Submitted by JOSIANE SANTOS DE OLIVEIRA (josianeso) on 2018-07-09T16:18:43Z No. of bitstreams: 1 Paôla Valentini_.pdf: 16360357 bytes, checksum: 11cfed092ec8572550d478091c843fbc (MD5) / Made available in DSpace on 2018-07-09T16:18:43Z (GMT). No. of bitstreams: 1 Paôla Valentini_.pdf: 16360357 bytes, checksum: 11cfed092ec8572550d478091c843fbc (MD5) Previous issue date: 2018-03-23 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Diversos fatores influenciam a durabilidade de argamassas de revestimento, sendo alguns deles: a absorção de água, porosidade e rugosidade da superfície do substrato; a execução, com o preparo ou não do substrato, a forma de aplicação e as condições de cura da argamassa; as condições climáticas, decorrentes da ação do vento, umidade e temperatura; e a própria argamassa com seus componentes. Partindo deste contexto, esta pesquisa tem como objetivo avaliar fatores relacionados ao substrato e à argamassa que influenciam na resistência de aderência à tração de sistemas de revestimento. O programa experimental buscou avaliar a influência da absorção de água total, da absorção por capilaridade e da rugosidade de três substratos cerâmicos e também da adição de fíler na argamassa, na resistência de aderência à tração de sistemas de revestimento. Os substratos cerâmicos foram queimados nas temperaturas de 800°C, 900°C e 1000°C, sendo que, das 144 peças cerâmicas do estudo, metade receberam aplicação de hidrofugante. Sobre as peças cerâmicas foram aplicadas argamassas confeccionadas com areia natural de rio e cimento Portland CP II-Z-32, no traço 1:3, em massa, com e sem adição de 5% de pó de quartzo. A partir dos resultados encontrados observou-se que a maior resistência de aderência à tração foi obtida nos blocos cerâmicos com temperatura de queima de 800°C, que apresentam simultaneamente maior rugosidade e maior absorção capilar de água. Verificou-se também que a adição de fíler à argamassa aumentou a resistência de aderência quando aplicada sobre os blocos de maior rugosidade, não sendo observado o mesmo comportamento nos blocos de baixa rugosidade. De um modo geral, o uso de hidrofugante sobre as peças cerâmicas diminuiu os resultados de resistência de aderência além de alterar a forma de ruptura dos revestimentos. / The durability of coating mortars applied on substrates are influenced by the water absorption, porosity and roughness of the substrate surface; the preparation of the coating´s substrate, the method used to apply and the cure conditions of the mortar; beyond the climatic conditions, through the wind, humidity and temperature; and the mortar itself with its components. Based on this context, this research aims to evaluate factors related to the coating´s substrate and the rendering mortar that influence the adhesion strength of mortar coating systems. The experimental program aimed to evaluate the influence of total water absorption, capillary absorption and roughness of three ceramic substrates, as well as the use of filler in the mortar, in the adhesion strength of mortar coating systems. The ceramic substrates were burned at 800°C, 900°C and 1000°C, and of the 144 ceramic pieces of the study, 72 were painted with water repellent. The coating mortars were made with natural river sand and Portland cement CP II-Z-32, in the proportion 1: 3 (by mass), with and without adding 5% of quartz filler. It was observed that the highest tensile strength was obtained with the substrates of ceramic blocks burned at 800°C, which simultaneously present the higher roughness and higher water absorption. The use of filler in the mortar composition increased the adhesion strength when applied on the blocks of greater roughness. In general, the use of water repellent on the ceramic substracts decrease the adhesion strength of mortar coating systems and modify the kind of rupture of the coatings.

