Uso de materiais diretos e indiretos para amplas restaurações: implicações clínicas e laboratoriais / Use of direct and indirect materials for extensive restorations: clinical and laboratory implicationsSkupien, Jovito Adiel 14 March 2014 (has links)
Made available in DSpace on 2014-08-20T14:30:19Z (GMT). No. of bitstreams: 1
Tese_Jovito_Adiel_Skupien.pdf: 8297294 bytes, checksum: 72ce694b2bb9e499cf0353c4c4b8df4e (MD5)
Previous issue date: 2014-03-14 / Glass fiber posts and composite resins are widely used materials in restorative dentistry. The various forms of presentation and technical approach, as well as different handling prior to their use, can result in diverse outcomes, which can determine the success or failure of the restorative procedure. Thus, the aim of this study was to evaluate the performance of glass fiber posts and composite resins in
front of several factors related to it uses in dentistry. For this, the study was divided into three parts: An in vitro study, an in vivo study and a systematic review. The in vitro study aimed to evaluate the effect of cementation delay of indirect composite resin restorations in previously hybridized dentin. Three strategies of cementation were tested through different protocols. Beam-shaped specimens from tooth/restoration were obtained and submitted to microtensile testing to evaluate the bond strength and types of failures, where the results were analyzed by ANOVA and Tukey s post hoc tests and linear regression. Regular cement and adhesive threestep
etch-and-rinse adhesive system showed the highest values of bond strength, followed by the same cement and two-step etch-and-rinse adhesive system and the lowest values for self-adhesive cement groups. Linear regression showed an
improvement in the bond strength values when three-step adhesive system was used, however, all groups had adequate values of bond strength, even in unfavorable
situations. The randomized clinical trial evaluated the longevity of metal-ceramic crown and composite resin restorations performed in endodontically treated teeth that received a glass fiber post. Fifty-six severely damaged teeth but with at least one entire wall were randomly allocated into two groups according to the type of restoration. The longevity was assessed through Kaplan-meier and clinical evaluation
by descriptive analysis. The recall rate was 100%, fifty-six teeth were re-evaluated with no absolute failure. However, eight composite resin restorations had failed (all reparable). A significant difference between type of restoration was found. Indirect restorations provided higher acceptable clinical performance after two-year of followup, although composite failures were liable to repair. The systematic review
compared factorts that can influence retention of glass fiber posts to intraradicular based on in vitro studies which compared the bond strength of resin cements. Searches were carried out in Pubmed and Scopus database up to December 2013. Thirty-four studies were included in the review and several variables were extracted.
The presence of endodontic treatment significantly decrease the bond strength, meanwhile other variables can influence according to the type of resin cement. Thus, factors as type of cement application and pretreatment of post can influence glass fiber post retention, however, self-adhesive resin cements are less sensitive to luting procedures / Pinos de fibra de vidro e resinas compostas são materiais amplamente utilizados em odontologia restauradora. As diferentes formas de apresentação e técnicas de emprego, bem como diferentes manobras prévias às suas utilizações podem implicar em desfechos clínicos mais ou menos favoráveis, que podem determinar o sucesso ou falha de um procedimento restaurador. Assim, o objetivo deste estudo foi
avaliar o desempenho de pinos de fibra de vidro e resinas compostas frente a diversos fatores relacionados ao seu uso em odontologia. Para isso, o estudo foi dividido em três partes: estudo in vitro, estudo in vivo e revisão sistemática. O estudo
in vitro objetivou avaliar o efeito do retardamento da cimentação de restaurações indiretas de resinas compostas em dentina previamente hibridizada. Três estratégias de cimentação foram testadas com diferentes protocolos. Palitos do conjunto dente/restauração foram obtidos e submetidos ao teste de microtração para avaliação da resistência de união e padrão de fratura, onde os valores foram analisados através de ANOVA e teste post hoc Tukey (!=0,05) e regressão linear.
