Orientador: Marcelo Coelho Goiato / Abstract: The purpose of this study was to analyse the influence of time exposure to the environmental factors, chemical disinfection with 2% chlorhexidine-based solution and two distincts pigments about dimensional changing and maintenance of details of two silicones for use in maxillofacial prosthesis. Thirty specimens were fabricated for each silicone using a matrix, conformed closely to the specifications for nonaqueous, elastomeric dental impression materials established by the Revised American Dental Association n° 19 and the ISO 4823:1984. Specimens were separated in three groups: control (colourless), pigmented with commercial cosmetic (makeup powders) and pigmented with iron oxid. Specimens were analysed in a comparator microscopic (Carl Zeiss) and stereoscopic loupe. The readings were realized after polymerization of the specimens, and after 30 and 60 days, with and 157 without disinfection. The data were submited to the statistic analysis, by the Tukey's Test. The results indicated that all groups presented contraction; the chemical disinfection only changed the dimensional stability of the Silastic cosmetic pigmented group; the dimensional stability of Silastic was affected after 60 days of exposition in all groups. For the Brascoved silicone, the chemical disinfection only didn't have influence about dimensional stability in initial period; the exposition factor had influence about the dimensional stability of Brascoved in all periods and groups. The details were maintained in all specimens for both silicones, independent of the exposition time, of the pigments or disinfection. / Mestre

Orientador: Marcelo Coelho Goiato / Banca: Mitsuru Ogata / Banca: Stefan Fiúza de Carvalho Dekon / Banca: Mário Alexandre Coelho Sinhoreti / Banca: Humberto Gennari Filho / Resumo: O insucesso das próteses faciais é causado pelas limitações das propriedades dos materiais existentes, sendo as mais críticas a flexibilidade e a durabilidade. Uma prótese facial deve ser resistente e ter longa duração, mas se manter suave e flexível para acompanhar os movimentos faciais do paciente. Diante destas considerações, o objetivo desta pesquisa foi o de avaliar a deterioração marginal e a dureza SHORE A de dois silicones para uso em prótese facial - o Silastic 732 R.T.V. e o Silastic MDX4-4210, sob a influência do tempo de armazenagem, da desinfecção diária com clorexidina a 2% e de dois tipos de pigmentação, considerando que sempre houve a necessidade de um material que combinasse a flexibilidade natural da pele humana com durabilidade no seu uso. Foram confeccionados 30 corpos-de-prova para cada material, divididos em 3 grupos: controle (incolor), pigmentados com maquiagem e com óxido de ferro. A análise da deterioração marginal foi realizada em microscópio eletrônico de varredura e o teste de dureza dos materiais foi realizado em durômetro SHORE A, imediatamente, 6 meses e um ano após a confecção dos corpos-de-prova, seguindo as especificações da ASTM. Os dados da dureza foram submetidos à análise estatística, utilizando-se do teste de Tukey com nível de 99% de confiabilidade. Os dois silicones para uso facial apresentaram um aumento da sua dureza SHORE A com o passar do tempo. Entretanto, a dureza SHORE A manteve-se estável no período de 6 meses a 1 ano. Quando os silicones foram comparados entre si, o Silastic 732 R.T.V. mostrou-se estatisticamente mais flexível que o MDX4-4210. Após a análise visual das fotomicroscopias (aumento de 1000x) foi possível perceber que todos os grupos sofreram deterioração marginal e alteração de sua textura superficial com o passar do tempo...(Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Prosthetic failure can be attributed to the inherent problems of the properties of materials, such as flexibility and durability. The maxillofacial prosthesis must be strong and have durability, but must be soft and flexible enough to respond to the facial motions of the patient. The purpose of this study was to analyse the influence of time’s storage, chemical disinfection with 2% chlorhexidine-based solution and two distincts pigments about marginal deterioration and SHORE A hardness of two silicones for use in maxillofacial prosthesis - the Silastic 732 R.T.V. and the Silastic MDX4-4210. Thirty specimens were fabricated for each silicone using a matrix. Specimens were separated in three groups: control (colourless), pigmented with commercial cosmetic (makeup powders) and pigmented with iron oxid. The marginal deterioration analysis was realized in scanning electron microscope (SEM) and the hardness test was realized in a SHORE A