Made available in DSpace on 2017-07-24T19:22:01Z (GMT). No. of bitstreams: 1 Driellen C Zarpellon.pdf: 2067341 bytes, checksum: 353cd12f8d341ee6a474a3f966dbe8e2 (MD5) Previous issue date: 2016-02-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Bonding adhesive systems and luting agents material inside the root canal is still a challenge in luting posts. This study evaluated the effects of applying three bonding agents using a vibrating sonic device on the push-out bond strength (BS) and nanolakage (NI) pattern, when these products were applied in the etch-and-rinse mode to bond fiber post to the root canal. Fifty-four roots of human premolars were endodontically prepared and divided into 6 groups according to combination of the main factors: products (Ambar Universal / AllCem, Single Bond Universal / RelyX ARC, Prime & Bond Elect / Enforce) and application mode (manual or sonic). The fiber posts were cemented and sectioned transversally into six 1-mm thick serial slices, which were subjected to a push-out bond strength test at 0.5 mm/min. In addition, two roots (n=2) were subjected to NI analysis using scanning electron microscopy after immersion of slices in silver nitrate. The data were analyzed by 2-way ANOVA and Bonferroni's post-hoc test (α=5%). Sonic application increased BS significantly only on the coronal third in the Ambar Universal group. When Single Bond Universal was used, higher BS values were observed when the bonding agent was manually applied in comparison to those when the sonic device was used. For Prime & Bond Elect, no significant difference in BS values was noted when the application methods were compared. Manual application also produced lower NI values than sonic application when Ambar Universal was used, while no significant difference in NI was noted when the other adhesive systems were used. The sonic application did not improve the bond strength of posts to root canal in comparison to manual application. / Adesão de sistemas adesivos e agentes de união ao canal radicular ainda é um desafio na cimentação de pinos. Este estudo avaliou os efeitos da aplicação de três agentes de união universais usando dispositivo de vibração sônica na resistência de união por push-out (RU) e padrão de nanoinfiltração (NI), quando esses produtos foram aplicados no modo convencional na adesão de pinos de fibra de vidro ao canal radicular. Raízes de 54 pré-molares humanos foram preparadas endodonticamente e divididas em 6 grupos de acordo com a combinação dos fatores principais: produtos (Ambar Universal / AllCem, Single Bond Universal / RelyX ARC, Prime & Bond Elect / Enforce) e modo de aplicação (manual ou sônico). Os pinos de fibra de vidro foram cimentados e seccionados transversalmente em 6 fatias de 1mm de altura, as quais foram submetidas ao teste de RU por push-out a uma velocidade de 0,5 mm/min. Além disso, duas raízes (n=2) foram submetidas à análise de NI usando microscópio eletrônico de varredura após imersão em nitrato de prata. Os dados foram analisados por ANOVA 2 fatores e teste de Bonferroni (α=5%). A aplicação sônica aumentou significativamente a RU apenas no terço coronal do grupo Ambar Universal. Quando o Single Bond Universal foi usado, valores mais altos de RU foram observados quando o agente de união foi aplicado manualmente em comparação aos valores quando o dispositivo sônico foi usado. Para o Prime & Bond Elect, nenhuma diferença significativa na RU foi observada na comparação entre métodos. Aplicação manual também produziu valores mais baixos de NI que aplicação sônica quando Ambar Universal foi usado, enquanto nenhuma diferença na NI foi observada nos outros sistemas de adesivos usados. A aplicação sônica não melhorou a adesão de pinos ao canal radicular comparado a aplicação manual.

Submitted by Angela Maria de Oliveira (amolivei@uepg.br) on 2018-09-26T20:23:10Z No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Max_Dobrovolski.pdf: 3607607 bytes, checksum: 331e5e608402c91f04ea1641d53747a5 (MD5) / Made available in DSpace on 2018-09-26T20:23:10Z (GMT). No. of bitstreams: 2 license_rdf: 811 bytes, checksum: e39d27027a6cc9cb039ad269a5db8e34 (MD5) Max_Dobrovolski.pdf: 3607607 bytes, checksum: 331e5e608402c91f04ea1641d53747a5 (MD5) Previous issue date: 2012-02-28 / Este estudo teve como objetivo avaliar quatro técnicas de inserção de cimento resinoso na retenção de pinos de fibra de vidro à dentina radicular nos diferentes terços radiculares, bem como a nanoinfiltração nestes diferentes terços. As raízes de cinqüenta e dois pré-molares inferiores humanos extraídos foram tratadas endodonticamente e padronizado o preparo dos condutos. Assim, elas foram divididas aleatoriamente em quatro grupos, de acordo com a técnica de inserção do cimento: GC - seringa Centrix® com ponta fina; GL - broca Lentulo 35, GP - cimento aplicado diretamente no pino e GI - seringa para aplicação de insulina. Os pinos intra-radiculares (White Post DC - FGM) tiveram suas superfícies tratadas de acordo com o fabricante e foram cimentados de acordo com cada técnica. Após o armazenamento em água a 37° C por uma semana, para cada grupo, dez raízes foram seccionadas transversalmente em seis discos com 1 mm de espessura cada, e os terços coronário (TC), médio (TM) e apical (TA) do canal radicular foram identificados. