Yes / The fracture resistance of polymethylmethacrylate (PMMA) as the most popular denture base material is not satisfactory. Different factors can be involved in denture fracture. Among them, flexural fatigue and impact are the most common failure mechanisms of an acrylic denture base. It has been shown that there is a correlation between the static strength and fatigue life of composite resins. Therefore, the transverse strength of the denture base materials can be an important indicator of their service life. In order to improve the fracture resistance of PMMA, extensive studies have been carried out; however, only a few promising results were achieved, which are limited to some mechanical properties of PMMA at the cost of other properties. This study aimed at optimizing the packing and processing condition of heat-cured PMMA as a denture base resin in order to improve its biaxial flexural strength (BFS). The results showed that the plain type of resin with a powder/monomer ratio of 2.5:1 or less, packed conventionally and cured in a water bath for 2 h at 95 °C provides the highest BFS. Also, it was found that the performance of the dry heat processor is inconsistent with the number of flasks being loaded.

Objetivo: O objetivo deste estudo foi avaliar clínica e hitologicamente a reação do material de preenchimento em dois sítios diferentes. Método: Vinte e duas femêas de ratos Wistar (Rattus novergicus) foram submetidas a aplicação de PMMA testando duas técnicas: subcutânea e transmuscular. Passados 3 meses do ato cirúrgico os ratos foram eutanasiados e as áreas injetadas foram excisadas, submetidas a técnica de inclusão em parafina e coloração por hematoxilina e eosina. As lâminas foram analisadas observando-se a resposta local à injeção do corpo estranho quanto ao grau de inflamação. Resultados: Foi encontrada diferença significativamente estatística entre os sítios muscular e subdérmico quanto a formação de granuloma (p<0,05), sendo que o grupo subdérmico obteve melhores resultados. Conclusão: A aplicação de materiais de preenchimento, que provoca maior trauma e sangramento nos tecidos, é a casusa de reações adversas. / Objective: The objective of this study was to evaluate clinical and hitopathology the reaction of the fill material at two different sites. Method: Twenty-two female Wistar rats (Rattus norvegicus) submitted the application of PMMA testing two techniques: subcutaneous and trans. After 3 months of surgery, the rats were euthanized and the injected areas were excised, subjected to paraffin embedding technique and stained with hematoxylin and eosin. The slides were analyzed by observing the local response to injection of foreign body in the degree of inflammation. Results: We found statistically significant differences between sites and subdermal muscle as granuloma formation (p <0.05), and the subdermal group achieved better results. Conclusion: The application of filling materials, which causes more injury and bleeding in the tissues, is Casusa of adverse reactions.

Objetivo: O objetivo deste estudo foi avaliar clínica e hitologicamente a reação do material de preenchimento em dois sítios diferentes. Método: Vinte e duas femêas de ratos Wistar (Rattus novergicus) foram submetidas a aplicação de PMMA testando duas técnicas: subcutânea e transmuscular. Passados 3 meses do ato cirúrgico os ratos foram eutanasiados e as áreas injetadas foram excisadas, submetidas a técnica de inclusão em parafina e coloração por hematoxilina e eosina. As lâminas foram analisadas observando-se a resposta local à injeção do corpo estranho quanto ao grau de inflamação. Resultados: Foi encontrada diferença significativamente estatística entre os sítios muscular e subdérmico quanto a formação de granuloma (p<0,05), sendo que o grupo subdérmico obteve melhores resultados. Conclusão: A aplicação de materiais de preenchimento, que provoca maior trauma e sangramento nos tecidos, é a casusa de reações adversas. / Objective: The objective of this study was to evaluate clinical and hitopathology the reaction of the fill material at two different sites. Method: Twenty-two female Wistar rats (Rattus norvegicus) submitted the application of PMMA testing two techniques: subcutaneous and trans. After 3 months of surgery, the rats were euthanized and the injected areas were excised, subjected to paraffin embedding technique and stained with hematoxylin and eosin. The slides were analyzed by observing the local response to injection of foreign body in the degree of inflammation. Results: We found statistically significant differences between sites and subdermal muscle as granuloma formation (p <0.05), and the subdermal group achieved better results. Conclusion: The application of filling materials, which causes more injury and bleeding in the tissues, is Casusa of adverse reactions.

