The electro-optical properties of the ZnO/Si heterojunction embedded with self-assembled gold nanoparticles on patterned silicon substrate are investigated in this master thesis. High quality n-type ZnO film is deposited on patterned p-type silicon substrate by radio-frequency sputtering to form a ZnO/Si pn junction. The patterned silicon substrates are prepared by ICP-RIE using self-assembled nickel metal dot and silicon dioxide as etching mask. The optimum ICP process conditions of silicon nanopillars are CF4/Ar ~ 40/40 sccm and bias/RF power 400/400 W. Silicon nanopillars of diameter ~ 50 nm and height 100~400 nm are formed on the substrate surface. ZnO film is then deposited of a growth rate ~ 12 nm/min at the substrate temperature = 200oC. The plasmonic effects on the electro-optical properties, including photoluminescence (PL), reflection, and electrical characteristics, are studied by adding self-assembled gold nanoparticles within the ZnO film. The self-assembled gold nanoparticles are formed by thermal deposition and rapid thermal annealing at 700oC. The gold nanoparticles are observed by scanning electron microscopy (SEM) and particles of diameter about 100 nm. The PL intensity of ZnO is enhanced more than ten times at the peak wavelength = 380 nm by adding the gold nanoparticles and silicon nanopillars. Strong blue emission light could be saw with the naked eyes. For the electric characteristics, self-assembled gold nanoparticles in patterned ZnO/Si heterojunction show photoelectric conversion phenomenon because of high electromagnetic absorption and plasmonic effects.