This master‘s thesis is focused on the study of the behavior of cement concrete at high temperatures with a focus on monitoring the impact of aggregate and cement type. This work describes the processes in aggregates and cement matrix at high temperatures. The theoretical part describes the selestion of a suitable aggregate and cement for the surroundings with potential exposure to high temperatures. In the experimental part is given design of composition of a concrete with two types of aggregates and four cements. It has been suggested 8 recipes. Changes were observed densities, compressive strength and tensile strength in bending, calculate the velocity of propagation of waves with ultrasonic pulsed method. Also evaluated the appearance of the surface samples after thermal load – cracks on the surface and measure the maximum crack width.

Nondestructive testing methods are employed as a tool for evaluation of parameters of building materials, especially to ascertain strength properties and to determine alteration occured during durability tests. An ultrasonic pulse velocity method is one of the most used nondestructive methods. A resonance method is employed among the nondestructive methods less. The aim of this work is to establish the calibration relationships between parameters of nondestructive testing and compressive strength value and flexural tensile strength value, respectively. Moreover, applicability of the calibration relationships is also discussed.

The dissertation thesis deals with the study of non-destructive acoustic methods as instruments for monitoring and analysing corrosion of reinforcing steel in reinforced concrete elements. Four acoustic methods were selected for this task - the impact-echo method, the nonlinear acoustic spectroscopy method, the acoustic emission method, and the ultrasonic pulse velocity method. To verify the functionality of these methods, testing was carried out on three sets of reinforced concrete samples that had been exposed to the effects of sodium chloride, which corroded the embedded steel reinforcement in these samples. Suitable parameters were proposed for individual acoustic methods to monitor corrosion of the reinforcements. In addition, experiments were designed to demonstrate the ability of the selected acoustic methods to reveal the corrosion of steel reinforcement and its influence on the concrete matrix and to assess the condition of the degraded elements and structures. The analysis of the measurement results based on their comparison shows the advantages and disadvantages of the individual methods and of their practical applications. To verify the results, correlation with common methods that are currently used for the study of corrosion was carried out and included for example the electrical resistivity measurement of the reinforcement and simultaneous monitoring of the sample surface using a confocal microscope to record the development of microcracks during the degradation.

This work solves creation of calibration relations to determine cube compressive strength, dynamic and static elastic modulus of alkali-activated concrete by non-destructive methods. Alkali-activated concrete is spoken of as a new material used in civil engineering. It shows different properties than normal concrete based on Portland cement. That's why the modification of common calibration relation seems necessary. Fresh concrete was made in the concrete plan ŽPSV a.s., Uherský Ostroh in three mixtures and always in the number of 18 cubes and 3 prisms. The samples were tested by impact hammer Schmidt type L, type N, SilverSchmidt PC-N and by ultrasound in 6 time periods of three specimens. After that, the cube compressive strength was determined. Status of static elastic modulus was determined in a time period of 28 days. The results are calibration relations to determine the progress of compressive strength and modulus of elasticity for each method and their combination.

The thesis deals with the measurement of the elastic modulus of concrete in existing structures and possibilities of applicability of equations for the calculation of characteristic values of concrete compressive strength on the modulus of elasticity. The modulus of elasticity is determined by dynamic and static methods on specimens taken from the concrete blocks, whose composition varies by a water cement ratio and varying amounts of admixtures. In conclusion, the results of the measurements are compared and the characteristic values of the modulus of elasticity is determined.

Since their inception, building materials are constantly improving. New ways to explore and improve the material's properties are constantly investigated (especially to improve the mechanical and deformation characteristics of the materials). This thesis is focused on identifying and comparing values of the modulus of elasticity of fine-grained composites. These features are compared with respect to water cement ratio, ageing and compressive strength of the investigated materials. Afterwards, the values of the modulus of elasticity are studied in the relation to the tested materials.

This diploma thesis targets on diagnostics and assessment of bridge structure Most Kaštanová přes Svitavu, reg. number 380-001. Concrete material characteristics have been assessed in laboratory, after visual inspection, diagnostical testing and sample core drilling were made. Findings from laboratory tests are summarized in the conclusion of the thesis. It focuses on an evaluation of current bridge condition and presents various options that will help polong lifetime of the bridge.

The master‘s thesis focuses on testing the shotcrete prepared in laboratory conditions. The main observed properties are compresive strenght of shotcrete and modulus of elasticity. The aim is assessment of methods for measuring those parameters. The calibrating correlations for strenght characteristics of shotcrete are given by obtaining the results of used methods. The shotcrete composition, amount and type of accelerating additive as well as economic aspect of using shotcrete is also assessed.