This thesis discusses the development of a new type of fibre-reinforced polymer (FRP) beam for use in civil engineering systems. After a detailed evaluation of the advantages and disadvantages of current FRP beam technology, a different approach is proposed which combines traditional laminates with a novel casting technique. To pre-dimension the beam, the classical beam theory is adapted to allow for FRP materials. The resulting formulae were used to determine critical parameters, such as laminate thickness and location in the cross-section, and core dimensions, and to identify failure modes. Based on the results of this analytical study, a detailed testing program was developed. In addition to classical tests, such as bending, shear, and lateral torsion, the performance of the beam was also examined under particular loading regimes specifically designed to induce local failure modes, such as buckling of the web and bearing failure of the section under concentrated loads. The experimental results revealed very good agreement with the analytical predictions. These results were corroborated by a detailed non-linear finite-element analysis, including core cracking and laminate damage. This analysis, in particular, highlighted the synergy between bending and shear behaviour of the beam. This study has revealed that this new type of FRP beam behaves in a predictable manner. Furthermore, the experimental results verified that the cross-section, which combines traditional laminates with cast polymer concrete, did not suffer from many of the disadvantages identified in current FRP beams. The cracking of the polymer concrete under shear, however, does cause the beam to fail prior to the laminates reaching their ultimate shear stress.

Applying lateral confinement to concrete columns using fibre-reinforced polymer (FRP) composites is a very promising technique. FRP rupture is the typical failure mode of FRP wrapped columns under axial compression. numerous experiments have shown that the FRP rupture strain in an FRP wrapped circular column is significantly lower than the FRP ultimate rupture strain determined from flat coupon test of FRP. Despite a large number of studies on the application of FRP confined columns, the mechanisms and level of lower-than-apparent FRP rupture strain still remain unclear. This thesis presents theoretical, Numerical and experimental studies aiming at developing a deeper understanding of the fundamental mechanisms of this phenomenon. A comprehensive literature review was presented providing the background on FRP confined columns, material properties of FRP composites as well as some factors which may lead to premature FRP rupture. A FE analysis was conducted to investigate the FRP hoop strains in the split-disk test, explaining for the first time that the fundamental mechanism of the lower FRP rupture strain in the split-disk test than in the flat coupon test is because strain localisation due to geometric discontinuities at the ends of the FRP and bending of the FRP ring at the gap due to change of curvature caused by the relative moment of the two half disks, as the FRP (as a brittle material) ruptures once the maximum strain at one of these locations reaches the FRP rupture strain. A list of contributory factors affecting the apparent FRP rupture strain in FRP wrapped columns were next identified and classified. An analytical solution was developed to investigate the influence of the triaxial stress state on the FRP strain efficiency, this factor has been shown to have a potentially significant effect on the failure of the FRP wrap but considerable discrepancies exist between predictions using different failure criteria so further research has been identified in this area. FE models were developed to examine the effect of the geometrical discontinuities on the strain efficiency of FRP jackets in FRP wrapped concrete-filled circular steel tubes and FRP wrapped concrete columns. It is demonstrated that severe FRP hoop strain concentrations occur in very small zones near the ends of the FRP wrap in both types of FRP wrapped columns, leading to premature FRP rupture and thus lower strain efficiency. The combined effects of end constraint and FRP overlap on the behaviour of FRP wrapped concrete columns was investigated using a three dimensional FE model considering one half of the length of an FRP-wrapped concrete cylinder. The results have shown that the frication between both ends of a column and the loading platens provides constraints to the ends of the column, but this constraint has little effect on the strain concentration caused by the geometrical discontinuities of the FRP overlap, though the ultimate axial strain of the FRP wrapped columns can be significantly overestimated if the end constraints are not considered.

In this study, a total of twelve beams continuous over two spans of 2,800 mm each were constructed and tested to failure. The beams were divided into two series. Series 1 included six T-beams under symmetrical loading, while Series 2 dealt with six rectangular beams under unsymmetrical loading conditions. In Series 1, the test variables included material type, assumed percentage of moment redistribution, spacing of lateral reinforcement in flange, arrangement of shear reinforcement, and serviceability requirements. In Series 2, three different loading cases were considered, I) loading both spans equally, II) loading both spans maintaining a load ratio of 1.5 and III) loading one span only. Under the loading case II, the parameters of reinforcing material type, assumed percentage of moment redistribution and serviceability requirements were investigated. The test results of both series showed that moment redistribution from the hogging to the sagging moment region took place in GFRP-RC beams which were designed for an assumed percentage of moment redistribution. In Series 1, the decrease of the stirrups spacing from 0.24d to 0.18d enhanced the moment redistribution percentage. Also, decreasing the spacing of lateral reinforcement in the flange from 450 to 150 mm improved the moment redistribution through enhancing the stiffness of the sagging moment region. In Series 2, the unsymmetrical loading conditions (loading case II and III) reduced the moment redistribution by reducing flexural stiffness in the heavily loaded span due to extensive cracking. Regarding serviceability in both series, the GFRP-RC beam designed for the same service moment calculated from the reference steel-RC beam, was able to meet the serviceability requirements for most types of the structural applications. / February 2017

Yes / A numerical method for estimating the curvature, deflection and moment capacity of reinforced concrete beams strengthened with prestressed near-surface-mounted (NSM) FRP bars/strips is presented. A sectional analysis is carried out to predict the moment–curvature relationship from which beam deflections and moment capacity are then calculated. Based on the amount of FRP bars, different failure modes were identified, namely tensile rupture of prestressed FRP bars and concrete crushing before or after yielding of steel reinforcement. Comparisons between experimental results available in the literature and predicted curvature, moment capacity and deflection of reinforced concrete beams with prestressed NSM FRP reinforcements show good agreement. A parametric study concluded that higher prestressing levels improved the cracking and yielding loads, but decreased the beam ductility compared with beams strengthened with nonprestressed NSM FRP bars/strips.

yes / This paper investigates the feasibility of using artificial neural networks (NNs) to predict the shear capacity of concrete members reinforced longitudinally with fibre reinforced polymer (FRP) bars, and without any shear reinforcement. An experimental database of 138 test specimens failed in shear is created and used to train and test NNs as well as to assess the accuracy of three existing shear design methods. The created NN predicted to a high level of accuracy the shear capacity of FRP reinforced concrete members. Garson index was employed to identify the relative importance of the influencing parameters on the shear capacity based on the trained NNs weightings. A parametric analysis was also conducted using the trained NN to establish the trend of the main influencing variables on the shear capacity. Many of the assumptions made by the shear design methods are predicted by the NN developed; however, few are inconsistent with the NN predictions.

yes / This paper presents an analytical method for estimating the flexural strength of reinforced concrete beams strengthened with externally bonded fibre reinforced polymer (FRP) laminates. The method is developed from the strain compatibility and equilibrium of forces. Based on the size of external FRP laminates, several flexural failure modes may be identified, namely tensile rupture of FRP laminates and concrete crushing before or after yielding of internal steel reinforcement. Upper and lower limits to the size of FRP laminates used are suggested to maintain ductile behaviour of strengthened reinforced concrete sections. Comparisons between the flexural strength obtained from the current method and experiments show good agreement. Design equations for calculating the size of FRP laminates externally bonded to reinforced concrete sections to enhance their flexural strength are proposed.