Objetivo: O objetivo deste estudo foi avaliar clínica e hitologicamente a reação do material de preenchimento em dois sítios diferentes. Método: Vinte e duas femêas de ratos Wistar (Rattus novergicus) foram submetidas a aplicação de PMMA testando duas técnicas: subcutânea e transmuscular. Passados 3 meses do ato cirúrgico os ratos foram eutanasiados e as áreas injetadas foram excisadas, submetidas a técnica de inclusão em parafina e coloração por hematoxilina e eosina. As lâminas foram analisadas observando-se a resposta local à injeção do corpo estranho quanto ao grau de inflamação. Resultados: Foi encontrada diferença significativamente estatística entre os sítios muscular e subdérmico quanto a formação de granuloma (p<0,05), sendo que o grupo subdérmico obteve melhores resultados. Conclusão: A aplicação de materiais de preenchimento, que provoca maior trauma e sangramento nos tecidos, é a casusa de reações adversas. / Objective: The objective of this study was to evaluate clinical and hitopathology the reaction of the fill material at two different sites. Method: Twenty-two female Wistar rats (Rattus norvegicus) submitted the application of PMMA testing two techniques: subcutaneous and trans. After 3 months of surgery, the rats were euthanized and the injected areas were excised, subjected to paraffin embedding technique and stained with hematoxylin and eosin. The slides were analyzed by observing the local response to injection of foreign body in the degree of inflammation. Results: We found statistically significant differences between sites and subdermal muscle as granuloma formation (p <0.05), and the subdermal group achieved better results. Conclusion: The application of filling materials, which causes more injury and bleeding in the tissues, is Casusa of adverse reactions.

Cette étude se concentre sur l'influence des conditions hydrodynamiques et de mélange sur les caractéristiques de microcapsules obtenues par inversion/précipitation. Ce processus est classiquement exécuté dans une cuve agitée alors qu'il a été montré que l'exécution de procédés de fabrication de produits chimiques peut être améliorée en utilisant des microtechnologies en raison du meilleur contrôle hydrodynamique et de l'intensification des échanges de chaleur et de matières. Donc, afin d'évaluer l'avantage potentiel de ces nouvelles technologies, des microcapsules de parfum enrobé dans du PMMA ont été fabriquées par inversion de phase/précipitation (système THF/Eau) dans une cuve semi-fermé agitée standard, dans un mélangeur structuré et dans un micromélangeur de type V (FZK). Les trois procédés sont évalués en terme de propriétés de capsules (la distribution de taille, l'épaisseur de membrane, l'efficacité d'encapsulation et la cinétique de libération). Il a été montré que le micromélangeur offre une vaste gamme de conditions de fonctionnement / This study focuses on the influence of the hydrodynamic and mixing conditions on the characteristics of microcapsules obtained by inversion/precipitation. This process is classically run in semi-batch stirred tank while it has been shown that the performance of chemical product manufacturing processes can be improved by using microtechnologies due to better hydrodynamic control and intensification of mass and heat exchanges. Therefore, in order to evaluate the potential benefit of these new technologies, microcapsules of perfume in PMMA have been manufactured by phase inversion/precipitation (system THF/Water) in a classical semi-batch stirred tank, in a structured mixer and in a V-Type micromixer (FZK). The three process is evaluated in term of capsules properties (size distribution, membrane thickness, encapsulation efficiency and release rate). It is shown that micromixer offers a wide range of operating conditions

V dnešní době se chirurgové zajímají o vliv viskozity kostních cementů na jejich penetraci do kosti při úplné kostní náhradě. Penetrace cementu závisí na jeho viskozitě, času vsunutí protézy, době tvrdnutí, atd. Viskozita je určena chemickým složením, teplotou a poměrem monomeru a prášku. V této práci bude porovnávána viskozita a penetrace vysoko- a nízko- viskózních cementů. Viskozita bude měřena dvěma modely. V prvním modelu je hrot s konstantní rychlostí vtlačován do cementu. V druhém modelu je cement vytlačován z kapiláry konst. rychlostí. Penetrace cementu po vstříknutí do kosti bude měřena pomocí rentgenu.