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Para avaliação da nanoinfiltração três raízes de cada grupo, ou seja, 6 discos por raiz, foram submetidos a imersão em Nitrato de Prata 50% para posterior obtenção de imagens feitas em microscopia eletrônica de varredura. As imagens foram analisadas por meio de software apropriado para obtenção das médias dos valores de nanoinfiltração convertidas em porcentagem. Os dados, submetidos a análise estatística por ANOVA 1 fator e Pós-teste Tukey (0,5%), mostraram que GC apresentou os melhores valores para resistência adesiva (MPa) e nanoinfiltração (%): 18,57 ± 4,19 e 37,70 ± 18,95 respectivamente, tendo GP o pior desempenho: 13,71 ± 1,61 e 65,11 ± 13,58 respectivamente. A técnica de inserção do cimento resinoso teve influencia nos valores de resistência adesiva e nanoinfiltração encontrados no estudo. / The aim of this study was to evaluate four techniques for insertion of resin cement on retention of glass fiber posts to root dentin in different root thirds, as well as these different nanoleakage in adhesive interface. The roots of the fifty-two human extracted pre-molars were endodontically treated and standardized preparation of the canals. It were divided into four groups according to the technique of insertion of the cement: GC - Centrix ® syringe with fine tip, GL - # 35 drill Lentulo, GP - cement applied directly to the post and GI - syringe for insulin delivery. The posts (White Post DC - FGM) had their surfaces treated in accordance with the manufacturer and were cemented according to each technique. After storage in water at 37° C for one week, each group of ten roots were sectioned transversely into six discs with 1 mm thick each, and coronal thirds (CT), medium (TM) and apical (TA) of root canal were identified. The push-out test was conducted at a speed of 0.5 mm / min. To evaluate the nanoleakage in the adhesive interface, three roots of each group, ie, 6 slices per root were submitted to immersion in 50% silver nitrate for subsequent obtaining of images made using scanning electron microscopy. Images were analyzed using appropriate software to obtain the mean nanoleakage values converted into percentage. The data were subjected to statistical analysis by ANOVA (one factor) and Tukey post-test (0.5%), showed that GC had the best values for bond strength (MPa) and nanoleakage (%):18,57 ± 4,19 e 37,70 ± 18,95 repectively and GP had the worst values: 13,71 ± 1,61 e 65,11 ± 13,58 respectively. The insertion technique of resin cement influenced on the bond strength values and on the nanoleakage found in the study.

Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2016-09-20T11:52:54Z No. of bitstreams: 2 Dissertação - Isabella Negro Favarão - 2014.pdf: 1147871 bytes, checksum: 0e08616a9e1bff5fb2e39258564e5493 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-09-20T11:53:59Z (GMT) No. of bitstreams: 2 Dissertação - Isabella Negro Favarão - 2014.pdf: 1147871 bytes, checksum: 0e08616a9e1bff5fb2e39258564e5493 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-09-20T11:53:59Z (GMT). No. of bitstreams: 2 Dissertação - Isabella Negro Favarão - 2014.pdf: 1147871 bytes, checksum: 0e08616a9e1bff5fb2e39258564e5493 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2014-02-06 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The aim of this study was to characterize the mechanical properties (Flexural strength, Diametral tensile strength, Knoop hardness, Young`s modulus, and Poisson's ratio) of a new experimental composite reinforced with glass fiber, and evaluate the fracture resistance and failure mode of bovine roots post-restored with a new experimental composite produce in direct or indirect (laboratory) mode and compare them with prefabricated fiber glass posts. Experimental composite specimens (22.5% resin, 30% 3mm-short silanized glass fibers, and 47.5% of filler particles) were prepared and tested in a universal testing machine according to the particular methodology of each test, scanning electron microscopy analysis was performed on samples fractured in bending test. Thirty endodontically treated bovine roots were divided into 3 groups (n = 10): PFP: prefabricated fiber glass posts EXP-DIR: posts made of experimental material directly polymerised into the root canal EXP-IND: posts made of experimental material indirectly polymerised. Specimens were subjected to compression load (0.5 mm/min), maximum load recorded in Newton, and fracture ranked as the failure mode. Descriptive analyzes showed averages: 259.91 ± 26.01 MPa (Flexural strength); 31.05 ± 2.97 MPa (Diametral Tensile strength); 135.6 ± 24.8 KHN (Knoop Hardness), 5.6 ± 0.95 GPa (Young`s modulus), 0.34 ± 0.02 (Poisson's ratio). ANOVA and Tukey analyzes showed statistical difference for fracture resistance (p <0.05): PFP (620.72 ± 59.29)A, EXP-IND (506.54 ± 27.07)B, EXP-DIR (157.76 ± 32.34)C. The developed composite showed appropriate mechanical properties and feasibility for production of intracanal posts, however dependent on the method of production, being the indirect method the best. / O objetivo deste estudo foi caracterizar as propriedades mecânicas (Resistência à Flexão, Resistência à Tração Diametral, Dureza Knoop, Módulo de Elasticidade, e Coeficiente de Poisson) de um novo compósito experimental reforçado com fibra de vidro polimerizado de maneira convencional, e avaliar a resistência e padrão de fratura de raízes de incisivos bovinos restauradas com pinos confeccionados com o novo compósito experimental de maneira direta ou indireta (laboratorial) e compará-las com pinos de fibra de vidro pré-fabricados. Amostras do compósito experimental (22,5% de resina, 30% de fibra de vidro curta silanizada (3mm), e 47,5% de partículas de carga) foram confeccionadas e testadas em máquina de ensaio universal de acordo com a metodologia específica de cada teste; análise em Microscopia Eletrônica de Varredura foi realizada nas amostras fraturadas no teste de flexão. Trinta raízes bovinas tratadas endodonticamente foram distribuídas em 3 grupos (n=10): PFP: pino de fibra de vidro pré-fabricado; EXP-DIR: pino de fibra de vidro confeccionado com material experimental polimerizado de forma direta no canal radicular; EXP-IND: pino de fibra de vidro confeccionado com o material experimental polimerizado de forma indireta. Os espécimes foram submetidos à carga compressiva (0,5 mm/min), carga máxima registrada em Newton, e classificados quanto ao padrão de fratura. Análises descritivas demonstraram médias: 259,91±26,01 MPa (Resistência Flexural); 31,05±2,97 MPa (Tração Diametral); 135,6±24,8 KHN (Dureza Knoop); 5,6±0,95 GPa (Módulo de Elasticidade); 0,34±0,02 (Coeficiente de Poisson). Análises com ANOVA e Tukey demonstraram diferença estatística (p<0,05) para o teste de resistência à fratura: PFP (620,72±59,29)A, EXP-IND (506,54±27,07)B, EXP-DIR (157,76±32,34)C. O compósito experimental desenvolvido demonstrou propriedades mecânicas adequadas e viabilidade para à confecção de retentores intrarradiculares, entretanto dependente do método de confecção, sendo a confecção indireta o melhor método.

