1 |
Analytical Description of Brittle-to-Ductile Transition in bcc Metals. Nucleation of dislocation loop at the crack tipVoskoboinikov, Roman E. 31 March 2010 (has links) (PDF)
Nucleation of dislocation loop at the crack tip in a material subjected to uniaxial loading is investigated. Analytical expression for the total energy of rectangular dislocation loop at the crack tip is found. Depencence of the nucleation energy barrier on dislocation loop shape and stress intensity factor at the crack tip is determined. It is established that the energetic barrier for nucleation of dislocation loop strongly depends on the stress intensity factor. Nucleation of dislocation loop is very sensitive to stress field modifiers (forest dislocations, precipitates, clusters of point defects, etc.) in the crack tip vicinity.
|
2 |
Analytical Description of Brittle-to-Ductile Transition in bcc Metals. Nucleation of dislocation loop at the crack tipVoskoboinikov, Roman E. January 2002 (has links)
Nucleation of dislocation loop at the crack tip in a material subjected to uniaxial loading is investigated. Analytical expression for the total energy of rectangular dislocation loop at the crack tip is found. Depencence of the nucleation energy barrier on dislocation loop shape and stress intensity factor at the crack tip is determined. It is established that the energetic barrier for nucleation of dislocation loop strongly depends on the stress intensity factor. Nucleation of dislocation loop is very sensitive to stress field modifiers (forest dislocations, precipitates, clusters of point defects, etc.) in the crack tip vicinity.
|
3 |
Estudo da usinabilidade do ZERODUR® no torneamento de ultraprecisão com ferramenta de diamante de ponta única / Study of ZERODUR® machinability using single point diamond turningOtoboni, José Antonio 30 August 2013 (has links)
Alguns espelhos usados em câmeras de satélite devem apresentar qualidade superficial elevada. Eles são normalmente fabricados em ZERODUR®, um material vitrocerâmico, por meio de processos abrasivos. Observou-se que a qualidade da superfície do material deteriora-se algum tempo após a usinagem, necessitando assim de retrabalho. A causa mais influente desse fenômeno é o crescimento de trincas devido à corrosão sobtensão. Estas trincas são geradas pelas condições impostas nos processos convencionais de lapidação e polimento. Este trabalho apresenta um estudo sobre a usinabilidade do ZERODUR® utilizando torneamento de ultraprecisão com ferramenta de diamante de ponta única como uma alternativa a estes métodos tradicionais. Amostras de ZERODUR® foram submetidas a testes de indentação e riscamento a fim de se estudar as propriedades mecânicas do material, a transição dúctil-frágil e os mecanismos de remoção de material. Com base nesses testes, foi delineado um experimento fatorial do tipo 23 para avaliar a influência das seguintes variáveis de usinagem: profundidade de corte, nos níveis 0,4 e 0,2 \'mü\'m, taxa de avanço, nos níveis 0,3 e 0,1 \'mü\'m/rev e ângulo de saída da ferramenta, nos níveis -5º e -20º. As amostras do experimento foram usinadas em um torno de ultraprecisão com a ferramenta de diamante de ponta única. A qualidade superficial de cada combinação foi avaliada por microscopia eletrônica de varredura e perfilometria óptica interferométrica. Os resultados dos experimentos foram analisados estatisticamente, por meio de análise de variância (ANOVA). Para os intervalos das variáveis testadas verificou-se que o ângulo de inclinação da ferramenta é o que mais afeta a qualidade superficial. Ângulos com inclinações mais negativas (-20º) proporcionaram as melhores qualidades superficiais (em torno de 200 nm). Nos resultados não houve evidência de que o corte do material tenha ocorrido dentro do regime dúctil. Porém, a rugosidade superficial encontrada em algumas combinações de corte sugere que o torneamento de ultraprecisão pode ser uma alternativa ao processo lapidação que antecede o polimento. Este trabalho de caráter exploratório contribui com estimativas de alguns parâmetros ótimos para usinagem do ZERODUR®, fornecendo subsídios para pesquisas futuras sobre este tema. / Some mirrors used in