The flexural behavior of a light-weight wood-based composite system was studied through destructive experiments. The composite panel system consisted of profiled dimensional lumber, which makes up the surface layers, and 1"-thick boards running across the surface layers. Considering the changes in cross-sections along the panel due to the presence of the embedded boards, classical theories such as the Euler-Bernoulli beam and Kirchhoff-Love plate could not be implemented. Instead, the deflections and maximum failure loads of the composite system under full- and short-span bending tests were measured during their destructive bending testing, and were compared against the mechanical properties of the conventional three-ply CLT panel with the same thickness as the panel with embedded cross-laminations. According to maximum failure loads and deflections, it was concluded that full-span panels with embedded cross-laminations exhibited higher strength and stiffness, whereas short-span panels exhibited higher strength and lower stiffness properties compared to conventional CLT panels.

Yes / Extensive experimental and theoretical studies have been conducted on the compressive strength of concrete-filled steel tubular (CFST) columns, but little attention has been paid to their compressive stiffness and deformation capacity. Despite this, strength prediction approaches in existing design codes still have various limitations. A finite element model, which was previously proposed by the authors and verified using a large amount of experimental data, is used in this paper to generate simulation data covering a wide range of parameters for circular and rectangular CFST stub columns under axial compression. Regression analysis is conducted to propose simplified models to predict the compressive strength, the compressive stiffness, and the compressive strain corresponding to the compressive strength (ductility) for the composite columns. Based on the new strength prediction model, the capacity reduction factors for the steel and concrete materials are recalibrated to achieve a target reliability index of 3.04 when considering resistance effect only.

O tratamento térmico da madeira (ou termorretificação) é realizado com o aquecimento da madeira em faixas de temperaturas inferiores à carbonização, até 280ºC. O objetivo desta tecnologia é melhorar as propriedades da madeira e, desta forma, proporcionar a obtenção de produtos com maior valor agregado. Neste trabalho, avaliou-se o comportamento em peças estruturais das espécies Eucalipto citriodora (Corymbia citriodora) e Pinus taeda, tratadas termicamente nas temperaturas de 160, 180, 200, 220 e 240ºC e, para o pínus, até a temperatura de 260ºC. Os ensaios experimentais realizados para a madeira tratada termicamente foram de classificação visual, obtenção de suas propriedades químicas, físicas, mecânicas (resistência e rigidez), entomológicas e com fungos. Quanto à análise química, foi identificado redução nos teores de extrativos e hemiceluloses, após termorretificação das amostras, e aumento no teor de celulose e lignina. A densidade aparente e a propriedade de inchamento das madeiras reduziram com o aumento da temperatura, e a permeabilidade a gás aumentou para o eucalipto. As mudanças nas propriedades colorimétricas das madeiras levaram ao escurecimento, devido à degradação dos seus principais componentes químicos, principalmente as hemiceluloses. De uma maneira geral, as propriedades de resistência (à compressão, à flexão, à tração e ao cisalhamento paralelo às fibras) das madeiras diminuiram e as propriedades de rigidez (módulo de elasticidade na compressão Eco e o MOE) aumentaram ao longo do tratamento com calor. A determinação dos valores característicos de resistência para cálculos estruturais foram adequados quando comparados à norma brasileira ABNT NBR 7190/97. O tratamento térmico proporcionou a proteção da madeira de Eucalipto citriodora quando ela foi exposta ao ataque de cupins subterrâneos Nasutitermes sp., de acordo com os ensaios de alimentação forçada, e das madeiras de E. citriodora e Pinus taeda, quando expostas ao fungo de podridão mole (Paecilomyces variotti). / Heat treatment of wood (or thermal rectification) is performed by heating wood below carbonization temperature, up to 280ºC. The aim of this technology is to improve the wood properties and thus to obtain products with higher added value. In this study, we evaluate the behavior of structural pieces of two species: Eucalyptus citriodora (Corymbia citriodora) and Pinus taeda, thermally treated at temperatures of 160, 180, 200, 220 e 240ºC, and pine up to the temperature of 260ºC. The experimental analyses to thermally treated wood were visual grading, chemical, physical, mechanical (strength and stiffness) and durability. Regarding chemical analysis, there was a reduction in the extractive and hemicellulose contents, while and the cellulose and lignin content increased; density and swelling properties decreased with increasing temperature, and the air permeability increased to eucalyptus. Changes in the colorimetric properties of wood caused the species in the study to become darker due to degradation of chemical components, mainly hemicellulose. In general, the strength properties (compression, bending, tension and shear parallel to the grain) of wood reduced and the stiffness properties (elasticity modulus by compression (Eco) and MOE) improved along thermal treatment. The determination of characteristic values of strength to structural calculations was adequate when compared to the Brazilian norm ABNT NBR 7190/97. It was observed that thermal treatment provided protection of wood of Eucalyptus citriodora from subterranean termites attack Nasutitermes sp., in the force-feeding test and Eucalyptus citriodora and Pinus taeda on soft rot fungi Paecilomyces variotti.

