The topic of this dissertation was the preparation of a high-quality sulphate binder based on secondary raw materials. For this purpose, the work was primarily focused on the laboratory preparation of beta gypsum from the selected industrial gypsum, the design of the technological process of production and its verification by pilot tests. In the next step, the thesis dealt with the modification of beta gypsum by a selected set of liquefiers. In addition to commercial dehumidifiers, the possible beta casting of beta gypsum was tested by increasing the zeta potential of the gypsum suspension. At the end, a complete complex of construction products was developed based on laboratory and semi-prepared beta plasters, consisting of gypsum plasters, mastics, gypsum premix and small plaster casts.

This work is oriented on the preparation of high-voluable sulphate binder based on gypsum waste. One of the potential mineral resources in Moravia is Pregips chemical gypsum, produced by Precheza. This is the raw material, which is characterized by high purity, high quality and is economically acceptable. Beta burned gypsum plaster from this, however, need to modify due to suppression of the high needs of water mixing, which is determined by its morphology. The need for mixing water has a large impact on the strength of gypsum binders. Therefore it is necessary to find a suitable additive, which would reduce the coefficient of water in the preparation of porridge normal consistency.

This thesis is focused at possibilities of preparation and characterization of XRD-amorphous delaminated and dehydroxylated talc phase – meta-talc, which can have its potential application and a starter material for a preparation of magnesium-silicate analogues of geopolymers. Changes in structure and morphology of talc ore were observed during this work. For the purposes of this research, two various talc ores – chloritic and dolomitic were examined. Whole process of meta-talc preparation was examined with whole scale of instrumental techniques such as X-ray diffraction, simultaneous thermogravimetric a differential thermal analysis, infrared spectroscopy, scanning electron microscopy or laser analysis of particle size. Meta-talc can be obtained via mechanochemical activation of talc ore with subsequent calcination. Mechanochemical treatment lead to destruction of original crystal structure and breaking of original bonds, i.e. the product of this treatment was almost amorphous and delaminated. Most of hydroxyl groups were converted to molecules of water which remained adsorbed or coordinated in ore structure. These molecules were removed during calcination step.