satellite cameras must present a high surface quality. They are usually made of ZERODUR®, a brittle glass ceramic, by means of abrasive processes. It was observed that the surface quality of the material deteriorates some time after the machining, thus requiring rework. The most influential cause of this phenomenon is the crack growth due to stress corrosion. These cracks are generated by the conventional machining processes of lapping and polishing. This work presents a study on the machinability of ZERODUR® using ultraprecision turning with single-point diamond tool as an alternative to these traditional methods. ZERODUR® samples were subjected to indentation and nano-scratching tests in order to study the ductile-brittle transition and material removal mechanisms. After that, a \'2 POT.3\' factorial experiment was designed in order to assess the influence of three machining parameters on the resulting surface roughness, which are: depth of cut (tested at levels 0,4 and 0,2 \'mü\'m), feed rate (tested at levels 0,3 and 0,1 \'mü\'m/rev) and rake angle of the cutting tool (tested at levels -5º e -20º). The samples were turned with single-point diamond tool using different combinations of the parameters at the levels described above. The surface quality of each sample was evaluated using an interferometric optical profiler and a scanning electron microscope (SEM). The results of the experiments were statistically evaluated by means of Analysis Of Variance (ANOVA). For the ranges tested, it was found that the rake angle of the tool was the most influential parameter. The angle of -20º provided the best values for surface quality, which were around 200 nm. There was no evidence that the cut of the material occurred in the ductile regime, however, the obtained surface roughness showed that the ultraprecision turning may be a feasible alternative for the lapping process of optical components. This exploratory research contributes to the existing knowledge by providing estimates for optimal parameters of ZERODUR® machining, furnishing empirical basis for future research in this field.
|
4 |
Estudo da usinabilidade do ZERODUR® no torneamento de ultraprecisão com ferramenta de diamante de ponta única / Study of ZERODUR® machinability using single point diamond turningJosé Antonio Otoboni 30 August 2013 (has links)
Alguns espelhos usados em câmeras de satélite devem apresentar qualidade superficial elevada. Eles são normalmente fabricados em ZERODUR®, um material vitrocerâmico, por meio de processos abrasivos. Observou-se que a qualidade da superfície do material deteriora-se algum tempo após a usinagem, necessitando assim de retrabalho. A causa mais influente desse fenômeno é o crescimento de trincas devido à corrosão sobtensão. Estas trincas são geradas pelas condições impostas nos processos convencionais de lapidação e polimento. Este trabalho apresenta um estudo sobre a usinabilidade do ZERODUR® utilizando torneamento de ultraprecisão com ferramenta de diamante de ponta única como uma alternativa a estes métodos tradicionais. Amostras de ZERODUR® foram submetidas a testes de indentação e riscamento a fim de se estudar as propriedades mecânicas do material, a transição dúctil-frágil e os mecanismos de remoção de material. Com base nesses testes, foi delineado um experimento fatorial do tipo 23 para avaliar a influência das seguintes variáveis de usinagem: profundidade de corte, nos níveis 0,4 e 0,2 \'mü\'m, taxa de avanço, nos níveis 0,3 e 0,1 \'mü\'m/rev e ângulo de saída da ferramenta, nos níveis -5º e -20º. As amostras do experimento foram usinadas em um torno de ultraprecisão com a ferramenta de diamante de ponta única. A qualidade superficial de cada combinação foi avaliada por microscopia eletrônica de varredura e perfilometria óptica interferométrica. Os resultados dos experimentos foram analisados estatisticamente, por meio de análise de variância (ANOVA). Para os intervalos das variáveis testadas verificou-se que o ângulo de inclinação da ferramenta é o que mais afeta a qualidade superficial. Ângulos com inclinações mais negativas (-20º) proporcionaram as melhores qualidades superficiais (em torno de 200 nm). Nos resultados