Main extrinsic and intrinsic modifiers factors of crack growth rate in AA7050-T7451 were assessed in order to provide tools for aeronautical structures designers. These tools cover most necessary information to project aircraft\'s structures using the studied alloy, under damage tolerance philosophy. The experimental methodology consisted of use CT specimens, on TL and LT rolling direction to test its behavior under different conditions of stress ratio, force waveform, and the environment. The stress ratio values were 0.1 and 0.5, the force waveform used were sine and trapezoidal or Dwell under normal air laboratory conditions and salt fog 3.5%NaCl weight in order to simulate the marine environment. In Dwell tests, results were checked with the electrical potential drop technique (DCPD) in addition to the crack opening displacement (COD) method. Using the Walker coefficients, calculated on the present research, could be projected accurately the crack propagation behavior on Paris region and do fatigue life predictions using da/dN and S-N diagrams for different stress ratio values. The corrosion environment increases both crack growth rate and ΔKth due to oxides formation on the crack path that generates a crack closure effect. Dwell carrying makes decrease the crack growth rate by decreasing the slope of the Paris line on log (da/dN) versus log (ΔK) curve, instead of shifting down the line as occurs on titanium alloys. Rolling direction change from LT to TL increase the FCG rate in both threshold and Paris region, where the rate change use to be small. / Os principais fatores modificadores extrínsecos e intrínsecos da taxa de propagação de trincas na liga AA7050-T7451 foram avaliados para fornecer subsídios para projetistas de estruturas aeronáuticas, com base na filosofía de tolerância ao dano. A metodologia experimental consistiu em ensaiar corpos de prova do tipo compact tension (CT) da liga nas direções de laminação TL e LT, para verificar seu comportamento sob diferentes razões de tensões, forma de onda e condição ambiente. Os valores de razão de tensão estudados foram 0,1 e 0,5, as formas de onda foram senoidal e trapezoidal ou de Dwell, em condições normais de laboratório, ao ar, e névoa salina 3,5% NaCl, em massa, para simular um ambiente marinho. No caso dos ensaios Dwell, os resultados foram conferidos pelo método de queda de potencial eléctrico (QPE), além do método de flexibilidade elástica. Usando os coeficientes de Walker calculados a partir dos resultados obtidos, pôde-se projetar com precisão o comportamento da propagação de trinca na região de Paris e prever a vida em fadiga usando os diagramas da/dN e S-N para diferentes valores da razão de tensões. O ambiente corrosivo aumenta tanto a taxa de propagação de trinca, quanto o valor de ΔKth por causa da formação de óxidos na trajetória da trinca, que geram um efeito de fechamento sobre a mesma. Quanto à forma de onda, verificou-se que o carregamento Dwell diminui a taxa de propagação de trinca, diminuindo a inclinação das curvas log (da/dN) versus log (ΔK) na região de Paris, ao invés de deslocá-la paralelamente como ocorre com ligas de titânio. A mudança da direção de laminação de LT para TL aumenta a taxa de propagação de trinca por fadiga (PTF) tanto na região de threshold, quanto na região de Paris, onde a mudança de taxa é pequena.

