The objective of this research was to characterize the seawater transport and its effect on the transverse tensile strength of a carbon/vinylester composite. The moisture contents of neat vinylester and unidirectional carbon/vinylester composite panels immersed in seawater were monitored until saturation. A model for moisture up-take was developed based on superposition of Fickian diffusion, and Darcy’s law for capillary transport of water. Both the predicted and measured saturation times increased with increasing panel size, however the diffusion model predicts much longer times while the capillary model predicts shorter time than observed experimentally. It was also found that the saturation moisture content decreased with increasing panel size. Testing of macroscopic and miniature composite transverse tensile specimens, and SEM failure inspection revealed more fiber/matrix debonding in the seawater saturated composite than the dry composite, consistent with a slightly reduced transverse tensile strength. / Includes bibliography. / Thesis (M.S.)--Florida Atlantic University, 2015. / FAU Electronic Theses and Dissertations Collection

Nesta Tese foram preparados, em solução, filmes híbridos de argila e poliestireno provenientes de copos descartáveis comercializados no mercado brasileiro, com acetato de etila e glicerol. Posteriormente, foi adicionado o Hemi-hidrato de sulfato de cálcio como carga de reforço. Tanto a argila quanto o glicerol, assim como o hemihidrato de sulfato de cálcio, foram utilizados nos percentuais relativos à massa do poliestireno fragmentado correspondendo a 1%,2%, 3%,4%, 5% e 7%. Dos filmes, nos percentuais 3, 4, 5 e 7, exclui-se o percentual de 4% e os demais foram fragmentados e submetidos a extrusão, com resfriamento natural, à seco, produzindo-se grãos com os quais foi avaliado o índice de fluidez e injetados para a moldagem de corpos de prova rígidos. O desempenho dos corpos rígidos, foi comparado com os resultados do HIPS 484, e o GPPS comercializados no mercado brasileiro. Os filmes foram caracterizados por difração de raios X, microscopia eletrônica de varredura (MEV), calorimetria exploratória diferencial (DSC), além dos testes de resistência à tração, fluorescência de raios X, EDS e FTIR. Amostra do filme, ultrafino, obtido a partir da solução com o percentual de 5% foi observada ao microscópio ótico e no microscópio eletrônico de transmissão, assim como amostras de corpos rígidos microtomizadas. Nos corpos rígidos, além das análises instrumentais citadas, foram avaliadas a resistência à flexão, modulo de flexão, resistência à tração, alongamento e resistência ao impacto Izod. O desempenho sob chama foi avaliado em amostras de filme e também do corpo rígido. Resultados do DRX, e da MET foram coerentes com a bibliografia para nanocompósitos argila-polímero e, associado às respostas dos demais ensaios, indicaram um material de boa qualidade morfológica e boas propriedades mecânicas comparadas ao HIPS 484 e ao GPPS. Sob a chama o material produzido apresentou maior resistência à queima avaliado pela quantidade aparente de material residual para um mesmo tempo sob fogo. Constatou-se, também, uma boa dispersão das cargas na matriz polimérica, assim como uma adequada interação entre os elementos orgânicos e inorgânicos do material, a delaminação parcial da argila e quebra da estrutura do hemi-hidrato. Isto resultou em um bom desempenho mecânico e térmico do compósito que pode ser atribuído, tanto a uma forte influência dos íons metálicos presentes nas cargas inorgânicas, quanto às adições presentes na formulação dos copos descartáveis. / In this work were prepared in solution, hybrid films of montmorillonite clay and polystyrene from disposable cups sold in the Brazilian market, with ethyl acetate and glycerol. Subsequently, the calcium sulphate hemihydrate was added as reinforcing filler. Both clay and glycerol, as well as calcium sulfate hemihydrate were used in percentage relative to the mass of the fragmented polystyrene corresponding to 1%, 2% and 3% and 3%, 4%, 5% and 7%. Of the specimens, the percentage 3, 4, 5 and 7, excluding the percentage of 4% and the rest were fragmented and subjected to extrusion, with natural cooling to dry, producing grains with which the flow rate was evaluated and injected to the molding of rigid specimens. The performance of rigid bodies were compared with HIPS 484 results and GPPS sold in the Brazilian market. The films were characterized by X-ray diffraction, scanning electron microscopy (SEM), differential scanning calorimetry (DSC), in addition to tensile strength tests, xray fluorescence, EDS and FTIR. Film sample, ultrathin, obtained from the solution to the percentage of 5% was observed in optical microscope and transmission electron microscope, as well as samples of rigid bodies after the microtome. In rigid bodies, in addition to instrumental analyzes described above were evaluated flexural strength, flexural modulus, tensile strength, elongation and Izod impact strength. The performance under fire was evaluated in film and the rigid body samples. Results of XRD and TEM were consistent with the literature for clay nanocomposites and polymer-associated responses of other tests indicated a morphological good quality material and good mechanical properties compared to 484 HIPS and GPPS. Under the flame, the material produced showed higher resistance to burning evaluated by the apparent amount of residual material for an equal time under fire. It was found, also good dispersion of the fillers in the polymer matrix, and an appropriate interaction between the organic material and inorganic elements, delamination of the clay and breaking the hemihydrate structure. It Results in a good mechanical and thermal performance of the composite that can be attributed, both, to a strong influence of metal ions present in the inorganic fillers as additions in the formulation of disposable cups.

