Ph.D. (Chemistry) / This study focuses on the morphology and crystal-growth behaviour of polyactide (PLA)-based blends and blends modified with organoclay thin films. The study further examined the effect of blending and the incorporation of organoclays on the enzymatic degradation behaviour. Thin films of unmodified and nanoclay-modified PLA/poly(butylene succinate) (PBS) blends were cast on a glass substrate by a spin coater, while thin films of biodegradable PLA/poly[(butylene succinate)-coadipate] PBSA blends and blends containing organoclays were cast on a silicon (100) wafer substrate. The morphology and crystal growth behaviour of the thin films crystallized at different temperatures were examined with an atomic force microscopy (AFM) equipped with a hot-stage scanner. In PLA/PBS blend thin films, AFM images showed that the size of the dispersed PBS phase was influenced by C30B clay loading on the blends. The dispersed size reduced on the addition of C30B clay up to 2 wt%, beyond which, dispersed size began to increase. Transmission electron microscopy studies indicated that this behaviour was due to the preferential location of silicates in the PBS phase than in the PLA phase. For thin films annealed at 60 °C, the additi on of organoclays to the blend quenched the growth of edge-on lamellae. The crystalline morphologies at 120 °C were dominated by edge-on lamellae grown, around the PBS phase to form spherulites. Morphologies of thin films crystallized at 120 °C from melt were dominated by the flat-on lamellae, while those crystallized at 70 °C from melt were dominated by the edge-on lamellae. In the case of PLA/PBSA blend thin films, the results indicated that the size and distribution of the dispersed phase were directly related to the blend composition. The crystal growth behaviours indicated the presence of homogeneous and heterogeneous nucleations, and the nature of nucleation was directly related to the blend ratio and the temperature at which crystallization occurred. Therefore, this study will facilitate the understanding of crystal growth behaviour in a confined environment and will enable the modulation of the blend properties.

As non-vascular, early land plants with an aquatic ancestry, mosses do not regulate internal water conditions separate from that of their environment and as a result, evolved mechanisms to survive in a terrestrial world out of water. Yet, there is a widely accepted dogma that moss reproductive success is solely dependent on rainfall events carrying swimming, bi-flagellate sperm across the landscape to reproductively mature and receptive female mosses--but this classic view of moss reproduction may be too simplistic. In this dissertation I test the assumptions of reproductive limitation in mosses and present novel findings in a basal, yet understudied terrestrial plant mating system. I find evidence of environmental desiccation tolerance in moss sperm, thus offering the potential for stress-tolerant gametes on the landscape possibly suited for various transport vectors, reminiscent of a pollen grain. To investigate the broad evolutionary implications of this newfound complexity in moss sexual reproduction, I tested classic tenets of plant-pollinator theory on the ancient mosses and their ubiquitous microarthropod inhabitants. Experimental results show that mosses and microarthropods are engaged in a "pollination-like" syndrome guided by sex-specific volatile cues that differentially affect microarthropod behavior. These data indicate an existing complex mutualistic relationship and provides new evidence of sexually dimorphic investment by male and female mosses into reproductive success. Further, these data put forth the idea that female mosses challenge an inherent mate limitation by investing into reproductive assurance via maintaining a relationship with microarthropods. Experimental work further confirms a role for invertebrates in moss reproductive success and tests mutualism theory through ongoing experiments. Such experiments include an assessment of moss genetic diversity, paternity, and male fitness traits as it relates to mosses with or without the presence of microarthropods, thereby testing for fitness benefits gained by mosses possibly engaged in a transport mutualism with microarthropods. I further tested mutualism, community ecology and moss sexual reproduction concepts in extreme geothermal moss populations living at the edges of inhabitable Earth, and results show that even geothermal moss canopies are diverse and host differential and abundant life. In a first field test of mutualism I found that although extreme heat stress may constrain sexual reproduction in mosses, a correlation between within-population moss genetic diversity and microarthropod abundances exists. To further examine mosses in extreme environments, and how these environments may constrain sexual reproductive success, I evaluated the effects of simulated warming on Antarctic moss physiology and reproductive biology. Data indicates that simulated warming relieves mosses of physiological stress, and results in a greater investment into primary productivity and sexual reproduction. These data support the hypothesis that with less stress, sexual reproduction is increased. Mosses are an ideal system by which to understand organisms that exist in environments ranging from the mesic to the extreme, in the laboratory and the field and even in the classroom, where the small functioning ecosystem of mosses can be used for discovery-based biology education as described in the Mosscosms curriculum. This work contributes significantly to the field of bryophyte and plant biology by revealing novel insights into the biotic and abiotic drivers of sexual reproduction in mosses.