Objetivo: Este estudo se propõe a verificar a influencia do tipo de luz fotopolimerizadora na força de retenção de pinos intra-radiculares, tanto na técnica direta como na direta indireta. Métodos: 40 raízes de dentes bovinos com comprimento de 12 mm foram tratadas endodonticamente e divididas aleatoriamente em 4 grupos de acordo com a técnica de obtenção dos pinos e luz fotopolimerizadora (n=10): grupo 1 (técnica direta associada à lâmpada halogena); grupo 2 (técnica direta ao LED); grupo 3 (técnica direta-indireta associada à lampada halógena); e grupo 4 (técnica direta-indireta associada ao LED). A força de retenção foi determinada através do teste de tração usando Universal Testing Machine (Instron). Todos os dados foram analisados usando one-way analysis of variance (ANOVA) com a significância de p<0.05 e complementadas com teste de Tukey. Após o teste, as interfaces adesivas onde ocorreram as falhas foram examinadas e classificadas. Resultado: Os grupos 3 (246,05N ± 29,51) e 4 (241,60N ± 28,95) não apresentaram força de retenção estatisticamente diferente mas foram maiores que os grupos 1 (142,30N ± 25,60) e 2 (178,56N ± 25,67). A maior parte das fraturas ocorreu na interface dentina/resina. Conclusão: Com base nos resultados obtidos, concluímos que o método direto-indireto proporcionou a melhor retenção dos pinos de fibra de vidro. / Objectives: The purpose of this study is to verify the influence of light curing type on retention force of direct technique and direct-indirect technique. Methods: Fourth bovine single root teeth with 12mm of length were used in this study. The roots were endodontically treated and randomly divided in four groups according to the light curing unit and technique used: group 1(direct technique, halogen lamp), group 2(direct technique, LED), group 3(direct-indirect technique, halogen lamp), group 4(direct-indirect technique, lamp). The retention force was determined sing a Universal Testing Machine (Instron). All data were analyzed using one-way analysis of variance (ANOVA) and Tukey test. After the test, the failure was examined and classified according to the fracture place: post/ resin; resin/dentin; mix. Results: Group 3 (246,05N ± 29,51) and 4(241,60N ± 28,95)4 (95,18N) did not show statistically difference but presented higher retention force than group 1 (142,30N ± 25,60) and 2 (178,56N ± 25,67). Most of fracture occurred in interface between dentin/resin. Conclusion: Based on the obtained results, it was concluded that adhesive cementation technique influenced in the retention of glass fiber post.

