The aim of this research is to understand the solid state physical properties of inulin in regards to the spray-drying treatments. In this context, inulin powders were produced by pilot spray-drying a commercial inulin dispersion under various feed (Tfeed) and inlet air (Tin) temperatures. More particularly, the amorphous and crystalline properties of the powders were studied by developing different fine characterization tools, such as modulated differential scanning calorimetry or powder X-ray diffraction. When the temperature of the inulin water systems increased, the crystallinity of the powder decreased. To a smaller extent, this tendency is also observed with the increase of the inlet air temperature of the spray drier. For example, an amorphous powder is obtained with a Tfeed of 90°C whatever the Tin (comprised between 120 and 230°C); whereas for a Tfeed of 80°C, a Tin of 230°C is necessary to obtain the same result. Adsorption isotherms were established on four powders covering a large range of crystallinity (crystallinity index from 0 to 92). The Guggenheim Anderson de Boer model was fitted to the experimental data. As the water content of the powders increased, the glass transition of inulin decreased. When the Tg droped below the storage temperature (20°C for example), the powders crystallized and underwent clumping phenomenon. Under these conditions, a continuous hard mass was observed for the amorphous powders; while their semi-crystalline counterparts were agglomerated but friable. To understand these changes, a kinetic study of the physical properties evolution and stability of an amorphous powder as a function of its water content was realized. These results allowed to correlate the Tg water content relationship to the evolution of the powders behaviour, such as stickiness or hardening during storage.