ELECTRODEPOSITION OF SULFIDE-CONTAINING THIN FILMS, AND THEIR APPLICATION TO ELECTROCHEMICAL SYSTEMSFan, Li 01 May 2019 (has links)
This dissertation presents studies of both anodic and cathodic electrodeposition of thin films, and their applications as supercapacitors and electrocatalysts for polysulfide reduction and oxidation.
|
2 |
Síntese de estruturas 3D de nanotubos de carbono verticalmente alinhados, dopados e não-dopados, decorados com nanopartículas de óxido de titânio, sua caracterização microestrutural e de propriedades fotocatalíticas e elétricasAcauan, Luiz Henrique January 2015 (has links)
Neste trabalho foi desenvolvido um procedimento experimental para a fabricação de estruturas 3D de nanotubos de carbono crescidos sobre substrato de cobre e decorados com partículas de óxido de titânio. Foram relacionados os três tipos diferentes de NTCs nesta estrutura (simples, dopados com nitrogênio e tratados com plasma) com a deposição do TiO2 por ALD. Foram igualmente propostas três aplicações para esta estrutura. A síntese dos NTCs verticalmente orientados, dopados e não dopados, foi otimizada dentre alguns parâmetros de síntese como temperatura, agente oxidante e principalmente, o filme catalisador. A introdução de defeitos nos NTCP através do tratamento a plasma oxidativo foi avaliada frente a variáveis como pressão, potência e tempo de exposição. A relação entre os defeitos destes três tipos de NTCs e a deposição de TiO2 por ALD foi avaliada por microscopia eletrônica de transmissão, Raman, XPS e TGA. O procedimento experimental para confecção da estrutura 3D foi desenvolvido etapa por etapa via diversas técnicas experimentais, desde caracterização química, imagem, até testes empíricos. Na estrutura final, foram avaliadas as propriedades fotocatalíticas pela decomposição de corante orgânico em meio aquoso, propriedades capacitivas por voltametria cíclica e propriedades de emissão por campo através de curvas de campo elétrico por corrente de emissão e diagramas F-N. Foram obtidas florestas de NTCs de boa qualidade com até 0.5mm de altura, de diâmetros e número de paredes regulares. Nestes foi possível introduzir defeitos de maneira controlável, mantendo o arranjo da floresta. As florestas de NTCNx alcançam uma altura de até 0,3mm com concentração de nitrogênio de 2% tendo os nanotubos uma estrutura típica “bamboo-like”. Os resultados mostram a relação entre o tipo de defeito e a deposição de TiO2 por ALD, obtendo-se partículas cristalinas para os NTCP e NTCNx, sendo neste ultimo as partículas homogeneamente distribuídas e com tamanho uniforme, enquanto nos NTCOx forma-se uma densa camada de TiO2 composta por grandes grãos monocristalinos A partir de processo como tratamentos térmicos e transferência dos NTC de substrato foi possível obter uma estrutura 3D composta de uma camada carbono grafítico e NTC-VAs sobre um substrato de cobre, sem alterar o arranjo inicial das florestas. As amostras mostraram efeito de emissão de elétrons por campo elétrico, porém estas requerem uma análise mais quantitativa. Os ensaios de fotocatálise mostraram que a imobilização do TiO2 em um suporte denso inviabiliza a degradação do corante em meio aquoso. Os NTCNx apresentaram maior capacitância que as mostras de NTCP, e o TiO2 foi aparentemente ineficaz para a melhoria desta propriedade. / In this work, we propose an experimental procedure for fabrication of 3D carbon nanotubes structures anchored with titanium oxide particles, on a copper substrate. We correlate three different types of CNTs from this structure (pristine, doped with nitrogen and treated with plasma) with the deposition of TiO2 by ALD. It was yet suggested, three applications for this structure. The synthesis of vertically aligned CNTs, doped and undoped, was optimized among several synthesis parameters such as temperature, oxidizing agent and specially, the catalyst film. The introduction of defects in NTCP by oxidative plasma treatment was evaluated against variables such as pressure, power and exposure time. The association between the defects from these three types of CNTs and the deposition of TiO2 by ALD was assessed by transmission microscopy, Raman, XPS and TGA. The experimental procedure for assembling the 3D structure had been studied step by step by various techniques, from chemical and imaging, up to empirical testing. In the final structure, the photocatalytic properties were evaluated by the organic dye decomposition in an aqueous medium, capacitive properties by cyclic voltammetry and field emission properties through electric field versus emission current curves and F-N diagram. Was obtained high quality NTCs with a height up to 0.5mm with regular diameters and number of walls. On these, it was introduced, in a controllable way, a high amount of defects without jeopardizing the forest structure. The NTCNx forest reach a 0,3nm height with a 2% nitrogen concentration in its typical structure “bamboo-like”. The results show the relation between the type of defect and the deposition of TiO2 by ALD, forming crystalline particles over the NTCP and NTCNx, in this last evenly distributed with uniform size, while on the NTCOx is is formed a dense TiO2 layer shaped by large monocrystalline grains. By process such as heat treatments and CNT transferring was achieved a 3d structure composed by a graphitic carbon layer and VACNTs over a cupper substrate, without disturb the forest assembly. The samples showed electron field emission effect, but its assessment for quantitative analysis was limited to technical issues. The photocatalysis tests showed that immobilization of TiO2 on a dense support prevents the dye degradation in an aqueous medium. The NTCNx shown higher capacitance than NTCP, and the TiO2 was apparently ineffective for improvement of this property.
