Made available in DSpace on 2016-04-18T21:35:59Z (GMT). No. of bitstreams: 6 Abner Cabral Neto1.pdf: 1258954 bytes, checksum: b313b3b1fab7d8527b0beebe3d85e296 (MD5) Abner Cabral Neto2.pdf: 1637124 bytes, checksum: e6adce65a686a9a65954859a81502165 (MD5) Abner Cabral Neto3.pdf: 2894302 bytes, checksum: 08df1415378df1d8bbbc4f294520af74 (MD5) Abner Cabral Neto4.pdf: 2413045 bytes, checksum: ad2ade011024c6311e21e837d19e7472 (MD5) Abner Cabral Neto5.pdf: 1446323 bytes, checksum: 5b5770c90f805a15cd113b45fac6c6be (MD5) Abner Cabral Neto6.pdf: 1990727 bytes, checksum: 5e28338676fe7434a39e9ebebcd05e28 (MD5) Previous issue date: 2009-03-27 / Fundo Mackenzie de Pesquisa / Study / Estudo

El presente trabajo se centra en la empresa “PROYECTOS & FERRETERÍA HOLGUS E.I.R.L” dedicada a la producción y comercialización de prendas de vestir y equipos de protección personal (EPP), ubicada en el distrito de José Leonardo Ortiz provincia de Chiclayo. La producción de la empresa ha ido incrementándose en los últimos años, siendo actualmente su producto principal la camisa manga corta color beige, con una producción mensual promedio de 500 unidades. En el proceso productivo de la camisa, específicamente, la etapa de corte de piezas, constituye el cuello de botella, con un tiempo de 10,03 minutos. El problema principal que tiene la empresa es que no se da abasto para producir lo esperado en el tiempo requerido, debido a la baja productividad que presenta, teniendo, entre otros: pérdidas económicas, por incumplimientos de contrato. Es por ello, que para aumentar la productividad se realizó un estudio de Ingeniería de Métodos y de Tiempos. Estandarizando los tiempos y con las mejoras propuestas se logró reducir el tiempo de flujo del proceso en un 23% con respecto al inicial y se logró aumentar la productividad global en un 27%. Así mismo, se obtuvo como costo beneficio 1,43 soles, una eficiencia económica de 2,21 que da una utilidad de 1,21 soles por cada sol invertido, con un ahorro de las penalizaciones por retrasos en los tiempos de entrega, puesto que con la mejora entregaríamos los pedidos en los plazos establecidos.

Made available in DSpace on 2016-03-15T19:37:00Z (GMT). No. of bitstreams: 1 Dionisio Mateo Cardille.pdf: 3138784 bytes, checksum: c27dcdc2765d16f7b30f2b6a5a588e37 (MD5) Previous issue date: 2009-08-18 / This study broaches the diesel engines cylinder liners waste concepts, characterizing abrasive waste, tribo-chemical waste and scuffing, with component external factors, like adultered fuel or with high sulfur level frequently found in Brazil. It presents the modern emissioned engines and the direct causes in the cylinder liners material requirement, with the tribologic evolution of piston, piston rings and cylinder. Some concepts of cylinders internal diameter surface finish and the direct involvement in the cylinder smooth, and the blow by flux besides oil consumption. The cylinder liners are manufactured in perlitic gray casting iron, and it was compared to a bainitic gray casting iron as alternative material, in order to satisfy the modern environment laws for emissions. The experiment technical was based on a dynamometric test in a 146kw diesel engine, during 500hs, with 27,4% overpower. The liners were assembled in the engine block in an intercalated way, avoiding benefits in the cylinders closer to the water pump. After the test, the liners were dimensioned with the respective piston rings. As result, was observed that the proposal bainitic material got a better waste resistance in comparison with the perlitic material, with a better dimensional stability. The piston rings presented similar waste when applied in both materials, respecting the project original tribological pair. / Este estudo aborda os conceitos de desgaste em camisas de cilindro para motores diesel, caracterizando desgaste abrasivo, tribo-químico e "scuffing", juntamente com fatores externos ao componente como a questão dos combustíveis adulterados ou com alto teor de enxofre, freqüentemente encontrados no Brasil. Apresenta o enquadramento dos motores nas modernas leis de emissões, e suas causas diretas na exigência de materiais para camisas de cilindro, juntamente com a evolução tribológica do conjunto pistão, anéis e camisa. Definem-se também alguns conceitos de rugosidade e acabamento superficial dos cilindros e suas implicações diretas no amaciamento neste componente, além do tema passagem de gases da câmara de combustão para o cárter (blow by) e consumo de óleo lubrificante. As camisas de cilindro são em sua maioria confeccionadas em liga de ferro fundido cinzento com matriz perlítica, a qual foi objeto de comparação com uma liga