Coating of High Strength Steels with a Zn-1.6Al-1.6Mg Bath / Selective Oxidation and Reactive Wetting of High Strength Steels by a Zn-1.6Al-1.6Mg BathDe Rango, Danielle M. January 2019 (has links)
Recently, Zn-XAl-YMg coatings have emerged as lighter-weight substitutes for traditional Zn-based coatings for the corrosion protection of steels; however, little is currently known concerning the interactions between the oxides present on advanced high strength steel (AHSS) surfaces and the Zn-Al-Mg bath. In the current contri- bution, the selective oxidation and reactive wetting of a series of C-Mn AHSS were determined with the objective of providing a quantitative description of this pro- cess. The process atmosphere pO2 was varied using dew points of −50◦C, −30◦C and −5◦C. The surface oxide chemistry and morphology were analysed by means of SEM and XPS techniques. Reactive wetting of the selectively oxidized surfaces using a Zn-1.6 wt.% Al-1.6 wt.% Mg bath was monitored as a function of annealing time at 60 s, 100 s and 140 s at 800◦C. The resulting bare spot defects in the Zn-1.6 wt.% Al-1.6 wt.% Mg coating were assessed by means of SAM-AES and FIB, while coating adhesion was analysed by 180◦ bend tests. Annealing the steel substrates resulted in the formation of surface MnO, which varied based on pO2 and Mn alloy content, and that this MnO greatly reduced the wettability of the steel by the Zn-1.6 wt.% Al- 1.6 wt.% Mg bath, resulting in bare spot defects. It was determined that the reactive wetting of the steel substrate was dependant on the oxide morphology and oxidation mode, which was a function of both alloying content of Mn in the steel and annealing pO2 process atmosphere (dew point). Finally, it was concluded that the bare spot area percentage on the coated panels was statistically invariant for annealing times of between 60 s and 140 s at 800◦C. / Thesis / Master of Applied Science (MASc) / Metallic coatings are applied to steels that are not naturally corrosion resistant. The aim of this research was to determine how well a coating containing zinc, aluminum and magnesium adhered to high strength automotive steel. It was deter- mined that manganese oxides formed on the steel during heating prior to applying the metallic coating. The manganese oxides prevented good adhesion between the steel and the coating, resulting in bare spot defects in the coating. The bare spot defects are undesirable as they leave the steel exposed and therefore susceptible to corrosion and are unsightly when painted.
|
Page generated in 0.0663 seconds