não houve evidência de que o corte do material tenha ocorrido dentro do regime dúctil. Porém, a rugosidade superficial encontrada em algumas combinações de corte sugere que o torneamento de ultraprecisão pode ser uma alternativa ao processo lapidação que antecede o polimento. Este trabalho de caráter exploratório contribui com estimativas de alguns parâmetros ótimos para usinagem do ZERODUR®, fornecendo subsídios para pesquisas futuras sobre este tema. / Some mirrors used in satellite cameras must present a high surface quality. They are usually made of ZERODUR®, a brittle glass ceramic, by means of abrasive processes. It was observed that the surface quality of the material deteriorates some time after the machining, thus requiring rework. The most influential cause of this phenomenon is the crack growth due to stress corrosion. These cracks are generated by the conventional machining processes of lapping and polishing. This work presents a study on the machinability of ZERODUR® using ultraprecision turning with single-point diamond tool as an alternative to these traditional methods. ZERODUR® samples were subjected to indentation and nano-scratching tests in order to study the ductile-brittle transition and material removal mechanisms. After that, a \'2 POT.3\' factorial experiment was designed in order to assess the influence of three machining parameters on the resulting surface roughness, which are: depth of cut (tested at levels 0,4 and 0,2 \'mü\'m), feed rate (tested at levels 0,3 and 0,1 \'mü\'m/rev) and rake angle of the cutting tool (tested at levels -5º e -20º). The samples were turned with single-point diamond tool using different combinations of the parameters at the levels described above. The surface quality of each sample was evaluated using an interferometric optical profiler and a scanning electron microscope (SEM). The results of the experiments were statistically evaluated by means of Analysis Of Variance (ANOVA). For the ranges tested, it was found that the rake angle of the tool was the most influential parameter. The angle of -20º provided the best values for surface quality, which were around 200 nm. There was no evidence that the cut of the material occurred in the ductile regime, however, the obtained surface roughness showed that the ultraprecision turning may be a feasible alternative for the lapping process of optical components. This exploratory research contributes to the existing knowledge by providing estimates for optimal parameters of ZERODUR® machining, furnishing empirical basis for future research in this field.
|
5 |
Influence du sodium liquide sur le comportement mécanique de l'acier T91 / Study of the influence of liquid sodium on the mechanical behavior of T91 steel in liquid sodiumHémery, Samuel 26 November 2013 (has links)
Nous avons étudié la sensibilité du T91 à la fragilisation par le sodium liquide. Une procédure expérimentale a été mise en place afin de procéder à des essais mécaniques en sodium sous atmosphère inerte. Grâce à l’introduction d’une étape préliminaire d’exposition au sodium, la mouillabilité du T91 par le sodium liquide et la structure de l’interface sodium/acier ont pu être étudiés en fonction des différents paramètres d’exposition. Une réduction significative des propriétés mécaniques est observée quand le mouillage de l’acier par le sodium est bon. L’utilisation de différentes teneurs en oxygène et en hydrogène suggère que l’oxygène joue un rôle primordial dans l’amélioration de la mouillabilité du T91. La sensibilité du phénomène de fragilisation à la vitesse de sollicitation et à la température a été caractérisée. A partir de ces résultats, l’existence d’une transition fragile/ductile, fonction de ces deux paramètres a été mis en évidence. L’étude de cette transition suggère qu’une étape de diffusion du sodium dans les joints de grains du T91 est limitante pour la fragilisation. Des analyses en microscopie électronique en transmission et par cartographies d’orientation de fissures arrêtées ont également permis de constater que le mode de rupture est interlatte ou intergranulaire, fournissant ainsi une image cohérente du processus de fragilisation. La même