Cimento convencional e sistema adesivo de 3 passos apresentaram os maiores valores de resistência de união, seguidos do mesmo cimento e sistema de 2 passos, sendo os menores valores para o grupo do cimento auto-adesivo. A regressão linear demonstrou uma melhora significativa nos valores de resistência quando o sistema de 3 passos foi utilizado, entretanto, todos os grupos tiveram resultados adequados, mesmo em condições desfavoráveis. O ensaio controlado randomizado avaliou a longevidade de restaurações metalo-cerâmicas e de resinas compostas confeccionadas em dentes tratados endodonticamente que receberam um pino de
fibra de vidro. Cinqüenta e seis dentes com a coroa danificada, porém, com uma face intacta, foram alocados em dois grupos aleatoriamente, de acordo com o tipo de restauração. A longevidade das restaurações foi avaliadas através de Kaplan- Meier e critérios clínicos foram analisados de forma descritiva. Com uma taxa de rechamada de 100%, 56 dentes foram reavaliados e nenhum foi perdido. Porém, 8 restaurações de resina composta falharam e sofreram reparos. Houve uma diferença significativa para o tipo de restauração em relação ao sucesso. Assim, restaurações indiretas apresentaram uma melhor performance clínica após 2 anos de acompanhamento, embora as falhas apresentadas no grupo que recebeu resinas
diretas tenham sido reparáveis. A revisão sistemática comparou fatores que podem influenciar na retenção de pinos de fibra de vidro em dentina intra-radicular baseado em estudos in vitro que compararam a resistência de união de cimentos resinosos.
Após uma busca realizada nos bancos de dados Pubmed e Scopus até dezembro de 2013, trinta e quatro estudos foram incluídos na revisão e diferentes variáveis foram extraídas. A presença de tratamento endodôntico diminuiu significativamente a resistência de união, enquanto que demais variáveis variam sua influência de acordo com o tipo de cimento resinoso. Assim, fatores como método de aplicação do
cimento e pré-tratamento do pino podem influenciar a retenção de pinos de fibra de vidro, porém, cimentos auto-adesivos são menos sensíveis à técnica de cimentação
|
192 |
Efeito da técnica restauradora, do tipo de preparo e do envelhecimento de restaurações de resina composta sobre a resistência à fratura dental, resistência adesiva e vedamento marginal / Restorative technique, kind of prepair and aging effects on composite resin restorations fracture strength, restoration retention and marginal adaptationSouza, Fábio Herrmann Coelho de 23 June 2006 (has links)
Made available in DSpace on 2014-08-20T14:30:20Z (GMT). No. of bitstreams: 1
Tese - Fabio Herrmann.pdf: 2352205 bytes, checksum: a6bcc0f4e7708f23fde2f31a66c02b83 (MD5)
Previous issue date: 2006-06-23 / The aim of this study was to evaluate, in vitro, the effect of composite resin restoration techniques, bevel and storage time on the fracture strength, restoration retention and gap formation. For the fracture strength test, standard MOD cavities were prepared in 100 upper premolars, which were divided in two storage times (24 hours and 6 months with 1000 thermocycles), and in each group, sub-groups
were randomly formed as follow: group 1 direct composite resin restoration(Filtek Z250 and Adper Single Bond 3M/ESPE) without bevel (butt joint); group 2 beveled direct composite resin restoration; group 3 indirect composite resin inlay (Z250 and Rely X ARC 3M/ESPE) without bevel(butt joint); group 4 beveled indirect composite resin inlay; group 5 sound teeth; group 6 teeth with MOD preparations (no restorations). For the retention test, the incisal edge of 90 lower incisors was sectioned, and divided in the same restorative groups as described above (except group 6). To evaluate gap presence or absence, proximal box cavities were prepared in 24 human third molars, which were restored with direct or indirect composite restorations, with or without bevel, similar to above described and examined under SEM evaluation. Data was statistically analysed by A NOVA, Tukey and t-student tests for fracture strength and retention tests, and Fisher s exact test for gap formation (=0,05). At the 24 hours, beveled restorations exhibited higher fracture strength values than non beveled restorations and most of the tested groups showed resistance similar or superior than sound teeth. After 6 months, the best results were obtained for beveled inlays and the worst values were observed for butt joint direct restorations. In the retention test,beveled restorations had superior performances than non-beveled restorations, in both periods of time. For both tests, a 6-month storage time and thermal cycling produced significant properties decrease in groups 1, 2 and 4 showed. Under SEM examination, no difference was observed among groups after 24 hours. However,after 6 months, beveled restotations remained without gap formation and they had better