|
3 |
Síntese de estruturas 3D de nanotubos de carbono verticalmente alinhados, dopados e não-dopados, decorados com nanopartículas de óxido de titânio, sua caracterização microestrutural e de propriedades fotocatalíticas e elétricasAcauan, Luiz Henrique January 2015 (has links)
Neste trabalho foi desenvolvido um procedimento experimental para a fabricação de estruturas 3D de nanotubos de carbono crescidos sobre substrato de cobre e decorados com partículas de óxido de titânio. Foram relacionados os três tipos diferentes de NTCs nesta estrutura (simples, dopados com nitrogênio e tratados com plasma) com a deposição do TiO2 por ALD. Foram igualmente propostas três aplicações para esta estrutura. A síntese dos NTCs verticalmente orientados, dopados e não dopados, foi otimizada dentre alguns parâmetros de síntese como temperatura, agente oxidante e principalmente, o filme catalisador. A introdução de defeitos nos NTCP através do tratamento a plasma oxidativo foi avaliada frente a variáveis como pressão, potência e tempo de exposição. A relação entre os defeitos destes três tipos de NTCs e a deposição de TiO2 por ALD foi avaliada por microscopia eletrônica de transmissão, Raman, XPS e TGA. O procedimento experimental para confecção da estrutura 3D foi desenvolvido etapa por etapa via diversas técnicas experimentais, desde caracterização química, imagem, até testes empíricos. Na estrutura final, foram avaliadas as propriedades fotocatalíticas pela decomposição de corante orgânico em meio aquoso, propriedades capacitivas por voltametria cíclica e propriedades de emissão por campo através de curvas de campo elétrico por corrente de emissão e diagramas F-N. Foram obtidas florestas de NTCs de boa qualidade com até 0.5mm de altura, de diâmetros e número de paredes regulares. Nestes foi possível introduzir defeitos de maneira controlável, mantendo o arranjo da floresta. As florestas de NTCNx alcançam uma altura de até 0,3mm com concentração de nitrogênio de 2% tendo os nanotubos uma estrutura típica “bamboo-like”. Os resultados mostram a relação entre o tipo de defeito e a deposição de TiO2 por ALD, obtendo-se partículas cristalinas para os NTCP e NTCNx, sendo neste ultimo as partículas homogeneamente distribuídas e com tamanho uniforme, enquanto nos NTCOx forma-se uma densa camada de TiO2 composta por grandes grãos monocristalinos A partir de processo como tratamentos térmicos e transferência dos NTC de substrato foi possível obter uma estrutura 3D composta de uma camada carbono grafítico e NTC-VAs sobre um substrato de cobre, sem alterar o arranjo inicial das florestas. As amostras mostraram efeito de emissão de elétrons por campo elétrico, porém estas requerem uma análise mais quantitativa. Os ensaios de fotocatálise mostraram que a imobilização do TiO2 em um suporte denso inviabiliza a degradação do corante em meio aquoso. Os NTCNx apresentaram maior capacitância que as mostras de NTCP, e o TiO2 foi aparentemente ineficaz para a melhoria desta propriedade. / In this work, we propose an experimental procedure for fabrication of 3D carbon nanotubes structures anchored with titanium oxide particles, on a copper substrate. We correlate three different types of CNTs from this structure (pristine, doped with nitrogen and treated with plasma) with the deposition of TiO2 by ALD. It was yet suggested, three applications for this structure. The synthesis of vertically aligned CNTs, doped and undoped, was optimized among several synthesis parameters such as temperature, oxidizing agent and specially, the catalyst film. The introduction of defects in NTCP by oxidative plasma treatment was evaluated against variables such as pressure, power and exposure time. The association between the defects from these three types of CNTs and the deposition of TiO2 by ALD was assessed by transmission microscopy, Raman, XPS and TGA. The experimental procedure for assembling the 3D structure had been studied step by step by various techniques, from chemical and imaging, up to empirical testing. In the final structure, the photocatalytic properties were evaluated by the organic dye decomposition in an aqueous medium, capacitive properties by cyclic voltammetry and field emission properties through electric field versus emission current curves and F-N diagram. Was obtained high quality NTCs with a height up to 0.5mm with regular diameters and number of walls. On these, it was introduced, in a controllable way, a high amount of defects without jeopardizing the forest structure. The NTCNx forest reach a 0,3nm height with a 2% nitrogen concentration in