durometer, according to ASTM, designation D 2240. The readings were realized after polymerization of the specimens (initial period), after 6 months and 1 year, with and without disinfection. The data of SHORE A hardness were submited to the statistic analysis, by the Tukey’s Test. Both silicones presented an increase of hardness over time. However, the hardness maintained stable at 6 months and 1 year periods. When both silicones were compared, the Silastic 732 R.T.V. showed statistically softer than MDX4-4210. After visual analysis of photomicrocopies (1000x), was possible note that all groups suffered marginal deterioration over time. The chemical disinfection also contributed to marginal deterioration of silicones, independent of time and pigmentation. Subject to the design, materials and methods used in this research, the following conclusions can be drawn:...(Complete abstract, click electronic address below) / Doutor

Orientador: Marcelo Coelho Goiato / Coorientador: Daniela Micheline dos Santos / Banca: Simone Cecílio Hallak Regalo / Banca: Stefan Fiuza Carvalho Dekon / Resumo: As próteses oculares são responsáveis pela recuperação da estética e auto-estima do usuário. Assim, os materiais utilizados na confecção de prótese ocular devem possuir propriedades específicas para sua indicação e durabilidade. Desse modo, é importante avaliar o comportamento destes materiais quando influenciados por diversas soluções desinfetantes. Este estudo teve como objetivo avaliar a microdureza, rugosidade superficial e alteração de cor de próteses oculares sobre a influência da desinfecção química e armazenagem. Foram confeccionadas 50 amostras simulando próteses oculares contendo duas resinas acrílicas (N1 e incolor), distribuídas em cinco grupos de acordo com o desinfetante utilizado: sabão neutro (I), opti-free (II), efferdent (III), hipoclorito a 1% (IV) e clorexidina a 4% (V). As amostras foram armazenadas por 120 dias, sendo desinfetadas durante este período. As leituras de microdureza, rugosidade e cor das amostras foram realizadas em um período inicial (B) e após 60 (T1) e 120 (T2) dias de armazenagem com desinfecção. A microdureza foi mensurada por meio de um microdurômetro, e a rugosidade determinada por um rugosímetro. A leitura de cor foi realizada por meio da espectrofotometria de reflexão, usando o sistema CIE L*a*b*. A alteração de cor (ΔE) foi calculada para os períodos entre T1 e B (T1B), e T2 e B (T2B). Pelos resultados obtidos a resina N1 para esclera apresentou menor microdureza estatisticamente significante, comparada a resina incolor (P<0,05). A maior alteração dos valores de microdureza e rugosidade foi obtida para os grupos IV e V. Ambos os períodos de desinfecção e armazenagem produziram alterações significativas (P<0,05) nas amostras com diminuição dos valores de... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Ocular prostheses are responsible to restore not only patient's aesthetic but also its self-esteem. The materials used to fabricate the ocular prostheses should present specific properties regarding its indication and durability. Therefore, it is important to investigate the physical behavior of such materials when subjected to different disinfectant solutions. This study evaluated the microhardness, surface roughness and color stability of ocular prostheses under the influence of different chemical disinfectant solutions and storage. A total of 50 samples simulating an ocular prosthesis containing two acrylic resins (N1 and colorless) were fabricated. They were divided into five groups as a function of disinfectant solution: neutral soap (I), opti-free (II), efferdent (III), 1% hypochlorite (IV) and 4% chlorhexidine (V). Samples were storage during 120 days, and they were disinfected throughout the period. Microhardness, roughness and color measurements were performed at baseline (B), after 60 (T1) and 120 (T2) days of storage with disinfection. The microharness and the roughness measurements were evaluated using a microdurometer and a roughness meter, respectively. Samples colors were measured with spectrophotometer using CIE L*a*b* system. Color differences (ΔE*) were calculated for periods between T1 and B (T1B), and T2 and B (T2B). The N1 acrylic resin exhibited statistically lower microhardness when compared to the colorless acrylic resin (P<0.05). The highest microhardness and roughness alterations were observed for groups IV and V. Both disinfection and storage periods statistically reduced the microhadness values and increased the roughness values of the samples (P<0.05). Color alteration was... (Complete abstract click electronic access below) / Mestre