performance than butt joint restorations. Pearson correlation test showed positive correlation between fracture strength and retention tests. Within the limitations of the study, it was concluded that aging impaired adhesive properties, bevel improved the performance in all tests and generally indirect restorations were not superior to direct restorations. / O objetivo do presente trabalho foi avaliar in vitro o efeito da técnica restauradora, da confecção de bisel e do tempo de armazenamento de restaurações de resina composta sobre a resistência à fratura dental, resistência à fratura de restaurações (resistência adesiva) e formação de fenda marginal. Para o teste de resistência à fratura dental, foram utilizados 100 pré-molares superiores, submetidos a preparos cavitários MOD, divididos em 2 tempos de armazenamento
(24 horas e 6 meses com termociclagem 1000 ciclos), subdivididos nos seguintes grupos: grupo 1 restaurados com resina composta direta (Filtek Z250 e Adper Single Bond 3M/ESPE) sem bisel; grupo 2 resina composta direta com bisel; grupo 3 resina composta semi-direta (Z250 e Rely X ARC 3M/ESPE) sem bisel; grupo 4 resina composta semi-direta com bisel; grupo 5 dentes hígidos; e grupo 6 dentes apenas preparados (n=10). Para o teste de resistência à fratura de restaurações, foram utilizados 90 incisivos inferiores, que receberam desgaste do bordo incisal e foram divididos nos mesmos grupos citados acima (exceto o grupo 6). Para a avaliação de presença ou ausência de fenda marginal,foram empregados 24 terceiros molares, que receberam preparos proximais, divididos nos mesmos grupos acima (exceto os grupos 5 e 6). Os dados foram submetidos à análise estatística (=0,05) através dos testes ANOVA, Tukey e t-student para resistência à fratura dental e resistência à fratura de restaurações e teste exato de Fisher para formação de fenda marginal. Os resultados mostraram que, para resistência à fratura dental, no tempo de 24 horas, as restaurações com bisel foram superiores às demais, enquanto as sem bisel não diferiram dos dentes hígidos. Após 6 meses, as restaurações semi-diretas com bisel foram superiores às demais, não diferindo das semi-diretas sem bisel; as restaurações diretas sem bisel foram inferiores às demais. Para resistência à fratura de restaurações, as restaurações com bisel foram superiores às demais para ambos os tempos de
armazenamento, e não diferiram dos dentes hígidos em 24 horas. Para os 2 testes citados, os grupos 1, 2 e 4 apresentaram redução significativa do seu desempenho após 6 meses de armazenamento e termociclagem. A avaliação de
fenda em esmalte mostrou que em 24 horas não houve diferença entre os grupos. Após 6 meses, as restaurações com bisel continuaram livres de fenda, enquanto as sem bisel apresentaram fenda na maioria dos espécimes. A análise de
correlação de Pearson mostrou resultado significativamente positivo para os 2 testes de resistência. Concluiu-se que o tempo de armazenamento e termociclagem foram fatores significativos na redução da performance adesiva; a
realização de bisel influenciou de forma positiva na melhora do desempenho das restaurações em todos os testes empregados; as restaurações semi-diretas de resina composta, de modo geral, não foram superiores às diretas.
|
193 |
Effect of simulated intraoral erosion and/or abrasion effects on etch-and-rinse bonding to enamel.Wang, Linda, Casas-Apayco, Leslie, Hipólito, Ana Carolina, Dreibi, Vanessa Manzini, Giacomini, Marina Ciccone, Bim Júnior, Odair, Rios, Daniela, Magalhães, Ana Carolina 02 1900 (has links)
El texto completo de este trabajo no está disponible en el Repositorio Académico UPC por
restricciones de la casa editorial donde ha sido publicado. / PURPOSE: To assess the influence of simulated oral erosive/abrasive challenges on the bond strength of an etch-and-rinse two-step bonding system to enamel using an in situ/ex vivo protocol. METHODS: Bovine enamel blocks were prepared and randomly assigned to four groups: CONT - control (no challenge), ABR - 3x/day-1 minute toothbrushing; ERO - 3x/day - 5 minutes extraoral immersion into regular Coca Cola; and ERO+ABR - erosive protocol followed by a 1-minute toothbrushing. Eight blocks were placed into an acrylic palatal appliance for each volunteer (n = 13), who wore the appliance for 5 days. Two blocks were subjected to each of the four challenges. Subsequently, all the blocks were washed with tap water and Adper Single Bond 2/Filtek Z350 were placed. After 24 hours, 1 mm2 beams were obtained from each block to be tested with the microtensile bond strength test (50 N load at 0.5 mm/minute). The data were statistically analyzed by one-way RM-ANOVA and Tukey's tests (alpha = 0.05). RESULTS: No difference was detected among the ABR, ERO, and CONT groups (P > 0.05). ERO+ABR group yielded lower bond strengths than either the ABR and ERO groups (P < 0.0113). / Revisión por pares
|