Objetivo: Este estudo se propõe a verificar a influência do adesivo, material de preenchimento e hibridização da dentina na força de retenção de pinos intra-radiculares na técnica direta indireta e comparar o teste de tração de push out com o pull out. Métodos: 60 raízes de dentes bovinos com comprimento de 12 mm foram tratadas endodonticamente e divididas aleatoriamente em 6 grupos (n=10): grupo 1 (técnica direta-indireta, adesivo fotopolimerizável, cimento resinoso, teste de pull out); grupo 2 (idem ao grupo 1 porém o cimento resinoso foi substituído pela resina composta); grupo 3 (idem ao grupo anterior porém o adesivo fotopolimerizável foi substituído pelo químico); grupo 4 (idem ao anterior porém o teste utilizado foi o de push out); grupo 5 (idem ao grupo anterior porém o adesivo utilizado foi o auto condicionante); e grupo 6 (idem ao grupo anterior porém a dentina foi pré hibridizada). A força de retenção foi determinada através do teste de tração usando Universal Testing Machine (Instron). Todos os dados foram analisados usando one-way analysis of variance (ANOVA) com a significância de p<0.05 e complementadas com teste de Tukey. Após o teste, as interfaces adesivas onde ocorreram as falhas foram examinadas e classificadas. Resultado: Houve diferença estatística na comparação de materiais (adesivo, material de preenchimento). A hibridização da dentina não apresentou melhoras na retenção dos pinos . A maior parte das fraturas ocorreu na interface dentina/resina. Conclusão: Com base nos resultados obtidos, concluímos que material de preenchimento, o tipo de adesivo, influenciaram na retenção de pinos de fibra; e a pré-hibridização da dentina não apresentou melhoras a retenção dos pinos. O teste de push out apresentou mais detalhes para verificar o valor da adesão de cada terço da raiz; e o teste de pull out, para a força de retenção do pino ao longo do interior do conduto e o tipo de falha. / Objective: The aims of this study is to verify the influence of adhesive, filling material and dentin hybridization on fiber post retention force in diretc -indirect technique and compare the tensile test of push out with pull out. Methods: 60 bovine single roots with a length of 12 mm were endodontically treated and randomly divided into 6 groups (n = 10): group 1 (direct-indirect technique, light-curing adhesive, resin cement, pull out test), group 2 (same as group 1 but the resin cement was replaced by composite resin), group 3 (same as previous group but the light-curing adhesive was replaced by the chemical), group 4 (same as group 3 but the test was used was push out test), group 5 (same as group 4 but the adhesive used was the self etching) and Group 6 (same as previous group but the dentin was pre-hybridized). The retention force was determined by Universal Testing Machine (Instron). All data were analyzed using one-way analysis of variance (ANOVA) with significance of p <0.05 and complemented with Tukey test. After testing, the adhesive interfaces were examined and classifie. Result: There was a significant difference between comparison of materials (adhesive and filling material). The hybridization of dentin showed no improvement in the retention post. Most fractures occurred at the interface dentin / resin. Conclusion: Based on the results, we conclude that filling material, adhesive, influenced the retention of fiber posts, and the prehybridization of dentin did not improve the retention of fiber post. The push out test showed more details to verify the bonding between the post and dentin, and the pull out test for the retention force of the post inside the canal.

Preparos para retentores intra-radiculares mais conservadores evitam desgaste desnecessário da estrutura dentinária, requer menos cimento e podem melhorar a retenção adesiva do pino. Assim o objetivo deste estudo foi avaliar a espessura de cimento ea resistência adesiva de pinos de fibra de vidro cônicos em preparo para retentor intra-radicular realizados com uma ponta ultrassônica desenvolvida. Trinta incisivos laterais superiores foram preparados com limas reciprocantes Wave One Gold (Dentsply Sirona, Ballaigues, Suiça) e aleatoriamente divididos em 2 grupos (n=15) de acordo com a técnica de preparo para pino: grupo US foram preparados com uma ponta ultrassônica desenvolvida, e grupo WP (controle) com a broca recomendada pelo fabricante do pino. Os pinos de fibra de vidro cônicos WhitePost DC 0.5 (FGM, Joinville, SC, Brasil) foram cimentados utilizando cimento resinoso dual nos terços cervical e médio do canal radicular. Isto posto, todos os espécimes foram seccionados transversalmente em três seções (cervical, média e apical do pino) para análise da área de cimento resinoso ao redor do pino que foi calculada através do programa AutoCAD, em seguida, para avaliar a resistência adesiva, o teste de cisalhamento por extrusão foi aplicado através de uma maquina de ensaio universal numa velocidade média de 0.5 mm/min até o deslocamento do conjunto restaurador intra-radicular e o tipo de falha avaliado por estereomicroscopia. A comparação entre grupos e entre terços da área de cimento e resistência adesiva foram analisadas pelo teste t independente e Anova com Tukey; e os tipos de falha entre os grupos por Mann-Whitney, todos com nível de significância de 5%. No grupo ultrassônico foi observado a menor quantidade de cimento (p<0.05) e a resistência adesiva nos diferentes grupos e terços se manifestou maior somente no terço apical do grupo ultrassônico (p<0.05). Falha adesiva entre cimento e dentina foi a mais prevalente do terço cervical e apical do grupo US e cervical de grupo WP. Falha adesiva entre cimento e pino foi a mais prevalente nos demais terços. Conclui-se que o preparo para retentor com a ponta ultrassônica desenvolvida requer menor quantidade de cimento e influencia na melhor resistência de união no terço apical do pino de fibra de vidro. / Conservative post space preparations for intra-radicular retainers prevent unnecessary desgaste of the dentin structure, require less cement and improve bond strength of the post. The aim of this study was to evaluate the influence of resin cement thickness and bond strength of prefabricated glass fiber circular postin post space preparations with an ultrasonic tip developed. Thirtymaxillarylateral incisors were prepared with Wave One Gold reciprocating files (Dentsply Sirona, Ballaigues, Switzerland) and randomly divided into 2 groups (n=15) according to the post preparation technique: gruoup US was prepared with an ultrasonic tip developed and group WP (control) with the drill recommended by the post fabricant. Every glass fiber posts WhitePost DC 0.5 (FGM, Joinville, SC, Brazil) was cemented using dual polymerizing resin cement in the cervical and middle thirdof the root canal. After that, every specimen was sectioned transversally into three sections(cervical, middle and apical of the post) and the resin cement thickness area was calculated with AutoCAD program, the bond strength test was done with an universal testing machineat medium velocity 0.5 mm/min and the failure pattern after the test was analyzed with stereomicroscopy. Datas obtained were analyzed statistically using Student\'s t-Test, ANOVA,andTukey\'s test. The comparison of failure modes between the groups in the different thirds was done using Mann-Whitney test, All of those at a 5% significance. Ultrasonic group presented thinnest layer of cement in all thirds (p<0,05), which also obtained a higher bond strength only in apical third (p<0,05). Adhesive failurebetween cement and dentinwas the most prevalent of the cervical and apical third of G1 and cervical of G2.Adhesive failure between cement and post was the most prevalent in the others thirds. It can be concluded that the postpreparation with the ultrasonic tip developed provides a smaller thickness of resin cement that influenced thebond strength in the apical third of the glass fiber post.

