Two industrial studies and one set of lab scale trials have been done. In addition, a theoretical study has been done. The main focus has been on non metallic inclusion composition during the ladle refining operation in industrial steel production. Sampling has been done together with careful inclusion determination. The inclusion composition is related to different variables. In the industrial trials samples have been taken at different steps during the ladle refining period. Steel and slag composition as well as temperature and oxygen activity have been determined. The thesis is based on five supplements with different major objectives, all related to the inclusion composition. The equilibrium top slag-steel bulk and inclusions-steel bulk were investigated by comparison between calculated and measured oxygen activity values. The oxygen activity and relation to temperature has also been discussed as well as oxygen activity and temperature gradients. The effect of vacuum pressure on inclusion composition has been evaluated in a theoretical study as well as lab scale trials. The inclusion composition has been studied during the industrial ladle treatment process. The inclusion composition was related to top slag composition and other parameters during ladle treatment. The major findings in the thesis are the lack of equilibrium conditions with respect to top-slag and steel bulk before vacuum treatment. The inclusions have been found to be closer to equilibrium with the steel bulk. Al/Al2O3 equilibrium has been found to control the oxygen activity after Al-deoxidation. Evaluation of inclusion composition during the ladle refining has revealed that the majority of the inclusions showed a continuous composition change throughout the ladle refining process, from high Al2O3, via MgO-spinel to finally complex types rich in CaO and Al2O3. The final inclusion composition after vacuum treatment was found to be close to the top slag composition. Vacuum pressure has been found to have a theoretical effect on inclusion composition at very low pressures. / QC 20100712

<p>The thesis is based on two supplements with two major objectives. In the first supplement equilibrium top slag-steel bulk and inclusions-steel bulk were investigated by comparison between calculated and measured oxygen activity values. This was done by applying different oxide activity models for slags combined with thermodynamic calculations. In the second supplement the inclusion composition is studied during the ladle refining process. The inclusion composition is related to top slag composition and other parameters during ladle</p><p>treatment.</p><p>The work was carried out by collecting data during well controlled sampling procedures at two different steel plants. Extensive inclusion analyses in Scanning Electron Microscope, SEM, were done. The data was used together with thermodynamics for a description of the interaction between slag-steel-inclusion interaction during ladle treatment.</p><p>Evaluation of inclusion composition during the ladle refining have revealed that the majority of the inclusions belonged to the system Al₂O₃-CaO-MgO-SiO₂and showed a continuous composition change throughout the ladle refining process, from high Al₂O_3, via MgO-spinel to finally complex types rich in CaO and Al₂O_3. The final composition after vacuum treatment was found to be close to the top slag composition. Small process parameter changes and practical variations during ladle refining were proven to give large differences of the inclusion composition.</p><p>Finally, it was concluded that equilibrium does not exist between top slag and steel bulk, with respect to oxygen, for the studied conditions. However, the equilibrium does exist between the steel bulk and inclusion.</p>

The thesis is based on two supplements with two major objectives. In the first supplement equilibrium top slag-steel bulk and inclusions-steel bulk were investigated by comparison between calculated and measured oxygen activity values. This was done by applying different oxide activity models for slags combined with thermodynamic calculations. In the second supplement the inclusion composition is studied during the ladle refining process. The inclusion composition is related to top slag composition and other parameters during ladle treatment. The work was carried out by collecting data during well controlled sampling procedures at two different steel plants. Extensive inclusion analyses in Scanning Electron Microscope, SEM, were done. The data was used together with thermodynamics for a description of the interaction between slag-steel-inclusion interaction during ladle treatment. Evaluation of inclusion composition during the ladle refining have revealed that the majority of the inclusions belonged to the system Al2O3-CaO-MgO-SiO2 and showed a continuous composition change throughout the ladle refining process, from high Al2O3, via MgO-spinel to finally complex types rich in CaO and Al2O3. The final composition after vacuum treatment was found to be close to the top slag composition. Small process parameter changes and practical variations during ladle refining were proven to give large differences of the inclusion composition. Finally, it was concluded that equilibrium does not exist between top slag and steel bulk, with respect to oxygen, for the studied conditions. However, the equilibrium does exist between the steel bulk and inclusion. / QC 20101109