The excessive quantity of byproduct coconut powder as result of processing of coconut fiber, aimlessly industrial application. The objective of this dissertation was the development of composites reinforced with fiberglass using two types of matrices: a pure matrix composite and matrix polyester modified with coir dust. Reducing the size of the coir dust was performed by processing in a ball mill resulting in upper production of particles that crossed off 200 mesh. The composites reinforced with fiberglass and polyester matrix were produced include 10% coir dust (percentage by weight). The viscosity of the pure polyester matrix increased from 244 cP to 480 cP with the addition of coir dust. The step up in viscosity not impair processing of composites, for the reinforcement (fiberglass) was incorporated satisfactorily the two matrices: pure polyester and polyester with coir dust. The mechanical properties were examined through tensile test, three point flexion and IZOD impact. The results of tensile testing of composites reinforced with glass fiber produced with pure polyester matrix and the polyester matrix with coir dust had similar properties. The addition of coconut fiber to matrix produced no change in its performance. Flexion tests showed a 40% reduction in resistance of the polyester matrix composites with coir dust relative to pure polyester matrix composites. The IZOD impact test showed similar results in composites with both types of arrays. There was a 10% reduction in production costs of polyester matrix composites with coir dust, inputs purchased on the overseas market / O pó de coco que é um subproduto da indústria de beneficiamento das fibras de coco é produzido em grande quantidade e não possui aplicações industriais. O objetivo desta pesquisa foi o desenvolvimento de compósitos reforçado com fibra de vidro empregando dois tipos de matrizes: poliéster puro e poliéster com pó de coco. A redução do tamanho do pó de coco foi realizado através de processamento em moinho de bolas obtendo-se alta produção de partículas que passaram na malha de 200 mesh. Os compósitos reforçados com fibra de vidro foram produzidos com matriz poliéster contendo 10 % de pó de coco (porcentagem em peso). A viscosidade da matriz poliéster pura aumentou de 244 cP para 480 cP com a adição de pó de coco. O aumento da viscosidade não prejudicou o processamento dos compósitos, pois o reforço (fibra de vidro) foi incorporado satisfatoriamente às duas matrizes: poliéster puro e poliéster com pó de coco. As propriedades mecânicas foram analisadas através de ensaios mecânicos de tração, flexão em três pontos e impacto IZOD. Os resultados dos ensaios de tração dos compósitos reforçados com fibra de vidro produzidos com matriz poliéster pura e matriz de poliéster com pó de coco apresentaram propriedades semelhantes. A adição do pó de coco à matriz não produziu mudanças no seu desempenho. Os ensaios de flexão apresentaram redução de 40% na resistência dos compósitos de matriz poliéster com pó de coco em relação aos compósitos de matriz poliéster pura. O ensaio de impacto IZOD apresentou resultados similares nos compósitos com os dois tipos de matrizes. Houve uma redução de 10% nos custos de produção dos compósitos de matriz poliéster com pó de coco, com insumos adquiridos no mercado internacional

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / This work comprises two studies on the evaluation of cement-coconut powder composite in curing and aging conditions. In the first study the composites were subjected to the accelerated carbonation process during the first 48 hours of cure, then were dried and subjected to curing conditions until saturated at 28 days. The results shows that the composites had a reduction in the water absorption and increased bulk density. The carbonated composites had a 26% increase in compression strength and 16% in the flexural strength as compared to no-carbonate composite. The interaction between the reduction of the Ca(OH)2 and increasing CaCO3 content was observed by thermogravimetric analysis. In the second study, the composites was evaluated by methods of external and internal natural aging for 6 months and by the accelerated carbonation for 84 days. Increased measurements from electrical resistivity and ultrasonic during cure age were related to the increase in the mechanical properties, reduction of porosity and hydration process of these composites. Three types of age showed similar mechanical and physical properties, the electrical resistivity measurements was related to the increase of CaCO3 content, verified by thermogravimetry. The different stages of this work the composites were characterized by X-ray diffraction, thermal analysis, scanning electron microscopy with energy dispersive spectroscopy and were evaluated for their physical and mechanical properties. / Este trabalho compreende dois estudos sobre a avaliação de compósitos cimento-pó de coco em condições de cura e de envelhecimento. No primeiro estudo, os compósitos foram submetidos ao processo de carbonatação acelerada durante as primeiras 48 horas de cura e, em seguida foram submetidos as condições de cura seca e saturada até 28 dias. Os resultados indicaram que os compósitos carbonatados tiverem uma absorção de água reduzida e aumento da densidade. Esses materiais apresentaram um aumento de 26% na resistência à compressão e de 16% no módulo de ruptura, em comparação com compósitos não carbonatados. A interação entre a diminuição do conteúdo de Ca(OH)2 e o aumento do teor de CaCO3 foi observada por análise termogravimétrica. No segundo estudo, os compósitos foram avaliados pelos métodos de envelhecimento natural externo e interno por até 6 meses, e pela carbonatação acelerada por até 84 dias. O aumento das medições de resistividade eléctrica e de ultrassom durante o período de cura foi relacionado com o aumento nas propriedades mecânicas, redução da porosidade e o processo de hidratação dos compósitos. Os três tipos de envelhecimento apresentaram propriedades físicas e mecânicas similares, as medidas de resistividade elétrica foram relacionadas com o aumento do teor de CaCO3 comprovado pela termogravimetria. Nas diferentes etapas do presente trabalho, os compósitos foram caracterizados por difração de raios X, análise térmica, microscopia eletrônica de varredura com espectroscopia por dispersão de energia e foram avaliadas as suas propriedades físicas e mecânicas.