méthodologie a été appliquée à l’acier non allié XC10. Les résultats montrent un comportement en tous points similaire à celui de l’acier T91 et suggèrent donc un mécanisme commun pour les aciers cubiques centrés. De plus, ils confirment que la transition fragile ductile observée semble la conséquence d’une vitesse de propagation de fissure fragile relativement limitée. Cette propagation est activée thermiquement avec une énergie d’activation d’environ 50 kJ/mol. Enfin, il a été montré que l’acier austénitique 304L est également sensible à la fragilisation par le sodium liquide. Certaines surfaces de rupture témoignent clairement d’une rupture intergranulaire, cependant des interrogations persistent à propos du chemin de fissuration. / We studied the sensitivity of T91 steel to embrittlement by liquid sodium. An experimental procedure was set up to proceed to mechanical testing in sodium under an inert atmosphere. The introduction of a liquid sodium pre-exposure step prior to mechanical testing enabled the study of both the wettability of T91 by sodium and the structure of the sodium steel/interface as a function of the exposure parameters. The mechanical properties of T91 steel are significantly reduced in liquid sodium provided the wetting conditions are good. The use of varying oxygen and hydrogen concentrations suggests that oxygen plays a major role in enhancing the wettability of T91. The sensitivity of the embrittlement to strain rate and temperature was characterized. These results showed the existence of a ductile to brittle transition depending on both parameters. Its characterization suggests that a diffusion step is the limiting rate phenomenon of this embrittlement case. TEM and EBSD analysis of arrested cracks enabled us to establish that the fracture mode is interlath or intergranular. This characteristic is coherent with the crack path commonly reported in liquid metal embrittlement. A similar procedure was applied to the unalloyed XC10 steel. The results show a behavior which is similar to the one of T91 steel and suggest a common mechanism for liquid sodium embrittlement of body centered cubic steels. Moreover, they confirm that the ductile to brittle transition seems associated with a limited crack propagation rate. The propagation is thermally activated with activation energy of about 50 kJ/mol. Finally, it was shown that 304L austenitic steel is sensitive to liquid sodium embrittlement as well. Some fracture surfaces testify of an intergranular fracture mode, but some questions still remain about the crack path.
|
6 |
Uticaj mikrostrukture na prelaznu temperaturu ADI materijala / Microstructure influence on ductile to brittle transition temperature of ADI materialsRajnović Dragan 10 July 2015 (has links)
<p>U disertaciji je izvršena karakterizacija mikrostrukture i mehaničkih osobina<br />nelegiranog austemperovanogi nodularnog liva (ADI materijala), kao i uticaja<br />mikrostrukture na prelaznu temperaturu u intervalu od -196 do +100°C.<br />Utvrđeno je da mehaničke osobine ADI-ja zavise od morfologije ausferitne<br />mikrostrukture i količine zadržanog austenita, tj. parametara austemperovanja.<br />Na osnovu mehaničkih osobina utvrđen je i opseg procesiranja u skladu sa<br />standardima ASTM, ISO i EN. Zaključeno je da prelazna temperatura ADI<br />materijala zavisi od količine i stabilnosti zadržanog austenita. U višem<br />temperaturnom opsegu (iznad cca. -25°C) dominantna je količina zadržanog<br />austenita, dok na nižim temperaturama, stabilnost. Visoka obogaćenost<br />ugljenikom, stabilnog zadržanog austenita sprečava stvaranje martenzita na<br />niskim temperaturama, a time i pojavu krtosti kod ADI-ja.</p> / <p>The object of this thesis was to characterize microstructure and mechanical properties<br />of the unalloyed ADI material (Austempered Ductile Iron). In addition, the influence of<br />microstructure on the ductile to brittle transition temperature (DBTT) by Charpy impact<br />test in temperature interval from 196 to +100°C has been studied. The all properties<br />obtained depend on the morphology of microstructure and the amount of retained<br />austenite, i.e. on the austempering parameters. According to the mechanical properties<br />and standard requirements (ASTM, ISO and EN) the processing window has been<br />proposed, also. It was found that DBTT is influenced by amount and stability of retained<br />austenite. In upper temperature range (above cca. 25°C) the most influence factor on<br />DBTT is amount of retained austenite, while at the lower temperatures the stability is<br />more prominent. Stability of high carbon retained austenite at lower temperatures<br />prevents transformation to martensite and thus the embrittlement of ADI.</p>