O cimento ósseo, utilizado para a fixação de componentes protéticos nas cirurgias de substituição articular, mais resistente às forças de compressão do que às forças de tração, tem suas propriedades mecânicas alteradas por vários fatores entre esses a formulação comercial e o método de preparação empregado. É o objetivo deste trabalho avaliar comparativamente as propriedades mecânicas à compressão de duas formulações comerciais de cimento ósseo preparadas manualmente e a vácuo, segundo as instruções do fabricante. Um conjunto de moldagem confeccionado em aço inoxidável permitiu preparar 48 corpos de prova para cada grupo experimental, totalizando 192 corpos de prova, que foram testados na Máquina Universal de Ensaios, tendo as especificações baseadas nas normas ISO 5833 e ASTM F451-86. A elaboração do diagrama tensão x deformação de cada grupo experimental analisou as propriedades mecânicas do cimento ósseo quanto ao módulo de elasticidade, tensão e deformação no limite de proporcionalidade, entre grupos de mesma formulação comercial e entre os grupos com mesmo método de mistura. Analisados estatisticamente pelo método de Variança de Kruskal-Wallis (p &#8804;0,001) e pelo método de Dunn's (p &#8804;0,05). Quanto ao módulo de elasticidade, o grupo 2M foi o que apresentou maior módulo, 1563 MPa, valor estatisticamente significante (p &#8804; 0,05) em relação aos grupos 1M, 1V e 2V. Para a tensão no limite de proporcionalidade os grupos 1M (39,40 MPa) e 2V (39,65 MPa) foram os maiores valores de tensão no limite de proporcionalidade, não havendo diferença estatisticamente significante entre eles, mas essas diferenças foram significativas quando comparadas aos grupos 1V e 2M. A deformação no limite de proporcionalidade de maior valor percentual foi para o grupo 1M, 3,36%, sendo esta diferença estatisticamente significante quando comparado ao grupo 2M. Os testes de resistência à compressão do cimento nacionalizado e importado, preparados manualmente e a vácuo, mostraram não haver diferença importante entre os dois tipos de cimento ósseo, nem entre as duas formas de misturá-los. / The bone cement used for the fixation of the prosthetic components in the surgeries of joint replacement, more resistant to the compression than to the traction, has its mechanical properties altered by several factors among those the commercial formulation and preparation employee's method. It is the objective of this work to evaluate the mechanical properties to the compression of the two commercial formulas of bone cement manually prepared and using vacuum, according to the manufacturer's instructions. A molding set was made in stainless steel and it allowed for the preparation of 48 bodies of proof for each experimental group, adding up to 192 proof bodies total which were tested in the Universal Rehearsal Machine, with the specifications based on the ISO 5833 and the ASTM F451-86 regulations. The elaboration of the diagram "tension vs. deformation" of each of the experimental group analyzed the mechanical properties of the bone cement in relation to the elasticity module, tension and deformation on the proportional limit among the groups with the same commercial formula and among the groups with the same mixture method. Analyzed statistically, by Kruskal-Wallis's method of the variation (p &#8804;0.001) and by the Dunn’s method (p &#8804;0.05). Regarding the elasticity, the group 2M was the one with the highest module, 1563 MPa, a statistically significant value (p &#8804;0.05) in relation to the groups 1M, 1V and 2V to the tension at the limit of the proportionality, there is no significant differences among them, but these differences were relevant when compared to groups 1V and 2M. The deformation at the limit of the proportionality of the highest percentage was to group 1M, 3.36%, being this the relevant statistical difference when compared to group 2M. The resistance tests to the compression of the national and international cement prepared manually and by vacuum show that there is no important difference between the two kind of bone cement, and neither between the two ways of mixing them.