proposta de matriz bainítica, como material alternativo, visando satisfazer as condições impostas pela moderna legislação ambiental. A técnica experimental empregada baseou-se em um ensaio dinamométrico em um motor diesel de 146kw, porém submetido a plena carga durante 500hs, com 27,4% de acréscimo de potência. As camisas foram montadas no motor de forma a estarem intercaladas e evitando favorecimentos em cilindros mais quentes do bloco. Após o teste, as camisas de cilindro foram dimensionadas, juntamente com os respectivos anéis de pistão. Como resultado, observou-se que o material proposto em liga com matriz bainítica teve uma melhor resposta ao desgaste em comparação com o material de matriz perlítica, inclusive com uma melhor estabilidade dimensional. Os anéis de pistão tiveram desgaste similar em ambos os materiais, respeitando o par tribológico original de projeto.

No presente trabalho quatro ligas Al-Si hipereutéticas, três das quais foram produzidas por conformação por \"spray\" e a outra por fundição, foram caracterizadas quanto a textura, dureza, microestrutura e resistência à corrosão em meio de condensado sintético automotivo (CSA). Duas das ligas conformadas por \"spray\" foram retiradas de camisas de cilindro e a outra de um pré-formado obtido em laboratório. A conformação por \"spray\" envolve a atomização de uma liga e a deposição de gotículas em um substrato, antes mesmo que todas se encontrem no estado sólido. Este processo permite a obtenção de materiais que se caracterizam por uma microestrutura livre de macrossegregações e bastante refinada, implicando melhor trabalhabilidade a quente. A caracterização da microestrutura das quatro ligas hipereutéticas revelou a presença de porosidades na liga obtida em laboratório, e microestrutura com distribuição homogênea de precipitados primários nas três ligas conformadas por \"spray\". A microestrutura de uma das ligas apresentou-se muito diferenciada, com a presença de eutético, sugerindo que esta foi fabricada por fundição. Nas camisas de cilindro foram feitas medidas de rugosidade, e em todas as ligas foram realizados ensaios de microdureza. A liga conformada por \"spray\" e obtida em laboratório foi laminada a quente e a frio. Foram realizados também estudos de textura, para tentar estabelecer uma correlação entre todas as ligas quanto ao processo de fabricação. A avaliação da textura indicou que a presença de fases de silício primário, finamente distribuídas impedem o aparecimento de texturas típicas de deformação de ligas de alumínio, mesmo após severas deformações, como as necessárias para a transformação de pré-formados em tubos que originam as camisas de cilindro. As medidas de rugosidade indicaram características próprias do acabamento superficial usado para a produção das camisas, por brunimento ou por ataque químico. Os ensaios de microdureza apresentaram variações de acordo com as rotas de fabricação sendo que a liga eutética apresentou os maiores valores de microdureza em comparação às ligas conformadas por \"spray\". Todas as ligas foram avaliadas quanto a resistência à corrosão por ensaios de espectroscopia de impedância eletroquímica em dois meios, CSA com pH 3,3 e CSA com pH 11. As quatro ligas hipereutéticas estudadas apresentaram mecanismo de corrosão similar em condensado sintético automotivo (CSA) pH 3,3. Em todas ocorreu o ataque intenso da matriz de alumínio e as partículas de silício primário atuaram como regiões catódicas. A liga 2 apresentou maior resistência à corrosão entre todas as ligas ensaiadas, tanto em CSA pH 3,3 como em pH 11. Neste último meio, uma camada de produtos de corrosão formou-se sobre todas as ligas, e os resultados indicaram mecanismos diferentes para o ataque da matriz de Al e para o crescimento da camada depositada na superfície das ligas estudadas. O ataque da matriz da liga 2 neste meio foi aparentemente mais lento do que sobre as demais ligas, com a formação de uma camada mais compacta de produtos de corrosão, estabelecendo um controle por difusão dos processos interfaciais para maiores períodos de ensaio. A camada formada sobre as demais ligas neste meio apresentou-se mais defeituosa, e nestas ocorreu também menor controle da velocidade das reações interfaciais por processos difusionais. / In the present study four hypereutectic Al-Si alloys, three produced by spray forming and one by casting, were characterized for microhardness, roughness, microstructure, texture and corrosion resistance in a synthetic automotive condensed solution (SACS). Two of the spray formed alloys tested were obtained from cylinder liners and the other was laboratory made. Spray forming involves alloy atomization and