This work is focused on the evaluation of the selected fracture parameters of quasi-brittle material, especially concrete, and an assessment of their dependence on the size and shape of the fracture process zone developing at the tip of the macroscopic crack during fracture. For this purpose, experimentally obtained loading diagrams published in the scientific literature have been utilized. These diagrams have been processed into a form enabling creation and calibration of numerical models of these tests in the ATENA FEM program. The results obtained from simulations of the three-point bending tests on beams of four sizes, with three notches lengths, using the created numerical models were used for determination of fracture parameters of concrete. Results of the work consist of the determined values of the specific energy dissipated for creation of new surfaces of the effective crack and an estimation of the specific energy dissipated in the volume of the fracture process zone, which exhibits specific parameters for each beam size and notch length.

The thesis is focused on a test on determination of the fracture-mechanical parameters of quasi-brittle materials, especially concrete. What is referred to as the wedge-splitting test is considered, for which a variety of shapes of notched specimen can be used. This work is exclusively focused on the cylinder-shaped specimen of diameter 150 mm and breadth of 100 mm. The test is performed virtually using Atena 2D FEM software. Progress of failure is observed during loading of the specimen for various notch lengths. The amount of energy released for the development the failure outside of the tested cross-sectional area (weakened by the notch) is quantified and the size of the fracture process zone is investigated. The described analysis is performed for several material sets witch differ in cohesive properties of the quasi-brittle material expressed via the so-called characteristic length. Suitable proportions of the test specimen are sought, in order to avoid the failure and thus also the energy dissipation outside of the specimen ligament area during the experimental tests, which shall lead to more accurate estimates of fracture-mechanical parameters of the tested material.