|
7 |
Metodologia para simulação computacional da distribuição de temperaturas para identificar sub-regiões reaquecidas da ZAC e avaliar suas influências nas propriedades mecânicas na soldagem multipasse de aço API 5L X80. / Sem título em inglêsFerreira, Dario Magno Batista 17 August 2017 (has links)
Em projetos de oleodutos e gasodutos utilizam-se aços de alta resistência e baixa liga (ARBL), como o aço API 5L X80. Na soldagem multipasse destas tubulações, a zona afetada pelo calor (ZAC) do passe de raiz é submetida a um novo ciclo térmico pelos passes de soldagem subsequentes. Isto resulta em alterações nos valores das propriedades físicas. Nos aços ARBL, a ZAC de grãos grosseiros reaquecida intercriticamente (IC-ZACGG) pode se tornar uma zona frágil localizada, isto é, uma zona com maior dureza. Consequentemente, falhas estruturais podem ocorrer, ocasionando paradas não desejadas no transporte de fluidos. O objetivo deste trabalho é desenvolver uma metodologia baseada no modelo de fontes de calor distribuídas de Mhyr e Gröng, para avaliar o fluxo de calor na soldagem considerando as propriedades físicas dependentes da temperatura. Estender a aplicação desta ferramenta em soldagens multipasses para identificar sub-regiões da ZAC de um passe anterior sendo afetada pela ZAC de passes subsequentes. As isotermas simuladas foram validadas através de medições realizadas em macrografias de juntas soldadas. Os ciclos térmicos simulados foram validados através das temperaturas máximas atingidas e pelos tempos de resfriamento de 800 a 500 ºC (?t8-5) dos ciclos térmicos experimentais. Ao aplicar a metodologia proposta, foi possível delimitar com acurácia as regiões reaquecidas da ZAC e analisar os efeitos dos passes subsequentes em cada uma das sub-regiões da ZAC do passe de raiz. A IC-ZACGG na região do passe de raiz foi localizada, mas não se comportou como zona frágil devido à boa soldabilidade do aço API 5L X80 comprovada pelos ensaios de dureza e de tenacidade ao impacto Charpy-V. / In pipelines projects, the high strength low alloy (HSLA) steels are used, such as the API 5L X80 steel. During the multipass welding of these pipes, the heat affected zone (HAZ) of the root pass is subjected to a new thermal cycle by the subsequent welding passes. This results in changes in the values of the physical properties. In the HSLA steels, the intercritical reheated coarse-grained heat-affected zone (IR-CGHAZ) can become a local brittle zone, that is, a region with greater hardness. Consequently, structural failures could happen, causing undesired shutdowns in fluid transportation. The objective of this work is to develop a methodology based on the distributed heat sources model of Mhyr and Gröng, to evaluate the heat flux in the welding considering the temperature-dependent physical properties. Extend the application of this tool in multipass welds to identify HAZ subregions of a previous pass being affected by the HAZ of subsequent passes. The simulated isotherms were validated through measurements made on macrographs of welded joints. The simulated thermal cycles were validated through the maximum temperatures reached and the cooling times from 800 °C to 500 ºC (?t8-5) of the experimental thermal cycles. By applying the proposed methodology, it was possible to accurately delimit reheated HAZ regions and analyze the effects of subsequent passes in each of the root pass HAZ subregions. The IRCGHAZ in the root pass region was localized, but it did not behave as a brittle zone due to the good weldability of the API 5L X80 steel as proven by the hardness and Charpy-V impact tests.