Made available in DSpace on 2017-07-24T19:22:01Z (GMT). No. of bitstreams: 1 Thais Bakaus.pdf: 1611331 bytes, checksum: 4d80c0ed64cbca5d883bbdad39b16c0d (MD5) Previous issue date: 2016-02-16 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The objective of this study was to evaluate the influence of a rotating device used to prepare the root canal in the adhesion of glass fiber posts and evaluate different bonding strategies using universal adhesive systems. One hundred human premolars were used, which had their crowns removed and their roots endodontically treated. Initially, the roots were divided into four groups, according to a combination of the factors: a rotating device used to prepare the root canal - carbide bur (CB) and diamond bur (DB) and cementation system (universal adhesive system associated with its respective resin cement - Single Bond Universal / RelyX ARC (SB) and Prime&Bond elect / Enforce (PB). They were then divided into subgroups according to the bonding strategy: Self-etch (SE) or Etch-and-rise (E&R). Eight teeth per group were evaluated in bond strength (BS) by the push-out test and 4 in nanoleakage teeth (NL) by scanning electron microscopy (SEM), and the roots for these tests were transversely sectioned in 6 slices. The data of BS and NI for each cementation system were subjected to 2-way ANOVA and Tukey (α = 0.05). For BS, only the major factors were significant (p <0.05), and for both cementation systems, the highest BS values were observed for the preparation with DB compared to the CB and SE adhesion strategy compared with E&R. Likewise, the interaction was not significant for NL (p> 0.05). For the cementation system PB, the lowest values were observed for groups using DB compared to the CB and SE adhesion strategy compared to E&R. For the SB cementation system, only the rotating device main factor was significant (p = 0.01), whereas the DB resulted in lower average nanoleakage compared to the CB. It can be concluded that to improve the adhesion of glass fiber posts to root canal, diamond bur should be used to prepare the root canal; and, in general, universal adhesive systems must be used in self-etch mode to obtain satisfactory results on intracanal adhesion. / Avaliou-se a influência do instrumento rotatório utilizado para preparo do conduto radicular na adesão de pinos de fibra de vidro e diferentes estratégias de adesão utilizando sistemas adesivos universais. Foram utilizados 100 pré-molares inferiores humanos, os quais tiveram suas coroas removidas e suas raízes tratadas endodonticamente. Inicialmente, as raízes foram divididas em quatro grupos, de acordo com a combinação dos seguintes fatores: instrumento rotatório utilizado para preparo do conduto radicular - broca carbide (BC) e ponta diamantada (PD) e sistema de cimentação (sistema adesivo universal associado com seu respectivo cimento resinoso) - Single Bond Universal/RelyX ARC (SB) e Prime&Bond elect/Enforce (PB). Foram divididos então em subgrupos de acordo com a estratégia de adesão: Self-etch (SE) ou Etch-and-rinse (E&R). Oito dentes por grupo foram avaliados em resistência de união (RU) pelo teste de push-out e 4 dentes em nanoinfiltração (NI) por microscopia eletrônica de varredura (MEV), sendo que para esses testes as raízes foram seccionadas transversalmente em 6 fatias. Os dados de RU e NI para cada sistema de cimentação foram submetidos à ANOVA 2 fatores e Tukey (α=0,05). Para RU, apenas os fatores principais foram significativos (p < 0,05), sendo que para ambos os sistemas de cimentação maiores valores de RU foram observados para o preparo radicular com PD em comparação com a BC e para a estratégia de adesão SE comparada a E&R. Da mesma maneira, a interação não foi significativa para NI (p > 0,05). Para o sistema de cimentação PB menores valores foram observados para os grupos que utilizaram PD em comparação com a BC e para a estratégia de adesão SE em comparação com a E&R. Para o sistema de cimentação SB, apenas o fator principal instrumento rotatório foi significante (p = 0,01), sendo que a PD resultou em menores médias de nanoinfiltração em comparação com a BC. Pode-se concluir que para melhorar a adesão de pinos de fibra de vidro ao canal radicular pontas diamantadas devem ser utilizadas para o preparo do conduto radicular; e, de maneira geral, os sistemas adesivos universais devem ser utilizados na maneira self-etch para obterem resultados satisfatórios de adesão intracanal.

