Submitted by Stefhany Costa Barbizan null (stefhanybarbizam@hotmail.com) on 2018-01-24T15:50:22Z No. of bitstreams: 1 DISS 2018.pdf: 9636418 bytes, checksum: 4d62ecb173fdcea62201fab783a6dfc1 (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-01-24T16:32:32Z (GMT) No. of bitstreams: 1 Astuti_scb_me_sjc.pdf: 9405812 bytes, checksum: 099df02868bd44f2c4a02f03b5a2e97f (MD5) / Made available in DSpace on 2018-01-24T16:32:32Z (GMT). No. of bitstreams: 1 Astuti_scb_me_sjc.pdf: 9405812 bytes, checksum: 099df02868bd44f2c4a02f03b5a2e97f (MD5) Previous issue date: 2017-12-14 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A literatura mostra escassez de informações sobre o envelhecimento de cerâmicas Y-TZP de uso odontológico, quando associado a escovação simulada. Sendo assim, o objetivo deste estudo foi avaliar o efeito da escovação simulada em algumas propriedades de zircônias estabilizadas por ítria (Y-TZP) após envelhecimento hidrotérmico. Foram confeccionados 36 discos da cerâmica (YZ®) – ISO 6872, 36 da cerâmica Cercon®Zirconia (DENTSPLY Ceramco, EUA) e 36 discos da cerâmica (Zirkon Transluzent - ICE Zirkonzahn®) os quais foram separados de acordo com o envelhecimento em reator hidrotérmico (controle e 6 horas de envelhecimento) e submissão à ciclagem de escovação simulada (controle e 72000 ciclos com carga de 350g e solução creme dental/água), resultando em 3 grupos de estudo, de acordo com o tipo de cerâmica utilizada para confecção da amostra e 4 Sub grupos, de acordo com a realização ou não do envelhecimento Hidrotérmico e escovação simulada nas amostras (n=9). Sendo YZ- Amostras realizadas com a cerâmica(YZ®);CZ- Amostras realizadas com a cerâmica-(Cercon®Zirconia);ZT- Amostras realizadas com a cerâmica (Zirkon Transluzent - ICE Zirkonzahn®).Teremos como subgrupos, 0- Grupo controle, amostras não submetidas nem ao envelhecimento, nem a escovação simulada; 1- Amostras submetidas apenas ao envelhecimento por 6 horas; 2- Amostras submetidas somente a escovação simulada; 3- Amostras submetidas ao envelhecimento hidrotérmico por 6 horas e escovação simulada. Os corpos de prova foram avaliados por difração de Raio-X para verificar transformação de fase T-M e uma amostra de cada grupo submetida à análise morfológica em microscopia eletrônica de varredura (MEV). As amostras foram submetidas ao teste de flexão biaxial em máquina de ensaios universal, ensaiadas até o momento da fratura e os dados obtidos foram submetidos a análise de variância de dois fatores. Também foi realizado o teste de Tukey (P<0,05), para analisarmos a interação entre o tipo de cerâmica e o tratamento realizado (CxT). As análises nos mostraram que os grupos envelhecidos sofreram maior alteração de fase que os grupos só escovados, e quando os dois procedimentos foram associados, a formação de fase monoclínica foi maior. Além disso, as micrografias mostraram que os grãos de zircônia se expandiram na tentativa de conter um possível defeito estrutural e muitos se soltaram devido a abrasão da escovação. Dessa forma, pode-se concluir que, as análises de DRX e MEV foram essenciais para identificação da alteração de fase sofrida pelas cerâmicas, confirmando o comportamento de desgaste já descrito na literatura, quando submetidas a tratamentos de envelhecimento hidrotérmico. / The literature shows a shortage of information about the aging of Y-TZP ceramics for dental use, when associated with simulated brushing. Therefore, the objective of this study was to evaluate the effect of simulated brushing on some properties of yttria stabilized zirconia (Y-TZP) after hydrothermal aging. Sixteen ceramic discs (YZ®) - ISO 6872, 36 Cercon®Zirconia ceramics (DENTSPLY Ceramco, USA) and 36 ceramic discs (Zirkon Transluzent - ICE Zirkonzahn®) were prepared, which were separated according to the aging in the reactor hydrothermal (control and 6 hours of aging) and submission to simulated brushing cycle (control and 72000 cycles with 350g load and toothpaste / water solution), resulting in 3 study groups, according to the type of ceramics used for cooking of the sample and 4 Sub groups, according to whether or not Hydrothermal aging and simulated brushing were performed in the samples (n = 9). (YZ®); CZ- Samples made with ceramics- (Cercon®Zirconia); ZT- Samples made with ceramics (Zirkon Transluzent - ICE Zirkonzahn®) .We will have as subgroups, 0- Control group, samples not submitted neither to aging nor simulated brushing; 1- Samples submitted only to aging for 6 hours; 2 - Samples submitted only to simulated brushing; 3 - Samples submitted to hydrothermal aging for 6 hours and simulated brushing. The specimens were evaluated by X-ray diffraction to verify T-M phase transformation and a sample of each group submitted to scanning electron microscopy (SEM) morphological analysis. The samples were submitted to the biaxial flexion test in a universal test machine, tested until the moment of fracture and the data obtained were submitted to two-way analysis of variance. The Tukey test (P <0.05) was also used to analyze the interaction between the type of ceramic and the treatment (CxT). The analyzes showed that the aged groups suffered a greater phase change than the groups only brushed, and when the two procedures were associated, the monoclinic phase formation was larger. In addition, the micrographs showed that the zirconia grains expanded in an attempt to contain a possible structural defect, and many were released due to abrasion of the brush. Thus, it can be concluded that the XRD and SEM analyzes were essential for the identification of the phase change suffered by the ceramics, confirming the wear behavior already described in the literature when submitted to hydrothermal aging treatments.

