Metal-organic frameworks (MOFs) are porous crystalline materials built by metal clusters coordinated to organic ligands. Synthesis of MOFs has attracted considerable attention in recent decades, owing to its potential for a wide range of applications such as gas separation, dye adsorption, and catalysis, etc. The development of MOF membranes further enhances the potential of this type of material in industrial applications. Membrane fabrication methods, including in-situ growth, seeded secondary growth, interfacial growth, and vapor-phase deposition, have been widely studied. However, most of these methods either require a complicated synthesis procedure or are timeconsuming. Recently, the electrochemical synthesis has emerged as a highly promising approach to fabricate MOF membranes in a scalable manner, because it allows shorter synthesis time, milder synthesis condition, continuous reaction, and crystal self-healing. In this thesis, for the first time, an aqueously cathodic deposition (ACD) approach was developed to fabricate ZIF-8 type of MOF membranes without the addition of any supporting electrolyte or modulator. The fabrication process used 100% water as the sole solvent, and a low-defect density membrane was obtained in only 60 min under room temperature without any pre-synthesis treatment. The membrane exhibited superior performance in C3H6/C3H8 separation with C3H6 permeance of 182 GPU and selectivity of 142, making it sit at the upper bound of permeance versus selectivity graph, outperforming the majority of the published data up to 2019. Notably, this approach used an extremely low current density (0.13 mA cm-2) operated under a facile apparatus setup, enabling an attractive method for environmentally friendly, energy-efficient, and scalable MOF membrane fabrications. This work demonstrates the enormous potential of aqueously electrochemical deposition of the MOF membrane in future research.

Metal-Organic Frameworks (MOFs) are nanoporous framework materials with tunable pore size and functionality, and hence attractive for gas separation membrane applications. Zeolitic Imidazolate Frameworks (ZIFs), a subclass of MOFs, are known for their high thermal and chemical stability. ZIF-8 has demonstrated potential to kinetically separate propane/propene in powder and membrane form. ZIF-8 membranes propane-propene separation performance is superior in comparison to polymer, mixed matrix and carbon membranes. The overarching theme of my research is to address challenges that hinder fabrication of MOF membranes on a commercial scale and in a reproducible and scalable manner. 1. Current approaches, are specific to a given ZIF, a general synthesis route is not available. Use of multiple steps for surface modification or seeding causes reproducibility and scalability issues. 2. Conventional fabrication techniques are batch processes, thereby limiting their commercialization. Here we demonstrate two new approaches that can potentially address these challenges. First, we report one step in situ synthesis of ZIF-8 membranes on more commonly used porous α-alumina supports. By incorporating sodium formate in the in situ growth solution, well intergrown ZIF-8 membranes were synthesized on unmodified supports. The mechanism by which sodium formate promotes heterogeneous nucleation was investigated. Sodium formate reacts with zinc source to form zinc oxide layer, which in turn promotes heterogeneous nucleation. Sodium formate promotes heterogeneous nucleation in other ZIF systems as well, leading to ZIF-7, Zn(Im)2 (ZIF-61 analogue), ZIF-90, and SIM-1 films. Thus one step in situ growth using sodium formate provides a simplified, reproducible and potentially general route for ZIF film fabrication. One step in situ route, although advantageous; is still conventional in nature and batch process with long synthesis time. This limits commercialization, due to scalability and manufacturing cost issues. Taking advantage of coordination chemistry of MOFs and using temperature as driving force, continuous well-intergrown membranes of HKUST-1 and ZIF-8 in relatively short time (15 min) using Rapid Thermal Deposition (RTD). With minimum precursor consumption and simplified synthesis protocol, RTD provides potential for a continuous, scalable, reproducible and commercializable route for MOF membrane fabrication. RTD-prepared MOF membranes show improved separation performances, indicating improved microstructure.

abstract: Membrane-based gas separation is promising for efficient propylene/propane (C3H6/C3H8) separation with low energy consumption and minimum environment impact. Two microporous inorganic membrane candidates, MFI-type zeolite membrane and carbon molecular sieve membrane (CMS) have demonstrated excellent thermal and chemical stability. Application of these membranes into C3H6/C3H8 separation has not been well investigated. This dissertation presents fundamental studies on membrane synthesis, characterization and C3H6/C3H8 separation properties of MFI zeolite membrane and CMS membrane. MFI zeolite membranes were synthesized on α-alumina supports by secondary growth method. Novel positron annihilation spectroscopy (PAS) techniques were used to non-destructively characterize the pore structure of these membranes. PAS reveals a bimodal pore structure consisting of intracrystalline zeolitic micropores of ~0.6 nm in diameter and irregular intercrystalline micropores of 1.4 to 1.8 nm in size for the membranes. The template-free synthesized membrane exhibited a high permeance but a low selectivity in C3H6/C3H8 mixture separation. CMS membranes were synthesized by coating/pyrolysis method on mesoporous γ-alumina support. Such supports allow coating of thin, high-quality polymer films and subsequent CMS membranes with no infiltration into support pores. The CMS membranes show strong molecular sieving effect, offering a high C3H6/C3H8 mixture selectivity of ~30. Reduction in membrane thickness from 500 nm to 300 nm causes an increase in C3H8 permeance and He/N2 selectivity, but a decrease in the permeance of He, N2 and C3H6 and C3H6/C3H8 selectivity. This can be explained by the thickness dependent chain mobility of the polymer film resulting in final carbon membrane of reduced pore size with different effects on transport of gas of different sizes, including possible closure of C3H6-accessible micropores. CMS membranes demonstrate excellent C3H6/C3H8 separation performance over a wide range of feed pressure, composition and operation temperature. No plasticization was observed at a feed pressure up to 100 psi. The permeation and separation is mainly controlled by diffusion instead of adsorption. CMS membrane experienced a decline in permeance, and an increase in selectivity over time under on-stream C3H6/C3H8 separation. This aging behavior is due to the reduction in effective pore size and porosity caused by oxygen chemisorption and physical aging of the membrane structure. / Dissertation/Thesis / Doctoral Dissertation Materials Science and Engineering 2015