Submitted by Cássia Santos (cassia.bcufg@gmail.com) on 2016-08-12T10:36:05Z No. of bitstreams: 2 Dissertação - Aline Crispim Canedo Girardi - 2016.pdf: 6052802 bytes, checksum: 19568ea8fd9027193ffed70b254b8bdc (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2016-08-12T14:17:29Z (GMT) No. of bitstreams: 2 Dissertação - Aline Crispim Canedo Girardi - 2016.pdf: 6052802 bytes, checksum: 19568ea8fd9027193ffed70b254b8bdc (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2016-08-12T14:17:29Z (GMT). No. of bitstreams: 2 Dissertação - Aline Crispim Canedo Girardi - 2016.pdf: 6052802 bytes, checksum: 19568ea8fd9027193ffed70b254b8bdc (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2016-05-31 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Although the use of CDW in the aggregate production is studied in Brazil for more than two decades, there are still gaps regarding their use in mortars. In this sense, the present study aims to evaluate mortar for rendering masonry produced with full replacement of natural sand by recycled aggregate, seeking to correlate the various properties and characteristics of aggregates and mortars with the performance of rendering with regard to the adhesive strength and absorption/water permeability. For the development of the research three types of aggregates were used (natural sand, mixed recycled ceramic and cement and cementitious recycled) in two particle sizes, passers-by screens 3 mm and 1.18 mm, which were widely characterized. With the data obtained in the characterization of aggregates, different traces were formulated for mortars, keeping fixed the content of total fine plasticizers. The mortars were evaluated on their consistency, bulk density, dimensional instability (shrinkage), water absorption, compressive and flexural strength. The renderings were applied on ceramic blocks, which were selected for initial water absorption rate ranges, avoiding the variability of results due to changes in the suction of the substrate. Two types of preparation of the base were performed, lime solution and roughcast, the latter was used only for the rendering that showed the best performance among those produced with recycled aggregates. As the main results, it was found that using a sieve with an opening of 1.18 mm is effective for reducing the content of fine aggregate, however, mortars and renderings produced with these aggregates showed unsatisfactory performance, falling short of results in materials with through 3 mm sieve. Mortars and rendering produced with recycled aggregate cement did not show compatible performance with the others, at the expense of the initial assumptions, which provided that this aggregate would exceed the aggregate mixed. It was also noticed that the recycled aggregates mixed ceramic and cementitious material, passers the sieve 3 mm, despite the high content of fine and high water absorption, resemble very to the natural aggregate with the same granulometry, when comparing the characteristics of mortars they have produced, mainly for resistance to compression. When assessing the rendering produced by these two aggregates, both are equivalent in the question of adhesive strength and showed no cracking. In general, it can be concluded that it is feasible the production of efficient rendering with complete replacement of natural sand for mixed recycled aggregates since the RCD origin and characteristics are known, Provided that limited the packing factor of grain , which directly influence the properties of mortars and renderings. / Apesar de a utilização de RCD na produção de agregado miúdo ser estudada no Brasil há mais de duas décadas, ainda não há correlações definidas entre as características dos agregados reciclados e o desempenho dos revestimentos, de forma a identificar as propriedades que deverão ser controladas no momento da escolha dos agregados que será incorporado às argamassas, independente do tipo de resíduo original. Nesse sentido, o presente trabalho visa determinar a viabilidade técnica da substituição total de agregado natural por agregado reciclado no preparo de argamassas de revestimento, buscando correlacionar as diversas propriedades e características dos agregados e das argamassas com o desempenho dos revestimentos, no que tange à resistência de aderência à tração e absorção/permeabilidade de água. Para o desenvolvimento da pesquisa utilizou-se três tipos de agregados (areia natural, reciclado misto de material cerâmico e cimentício e reciclado cimentício), em duas granulometrias, passantes pelas peneiras 3 mm e 1,18 mm, os quais foram amplamente caracterizados. As argamassas produzidas foram avaliadas quanto à consistência, densidade de massa, retração, absorção de água por imersão, resistência à compressão e resistência à tração. Os revestimentos foram aplicados sobre blocos cerâmicos, preparados com solução de cal ou chapisco, sendo este último apenas para o revestimento que apresentou o melhor desempenho dentre os produzidos com agregados reciclados. Como principais resultados, verificou-se que a utilização de peneira com abertura de 1,18 mm é eficiente para a redução do teor de finos dos agregados, entretanto, as argamassas e os revestimentos produzidos não apresentaram desempenho satisfatório, ficando aquém dos resultados obtidos com materiais passantes na peneira 3 mm. As argamassas e revestimentos contendo agregado reciclado cimentício não apresentaram desempenho compatível com as demais, em detrimento das suposições iniciais, que previam que esse agregado seria superior ao agregado misto. Também se percebeu que os agregados reciclados mistos de material cerâmico e cimentício, passantes na peneira 3 mm, apesar do alto teor de finos e da elevada absorção de água, assemelham-se muito ao agregado natural de mesma granulometria, quando comparadas as características das argamassas por estes produzidas, principalmente quanto à resistência à compressão. Quando se avaliam os revestimentos produzidos por esses dois agregados, ambos são equivalentes em questão de resistência de aderência à tração e não apresentaram nenhuma fissuração. Em linhas gerais, pode-se concluir que é viável a produção de revestimentos eficientes com substituição total da areia natural por agregados reciclados, desde que limitado o fator de empacotamento dos grãos, que influência diretamente nas propriedades das argamassas e revestimentos.