Made available in DSpace on 2017-07-24T19:22:05Z (GMT). No. of bitstreams: 1 MANOELA HASS DOLINSKI THOMASSEWSKI.pdf: 1885236 bytes, checksum: f6df4dd8ee0fdb0bea20dba5b9c53058 (MD5) Previous issue date: 2008-02-26 / The purpose of this study was to measure mass loss and surface roughness (Ra) changes of differents glass ionomer cement indicated to atraumatic restorative treatment, with a resin composite used as control material, after a simulated toothbrushing test. The surface characteristics before and after abrasion were evaluated on scanning electron microscopy (SEM). The tested materials were: Vitro Fil LC® ,Fuji IX® , Vitro Molar® , Maxxion R®, and the resin composite Filtek Z100®. Ten samples (6mm in diameter and 5mm thick) on all samples from each were prepared according to manufacturers’ instructions. Toothbrushing abrasion was performed on all specimens from each of the materials using a simulator. The mass loss, surface roughness and qualitative analyse were assessed before and after 20000 brushstrokes, using Shimadzu analytical balance of 0,0001g accuracy, a Mitutoyo surftest-301 and Shimadzu SSX-550 Superscan respectively. The measurements of both properties were statiscally compared by Anova one-way and then paired t-test and Tukey’s test. Correlation between mass loss and surface roughness was calculated. The level significance was α=5% (p<0,05). All materials presented a statistically significant mass loss comparing initial and final values. The loss mass in order decreasing was Vitro Fil LC>Maxxion R> Vitro Molar>Filtek Z100>Fuji IX. All materials became rougher with the exception of Vitro Molar that presented low roughness after toothbrushing test. There was no correlation between wear and surface roughness and SEM observations were in accordance to those roughness measured. In conclusion, the findings of this study showed that, the high viscosity glass cement ionomer presented wear and roughness seems to control material and the fluoride release propertie, this may be adequate for atraumatic restorative treatment. However, long-term clinical evaluation are necessary to better indicate this category of materials / O objetivo deste estudo foi mensurar a perda de massa e as alterações de rugosidade média superficial (Ra) de diferentes cimentos de ionômero de vidro indicados para tratamento restaurador atraumático tendo uma resina composta como material controle, após teste de escovação simulada. As características de superfície antes e após abrasão foram avaliadas em microscópio eletrônico de varredura (MEV). Os materiais testados foram: Vitro Fil LC® ,Fuji IX® , Vitro Molar® , Maxxion R®, e a resina composta microhíbrida Filtek Z100®. Dez amostras (6mm de diâmetro e 5mm de espessura) de cada material foram confeccionados de acordo com as instruções do fabricante. O teste foi conduzido em uma máquina de escovação simulada, em todas as amostras de todos os materiais, totalizando 20000 ciclos. Antes e após o teste, a massa, rugosidade e analise qualitativa em MEV, de cada material foram aferidas em um balança analítica Shimadzu de 0,0001g de precisão, pelo equipamento Mitutoyo modelo surftest-301 e pelo microscópio Shimadzu SSX-550 Superscan., respectivamente. Os resultados das variáveis perda de massa e rugosidade foram analisados pelo teste ANOVA de um critério e então o pós-teste para comparações múltiplas de Tukey, com o objetivo de identificar entre quais grupos situavam as diferenças. Para analisar a relação entre perda de massa e rugosidade média foi utilizada a análise de regressão linear. O nível de significância empregado foi de α=5% (p<0,05), utilizado para todas as análises. Todos os materiais apresentaram diferenças estatísticas de perda de massa entre valores iniciais e finais. A perda de massa em ordem decrescente foi Vitro Fil LC>Maxxion R> Vitro Molar>Filtek Z100>Fuji IX. Os materiais se tornaram mais rugosos exceto o Vitro Molar que apresentou menor rugosidade após teste. Não houve correlação entre perda de massa e rugosidade superficial. Observações ao MEV estavam de acordo com as medidas de rugosidade. Concluindo, os achados deste estudo mostraram que os cimentos de alta viscosidade apresentaram desgaste e rugosidade semelhantes ao material controle e ainda possuem a propriedade de liberar flúor, sendo adequado para tratamento restaurador atraumático. Entretanto, avaliações clínicas são necessárias para melhor indicar esta categoria de material.