Background: Anterior cruciate ligament (ACL) injuries have become commonplace among female athletes in today’s society. With more than 70% of injuries resulting from noncontact mechanisms such as jump landing, the relationship between fatigue and altered movements patterns has become an important topic of research. Purpose: The main purpose of this study was to investigate the influence of residual fatigue on lower extremity kinematics and vertical leg stiffness at landing as experienced by female athletes. Method: The participants in this study were 12 NCAA female intercollegiate soccer players. Participants completed five single-leg drop jumps on their dominant leg every day for 4 days. The first day was completed without intervention to obtain pre-fatigue data and drop jumps on days two through four were completed after a fatigue protocol. Results: A repeated measures MANOVA did not reveal significant differences in post-fatigue peak knee flexion angle, vertical ground reaction forces, or vertical leg stiffness. Despite lack of statistical significance, vertical leg stiffness was increased during post-fatigue testing when compared to pre-fatigue values. Implications: The increased vertical leg stiffness may indicate altered landing techniques in post-fatigue states. If fatigue results in compromised movement patterns, it may explain the increased number of ACL injuries during the end of soccer matches. Suggestions for Future Research: Future research with a larger sample size should include post-fatigue dominant and nondominant leg comparison due to previous conflicting findings regarding which limb is most often injured. Future researchers should also quantify the magnitude of fatigue induced by the fatiguing protocol to document the strength of the independent variable. / text

Master's thesis deals with the damage tolerance analysis of wing-to-fuselage joint of L 410 NG airplane. Thesis includes determination of the load distribution to the individual attachments of wing-to-fuselage joint, residual strength analysis and residual fatigue life analysis of the most loaded attachment lugs, calculation of fatigue crack growth curves in the attachment solids and inspection program proposal. This analysis was performed using FE model of the wing and central part of the fuselage and AFGROW software.

This Ph.D. thesis deals with methodology for determination of residual fatigue lifetime of railway axles based on damage tolerance approach. This approach accepts an existence of potential defect, which could lead to fatigue failure of whole axle. The behavior of crack in railway axle is described by approaches of linear elastic fracture mechanics. There are plenty of factors, which more or less influence determined residual fatigue lifetime. The aim of this thesis is to quantify effects of these factors. The first part of Ph.D. thesis represents overview of studied problems relating to fatigue damage of railway axles. This part is focused on parameters, which influence fatigue crack growth in railway axle materials. The second part of thesis shows procedure for determination of residual fatigue lifetime, which was developed at the Institute of Physics of Materials of the Academy of Sciences of the Czech Republic. The main aim of this thesis was to improve current procedure for more precise estimation of residual fatigue lifetime. Significant part of this work is determination of significance of studied factors, which influencing calculated residual fatigue lifetime of railway axles (e.g. effect of threshold value, load spectrum, retardation effects, residual stress, axle geometry, material of axle etc.). The procedures described and results obtained can be also used for determination of residual fatigue lifetime of general mechanical component (not only railway axles). Therefore, results obtained in this Ph.D. thesis can be used e.g. for assessment of regular inspection intervals of cyclically loaded general mechanical parts.

This Ph.D. thesis deals with methodology for determination of residual fatigue lifetime of railway axles based on damage tolerance approach. This approach accepts an existence of potential defect, which could lead to fatigue failure of whole axle. The behavior of crack in railway axle is described by approaches of linear elastic fracture mechanics. There are plenty of factors, which more or less influence determined residual fatigue lifetime. The aim of this thesis is to quantify effects of these factors. The first part of Ph.D. thesis represents overview of studied problems relating to fatigue damage of railway axles. This part is focused on parameters, which influence fatigue crack growth in railway axle materials. The second part of thesis shows procedure for determination of residual fatigue lifetime, which was developed at the Institute of Physics of Materials of the Academy of Sciences of the Czech Republic. The main aim of this thesis was to improve current procedure for more precise estimation of residual fatigue lifetime. Significant part of this work is determination of significance of studied factors, which influencing calculated residual fatigue lifetime of railway axles (e.g. effect of threshold value, load spectrum, retardation effects, residual stress, axle geometry, material of axle etc.). The procedures described and results obtained can be also used for determination of residual fatigue lifetime of general mechanical component (not only railway axles). Therefore, results obtained in this Ph.D. thesis can be used e.g. for assessment of regular inspection intervals of cyclically loaded general mechanical parts.

The aim of this diploma thesis is to estimate the residual fatigue lifetime of the model train axle. Primarily, the thesis is focused on determination of the stress intesity factor, the main variable for estimation of the residual fatigue lifetime. At first, the theoretical approaches of estimation of the residual fatigue lifetime are listed and then the residual fatigue lifetime of the model train axle is estimated.