O tratamento térmico da madeira (ou termorretificação) é realizado com o aquecimento da madeira em faixas de temperaturas inferiores à carbonização, até 280ºC. O objetivo desta tecnologia é melhorar as propriedades da madeira e, desta forma, proporcionar a obtenção de produtos com maior valor agregado. Neste trabalho, avaliou-se o comportamento em peças estruturais das espécies Eucalipto citriodora (Corymbia citriodora) e Pinus taeda, tratadas termicamente nas temperaturas de 160, 180, 200, 220 e 240ºC e, para o pínus, até a temperatura de 260ºC. Os ensaios experimentais realizados para a madeira tratada termicamente foram de classificação visual, obtenção de suas propriedades químicas, físicas, mecânicas (resistência e rigidez), entomológicas e com fungos. Quanto à análise química, foi identificado redução nos teores de extrativos e hemiceluloses, após termorretificação das amostras, e aumento no teor de celulose e lignina. A densidade aparente e a propriedade de inchamento das madeiras reduziram com o aumento da temperatura, e a permeabilidade a gás aumentou para o eucalipto. As mudanças nas propriedades colorimétricas das madeiras levaram ao escurecimento, devido à degradação dos seus principais componentes químicos, principalmente as hemiceluloses. De uma maneira geral, as propriedades de resistência (à compressão, à flexão, à tração e ao cisalhamento paralelo às fibras) das madeiras diminuiram e as propriedades de rigidez (módulo de elasticidade na compressão Eco e o MOE) aumentaram ao longo do tratamento com calor. A determinação dos valores característicos de resistência para cálculos estruturais foram adequados quando comparados à norma brasileira ABNT NBR 7190/97. O tratamento térmico proporcionou a proteção da madeira de Eucalipto citriodora quando ela foi exposta ao ataque de cupins subterrâneos Nasutitermes sp., de acordo com os ensaios de alimentação forçada, e das madeiras de E. citriodora e Pinus taeda, quando expostas ao fungo de podridão mole (Paecilomyces variotti). / Heat treatment of wood (or thermal rectification) is performed by heating wood below carbonization temperature, up to 280ºC. The aim of this technology is to improve the wood properties and thus to obtain products with higher added value. In this study, we evaluate the behavior of structural pieces of two species: Eucalyptus citriodora (Corymbia citriodora) and Pinus taeda, thermally treated at temperatures of 160, 180, 200, 220 e 240ºC, and pine up to the temperature of 260ºC. The experimental analyses to thermally treated wood were visual grading, chemical, physical, mechanical (strength and stiffness) and durability. Regarding chemical analysis, there was a reduction in the extractive and hemicellulose contents, while and the cellulose and lignin content increased; density and swelling properties decreased with increasing temperature, and the air permeability increased to eucalyptus. Changes in the colorimetric properties of wood caused the species in the study to become darker due to degradation of chemical components, mainly hemicellulose. In general, the strength properties (compression, bending, tension and shear parallel to the grain) of wood reduced and the stiffness properties (elasticity modulus by compression (Eco) and MOE) improved along thermal treatment. The determination of characteristic values of strength to structural calculations was adequate when compared to the Brazilian norm ABNT NBR 7190/97. It was observed that thermal treatment provided protection of wood of Eucalyptus citriodora from subterranean termites attack Nasutitermes sp., in the force-feeding test and Eucalyptus citriodora and Pinus taeda on soft rot fungi Paecilomyces variotti.