This thesis is on fatigue crack growth experiments and assessments of fatigue crack growth rates. Both constant and variable amplitude loads in two different materials are considered; a nickel based super-alloy Inconel 718 and a stainless steel 316L. The considered load levels extend from small scale yielding (SSY) to large scale yielding (LSY) for both materials. The effect of different load schemes on the fatigue crack growth rates is investigated on Inconel 718 and compact tension specimens in Paper A. It is concluded that load decreasing schemes give a to high Paris law exponent compared to constant or increasing load amplitude schemes. Inconel 718 is further analyzed in Paper B where growth rates at variable amplitude loading in notched tensile specimens are assessed. The predictions are based on the fatigue crack growth parameters obtained in Paper A. The crack closure levels are taken into consideration and it is concluded that linear elastic fracture mechanics is incapable of predicting the growth rates in notches that experience large plastic cyclic strains. Even if crack closure free fatigue parameters are used and residual stresses due to plasticity are included. It is also concluded that crack closure free and nominal fatigue crack growth data predict the growth rates equally well. However, if the crack closure free parameters are used, then it is possible to make a statement in advance on the prediction in relation to the experimental outcome. This is not possible with nominal fatigue crack growth parameters. The last three papers consider fatigue crack growth in stainless steel 316L. Here the load is defined as the crack tip opening displacement parameter. Paper C constitutes an investigation on the effect of plastic deformation on the potential drop and consequently the measured crack length. It is concluded that the nominal calibration equation obtained in the undeformed geometry can be used at large plastic deformations. However, two conditions must be met: the reference potential must be taken in the deformed geometry and the reference potential needs to be adjusted at every major change of plastic deformation. The potential drop technique is further used in Paper D and Paper E for crack length measurements at monotonic LSY. Constant amplitude loads are considered in Paper D and two different variable amplitude block loads are investigated in Paper E. The crack tip opening displacement is concluded in Paper D to be an objective parameter able to characterize the load state in two different geometries and at the present load levels. Furthermore, if the crack tip opening displacement is controlled in an experiment and the local load ratio set to zero, then only monotonic LSY will appear due to extensive isotropic hardening, i.e. elastic shake-down. This is also the reason why the linear elastic stress-intensity factor successfully could merge all growth rates, extending from SSY to monotonic LSY along a single line in a Paris law type of diagram, even though the generally accepted criteria for SSY is never fulfilled. For the variable amplitude loads investigated in Paper E, the effect of plastic deformation on measured potential drop is more pronounced. However, also here both the crack tip opening displacement parameter and the linear elastic stress-intensity factor successfully characterized the load state. / <p>QC 20130108</p>

Main extrinsic and intrinsic modifiers factors of crack growth rate in AA7050-T7451 were assessed in order to provide tools for aeronautical structures designers. These tools cover most necessary information to project aircraft\'s structures using the studied alloy, under damage tolerance philosophy. The experimental methodology consisted of use CT specimens, on TL and LT rolling direction to test its behavior under different conditions of stress ratio, force waveform, and the environment. The stress ratio values were 0.1 and 0.5, the force waveform used were sine and trapezoidal or Dwell under normal air laboratory conditions and salt fog 3.5%NaCl weight in order to simulate the marine environment. In Dwell tests, results were checked with the electrical potential drop technique (DCPD) in addition to the crack opening displacement (COD) method. Using the Walker coefficients, calculated on the present research, could be projected accurately the crack propagation behavior on Paris region and do fatigue life predictions using da/dN and S-N diagrams for different stress ratio values. The corrosion environment increases both crack growth rate and &Delta;Kth due to oxides formation on the crack path that generates a crack closure effect. Dwell carrying makes decrease the crack growth rate by decreasing the slope of the Paris line on log (da/dN) versus log (&Delta;K) curve, instead of shifting down the line as occurs on titanium alloys. Rolling direction change from LT to TL increase the FCG rate in both threshold and Paris region, where the rate change use to be small. / Os principais fatores modificadores extrínsecos e intrínsecos da taxa de propagação de trincas na liga AA7050-T7451 foram avaliados para fornecer subsídios para projetistas de estruturas aeronáuticas, com base na filosofía de tolerância ao dano. A metodologia experimental consistiu em ensaiar corpos de prova do tipo compact tension (CT) da liga nas direções de laminação TL e LT, para verificar seu comportamento sob diferentes razões de tensões, forma de onda e condição ambiente. Os valores de razão de tensão estudados foram 0,1 e 0,5, as formas de onda foram senoidal e trapezoidal ou de Dwell, em condições normais de laboratório, ao ar, e névoa salina 3,5% NaCl, em massa, para simular um ambiente marinho. No caso dos ensaios Dwell, os resultados foram conferidos pelo método de queda de potencial eléctrico (QPE), além do método de flexibilidade elástica. Usando os coeficientes de Walker calculados a partir dos resultados obtidos, pôde-se projetar com precisão o comportamento da propagação de trinca na região de Paris e prever a vida em fadiga usando os diagramas da/dN e S-N para diferentes valores da razão de tensões. O ambiente corrosivo aumenta tanto a taxa de propagação de trinca, quanto o valor de &Delta;Kth por causa da formação de óxidos na trajetória da trinca, que geram um efeito de fechamento sobre a mesma. Quanto à forma de onda, verificou-se que o carregamento Dwell diminui a taxa de propagação de trinca, diminuindo a inclinação das curvas log (da/dN) versus log (&Delta;K) na região de Paris, ao invés de deslocá-la paralelamente como ocorre com ligas de titânio. A mudança da direção de laminação de LT para TL aumenta a taxa de propagação de trinca por fadiga (PTF) tanto na região de threshold, quanto na região de Paris, onde a mudança de taxa é pequena.