Spelling suggestions: "subject:"rejection force""
1 |
A study of the influence of lubricants on the ejection force of the tablets.Novotná, Nikola January 2015 (has links)
The aim of this study was to evaluate the effect of the type of lubricant, its concentration and mixing time with granules on the tablet hardness, ejection force and the lubrication index. Lactose was used as a filler in granules and polyvinylpyrolidone as a binder. Granules were prepared by wet granulation. Three types of talc were used in concentrations 1%, 3%, 5%, 7% a 10% and magnesium stearate in concetrations 1%, 2% a 3% as lubricants. Tablets were produced by tablet press DOTT Bonapace (model CPR-6) with the possibility to measure the force of the upper and lower punch and force-displacement. These values were used for the calculation of the lubrication index. The values of lubrication index were used for the lubricants comparison. The lubrication index with magnesium stearate did not change either with increasing concentration or with mixing time with granules. In case of each type of talc, the lubrication effect rose with increasing concentration but time of the mixing did not have any significant effect on the lubrication potential. Tablet strength decreased with higher lubricant concentration and longer mixing time when magnesium stearate was used. With increasing concentration of the lubricant tablet strength with talc first increased then stagnated or started to decrease. The higher...
|
2 |
Ejection forces and static friction coefficients for rapid tooled injection mold insertsKinsella, Mary E. 29 September 2004 (has links)
No description available.
|
3 |
Unapređenje kvaliteta alata za livenje pod pritiskom primenom tehnologija inženjerstva površina / Application of surface engineering technologies for improvement of diecasting tools qualityTerek Pal 21 September 2016 (has links)
<p>Proučavane su koroziona postojanost i tendencija lepljenja različitih<br />materijala u kontaktu sa tečnom Al–Si–Cu legurom. Ispitivanjem su<br />obuhvaćeni čelik za rad na toplo, plazma nitrirani čelik i dupleks<br />slojevi sa CrN, TiAlN, TiAlSiN i CrAlN prevlakama, različitog nivoa<br />površinske hrapavosti. Za ispitivanja pomenutih fenomena<br />primenjena je metoda izvlačenja, koja je unapređena kako bi se povećale<br />njena tačnost i verodostojnost simulacije procesa livenja. Korozioni<br />efekti su pojačani tako što su uzorci osim kratkog kontakta sa odlivkom<br />zadržavani i u dužim periodima u kontaktu sa tečnom legurom (5 i 20<br />min). Uprkos opštim stavovima, za ispitivane materijale je<br />ustanovljeno da su sile izvlačenja uzoraka iz Al–Si–Cu odlivaka<br />nezavisne od njihovog hemijskog sastava. Uticaj hrapavosti je izražen<br />kod uzoraka sa prevlakama kod kojih pri smanjenju hrapavosti dolazi do<br />povećanja sile izvlačenja. Sve ispitane prevlake su sklone mehaničkom<br />lepljenju Al–Si–Cu legure za svoje površine, ali sa aspekta korozije u<br />tečnom metalu značajno prevazilaze performanse čelika i plazma<br />nitriranog sloja. Duži kontakt livene legure sa površinama prevlaka<br />uzrokovao je niže vrednosti sila izvlačenja, što je posledica<br />oksidacije površina prevlaka. Ustanovljeno je da su ispitivane<br />prevlake inertne ka tečnoj leguri aluminijuma. Međutim, dolazi do<br />oksidacije i korozije materijala podloge kroz greške rasta koje su<br />prisutne u prevlakama. Stečena znanja o identifikovanim<br />mehanizmima habanja i propadanja zaštitnih slojeva prevlaka<br />poslužiće daljem razvoju dupleks slojeva namenjenih za zaštitu alata<br />za livenje pod pritiskom.</p> / <p>Corrosion resistance and soldering tendency of different materials in molten<br />Al–Si–Cu alloy were studied. Hot-working tool steel, plasma nitrided steel and<br />duplex layers with CrN, TiAlN, TiAlSiN and CrAlN top coatings, which were<br />produced to various degree of surface roughness, were covered by the study.<br />An ejection test was employed for investigation of the concerned phenomena.<br />The ejection test was improved in order to increase its accuracy and the<br />reliability of process simulation. Samples were examined in both short and<br />extended periods of contact (5 and 20 min) with liquid casting. Casting<br />solidification was extended in order to intensify the corrosion effects. Contrary<br />to common findings, it was found that the ejection force of the investigated<br />materials does not depend on their chemical composition. For the coated<br />samples, a pronounced dependence of the ejection force on the surface<br />roughness was found. The ejection force increases with decrease in surface<br />roughness. All investigated coatings are prone to mechanical soldering by Al–<br />Si–Cu alloy. Still, their corrosion resistance substantially exceeds the corrosion<br />resistance of steel and plasma nitrided layer. Longer exposure of coated<br />samples to cast alloy induced lower ejection forces, which is a consequence<br />of coatings oxidation. It was found that the investigated coatings are inert to<br />liquid aluminium. However, the underlying material undergoes oxidation and<br />corrosion through coating growth defects. The findings concerning the wear<br />mechanisms of protective layers support further development of duplex layers<br />intended for die casting tools protection.</p>
|
Page generated in 0.0939 seconds