its typical structure “bamboo-like”. The results show the relation between the type of defect and the deposition of TiO2 by ALD, forming crystalline particles over the NTCP and NTCNx, in this last evenly distributed with uniform size, while on the NTCOx is is formed a dense TiO2 layer shaped by large monocrystalline grains. By process such as heat treatments and CNT transferring was achieved a 3d structure composed by a graphitic carbon layer and VACNTs over a cupper substrate, without disturb the forest assembly. The samples showed electron field emission effect, but its assessment for quantitative analysis was limited to technical issues. The photocatalysis tests showed that immobilization of TiO2 on a dense support prevents the dye degradation in an aqueous medium. The NTCNx shown higher capacitance than NTCP, and the TiO2 was apparently ineffective for improvement of this property.
|
4 |
Síntese de estruturas 3D de nanotubos de carbono verticalmente alinhados, dopados e não-dopados, decorados com nanopartículas de óxido de titânio, sua caracterização microestrutural e de propriedades fotocatalíticas e elétricasAcauan, Luiz Henrique January 2015 (has links)
Neste trabalho foi desenvolvido um procedimento experimental para a fabricação de estruturas 3D de nanotubos de carbono crescidos sobre substrato de cobre e decorados com partículas de óxido de titânio. Foram relacionados os três tipos diferentes de NTCs nesta estrutura (simples, dopados com nitrogênio e tratados com plasma) com a deposição do TiO2 por ALD. Foram igualmente propostas três aplicações para esta estrutura. A síntese dos NTCs verticalmente orientados, dopados e não dopados, foi otimizada dentre alguns parâmetros de síntese como temperatura, agente oxidante e principalmente, o filme catalisador. A introdução de defeitos nos NTCP através do tratamento a plasma oxidativo foi avaliada frente a variáveis como pressão, potência e tempo de exposição. A relação entre os defeitos destes três tipos de NTCs e a deposição de TiO2 por ALD foi avaliada por microscopia eletrônica de transmissão, Raman, XPS e TGA. O procedimento experimental para confecção da estrutura 3D foi desenvolvido etapa por etapa via diversas técnicas experimentais, desde caracterização química, imagem, até testes empíricos. Na estrutura final, foram avaliadas as propriedades fotocatalíticas pela decomposição de corante orgânico em meio aquoso, propriedades capacitivas por voltametria cíclica e propriedades de emissão por campo através de curvas de campo elétrico por corrente de emissão e diagramas F-N. Foram obtidas florestas de NTCs de boa qualidade com até 0.5mm de altura, de diâmetros e número de paredes regulares. Nestes foi possível introduzir defeitos de maneira controlável, mantendo o arranjo da floresta. As florestas de NTCNx alcançam uma altura de até 0,3mm com concentração de nitrogênio de 2% tendo os nanotubos uma estrutura típica “bamboo-like”. Os resultados mostram a relação entre o tipo de defeito e a deposição de TiO2 por ALD, obtendo-se partículas cristalinas para os NTCP e NTCNx, sendo neste ultimo as partículas homogeneamente distribuídas e com tamanho uniforme, enquanto nos NTCOx forma-se uma densa camada de TiO2 composta por grandes grãos monocristalinos A partir de processo como tratamentos térmicos e transferência dos NTC de substrato foi possível obter uma estrutura 3D composta de uma camada carbono grafítico e NTC-VAs sobre um substrato de cobre, sem alterar o arranjo inicial das florestas. As amostras mostraram efeito de emissão de elétrons por campo elétrico, porém estas requerem uma análise mais quantitativa. Os ensaios de fotocatálise mostraram que a imobilização do TiO2 em um suporte denso inviabiliza a degradação do corante em meio aquoso. Os NTCNx apresentaram maior capacitância que as mostras de NTCP, e o TiO2 foi aparentemente ineficaz para a melhoria desta propriedade. / In this work, we propose an experimental procedure for fabrication of 3D carbon nanotubes structures anchored with titanium oxide particles, on a copper substrate. We correlate three different types of CNTs from this structure (pristine, doped with nitrogen and treated with plasma) with the deposition of TiO2 by ALD. It was yet suggested, three applications for this structure. The synthesis of vertically aligned CNTs, doped and undoped, was optimized among several synthesis parameters such as temperature, oxidizing agent and specially, the catalyst film. The introduction of defects in NTCP by oxidative plasma treatment was evaluated against variables such as pressure, power and exposure