Thesis (M Dent(Operative Dentistry))-- University of Limpopo, 2012. / The importance and demand for aesthetics has resulted in an increase in tooth-coloured restorations in dental practice. Composite undergoes polymerization using a curing device, after which it gains its physical and aesthetic properties. An improperly cured composite restoration is weak and prone to discolouration and secondary decay. The aim of this study was to determine and compare the effect that composite shade and curing distance would have on the depth of cure (DOC) of composite Filtek Silorane, Filtek Supreme XT and Z100. The scrape and penetrometer techniques were used to determine the DOC of the 450 specimens prepared. The DOC decreased with an increase in the curing distance and the darker shade had a lower DOC than the lighter shade for each of the composites tested. Both the scrape and penetrometer techniques yielded similar results in the DOC. Z100 had the highest DOC followed by Supreme XT and lastly Silorane. Thus a lighter composite shade in posterior teeth (non-aesthetic zone) and in deep Class II cavities will ensure an optimal depth of cure. The curing distance should be minimal and as close as possible to the composite surface to achieve an optimal depth of cure.

Thesis (M.S.)--University of Michigan, 1980.

Thesis (M.S.)--University of Michigan, 1980.

Thesis (M.S.)--University of Michigan, 1980.

Thesis (M.S.)--University of Michigan, 1980.

Thesis (M.S.)--University of Michigan, 1961.

Orientador: Rafael Leonardo Xediek Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:07:44Z (GMT). No. of bitstreams: 1 Cardoso_Leandro_M.pdf: 718836 bytes, checksum: 03cc173acd1c7745a9df4dd35a8a70dc (MD5) Previous issue date: 2009 / Resumo: O objetivo deste trabalho foi verificar a resistência ao impacto da união denteresina acrílica, sob efeito da desinfecção simulada por energia de microondas. Cento e sessenta matrizes retangulares de cera utilidade (30x15x5mm) foram incluídas na parte inferior de muflas, com gesso pedra tipo III. Depois da cristalização do gesso, a cera foi removida e cada um dos 160 moldes de gesso resultante foi preenchido com silicone laboratorial. Sobre o silicone foi adaptado um dente molar de resina acrílica contendo um cilindro de cera (25mm de comprimento por 6mm de diâmetro) fixado na base. O conjunto foi revestido com silicone, a mufla preenchida com gesso pedra tipo III e levada à prensa de bancada por 1 hora. Em seguida, a mufla foi aberta e os conjuntos dente-cilindros removidos dos moldes. Os dentes foram escovados com solução de água quente e detergente líquido e adaptados nos moldes, com as bases submetidas previamente aos seguintes tratamentos: 1- sem tratamento, 2- desgaste com broca, 3- retenção com broca e 4- condicionamento com monômero. Oitenta cilindros de resina unidos à base dos dentes foram confeccionados com resina acrílica Clássico, em ciclo de água à temperatura de 74ºC por 9 horas, em termopolimerizadora automática (Termotron) e outros 80 com resina para microondas Onda-Cryl, em forno doméstico com 900W de potência: fase 1- três minutos com 40% da potência; fase 2- quatro minutos com 0% da potência; e fase 3- três minutos com 90% da potência. Os corpos-de-prova foram desincluídos após esfriamento das muflas em bancada. Metade dos corpos-de-prova de cada resina foi submetido à desinfecção simulada por microondas, em forno doméstico a 650W por 3 minutos, imersos individualmente em 150mL de água. Os demais corpos-de-prova não foram desinfectados (controle). Após armazenagem em água à temperatura de 37ºC por 24 horas, os corpos-de-prova foram submetidos ao teste de resistência ao impacto da união dente-resina, numa máquina Otto Wolpert Werke (sistema Charpy) com 40 kpcm de impacto. Os resultados obtidos foram submetidos à análise de variância e ao teste de Tukey para comparação das médias, em nível de 5% de significância. Os diferentes tratamentos na base dos dentes promoveram diferentes efeitos sobre a resistência da união dente-resina, em ambas as condições de desinfeção por microondas / Abstract: The aim of this study was to evaluate the effect of microwave disinfection in bond strength of acrylic teeth and a denture base resin. A hundred sixty rectangular wax patterns (30x15x5mm) were embedded in flasks with type III dental stone. After cristalization, the resulting moulds were filled with laboratorial silicone (Zetalabor), in which a molar acrylic tooth was included (36 Biotone IPN Vita) using a cylindrical wax (6x25mm) to join to the tooth base. The set was invested using laboratorial silicone and type III dental stone. After 1 hour, the flask was opened, the cylindrical wax removed from the tooth. Teeth were adapted in the moulds with the ridge laps submitted previously to the following treatments: 1 - no treatment; 2 -bur abrasion; 3 - bur grooving, and 4 - etched by monomer. Eighty rods of the Clássico acrylic resin atached to the tooth ridge lap were polymerized in bath cycle at 74ºC for 9 hours and deflasked after flask cooling, and 80 of Onda-Cryl acrylic resin were polymerized in 900W-domestic microwave oven following manufacturer's instructions. Specimens were deflasked after bench cooling. Fourty specimens of each acrylic resin were submitted to microwave disinfection, in a domestic oven at 650W for 3 minutes, individually immersed in 150mL of water. Other specimens were not disinfected (control). Specimens were stored in water at 37oC for 24 hours before impact test. Charpy impact strength test was performed using an impact testing machine (Otto Wolpert Werke) calibrated to 40 kpcm. Data were submitted to analysis of variance and Tukey's test at 5% of significance level. Different treatments on tooth ridge lap promoted different effects in the tooth-resin bond strength, in both conditions of simulated disinfection by microwave energy / Mestrado / Protese Dental / Mestre em Clínica Odontológica

Thesis (M.S.)--University of Michigan, 1970.