droplets deposition on a substrate, previous to the solidification of all of the droplets. This process favours the production of materials with a fine microstructure free of macrosegregation that is related to improved hot workability. The microstructure characterization of the four alloys revealed the presence of porosities in the laboratory made alloy. All the three alloys produced by spray forming showed a homogeneous distribution of primary precipitates. The microstructure of one of the alloys showed eutectic microstructure, indicating that this alloy was fabricated by casting. In the cylinder liners, the surface roughness was measured and the microhardness of all the alloys was also evaluated. Furthermore, the laboratory made alloy was hot and cold rolled. Texture determinations were carried out to investigate the correlation between the alloy type and their fabrication process. The texture investigation indicated that the fine distribution of primary silicon phase in the alloy hindered the development of texture typical of aluminium alloys deformation, even after severe mechanical work, such as those used in the conversion of pre-formed in cylinder liners. The surface roughness results indicated typical characteristics of the surface finishing used, honing or chemical etching. The microhardness results were dependent on the fabrication process used, with higher microhardness associated to the eutectic alloy comparatively to the spray formed ones. All hypereutectic alloys were tested for corrosion resistance using electrochemical impedance spectroscopy in two electrolytes, SACS with pH 3.3 and SACS with pH 11. The four tested alloys showed similar corrosion mechanisms in the acid electrolyte (SACS pH 3.3). The intense attack of the aluminium matrix occurred in ali tested alloys and the primary silicon phase was unattacked and appeared as emerging from the surface after corrosion immersion test. The primary silicon particles acted as cathodic sites. The alloy 2 showed the highest corrosion resistance among the tested alloys in both electrolytes, SACS pH 3.3 and SACS pH 11. In this last medium, a layer of corrosion products formed on all the alloys, and the results indicated different mechanisms for the aluminium matrix corrosive attack and growth of the deposited layer on the alloys surface. The kinetics of aluminium matrix attack was apparently slower in the alloy 2 than for the other alloys, resulting in the formation of a more compact layer of corrosion products, leading to diffusion controlled interfacial processes for longer test periods. The layer of corrosion products on the other three alloys (1, 3, and 4) had more defects and for these alloys diffusional controlled interfacial processes were not as significant as for alloy 2.

No presente trabalho quatro ligas Al-Si hipereutéticas, três das quais foram produzidas por conformação por \"spray\" e a outra por fundição, foram caracterizadas quanto a textura, dureza, microestrutura e resistência à corrosão em meio de condensado sintético automotivo (CSA). Duas das ligas conformadas por \"spray\" foram retiradas de camisas de cilindro e a outra de um pré-formado obtido em laboratório. A conformação por \"spray\" envolve a atomização de uma liga e a deposição de gotículas em um substrato, antes mesmo que todas se encontrem no estado sólido. Este processo permite a obtenção de materiais que se caracterizam por uma microestrutura livre de macrossegregações e bastante refinada, implicando melhor trabalhabilidade a quente. A caracterização da microestrutura das quatro ligas hipereutéticas revelou a presença de porosidades na liga obtida em laboratório, e microestrutura com distribuição homogênea de precipitados primários nas três ligas conformadas por \"spray\". A microestrutura de uma das ligas apresentou-se muito diferenciada, com a presença de eutético, sugerindo que esta foi fabricada por fundição. Nas camisas de cilindro foram feitas medidas de rugosidade, e em todas as ligas foram realizados ensaios de microdureza. A liga conformada por \"spray\" e obtida em laboratório foi laminada a quente e a frio. Foram realizados também estudos de textura, para tentar estabelecer uma correlação entre todas as ligas quanto ao processo de fabricação. A avaliação da textura indicou que a presença de fases de silício primário, finamente distribuídas impedem o aparecimento de texturas típicas de deformação de ligas de alumínio, mesmo após severas deformações, como as necessárias para a transformação de pré-formados em tubos que originam as camisas de cilindro. As medidas de rugosidade indicaram características próprias do acabamento superficial usado para a produção