time. The association between the defects from these three types of CNTs and the deposition of TiO2 by ALD was assessed by transmission microscopy, Raman, XPS and TGA. The experimental procedure for assembling the 3D structure had been studied step by step by various techniques, from chemical and imaging, up to empirical testing. In the final structure, the photocatalytic properties were evaluated by the organic dye decomposition in an aqueous medium, capacitive properties by cyclic voltammetry and field emission properties through electric field versus emission current curves and F-N diagram. Was obtained high quality NTCs with a height up to 0.5mm with regular diameters and number of walls. On these, it was introduced, in a controllable way, a high amount of defects without jeopardizing the forest structure. The NTCNx forest reach a 0,3nm height with a 2% nitrogen concentration in its typical structure “bamboo-like”. The results show the relation between the type of defect and the deposition of TiO2 by ALD, forming crystalline particles over the NTCP and NTCNx, in this last evenly distributed with uniform size, while on the NTCOx is is formed a dense TiO2 layer shaped by large monocrystalline grains. By process such as heat treatments and CNT transferring was achieved a 3d structure composed by a graphitic carbon layer and VACNTs over a cupper substrate, without disturb the forest assembly. The samples showed electron field emission effect, but its assessment for quantitative analysis was limited to technical issues. The photocatalysis tests showed that immobilization of TiO2 on a dense support prevents the dye degradation in an aqueous medium. The NTCNx shown higher capacitance than NTCP, and the TiO2 was apparently ineffective for improvement of this property.
|
5 |
Ionic and electronic transport in electrochemical and polymer based systemsVolkov, Anton January 2017 (has links)
Electrochemical systems, which rely on coupled phenomena of the chemical change and electricity, have been utilized for development an interface between biological systems and conventional electronics. The development and detailed understanding of the operation mechanism of such interfaces have a great importance to many fields within life science and conventional electronics. Conducting polymer materials are extensively used as a building block in various applications due to their ability to transduce chemical signal to electrical one and vice versa. The mechanism of the coupling between the mass and charge transfer in electrochemical systems, and particularly in conductive polymer based system, is highly complex and depends on various physical and chemical properties of the materials composing the system of interest. The aims of this thesis have been to study electrochemical systems including conductive polymer based systems and provide knowledge for future development of the devices, which can operate with both chemical and electrical signals. Within the thesis, we studied the operation mechanism of ion bipolar junction transistor (IBJT), which have been previously utilized to modulate delivery of charged molecules. We analysed the different operation modes of IBJT and transition between them on the basis of detailed concentration and potential profiles provided by the model. We also performed investigation of capacitive charging in conductive PEDOT:PSS polymer electrode. We demonstrated that capacitive charging of PEDOT:PSS electrode at the cyclic voltammetry, can be understood within a modified Nernst-Planck-Poisson formalism for two phase system in terms of the coupled ion-electron diffusion and migration without invoking the assumption of any redox reactions. Further, we studied electronic structure and optical properties of a self-doped p-type conducting polymer, which can polymerize itself along the stem of the plants. We performed ab initio calculations for this system in undoped, polaron and bipolaron electronic states. Comparison with experimental data confirmed the formation of undoped or bipolaron states in polymer film depending on applied biases. Finally, we performed simulation of the reduction-oxidation reaction at microband array electrodes. We showed that faradaic current density at microband array electrodes increases due to non-linear mass transport on the microscale compared to the corresponding macroscale systems. The studied microband array electrode was used for developing a laccase-based microband biosensor. The biosensor revealed improved analytical performance, and was utilized for in situ phenol detection.
|