Made available in DSpace on 2017-07-24T19:22:11Z (GMT). No. of bitstreams: 1 Giovana Mongruel Gomes.pdf: 1282438 bytes, checksum: 3923d5e2e659866f5b3a3e842b6cceb4 (MD5) Previous issue date: 2010-02-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The aim of this study was to evaluate the influence of the operator skill and resin cement system on the bond strength (BS) of glass fiber post to radicular dentin in different root thirds. Forty-eight extracted human upper central incisors were sectioned transversally immediately below the cement-enamel junction and the roots were treated endodontically. After one week, standardized post space cavities were prepared, and the roots randomly divided into two groups (n=24), according to the operator skill: professional (CD) vs academic (AC). The roots were then subdivided into three subgroups (n=8) according to the cementation system: CD1 and AC1 (Adper Scotchbond Multi-Purpose [SBMP] + RelyX ARC [ARC]), CD2 and AC2 (Adper Single Bond 2 [SB] + ARC) and CD3 and AC3 (RelyX U100 [U100]). The glass fiber post (Tenax Fiber Trans Esthetic Post System) were cemented following the manufacturer’s instructions of each cementation system. After water storage at 37o C for one week, each root was sectioned transversely into six 1-mm thick discs and the coronal (TC), middle (TM) and apical (TA) thirds of the root canal identified. A push-out test was carried out at a crosshead speed of 0,5 mm/min. The data were statistically analyzed by ANOVA and post-hoc Tukey's tests (p=0.05). The mean bond strengths (BS) values (MPa) and standard deviations (SD) of each subgroup were: CD1: 12.83±7.26; CD2: 11.46±4.22; CD3: 14.27±6.59; AC1: 9.70±4.37; AC2: 8.02±5.25 and AC3: 13.40±4.93. The BS of the CD and AC groups were 12.85±6.18 and 10.37±5.30, respectively. In regard to the root thirds, the means and SD were: TC: 14.46±5.55; TM: 10.04±5.07 and TA: 10.35±6.01. The mean and SD for the cementation systems were: SBMP + ARC: 11.27±6.13; SB + ARC: 9.74±5.03 and U100: 13.83±5.77. The highest BS means were obtained for CD group (p=0.004); no significant differences were detected among the three cementation systems for CD group (p=0.294); U100 cement reached statistically higher BS than the other cementation systems for AC group (p=0.001). The resin cement U100 was statistically higher than the other materials (p=0.0010) regardless the operator skill. The BS in the cervical third was statistically higher than in the TM and TA (p<0.0001). It can be concluded that the bond strength to the root canal is significantly affected by the operator skill, cementation system and root region. / O propósito desse estudo foi avaliar a influência do operador e do sistema de cimentação na resistência de união (RU) de pino de fibra de vidro à dentina radicular nos diferentes terços radiculares. Quarenta e oito incisivos centrais superiores humanos extraídos foram seccionados transversalmente imediatamente após a junção cemento-esmalte, e as raízes foram tratadas endodonticamente. Após uma semana, foi realizado o preparo padronizado dos condutos, e as raízes foram aleatoriamente divididas em dois grupos (n=24), de acordo com o operador: profissional (CD) vs acadêmico (AC). As raízes foram então subdivididas em três subgrupos cada (n=8) de acordo com o sistema de cimentação: CD1 e AC1 (Adper Scotchbond Multi-Purpose [SBMP] + RelyX ARC [ARC]), CD2 e AC2 (Adper Single Bond 2 [SB] + ARC) e CD3 e AC3 (RelyX U100 [U100]). Os pinos de fibra de vidro (Tenax Fiber Trans Esthetic Post System) foram cimentados de acordo com as recomendações dos fabricantes de cada sistema de cimentação. Após o armazenamento em água a 37o C por uma semana, cada raiz foi seccionada transversalmente em seis discos com 1 mm de espessura, e os terços coronário (TC), médio (TM) e apical (TA) do canal radicular foram identificados. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA e pós teste de Tukey (p=0,05). Os valores médios de RU (MPa) e desvio padrão (DP) para cada subgrupo foram: CD1: 12,83±7,26; CD2: 11,46±4,22; CD3: 14,27±6,59; AC1: 9,70±4,37; AC2: 8,02±5,25 e AC3: 13,40±4,93. A RU e DP para o grupo dos CD e dos AC foram 12,85±6,18 e 10,37±5,30, respectivamente. Em relação aos terços radiculares, as médias e o DP foram: TC: 14,46±5,55; TM: 10,04±5,07 e TA: 10,35± 6,01. As médias e DP para os sistemas de cimentação foram: SBMP + ARC: 11,27±6,13; SB + ARC: 9,74±5,03 e U100: 13,83±5,77. As maiores médias de RU foram obtidas para o grupo dos CD (p=0,004); não houve diferenças significativas entre os três sistemas de cimentação para o grupo dos CD (p=0,294); o cimento U100 foi estatisticamente superior aos demais sistemas de cimentação para o grupo dos AC (p=0,001). O cimento resinoso U100 foi estatisticamente superior aos demais sistemas de cimentação (p=0,001) independente do operador. A RU no terço coronário foi estatisticamente superior aos TM e TA (p<0,0001). Pode-se concluir que a resistência de união do canal radicular foi significativamente afetada pelo operador, sistema de cimentação e região radicular.