The aim of this work is to optimize the acoustic nondestructive method (NDT) Impact-Echo (IE) as a complementary diagnostic tool for the assessment of concrete structures exposed to high temperatures. Commonly used diagnostic procedures for concrete structures affected by fire are most often limited to in-situ core drilling and subsequent testing of the drilled holes by destructive testing. The Impact-Echo method allows non-destructive testing of variously degraded test specimens and concrete structures, but its use for the assessment of temperature-degraded cementitious composites is hardly ever used in practice. Many studies suggest that Impact-Echo is one of the most suitable non-destructive methods for assessing the rate of degradation by elevated temperature. The dissertation work consists of three main stages, where the first stage is devoted to the production of test specimens of different mixtures and their subsequent degradation by elevated temperature and testing by the IE method and by reference destructive and non-destructive methods. The second stage consists of manufacturing a reinforced concrete element with built-in thermocouples and its subsequent inhomogeneous degradation by a local source of elevated temperature. The controlled degraded element thus prepared contains all grades of thermally degraded concrete tested in the first stage. Subsequent testing consists of verification of standard procedures in the field of acoustic NDT with simultaneous use of experimental modal analysis. In the third stage, the objective is to interpret the measured data from both previous parts, to verify whether within the closed element temperature-degraded areas can be distinguished from one another, or the degree of thermal degradation of concrete. Based on these results, the optimal testing procedure was determined and the basic assumptions for the creation of degrees of damage of the concrete by increased temperature were determined.

No description available.

Actuator applications of shape memory alloys have typically been limited by their phase transformation temperatures to around 100 degrees C. However, recently with a focus on aerospace and turbomachinery applications there have been successful efforts to increase the phase transformation temperatures. Several of these alloy development efforts have involved ternary and quaternary elemental additions (e.g., Pt, Pd, etc.) to binary NiTi alloys. Experimentally assessing the effects of varying composition and thermo-mechanical processing parameters can be cost intensive, especially when expensive, high-purity elemental additions are involved. Thus, in order to save on development costs there is value in establishing a methodology that facilitates the fabrication, processing and testing of smaller specimens, rather than larger specimens from commercial billets. With the objective of establishing such a methodology, this work compares thermo-mechanical test results from bulk dog-bone tensile Ni29.5Ti50.5Pd20 samples (7.62 mm diameter) with that of thin wires (100 μm-150 µm diameter) extracted from comparable, untested bulk samples by wire electrical-discharge machining (EDM). The wires were subsequently electropolished to different cross-sections, characterized with Scanning Electron Microscopy, Transmission Electron Microscopy and Energy Dispersive X-Ray Spectroscopy to verify the removal of the heat affected zone following EDM and subjected to Laser Scanning Confocal Microscopy to accurately determine their cross-sections before thermo-mechanical testing. Stress-strain and load-bias experiments were then performed on these wires using a dynamic mechanical analyzer and compared with results established in iv previous studies for comparable bulk tensile specimens. On comparing the results from a bulk tensile sample with that of the micron-scale wires, the overall thermomechanical trends were accurately captured by the micron-scale wires for both the constrained recovery and monotonic tensile tests. Specifically, there was good agreement between the stress-strain response in both the martensitic and austenitic phases, the transformation strains at lower stresses in constrained recovery, and the transformation temperatures at higher stresses in constrained recovery. This work thus validated that carefully prepared micron-diameter samples can be used to obtain representative bulk thermo-mechanical properties, and is useful for fabricating and optimizing composition and thermomechanical processing parameters in prototype button melts prior to commercial production. This work additionally assesses potential applications of high temperature shape memory alloy actuator seals in turbomachinery. A concept for a shape memory alloy turbine labyrinth seal is also presented. Funding support from NASA’s Fundamental Aeronautics Program, Supersonics Project (NNX08AB51A) and Siemens Energy is acknowledged.

Numerous techniques exist for measuring temperature using passive devices such as SAW filters. However, SAW filters have a significant limitation regarding high temperature environments exceeding 1000⁰C [1]. There are several applications for a high temperature sensor in this range, most notably heat flux or temperature in turbine engines. For these environments, an alternative to SAW filters is to use a passive resonator. The resonate frequency will vary depending on the environment temperature. Understanding how the frequency changes with temperature will allow us to determine the environmental temperature. In order for this approach to work, it is necessary to induce resonance in the device and measure the resonance frequency. However, the extreme high temperature makes wired connections impractical, therefore wireless interrogation is necessary. To be practical a system of wireless interrogation of up to 20cm is desired.

M.S.

High pressure, high temperature technics were employed to successfully synthesize HoTe1.7, ErTe1.7, TmTe1.7, LuTe1.7, YTe1.7, and LuTe3. The pressure-temperature regions in which synthesis of each compound is successful were determined. Pressures to 100 kbars concurrently with temperatures to 1200 °C were used in an attempt to prepare ScTe1.7 and ScTe3, but these efforts met with failure. X-ray studies of these new compounds confirmed that they are extensions of the LTe2-X (0≤x

No description available.

Thesis (Ph.D.)--Massachusetts Institute of Technology, Dept. of Earth and Planetary Sciences, 1981. / Microfiche copy available in Archives and Science. / Vita. / Includes bibliographies. / by Yves Denis Caristan. / Ph.D.