In the pipe manufacturing and pipe processing industry, the demand for cost-effective pipes with high strength and good ductility is increasing. In the present study, the inductive longitudinal welding process was combined with a Quenching and Partitioning (Q&P) treatment to manufacture pipes with enhanced mechanical properties. The aim of the Q&P process is to establish a martensitic structure with increased retained austenite content. This allows for the beneficial use of both phases: the strength of martensite as well as the ductility of retained austenite. A 42SiCr steel, developed for Q&P processes, was joined at the longitudinal seam by a high-frequency induction (HFI) welding process and was subsequently heat-treated. The applied heat treatments included normalizing, austenitizing, quenching, and two Q&P strategies (Q&P-A/Q&P-B) with distinct quenching (Tq = 200/150 °C) and partitioning temperatures (Tp = 300/250 °C). Investigations of the microstructures revealed that Q&P tubes exhibit increased amounts of retained austenite in the martensitic matrix. Differences between the weld junction and the base material occurred, especially regarding the morphology of the martensite; the martensite found in the weld junction is finer and corresponds more to the lath-type morphology, compared to the base material in the circumference. In all zones of the welded tube circumference, retained austenite has been found in similar distributions. The mechanical testing of the individual tubes demonstrated that the Q&P treatments offer increased strength compared to all other states and significantly improved ductility compared to the quenched condition. Therefore, the approach of Q&P treatment of HFI-welded tubes represents a route for the mass production of high-strength tubular products with improved ductility.

Quenching and partitioning (Q&P) steels show a good balance between strength and ductility due to a special heat treatment that allows to adjust a microstructure of martensite with a fraction of stabilized retained austenite. The final heat treatment step is performed at low temperatures. Therefore, joining of Q&P steels is a big challenge. On the one hand, a low joining temperature is necessary in order not to influence the adjusted microstructure; on the other hand, high joint strengths are required. In this study, joining of Q&P steels with Ag nanoparticles is investigated. Due to the nano-effect, high-strength and temperature-resistant joints can be produced at low temperatures with nanoparticles, which meets the contradictory requirements for joining of Q&P steels. In addition to the Ag nanoparticles, activating materials (SnAg and Sn) are used at the interface to achieve an improved bonding to the steel substrate. The results show that the activating materials play an important role in the successful formation of joints. Only with the activating materials, can joints be produced. Due to the low joining temperature (max. 237 °C), the microstructure of the Q&P steel is hardly influenced.