Thesis (M.S.)--University of Michigan, 1970.

Orientador: Rafael Leonardo Xediek Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T08:12:10Z (GMT). No. of bitstreams: 1 Negreiros_WagnerAraujode_M.pdf: 1023466 bytes, checksum: 7bb8b4a8d3aafd26ecacaad6cdd6c73f (MD5) Previous issue date: 2006 / Resumo: A movimentação de dentes artificiais é um fenômeno frequentemente observado, em maior ou em menor grau, após o processamento das próteses totais. Diversos são os fatores implicados e essa alteração pode desequilibrar posições oclusais inicialmente planejadas. Este trabalho verificou o efeito dos tipos de contensão de muflas e do tempo pós-prensagem na movimentação de dentes em próteses totais, confeccionadas com 2 marcas de resina acrílica: Clássico (Clássico Produtos Odontológicos, SP, Brasil) e QC-20 (Dentsply Indústria e Comércio Ltda., Petrópolis, RJ). Foram confeccionadas 40 próteses totais superiores distribuídas aleatoriamente em 8 grupos (n=5) de acordo com o tipo de contensão (metálico convencional e RS) e com o tempo pós-prensagem (imediato e após 6 horas). Pinos referenciais metálicos foram posicionados na borda incisal dos incisivos centrais, na cúspide vestibular do primeiro pré-molar e cúspide mésio-vestibular dos segundos molares. As distâncias transversais I-I (incisivo a incisivo), PM-PM (pré-molar a pré-molar) e M-M (molar a molar), e ântero-posteriores ID-MD (incisivo direito a molar direito) e IE-ME (incisivo esquerdo e molar esquerdo) foram mensuradas antes e após o processamento, utilizando microscópio comparador (Olympus Optical Co., Tokyo, Japan), com precisão de 0,0005mm. As resinas acrílicas Clássico e QC-20 foram proporcionadas e manipuladas de acordo com as instruções dos fabricantes e submetidas aos ciclos de polimerização em água a 74ºC por 9 horas e em água em ebulição por 20 minutos, respectivamente. Os dados coletados foram transformados segundo o arco seno da raiz de x/100 e submetidos à análise de variância. As médias percentuais foram comparadas pelo teste de Tukey em nível de 5% de significância. As interações resina-tipo de contensão e resina-tempo pós-prensagem, independente dos demais fatores não mostraram diferença estatística significativa no percentual médio de movimentação dental; houve diferença estatística significativa na distância I-I para a contensão convencional na pós-prensagem imediata, com maior valor para a resina Clássico. Na pós-prensagem 6 horas não houve diferença estatística significativa entre as resinas; houve diferença estatística significativa na distância I-I para o sistema RS na pós-prensagem imediata, com maior valor para a resina Clássico. Na pós-prensagem 6 horas, as distâncias I-I e IE-ME foram com diferença estatística significativa, sendo maior para a resina Clássico na distância I-I e menor na distância IE-ME; somente a distância I-I apresentou diferença estatística significativa para a resina Clássico com grampo convencional, sendo o maior valor no tempo imediato; o percentual médio de deslocamento dental para as resinas Clássico e QC-20 com o sistema RS foi sem diferença estatística significativa entre os tempos pós-prensagem. O autor concluiu que as alterações percentuais não foram uniformes sofrendo influência de resinas, tempo pós-prensagem e distância entre dentes / Abstract: Tooth displacement is a common phenomenon observed after complete denture processing. Some factors may be involved and this alteration can modify the proposed occlusal scheme. This study verified the effect of the flask pressure methods and post-pressing time prior to polymerization on tooth movement in maxillary complete dentures fabricated with Classico and QC-20 heat-cured acrylic resins. Forty maxillary complete dentures were fabricated and randomly assigned into 8 groups (n=5), according to the flask pressure methods (conventional and RS system) and the post-pressing time (immediate and after 6 hours). Metallic referential pins were placed in the incisal border of the central incisors, vestibular cusp of the first premolars and the mesio-vestibular cusp of the second molars. The I-I (incisor to incisor), PM-PM (premolar to premolar), M-M (molar to molar) transversal distances and RI-RM (right incisor to right molar) and LI-LM (left incisor to left molar) anteroposterior distances were measured before and after complete dentures processing with a linear Olympus optical microscope, with an accuracy of 0,0005mm. Classico and QC-20 acrylic resins were proportioned and manipulated following the manufacturer¿s directions, and submitted to the conventional water bath at 74ºC for 9 hours or to water boiled bath for 20 minutes curings. Collected data in percent were transformed in arch seno of the root of x/100 and submitted to the variance analysis and Tukey test at 5% of significance. The resin-flask pressure methods and resin-post pressing time interactions, independently of other factor showed no statistically significant difference in the mean percentages of dental displacement; there was statistically significant difference in the I-I distance for conventional clamp in immediate post-pressing, with greater value for Classico resin. In the 6-hour post-pressing there was no statistically significant difference between resins; there was statistically significant difference in the I-I distance for RS system in the immediate post-pressing, with greater value for Classico resin. In the 6-hour post-pressing, the I-I and IE-ME distances were with statistically significant difference, being greater for Classico resin in I-I distance and smaller in IE-ME distance; only the I-I distance showed statistically significant difference for Classico resin with conventional clamp, being greater for the immediate post-pressing time; the mean percentages in the tooth displacement for Classico and QC-20 resins with the RS system was without statistically significant difference between post-pressing times. The author concluded that the percentage changes were not uniform being influenced by resins, post-pressing time and distance among teeth / Mestrado / Protese Dental / Mestre em Clínica Odontológica