|
8 |
Avaliação da tenacidade à fratura e do efeito da microtextura e mesotextura na curva de transição dúctil frágil do aço API 5L X70Haskel, Hudison Loch 25 March 2013 (has links)
Made available in DSpace on 2017-07-21T20:42:39Z (GMT). No. of bitstreams: 1
Hudison.pdf: 7678712 bytes, checksum: 77d524c573ba60402f77fbda4e17c5e9 (MD5)
Previous issue date: 2013-03-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In the present study was investigated the API 5L X70 steel mechanical behavior through tensile and instrumented impact tests. Results from the instrumented Charpy impact test have allowed quantify the forces, energies and deflections of the specimens. It was used to obtain the fracture mechanics parameters such as the dynamic fracture toughness JId, the stress intensity factor for dynamic loading KId, as also range the ductile brittle transition temperature. Simultaneously was evaluated the mechanisms that induce to the delamination phenomenon as well as the investigation of their influence on the absorbed energy during the impact test. It was also analyzed the microtexture and mesotexture of different samples from the brittle, ductile and mixed regions from the ductile brittle transition temperature curve. Results have shown that the longitudinal direction was slightly superior mechanical properties when compared to the transverse direction. The dynamic fracture toughness JId was higher for the L-T specimen orientation when compared to the T-L orientation and it tends to increase with increasing temperature for both directions. The stress intensity factor values for dynamic loading was close to in both L-T and T-L orientations. The microtexture has revealed that deformation process from the impact test preserves some of its characteristics from the prior processing such as phase transformations and recrystallization components. While the mesotexture feature has shown higher energy values in the ductile brittle transition temperature curve, it is resulted from the formation of deformation substructure. Results obtained by scanning electron microscopy and light microscopy have shown that the main factors that may be contributing to the formation of crack-divider type delaminations are banded microstructure and elongated ferrite grains. While the microtexture from the edges delamination has shown that propagation mechanism is intergranular. Taylor factor mapping has shown that the mechanism responsible for the formation of delamination is accompanied by low plastic deformation. / No presente trabalho foi investigado o comportamento mecânico do aço API 5L X70 através de ensaios de tração e impacto instrumentado. O ensaio de impacto Charpy instrumentado permitiu quantificar as forças, energias e deflexões dos corpos de prova. Com a utilização destes dados foram obtidos parâmetros da mecânica da fratura, tais como, a tenacidade à fratura dinâmica JId, o fator de intensidade de tensão para carregamento dinâmico KId, além da faixa de valores da temperatura de transição dúctil frágil. Concomitantemente foram avaliados os mecanismos que contribuem na formação do fenômeno conhecido como delaminação, bem como a investigação de sua influência sobre a energia absorvida durante o ensaio de impacto. Foram também analisadas a microtextura e mesotextura de diferentes amostras retiradas da região frágil, dúctil e mista, da curva de transição dúctil frágil do material. Os resultados mostraram que o material possui propriedades mecânicas de impacto ligeiramente superiores na direção longitudinal à laminação comparado à direção transversal. Os valores encontrados para a tenacidade à fratura dinâmica JId são superiores para corpos de prova com orientação L-T quando comparados para a orientação T-L, e tendem a aumentar com o aumento da temperatura para ambas orientações. Os valores encontrados para o fator de intensidade de tensão para carregamento dinâmico foram próximos para ambas as orientações L-T e T-L. A microtextura revelou que após a deformação no ensaio de impacto o aço preserva algumas das características do seu histórico de processamento tais como componentes de transformações de fase e recristalização. Enquanto que o estudo da mesotextura mostrou que maiores valores de energia na curva de transição dúctil frágil resultam na formação de uma subestrutura de deformação. Resultados obtidos por microscopia eletrônica de varredura e microscopia ótica mostraram que os principais fatores que podem estar contribuindo para formação de delaminações do tipo trinca divisora são a microestrutura bandeada e grãos alongados de ferrita. Enquanto que a microtextura nas bordas da delaminação mostrou que o seu mecanismo de propagação é intergranular. O mapeamento do fator de Taylor mostrou que o mecanismo responsável pela formação da delaminação é acompanhado por pouca deformação plástica.
|
9 |
Integridad estructural de vasijas nucleares en base a la curva patrón obtenida mediante probetas reconstruidasFerreño Blanco, Diego 01 February 2008 (has links)
En esta tesis se ha caracterizado el acero, virgen e irradiado, de la vasija de una central nuclear española actualmente en servicio, en la región de temperaturas conocida como Zona de Transición Dúctil-Frágil. Para ello, se han ensayado probetas propias de la Mecánica de Fractura, reconstruidas a partir de mitades de probetas de impacto previamente ensayadas. Para describir la tenacidad a fractura en la Zona de Transición se ha empleado el modelo de la Curva Patrón.Finalmente, se ha analizado el impacto del procedimiento de caracterización y del modelo de la Curva Patrón sobre la Integridad Estructural de la vasija, comparando sus predicciones con las que se obtienen de aplicar los procedimientos convencionales que contempla la normativa vigente, representada por el Código ASME. En esta comparación se ha hecho uso del procedimiento FITNET de Integridad Estructural. / In this thesis, the steel, virgin and irradiated, from the vessel of a Spanish Nuclear Plant currently operating, has been characterized in the range of temperatures known as Ductile to Brittle Transition Region. For this purpose, Fracture Mechanics specimens, reconstituted from halves of impact specimens previously broken, have been tested. To describe fracture toughness in the Transition Region, the Master Curve method has been used.Eventually, the influence of the characterization procedure together with the Master Curve method on the Structural Integrity of the vessel has been analyzed, comparing their predictions with those coming from applying conventional procedures proposed by the current regulations, represented by the ASME Code. In this comparison, the FITNET Structural Integrity procedure has been used.