O cimento ósseo, utilizado para a fixação de componentes protéticos nas cirurgias de substituição articular, mais resistente às forças de compressão do que às forças de tração, tem suas propriedades mecânicas alteradas por vários fatores entre esses a formulação comercial e o método de preparação empregado. É o objetivo deste trabalho avaliar comparativamente as propriedades mecânicas à compressão de duas formulações comerciais de cimento ósseo preparadas manualmente e a vácuo, segundo as instruções do fabricante. Um conjunto de moldagem confeccionado em aço inoxidável permitiu preparar 48 corpos de prova para cada grupo experimental, totalizando 192 corpos de prova, que foram testados na Máquina Universal de Ensaios, tendo as especificações baseadas nas normas ISO 5833 e ASTM F451-86. A elaboração do diagrama tensão x deformação de cada grupo experimental analisou as propriedades mecânicas do cimento ósseo quanto ao módulo de elasticidade, tensão e deformação no limite de proporcionalidade, entre grupos de mesma formulação comercial e entre os grupos com mesmo método de mistura. Analisados estatisticamente pelo método de Variança de Kruskal-Wallis (p &#8804;0,001) e pelo método de Dunn's (p &#8804;0,05). Quanto ao módulo de elasticidade, o grupo 2M foi o que apresentou maior módulo, 1563 MPa, valor estatisticamente significante (p &#8804; 0,05) em relação aos grupos 1M, 1V e 2V. Para a tensão no limite de proporcionalidade os grupos 1M (39,40 MPa) e 2V (39,65 MPa) foram os maiores valores de tensão no limite de proporcionalidade, não havendo diferença estatisticamente significante entre eles, mas essas diferenças foram significativas quando comparadas aos grupos 1V e 2M. A deformação no limite de proporcionalidade de maior valor percentual foi para o grupo 1M, 3,36%, sendo esta diferença estatisticamente significante quando comparado ao grupo 2M. Os testes de resistência à compressão do cimento nacionalizado e importado, preparados manualmente e a vácuo, mostraram não haver diferença importante entre os dois tipos de cimento ósseo, nem entre as duas formas de misturá-los. / The bone cement used for the fixation of the prosthetic components in the surgeries of joint replacement, more resistant to the compression than to the traction, has its mechanical properties altered by several factors among those the commercial formulation and preparation employee's method. It is the objective of this work to evaluate the mechanical properties to the compression of the two commercial formulas of bone cement manually prepared and using vacuum, according to the manufacturer's instructions. A molding set was made in stainless steel and it allowed for the preparation of 48 bodies of proof for each experimental group, adding up to 192 proof bodies total which were tested in the Universal Rehearsal Machine, with the specifications based on the ISO 5833 and the ASTM F451-86 regulations. The elaboration of the diagram "tension vs. deformation" of each of the experimental group analyzed the mechanical properties of the bone cement in relation to the elasticity module, tension and deformation on the proportional limit among the groups with the same commercial formula and among the groups with the same mixture method. Analyzed statistically, by Kruskal-Wallis's method of the variation (p &#8804;0.001) and by the Dunn’s method (p &#8804;0.05). Regarding the elasticity, the group 2M was the one with the highest module, 1563 MPa, a statistically significant value (p &#8804;0.05) in relation to the groups 1M, 1V and 2V to the tension at the limit of the proportionality, there is no significant differences among them, but these differences were relevant when compared to groups 1V and 2M. The deformation at the limit of the proportionality of the highest percentage was to group 1M, 3.36%, being this the relevant statistical difference when compared to group 2M. The resistance tests to the compression of the national and international cement prepared manually and by vacuum show that there is no important difference between the two kind of bone cement, and neither between the two ways of mixing them.