Nesta Tese foram preparados, em solução, filmes híbridos de argila e poliestireno provenientes de copos descartáveis comercializados no mercado brasileiro, com acetato de etila e glicerol. Posteriormente, foi adicionado o Hemi-hidrato de sulfato de cálcio como carga de reforço. Tanto a argila quanto o glicerol, assim como o hemihidrato de sulfato de cálcio, foram utilizados nos percentuais relativos à massa do poliestireno fragmentado correspondendo a 1%,2%, 3%,4%, 5% e 7%. Dos filmes, nos percentuais 3, 4, 5 e 7, exclui-se o percentual de 4% e os demais foram fragmentados e submetidos a extrusão, com resfriamento natural, à seco, produzindo-se grãos com os quais foi avaliado o índice de fluidez e injetados para a moldagem de corpos de prova rígidos. O desempenho dos corpos rígidos, foi comparado com os resultados do HIPS 484, e o GPPS comercializados no mercado brasileiro. Os filmes foram caracterizados por difração de raios X, microscopia eletrônica de varredura (MEV), calorimetria exploratória diferencial (DSC), além dos testes de resistência à tração, fluorescência de raios X, EDS e FTIR. Amostra do filme, ultrafino, obtido a partir da solução com o percentual de 5% foi observada ao microscópio ótico e no microscópio eletrônico de transmissão, assim como amostras de corpos rígidos microtomizadas. Nos corpos rígidos, além das análises instrumentais citadas, foram avaliadas a resistência à flexão, modulo de flexão, resistência à tração, alongamento e resistência ao impacto Izod. O desempenho sob chama foi avaliado em amostras de filme e também do corpo rígido. Resultados do DRX, e da MET foram coerentes com a bibliografia para nanocompósitos argila-polímero e, associado às respostas dos demais ensaios, indicaram um material de boa qualidade morfológica e boas propriedades mecânicas comparadas ao HIPS 484 e ao GPPS. Sob a chama o material produzido apresentou maior resistência à queima avaliado pela quantidade aparente de material residual para um mesmo tempo sob fogo. Constatou-se, também, uma boa dispersão das cargas na matriz polimérica, assim como uma adequada interação entre os elementos orgânicos e inorgânicos do material, a delaminação parcial da argila e quebra da estrutura do hemi-hidrato. Isto resultou em um bom desempenho mecânico e térmico do compósito que pode ser atribuído, tanto a uma forte influência dos íons metálicos presentes nas cargas inorgânicas, quanto às adições presentes na formulação dos copos descartáveis. / In this work were prepared in solution, hybrid films of montmorillonite clay and polystyrene from disposable cups sold in the Brazilian market, with ethyl acetate and glycerol. Subsequently, the calcium sulphate hemihydrate was added as reinforcing filler. Both clay and glycerol, as well as calcium sulfate hemihydrate were used in percentage relative to the mass of the fragmented polystyrene corresponding to 1%, 2% and 3% and 3%, 4%, 5% and 7%. Of the specimens, the percentage 3, 4, 5 and 7, excluding the percentage of 4% and the rest were fragmented and subjected to extrusion, with natural cooling to dry, producing grains with which the flow rate was evaluated and injected to the molding of rigid specimens. The performance of rigid bodies were compared with HIPS 484 results and GPPS sold in the Brazilian market. The films were characterized by X-ray diffraction, scanning electron microscopy (SEM), differential scanning calorimetry (DSC), in addition to tensile strength tests, xray fluorescence, EDS and FTIR. Film sample, ultrathin, obtained from the solution to the percentage of 5% was observed in optical microscope and transmission electron microscope, as well as samples of rigid bodies after the microtome. In rigid bodies, in addition to instrumental analyzes described above were evaluated flexural strength, flexural modulus, tensile strength, elongation and Izod impact strength. The performance under fire was evaluated in film and the rigid body samples. Results of XRD and TEM were consistent with the literature for clay nanocomposites and polymer-associated responses of other tests indicated a morphological good quality material and good mechanical properties compared to 484 HIPS and GPPS. Under the flame, the material produced showed higher resistance to burning evaluated by the apparent amount of residual material for an equal time under fire. It was found, also good dispersion of the fillers in the polymer matrix, and an appropriate interaction between the organic material and inorganic elements, delamination of the clay and breaking the hemihydrate structure. It Results in a good mechanical and thermal performance of the composite that can be attributed, both, to a strong influence of metal ions present in the inorganic fillers as additions in the formulation of disposable cups.