogrid polymer type; analyze the collection of data for trends related to the presence of fines in the fill material; compare the collected data to previous studies on the effects of geogrid specimen length on pullout performance; and compare the collected data to previous studies on the effect of geogrid rib thickness to mean particle size ratio on normalized bearing stress and CI values.
The data from 101 pullout tests are presented in tabular and graphic form so that the coefficient of interaction may be interpolated for many geogrid/fill material combinations. The effect of polymer type (PET vs HDPE) was shown to have little effect on how a geogrid performs in a fill material. In one case, the two polymer types exhibit differing trends within the same fill material. The presence of fines (>12% by weight) in the fill material results in a significant decrease in the coefficient of interaction when compared to clean granular fills. The effects of geogrid embedment length have significant effects on the results of geogrid pullout tests. Samples with shorter lengths were shown to carry a greater load per unit area than longer samples. Normalized bearing stress is shown to be heavily influenced by the geogrid transverse rib thickness to mean particle size ratio (B/D50). For a particular fill material, normalized bearing stress decreases linearly with increasing B/D50. For a particular geogrid, normalized bearing stress is shown to have a bi-linear behavior with increasing B/D50. Initially, normalized bearing stress increases with increasing B/D50. After reaching a peak, normalized bearing stress begins to decrease with increasing B/D50. / text
|
4 |
3D-druckbarer Normalbeton mit grober GesteinskörnungTaubert, Markus, Mechtcherine, Viktor 10 November 2022 (has links)
Angetrieben von vielversprechenden Effizienzsteigerungen wird der Beton-3D-Druck stetig weiterentwickelt. Um die gewonnenen Erkenntnisse niederschwellig in die Baupraxis zu überführen, empfehlen sich druckbare Betone im Rahmen des geltenden Regelwerks. Dabei stellt die Limitierung des Mehlkorngehalts eine Herausforderung dar. Um diese zu meistern, wird eine verallgemeinerbare, numerisch unterstützte Anwendung der Korngrößenverteilung nach Andreasen und Andersen als Basis für den Betonentwurf vorgeschlagen. Experimentelle Untersuchungen haben eine gute Verbaubarkeit und hinreichende Extrudierbarkeit eines Betons mit einem 16 mm Größtkorn und einem Mehlkorngehalt von 500 kg/m³ demonstriert.
|