Made available in DSpace on 2017-07-24T19:22:21Z (GMT). No. of bitstreams: 1 Felipe Villa Verde.pdf: 899114 bytes, checksum: 339db35f81d16c1053ac909db81b72f5 (MD5) Previous issue date: 2012-02-27 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The aim of this study was to evaluate in vitro through the push-out test, if the use of opaque glass fiber posts (Exacto – Angelus [PO]) and translucent (Exacto Translucent – Angelus [PT]), adhesively cemented into the root with dual resin cement (Variolink II - Ivoclar Vivadent) under different polymerization time had an influence on the bond strength in three different root canal thirds. Forty-eight singlerooted extracted human premolars were selected from the Tooth Bank UEPG for research. They had their crowns sectioned to form roots with 15 mm in length. All teeth received endodontic treatment and then were divided into 6 groups (n=8), to receive the cementation according to the type of glass fiber post (opaque vs.translucent) and the time of photoactivation of resin cement (20, 40 and 60 seconds). After storage in water at 37° C for one week, the teeth were embedded in acrylic resin and sectioned perpendicular to its long axis to form discs 1 mm thick, with two discs for each root third, and then were taken to the machine universal testing. The push-out test was performed at a speed of 0.5 mm/min. The data were statistically analyzed by ANOVA and Tukey's test (p = 0.05). The mean values of bond strength (MPa) and standard deviation (SD) for groups in the cervical third, middle and apical regions were: PO20 - 21.02 ± 3.52, 15.83 ± 4.94 and 5.20 ± 10:48; PO40 - 14.42 ± 3.98, 12.12 ± 4.40 and 11.59 ± 4.89; PO60 - 16.27 ± 7.14, 13.33 ± 5.22 and 16.99 ± 7.82; PT20 - 18.34 ± 5.47, 10.83 ± 4.63 and 9.98 ± 4.76; PT40 - 17.51 ± 6.55, 14.06 ± 3.85 and 10.95 ± 4.65; PT60 - 19.42 ± 5.86, 15.35 ± 5.43 and 12.77 ± 5.93). There were no significant differences between the types of fiber posts used and the different times of polymerization (p>0.05) in relation to the root area were statistically significant differences only between the cervical and the other thirds (p>0.05). It can be concluded that the bond strength of the root canals was not affected by the type of glass fiber post (opaque vs. translucent) and photoactivation time. / O objetivo deste estudo in vitro foi avaliar por meio do teste de push-out, se a utilização de pinos de fibra de vidro opaco (Exacto – Angelus [PO]) e translúcido (Exacto Translúcido – Angelus [PT]), cimentados adesivamente no canal radicular com cimento resinoso de presa dual (Variolink II – Ivoclar Vivadent) sob diferentes tempos de fotoativação apresentavam influência na resistência de união nos três diferentes terços do canal radicular. Quarenta e oito pré-molares unirradiculares humanos extraídos foram selecionados no Banco de Dentes da UEPG para a pesquisa. Tiveram suas coroas seccionadas para formar raízes com 15 mm de comprimento. Todos os dentes receberam tratamento endodôntico e em seguida foram divididos em 6 grupos (n=8), para receber a cimentação de acordo com o tipo de pino de fibra de vidro (opaco vs translúcido) e com o tempo de fotoativação do cimento resinoso (20, 40 e 60 segundos). Após o armazenamento em água a 37o C por uma semana, os dentes foram embutidos em resina acrílica e seccionados perpendicularmente ao seu longo eixo para formar discos de 1 mm de espessura, sendo 2 discos para cada terço radicular, e em seguida foram levados à máquina de ensaios universal. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA e pós-teste de Tukey (p=0,05). Os valores médios de RU (MPa) e desvio padrão (DP) para os grupos nos terços cervical, médio e apical foram respectivamente: PO20 – 21,02 ± 3,52, 15,83 ± 4,94 e 10,48 ± 5,20; PO40 – 14,42 ± 3,98, 12,12 ± 4,40 e 11,59 ± 4,89; PO60 – 16,27 ± 7,14, 13,33 ± 5,22 e 16,99 ± 7,82; PT20 – 18,34 ± 5,47, 10,83 ± 4,63 e 9,98 ± 4,76; PT40 – 17,51 ± 6,55, 14,06 ± 3,85 e 10,95 ± 4,65; PT60 – 19,42 ± 5,86, 15,35 ± 5,43 e 12,77 ± 5,93. Não foram observadas diferenças significativas entre os tipos de pino de fibra utilizados e os diferentes tempos de fotoativação (p > 0,05); em relação à região radicular foram encontradas diferenças estatisticamente significativas somente entre o terço cervical e os demais terços (p > 0,05). Pode-se concluir que a resistência de união do canal radicular não foi afetada pelo tipo de pino de fibra de vidro (opaco vs translúcido) e tempo de fotoativação. O objetivo deste estudo in vitro foi avaliar por meio do teste de push-out, se a utilização de pinos de fibra de vidro opaco (Exacto – Angelus [PO]) e translúcido (Exacto Translúcido – Angelus [PT]), cimentados adesivamente no canal radicular com cimento resinoso de presa dual (Variolink II – Ivoclar Vivadent) sob diferentes tempos de fotoativação apresentavam influência na resistência de união nos três diferentes terços do canal radicular. Quarenta e oito pré-molares unirradiculares humanos extraídos foram selecionados no Banco de Dentes da UEPG para a pesquisa. Tiveram suas coroas seccionadas para formar raízes com 15 mm de comprimento. Todos os dentes receberam tratamento endodôntico e em seguida foram divididos em 6 grupos (n=8), para receber a cimentação de acordo com o tipo de pino de fibra de vidro (opaco vs translúcido) e com o tempo de fotoativação do cimento resinoso (20, 40 e 60 segundos). Após o armazenamento em água a 37o C por uma semana, os dentes foram embutidos em resina acrílica e seccionados perpendicularmente ao seu longo eixo para formar discos de 1 mm de espessura, sendo 2 discos para cada terço radicular, e em seguida foram levados à máquina de ensaios universal. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA e pós-teste de Tukey (p=0,05). Os valores médios de RU (MPa) e desvio padrão (DP) para os grupos nos terços cervical, médio e apical foram respectivamente: PO20 – 21,02 ± 3,52, 15,83 ± 4,94 e 10,48 ± 5,20; PO40 – 14,42 ± 3,98, 12,12 ± 4,40 e 11,59 ± 4,89; PO60 – 16,27 ± 7,14, 13,33 ± 5,22 e 16,99 ± 7,82; PT20 – 18,34 ± 5,47, 10,83 ± 4,63 e 9,98 ± 4,76; PT40 – 17,51 ± 6,55, 14,06 ± 3,85 e 10,95 ± 4,65; PT60 – 19,42 ± 5,86, 15,35 ± 5,43 e 12,77 ± 5,93. Não foram observadas diferenças significativas entre os tipos de pino de fibra utilizados e os diferentes tempos de fotoativação (p > 0,05); em relação à região radicular foram encontradas diferenças estatisticamente significativas somente entre o terço cervical e os demais terços (p > 0,05). Pode-se concluir que a resistência de união do canal radicular não foi afetada pelo tipo de pino de fibra de vidro (opaco vs translúcido) e tempo de fotoativação.

