ROCHA, Gilvan Nóbrega da. Obtenção das cerâmicas dielétricas BiTRWO6 (TR = Y, Gd ou Nd) por radiação de micro-ondas e sua aplicação em dispositivos eletrônicos. 2012. 121 f. Dissertação (Mestrado em química)- Universidade Federal do Ceará, Fortaleza-CE, 2012. / Submitted by Elineudson Ribeiro (elineudsonr@gmail.com) on 2016-05-31T19:57:58Z No. of bitstreams: 1 2012_dis_gnrocha.pdf: 4722446 bytes, checksum: 23e67f757b6eb73afa4b518ad3d87636 (MD5) / Approved for entry into archive by José Jairo Viana de Sousa (jairo@ufc.br) on 2016-05-31T20:30:22Z (GMT) No. of bitstreams: 1 2012_dis_gnrocha.pdf: 4722446 bytes, checksum: 23e67f757b6eb73afa4b518ad3d87636 (MD5) / Made available in DSpace on 2016-05-31T20:30:22Z (GMT). No. of bitstreams: 1 2012_dis_gnrocha.pdf: 4722446 bytes, checksum: 23e67f757b6eb73afa4b518ad3d87636 (MD5) Previous issue date: 2012 / The mixture heat of the metal oxides may promote the formation of ceramic materials, depending on their dielectric properties and its crystalline structure may be used with electronic components for a variety of functions in electrical circuits. Heating method is directly related to the material properties. This work aims to use a commercial microwave oven modified to carry out reactions in the solid state, in order to promote the reaction between oxides of bismuth and tungsten with oxides of rare earths. The oxides of gadolinium, yttrium and neodymium were selected for the experiment, where the materials were BiGdWO6 dielectric ceramics, and BiYWO6 BiNdWO6. The proof of obtaining the phase ceramics and structural study of these were performed by means of X-ray diffraction (XRD) and infrared and Raman spectroscopy. It was also studied the electrical properties in order to evaluate the applicability of the material as electronic apparatus. Tests of materials for application as electronic components in the microwave region suggested, after the analysis of dielectric measurements, its use as microstrip and monopole antennas. The dielectric properties (permittivity and loss) of the samples proved to be attractive for capacitor applications and certainly for microelectronics devices, microwave (antenna for mobile phones, for example). / O aquecimento de uma mistura de óxidos metálicos pode promover a formação de materiais cerâmicos que, dependendo de suas propriedades dielétricas e de sua estrutura cristalina, podem ser utilizados para fabricação de componentes eletrônicos de funções variadas. Este trabalho tem por objetivo a utilização de um forno de micro-ondas comercial, modificado para realização de reações no estado sólido, no intuito de promover a reação entre os óxidos de bismuto e tungstênio com óxidos de terras raras. Os óxidos de gadolínio, ítrio e neodímio, foram selecionados para o experimento, onde os materiais obtidos foram as cerâmicas dielétricas BiGdWO6, BiYWO6 e BiNdWO6. A comprovação da obtenção das fases cerâmicas e o estudo estrutural das mesmas foram realizados por meio de difração de raios-X (DRX) e espectroscopia no infravermelho e Raman. Foram também realizados os estudos das propriedades elétricas com o intuito de avaliar a aplicabilidade do material como dispositivo eletrônico. Os testes para aplicação dos materiais como componentes eletrônicos na região das micro-ondas sugeriram, após as análises das medidas dielétricas, sua utilização como antenas de Microfita e monopolo. As propriedades dielétricas (permissividade e perda) das amostras apresentaram valores atraentes para aplicações em capacitores e, certamente, para dispositivos microeletrônicos, de micro-ondas (antena para telefones celulares, por exemplo).

Made available in DSpace on 2014-07-29T15:12:45Z (GMT). No. of bitstreams: 1 dissertacaokatiusciaDaia.pdf: 861870 bytes, checksum: 844752d18d747dab701abe725ec66d0d (MD5) Previous issue date: 2008-08-18 / I n this work a systematic study on the phase formation and stability in the system Bi2O3-ZrO2 was realized, the solubility of the Zr4+ ion in Bi12TiO20 (BTO) was investigated and Zr-doped BTO crystals (BTO:Zr) were grown and optically characterized. It was verified that a tetragonal phase was formed in the following wide composition interval: (6-x)Bi2O3:(1+x)ZrO2, with x = 0.5, 0.3, 0.2, 0.1, 0, -0.1, -0.2, -0.3, -0.5, -0.65 e -0.7. The phases were synthesized by solid state reaction and the powders were characterized by Xray diffraction and diferential thermal analysis. The formed tetragonal phase, however, was metastable for all investigated compositions and its preparation was dependent on the sample thermal history. The stable phase at room temperature was a monoclinic one. A low solubility of Zr4+ in BTO was verified, but BTO:Zr single crystals were grown by Top Seeded Solution Growth (TSSG) technique. Good quality crystalline samples were prepared and characterized by chemical compositon and by optical activity, photoconductivity and electro-optical measurements. The results shown that Zr-doping produced a decreasing in the crystal photosensitivity, and almost no changes in the optical activity and electro-optical coefficient were generated. / Neste trabalho foi realizado um estudo sistemático das condições de preparação e estabilidade de fases no sistema Bi2O3-ZrO2, a solubilidade do íon Zr4+ no Bi12TiO20 (BTO) foi investigada e cristais de BTO dopados com Zr4+ (BTO:Zr) foram crescidos e caracterizados opticamente. Verificou-se que uma fase tetragonal é formada no amplo intervalo de composições (6- x)Bi2O3:(1+x)ZrO2, com x = 0,5, 0,3, 0,2, 0,1, 0, -0,1, -0.2, -0,3, -0,5, -0,65 e - 0,7. As fases foram sintetizadas por reação no estado sólido e os pós foram caracterizados por difração de raios-X e análise térmica diferencial. A fase tetragonal formada, no entanto, é metaestável em todo o intervalo de composições investigadas, sendo sua obtenção condicionada à história térmica da amostra. A fase estável à temperatura ambiente é monoclínica. Foi constatado que a solubilidade do Zr4+ no BTO é baixa, mas cristais de BTO:Zr foram crescidos através da técnica Top Seeded Solution Growth (TSSG). Amostras cristalinas de boa qualidade óptica e estrutural foram preparadas e caracterizadas quanto à composição química e através de medidas de atividade óptica, fotocondutividade e coeficiente eletro-óptico. Os resultados demonstram que o Zr produz uma diminuição na fotosensibilidade do cristal, provocando pouca alteração nos valores de atividade óptica e coeficiente eletro-óptico