Submitted by Silvana Teresinha Dornelles Studzinski (sstudzinski) on 2015-05-07T17:06:36Z No. of bitstreams: 1 Leandro Moosher.pdf: 3103618 bytes, checksum: f239d2771f04dbfaee064ee603b2bc29 (MD5) / Made available in DSpace on 2015-05-07T17:06:36Z (GMT). No. of bitstreams: 1 Leandro Moosher.pdf: 3103618 bytes, checksum: f239d2771f04dbfaee064ee603b2bc29 (MD5) Previous issue date: 2013-08-15 / CNPQ – Conselho Nacional de Desenvolvimento Científico e Tecnológico / Milton Valente / NUCMAT - Núcleo de Caracterização de Materiais / A geração de resíduos sólidos nos centros urbanos está relacionada principalmente com o aumento da população e com a intensificação dos processos de industrialização. O gerenciamento desde sua origem, produção, processamento, destino final e reciclagem desses resíduos é atualmente um dos maiores desafios de empresas geradoras, de instituições de pesquisa, órgãos governamentais e empresas afins que buscam uma solução para minimizar ou até eliminar a geração de resíduos ou a sua reciclagem e posterior uso em diversas áreas da indústria, ou até transformando-os em produtos de interesse comercial. Neste sentido, os resíduos de fundição gerados durante a produção de ligas fundidas vêm sendo estudado para seu uso como co-produto em diferentes segmentos industriais, tais como a própria fundição e o da construção civil. Este trabalho objetiva avaliar a viabilidade de aplicação de dois diferentes resíduos, as areias fenólica e verde usadas de fundição, como matéria-prima com valor agregado, esta sendo usada na fabricação de blocos de concreto para pavimentação, avaliando sua transformação para co-produto. Alguns estudos já demonstraram o potencial de aplicação desses resíduos de diversas formas e em diferentes setores da indústria. A aplicabilidade específica desses resíduos dependerá das suas caracterizações, seja ambiental, química, física ou de fases, sendo essa uma etapa fundamental para avaliar a viabilidade de reciclagem e econômica. Desta forma a caracterização destes resíduos configurou-se na etapa essencial do trabalho para depois destiná-los a uma melhor aplicação tecnológica. Foram produzidos blocos com 0%, 25% e 50% de substituição parcial da areia natural pelo co-produto. Esses blocos foram ensaiados quanto a resistência mecânica à compressão aos 7 e 28 dias de cura, absorção de água, resistência ao desgaste por abrasão, índice de porosidade, MEV, avaliação ambiental e viabilidade financeira dos blocos gerados com o uso dos resíduos de fundição. O traço com ter de substituição de 25% da combinação dos resíduos foi o que apresentou os melhores resultados, tanto na resistência à compressão quanto a resistência ao desgaste à abrasão. Os blocos com uso da combinação dos dois resíduos foram classificados ambientalmente como Classe II A – Não Inerte e apresentaram menor custo na produção de blocos de concreto para pavimentação. / The generation of solid waste in urban centers is related mainly to the increase in population and the intensification of the processes of industrialization. The management since its origin, production, processing, recycling and final destination of such waste is currently one of the biggest challenges of generating companies, research institutions, government agencies and companies alike who seek a solution to minimize or even eliminate the generation of waste or recycling and subsequent use in various fields of industry, or even turning them into products of commercial interest. In this sense, the foundry waste generated during the production of cast alloys have been studied for use as a by-product in different industries, such as own foundry and construction. This study evaluates the feasibility of applying two different residues of foundry, spent phenolic sand and spent green sand as raw material with value added, this being used in the manufacture of concrete block paving, evaluating its transformation to co-product. Some studies have demonstrated the potential application of the wastes in various forms and in different industry sectors. The specific applicability of these residues depend on their characterizations, whether environmental, chemical, physical or phases, this being a fundamental step to assess the feasibility of recycling and economic. Thus the characterization of this waste was configured in the key step of the work and then consign them to a better technological application. Blocks were made with 0%, 25% and 50% replacement of natural sand per by-product. These blocks were analysed for compressive strength at 7 and 28 days of curing, water absorption, abrasion strength, porosity index, SEM, environmental assessment and financial feasibility of the blocks generated with the use of the by-product. The mark with having to replace 25% of combination of two foundry waste showed the best results in both compression strength as the abrasion strength. Blocks using the combination of foundry waste were environmental ly classified as Class II A - Not Inert and had lower costs in producing concrete block paving.

Made available in DSpace on 2016-12-08T15:56:17Z (GMT). No. of bitstreams: 1 resumo tese.pdf: 15008 bytes, checksum: b3fcb8e618165bdab7dabdeefc264a32 (MD5) Previous issue date: 2014-08-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The use of casting waste powder from industry in mortars brings environmental benefits by minimizing the impact caused by the disposal of waste on the environment. Casting exhaust powder is a waste product from the regeneration of sand molds from the core making process sector from a foundry industry located in Joinville/SC. This work aims to propose a formulation method for laying mortars, and wall and ceiling coating mortars incorporating casting waste powder whose use would result in a product with adequate technical performance. The fine aggregates, the casting waste powder and mortars were characterized by standard assays, electron microscopy and X-ray powder diffraction. The laying and coating mortar compositions were based on a system of equations obtained using the mixture design methodology. Through this study, results of experimental character and a method for formulating mortars that can be useful in the construction sector were obtained, thus contributing to a better understanding of the use of casting waste in mortars. / O uso de resíduos de fundição como o pó de exaustão em argamassas traz benefícios ambientais através da minimização do impacto causado pelo descarte do resíduo no meio ambiente. O pó de exaustão de fundição é um resíduo proveniente da regeneração dos moldes de areias do setor de macharia de uma indústria de fundição localizada em Joinville/SC. Este trabalho tem por objetivo propor um método de formulação para argamassas de assentamento e revestimento de paredes e tetos com incorporação de pó de exaustão cuja utilização resulte em um produto com desempenho técnico adequado. Os agregados miúdos, o resíduo pó de exaustão de fundição e as argamassas foram caracterizados por ensaios normalizados, microscopia eletrônica e difração de raios-X. As composições das argamassas em massa foram obtidas através de planejamento de experimentos de delineamento por misturas. A proposta de formulação de argamassas de assentamento e revestimento de paredes e tetos foi baseada na resolução de sistemas de equações obtidas através do modelamento estatístico das propriedades. Por meio deste estudo, foram obtidos resultados de caráter experimental e um método de formulação de argamassas que podem ser úteis ao setor de construção civil, contribuindo desta forma com o melhor entendimento do uso de resíduos de fundição em argamassas.