Ultra-pure reagents, platinum resistance thermometry and modern inert atmosphere glove box facilities have made possible a detailed examination of the NaK system at atmospheric pressure. A thermoanalytical study of solid-liquid phase equilibria in the NaK alloy system was conducted in the tetrahedral press to 55 kbars to investigate possible intermediate compound formation and shifting of the invariant points at various pressures. An expected shift in the eutectic composition to lower potassium content with an increase in the halt temperature on increasing pressure was confirmed. A merging of the meritectic and eutectic points at 343 ±2°K and 37 ±3 kbars occurred at 0.40 mole fraction K. Above 35 kbars the original meritectic halt behaves much like elemental cesium, suggesting new structural modifications. The possibility of a eutectoid with increased solid solubility limits is suggested for the invariant point which decreases with increasing pressure. The formation of NaK2 under pressure is suggested but not confirmed.

Alkali compounds were added to a South African coal with a high swelling propensity and the behaviour of the blends were investigated. A vitrinite-rich bituminous coal from the Tshikondeni coal mine in the Limpopo province of South Africa was used. To reduce the influence of the minerals in the coal, the coal was partially demineralized by leaching with HCl and HF. The ash content of the coal sample was successfully reduced from 17.7% to 0.6%. KOH, KCl, K2CO3 and KCH3CO2 were then added to the demineralized coal in mass percentages of 1%, 4%, 5% and 10%. The free swelling indices (FSI) of the blends were determined and the samples were subjected to acquisition of TMA and TG-MS data. Addition of these potassium compounds to the demineralized coal reduced the swelling of the vitrinite-rich coal. From the free swelling indices of the various mixtures, it was concluded that the potassium compounds reduce the swelling of the coal in the following order of decreasing impact: KCH3CO2 > KOH > K2CO3 > KCl. From dilatometry experiments done on the blends with the 10% addition of potassium compounds, it was seen that with the addition of potassium compounds to the demineralized coal, a reduction in dilatation volume was obtained. The influence of the potassium compound in decreasing order: K2CO3> KOH> KCH3CO2> KCl. An increase in the softening temperature was observed for the demineralized coal-alkali blends. Thermogravimetric analyses were performed on the demineralized coal-potassium blended samples (<75 μm). These samples were pyrolyzed under a nitrogen atmosphere to a maximum temperature of 1200 °C using a heating rate of 10 °C/min. The relative reactivity for each of the blends with the different wt% addition was determined. From these results it was seen that KCH3CO2 increased the relative reactivity, whereas the KOH, KCl and K2CO3 showed an inhibiting influence. The attached mass spectrometer provided information on the low molecular mass gaseous products formed in the various temperature ranges as the thermal treatment proceeded. From the mass spectroscopy results, it was found that the potassium compounds decreased the temperature at which maximum evolution of H2 takes place. Thermomechanical analyses were performed on the 10 wt% addition of the potassium compounds to the demineralized coal. During TMA analyses, the sample was heated to 1000 °C using a heating rate of 10 °C/min. From the TMA result obtained it was clear that the addition of KCl did not have an influence on the swelling of the demineralized coal. All results are discussed. / MSc (Chemistry), North-West University, Potchefstroom Campus, 2014

Alkali compounds were added to a South African coal with a high swelling propensity and the behaviour of the blends were investigated. A vitrinite-rich bituminous coal from the Tshikondeni coal mine in the Limpopo province of South Africa was used. To reduce the influence of the minerals in the coal, the coal was partially demineralized by leaching with HCl and HF. The ash content of the coal sample was successfully reduced from 17.7% to 0.6%. KOH, KCl, K2CO3 and KCH3CO2 were then added to the demineralized coal in mass percentages of 1%, 4%, 5% and 10%. The free swelling indices (FSI) of the blends were determined and the samples were subjected to acquisition of TMA and TG-MS data. Addition of these potassium compounds to the demineralized coal reduced the swelling of the vitrinite-rich coal. From the free swelling indices of the various mixtures, it was concluded that the potassium compounds reduce the swelling of the coal in the following order of decreasing impact: KCH3CO2 > KOH > K2CO3 > KCl. From dilatometry experiments done on the blends with the 10% addition of potassium compounds, it was seen that with the addition of potassium compounds to the demineralized coal, a reduction in dilatation volume was obtained. The influence of the potassium compound in decreasing order: K2CO3> KOH> KCH3CO2> KCl. An increase in the softening temperature was observed for the demineralized coal-alkali blends. Thermogravimetric analyses were performed on the demineralized coal-potassium blended samples (<75 μm). These samples were pyrolyzed under a nitrogen atmosphere to a maximum temperature of 1200 °C using a heating rate of 10 °C/min. The relative reactivity for each of the blends with the different wt% addition was determined. From these results it was seen that KCH3CO2 increased the relative reactivity, whereas the KOH, KCl and K2CO3 showed an inhibiting influence. The attached mass spectrometer provided information on the low molecular mass gaseous products formed in the various temperature ranges as the thermal treatment proceeded. From the mass spectroscopy results, it was found that the potassium compounds decreased the temperature at which maximum evolution of H2 takes place. Thermomechanical analyses were performed on the 10 wt% addition of the potassium compounds to the demineralized coal. During TMA analyses, the sample was heated to 1000 °C using a heating rate of 10 °C/min. From the TMA result obtained it was clear that the addition of KCl did not have an influence on the swelling of the demineralized coal. All results are discussed. / MSc (Chemistry), North-West University, Potchefstroom Campus, 2014

No description available.