Made available in DSpace on 2017-07-24T19:22:21Z (GMT). No. of bitstreams: 1 lucas m ruiz.pdf: 809225 bytes, checksum: 4f9a5e3d41d46a1259de31458f886bd4 (MD5) Previous issue date: 2012-02-27 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The purpose of this study was to evaluate the influence of root canal sealers on the bond strength (BS) of glass fiber posts to root dentin using two cementation systems, two storage periods and the different root regions. It was used 56 human teeth,healthy canines, transversely sectioned immediately after the cement-enamel junction. Then the roots were divided into two groups (n = 28) according to the sealer (with or without eugenol [Endofill and Sealer 26, respectively]). Subsequently, the roots were subdivided into two subgroups each (n = 14) according to the period of storage before the adhesive cementation, 7 and 180 days. Each subgroup was further again subdivided according to the resin cement to be used, being a conventional dual resin cement (Variolink® II ) and a dual adhesive system (Excite DSC), and the other a dual resin cement autoconditioning and self-adhesive (RelyX™ U100). The glass fiber posts (White Post DC) were cemented according to manufacturer's instructions for each cementation system. All roots were stored for one week after adhesive cementation, and were subsequently sectioned transversely into six discs about 1 mm thick each, and the coronal (CT), middle (MT) and apical (AT) thirds of the root canal identified. The push-out test was carried out at a crosshead speed of 0.5 mm/min. The data were statistically analyzed by ANOVA factorial and post-hoc Tukey`s test (p=0.05). The analysis of variance showed a statistically significant effect for the factors time (F=6.58, p=0.01) and root third (F=26.67, p=0.0005). The specimens that received intra-canal posts 6 months after the endodontic treatment had higher BS than the specimens treated 7 days after endodontic treatment. The AT showed statistically lower BS than those of CT and MT. It can be concluded that the bond strength of fiber posts to root dentin was not affected by the root canal sealers and cementation systems. / O propósito deste estudo foi avaliar a influência dos cimentos endodônticos na resistência de união (RU) de pinos de fibra de vidro à dentina radicular, utilizando dois sistemas de cimentação, dois períodos de armazenamento e as diferentes regiões radiculares. Foram utilizados 56 dentes humanos, caninos hígidos, seccionados transversalmente imediatamente após a junção cemento-esmalte. Em seguida, as raízes foram divididas em dois grupos (n=28) de acordo com o cimento endodôntico (com ou sem eugenol [Endofill e Sealer 26, respectivamente]).Posteriormente, as raízes foram subdivididas em dois subgrupos cada (n=14) de acordo com o período de armazenamento antes da cimentação adesiva, sendo 7 e 180 dias. Cada subgrupo foi novamente subdividido de acordo com o cimento resinoso a ser utilizado sendo um cimento resinoso convencional dual (Variolink II) e sistema adesivo dual (Excite DSC), e outro cimento resinoso dual auto condicionante e auto adesivo (RelyX U100). Os pinos de fibra de vidro (White Post DC) foram cimentados de acordo com as instruções do fabricante de cada sistema de cimentação. Todas as raízes foram armazenadas por uma semana após a cimentação adesiva, e posteriormente seccionadas transversalmente em seis discos de aproximadamente 1 mm de espessura cada, e os terços coronário (TC), médio (TM) e apical (TA) do canal radicular foram identificados. O teste de push-out foi realizado a uma velocidade de 0,5 mm/min. Os dados obtidos foram analisados estatisticamente por meio do teste ANOVA fatorial e pós teste de Tukey (p=0,05). A análise de variância demonstrou um efeito estatisticamente significante para os fatores tempo (F=6,58; p=0,01) e terço radicular (F=26,67; p=0,0005). Os espécimes que receberam pino intra-canal após 6 meses do tratamento endodôntico apresentaram maior RU do que os espécimes tratados após 7 dias do tratamento endodôntico. O TA demonstrou valores de RU estatisticamente inferiores às dos TC e TM. Pode-se concluir que a resistência de união dos pinos de fibra à dentina radicular não foi afetada pelos cimentos endodônticos e sistemas de cimentação.