das camisas, por brunimento ou por ataque químico. Os ensaios de microdureza apresentaram variações de acordo com as rotas de fabricação sendo que a liga eutética apresentou os maiores valores de microdureza em comparação às ligas conformadas por \"spray\". Todas as ligas foram avaliadas quanto a resistência à corrosão por ensaios de espectroscopia de impedância eletroquímica em dois meios, CSA com pH 3,3 e CSA com pH 11. As quatro ligas hipereutéticas estudadas apresentaram mecanismo de corrosão similar em condensado sintético automotivo (CSA) pH 3,3. Em todas ocorreu o ataque intenso da matriz de alumínio e as partículas de silício primário atuaram como regiões catódicas. A liga 2 apresentou maior resistência à corrosão entre todas as ligas ensaiadas, tanto em CSA pH 3,3 como em pH 11. Neste último meio, uma camada de produtos de corrosão formou-se sobre todas as ligas, e os resultados indicaram mecanismos diferentes para o ataque da matriz de Al e para o crescimento da camada depositada na superfície das ligas estudadas. O ataque da matriz da liga 2 neste meio foi aparentemente mais lento do que sobre as demais ligas, com a formação de uma camada mais compacta de produtos de corrosão, estabelecendo um controle por difusão dos processos interfaciais para maiores períodos de ensaio. A camada formada sobre as demais ligas neste meio apresentou-se mais defeituosa, e nestas ocorreu também menor controle da velocidade das reações interfaciais por processos difusionais. / In the present study four hypereutectic Al-Si alloys, three produced by spray forming and one by casting, were characterized for microhardness, roughness, microstructure, texture and corrosion resistance in a synthetic automotive condensed solution (SACS). Two of the spray formed alloys tested were obtained from cylinder liners and the other was laboratory made. Spray forming involves alloy atomization and droplets deposition on a substrate, previous to the solidification of all of the droplets. This process favours the production of materials with a fine microstructure free of macrosegregation that is related to improved hot workability. The microstructure characterization of the four alloys revealed the presence of porosities in the laboratory made alloy. All the three alloys produced by spray forming showed a homogeneous distribution of primary precipitates. The microstructure of one of the alloys showed eutectic microstructure, indicating that this alloy was fabricated by casting. In the cylinder liners, the surface roughness was measured and the microhardness of all the alloys was also evaluated. Furthermore, the laboratory made alloy was hot and cold rolled. Texture determinations were carried out to investigate the correlation between the alloy type and their fabrication process. The texture investigation indicated that the fine distribution of primary silicon phase in the alloy hindered the development of texture typical of aluminium alloys deformation, even after severe mechanical work, such as those used in the conversion of pre-formed in cylinder liners. The surface roughness results indicated typical characteristics of the surface finishing used, honing or chemical etching. The microhardness results were dependent on the fabrication process used, with higher microhardness associated to the eutectic alloy comparatively to the spray formed ones. All hypereutectic alloys were tested for corrosion resistance using electrochemical impedance spectroscopy in two electrolytes, SACS with pH 3.3 and SACS with pH 11. The four tested alloys showed similar corrosion mechanisms in the acid electrolyte (SACS pH 3.3). The intense attack of the aluminium matrix occurred in ali tested alloys and the primary silicon phase was unattacked and appeared as emerging from the surface after corrosion immersion test. The primary silicon particles acted as cathodic sites. The alloy 2 showed the highest corrosion resistance among the tested alloys in both electrolytes, SACS pH 3.3 and SACS pH 11. In this last medium, a layer of corrosion products formed on all the alloys, and the results indicated different mechanisms for the aluminium matrix corrosive attack and growth of the deposited layer on the alloys surface. The kinetics of aluminium matrix attack was apparently slower in the alloy 2 than for the other alloys, resulting in the formation of a more compact layer of corrosion products, leading to diffusion controlled interfacial processes for longer test periods. The layer of corrosion products on the other three alloys (1, 3, and 4) had more defects and for these alloys diffusional controlled interfacial processes were not as significant as for alloy 2.