|
10 |
Metodologia para simulação computacional da distribuição de temperaturas para identificar sub-regiões reaquecidas da ZAC e avaliar suas influências nas propriedades mecânicas na soldagem multipasse de aço API 5L X80. / Sem título em inglêsDario Magno Batista Ferreira 17 August 2017 (has links)
Em projetos de oleodutos e gasodutos utilizam-se aços de alta resistência e baixa liga (ARBL), como o aço API 5L X80. Na soldagem multipasse destas tubulações, a zona afetada pelo calor (ZAC) do passe de raiz é submetida a um novo ciclo térmico pelos passes de soldagem subsequentes. Isto resulta em alterações nos valores das propriedades físicas. Nos aços ARBL, a ZAC de grãos grosseiros reaquecida intercriticamente (IC-ZACGG) pode se tornar uma zona frágil localizada, isto é, uma zona com maior dureza. Consequentemente, falhas estruturais podem ocorrer, ocasionando paradas não desejadas no transporte de fluidos. O objetivo deste trabalho é desenvolver uma metodologia baseada no modelo de fontes de calor distribuídas de Mhyr e Gröng, para avaliar o fluxo de calor na soldagem considerando as propriedades físicas dependentes da temperatura. Estender a aplicação desta ferramenta em soldagens multipasses para identificar sub-regiões da ZAC de um passe anterior sendo afetada pela ZAC de passes subsequentes. As isotermas simuladas foram validadas através de medições realizadas em macrografias de juntas soldadas. Os ciclos térmicos simulados foram validados através das temperaturas máximas atingidas e pelos tempos de resfriamento de 800 a 500 ºC (?t8-5) dos ciclos térmicos experimentais. Ao aplicar a metodologia proposta, foi possível delimitar com acurácia as regiões reaquecidas da ZAC e analisar os efeitos dos passes subsequentes em cada uma das sub-regiões da ZAC do passe de raiz. A IC-ZACGG na região do passe de raiz foi localizada, mas não se comportou como zona frágil devido à boa soldabilidade do aço API 5L X80 comprovada pelos ensaios de dureza e de tenacidade ao impacto Charpy-V. / In pipelines projects, the high strength low alloy (HSLA) steels are used, such as the API 5L X80 steel. During the multipass welding of these pipes, the heat affected zone (HAZ) of the root pass is subjected to a new thermal cycle by the subsequent welding passes. This results in changes in the values of the physical properties. In the HSLA steels, the intercritical reheated coarse-grained heat-affected zone (IR-CGHAZ) can become a local brittle zone, that is, a region with greater hardness. Consequently, structural failures could happen, causing undesired shutdowns in fluid transportation. The objective of this work is to develop a methodology based on the distributed heat sources model of Mhyr and Gröng, to evaluate the heat flux in the welding considering the temperature-dependent physical properties. Extend the application of this tool in multipass welds to identify HAZ subregions of a previous pass being affected by the HAZ of subsequent passes. The simulated isotherms were validated through measurements made on macrographs of welded joints. The simulated thermal cycles were validated through the maximum temperatures reached and the cooling times from 800 °C to 500 ºC (?t8-5) of the experimental thermal cycles. By applying the proposed methodology, it was possible to accurately delimit reheated HAZ regions and analyze the effects of subsequent passes in each of the root pass HAZ subregions. The IRCGHAZ in the root pass region was localized, but it did not behave as a brittle zone due to the good weldability of the API 5L X80 steel as proven by the hardness and Charpy-V impact tests.
|