JÚNIOR, J.M.F. Obtenção e caracterização de revestimento de ZN-Mn em meio de sulfato. 2008. 72 f. Dissertação (Mestrado em Ciências Química Orgânica e Inorgânica) – Centro de Ciências, Universidade Federal do Ceará, Fortaleza, 2008. / Submitted by irlana araujo (irlanaaraujo@gmail.com) on 2011-12-26T16:51:40Z No. of bitstreams: 1 2008_dis_ Jos Júnior.pdf: 3771509 bytes, checksum: d121eb98621555284579628b27a13c5f (MD5) / Approved for entry into archive by Aline Nascimento(vieiraaline@yahoo.com.br) on 2012-01-20T13:28:12Z (GMT) No. of bitstreams: 1 2008_dis_ Jos Júnior.pdf: 3771509 bytes, checksum: d121eb98621555284579628b27a13c5f (MD5) / Made available in DSpace on 2012-01-20T13:28:12Z (GMT). No. of bitstreams: 1 2008_dis_ Jos Júnior.pdf: 3771509 bytes, checksum: d121eb98621555284579628b27a13c5f (MD5) Previous issue date: 2008-05-21 / The development of alloys that are resistant to corrosion and good wear resistance led to several studies on the electrodeposition field. With the intention of carry out alloys with good mechanic properties, associated to a high corrosion resistance, Zn-Mn alloys have been frequently studied in the last years, once they offer better anticorrosive characteristics when compared to metallic zinc films, usually used in the conventional industry. This work aimed obtain and characterize Zn-Mn alloy electrodeposited on platinum electrode and metallic cooper from solutions composed by sulfate salts from the metals previously mentioned. Zn-Mn alloys were studied by using of cyclic and linear voltammetry, and also chronoamperommetry, in which all samples were obtained in bath without agitation, room temperature, 25º C, on different current densities. The physical and morphological structure of the alloys that have been obtained were analyzed by using technique such as scanning electronic microscopy (SEM) and X-ray dispersive energy (XDE), varying parameters such as: current density applied, pH, deposition temperature and reagents concentration in the bath. In order to analyze the chemical structure of the species formed on the alloy mentioned, a x-ray diffraction (XRD) technique was used with the samples obtained in cooper electrode. From the results obtained through voltammetric analyses, it is possible to determine the potential of reduction and oxidation of Zn-Mn alloy, which occurred separately to zinc and manganese. It was possible to observe that the manganese in the alloy appears as the oxide and the zinc as an isolated metal. Through XRD analysis, it was possible to determine the phases in which the Zn-Mn species appears in the alloy, and also isolated zinc and manganese. The best results were obtained when was applied 10mA.cm-2 current density; pH 6,0; room temperature and 1:1 proportion of zinc and manganese in the electrolytic bath. / O desenvolvimento de revestimentos metálicos cada vez mais resistentes à corrosão e ao desgaste mecânico tem originado inúmeros estudos na área de eletrodeposição. Com intuito de se obter ligas metálicas com boas propriedades mecânicas, associadas a uma elevada resistência à corrosão, é que os revestimentos de Zn-Mn têm sido bastante abordados nos últimos anos, tendo em vista que estes oferecem melhores características anticorrosivas quando comparados com revestimentos de zinco metálico, usualmente utilizados na indústria convencional. Neste trabalho, objetivou-se a obtenção e caracterização das ligas de Zn-Mn eletrodepositadas sobre eletrodos de platina e cobre metálico a partir de soluções a base de sais de sulfato dos metais em questão. Estudou-se a liga de Zn-Mn com utilização de voltametria cíclica e linear, como também de cronoamperometria, onde nesta etapa todas as amostras foram obtidas em banho sem agitação, à temperatura ambiente, 25ºC, em diferentes densidades de corrente. Analisou-se também a estrutura física e morfológica das ligas obtidas com uso de técnicas como Microscopia Eletrônica de Varredura (MEV) e Energia Dispersiva de Raios-X (EDX), variando-se parâmetros como: densidade de corrente aplicada, pH da solução eletrolítica, temperatura de deposição e concentração dos reagentes presentes no eletrólito. Para análise da estrutura química das espécies formadas na liga em questão, utilizou-se a técnica de Difração de Raios-X (DRX) nas amostras obtidas em eletrodo de cobre. A partir dos resultados obtidos por meio das análises voltamétricas, pôde-se determinar os potenciais de redução e oxidação para a liga Zn-Mn onde estes ocorreram isoladamente para o zinco e para o manganês. Para as análises de MEV e EDX observou-se que o manganês na liga apresenta-se na forma de oxido e o zinco na forma de metal isolado. Para as análises de DRX, pôde-se determinar as fases em que as espécies de Zn-Mn apresentam-se na liga, assim como também espécies de zinco e manganês isoladas. Os melhores resultados foram obtidos quando se aplicou uma densidade de corrente de 10 mA.cm-2, pH 6,0, temperatura ambiente e proporção de 1:1 entre o zinco e o manganês no eletrólito.

Este trabalho tem como principal objetivo a análise experimental comprovativa do efeito de deformação em revestimentos de alumínio quando aplicado um determinado processo de rebitagem. São objetivos secundários: identificar dentre os fatores elegíveis (diâmetro do furo, altura do escareado, material do rebite, espessura do revestimento e tipo de rebitagem - manual ou automática) aqueles que possuem influência e o grau dessa influência na deformação do revestimento. Primeiramente, foi utilizado um questionário e uma matriz de avaliação para eleger os fatores mais relevantes do processo baseado na experiência e conhecimento técnico de especialistas em processo de rebitagem e ciência dos materiais. Na segunda etapa, realizou-se a medição de corpos de prova com combinações saturadas de todos os fatores previamente eleitos baseado na técnica de Taguchi de Arranjos Ortogonais. Por último foi realizada a análise de dados utilizando o conceito da ANAVA - Análise de Variância -utilizando o software MINITABÔ. Os resultados obtidos comprovam a expansão do revestimento após a rebitagem e identifica os principais fatores e seus respectivos efeitos na expansão.

MAGALHÃES, S. G. Avaliação do revestimento a base de liga de níquel em aço estrutural, empregando o metal de adição ERNiCrMo-3 através da soldagem MIG/MAG. 2008. 97 f. Dissertação (Mestrado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2008. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2016-04-01T12:29:37Z No. of bitstreams: 1 2008_dis_sgmagalhães.pdf: 6796878 bytes, checksum: c82071f9343873e0f6aa85450c77197f (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2016-04-07T17:24:08Z (GMT) No. of bitstreams: 1 2008_dis_sgmagalhães.pdf: 6796878 bytes, checksum: c82071f9343873e0f6aa85450c77197f (MD5) / Made available in DSpace on 2016-04-07T17:24:08Z (GMT). No. of bitstreams: 1 2008_dis_sgmagalhães.pdf: 6796878 bytes, checksum: c82071f9343873e0f6aa85450c77197f (MD5) Previous issue date: 2008-04-04 / The use of nickel alloy cladding components could be more frequently in petroleum industry. The crescent naphthenic corrosion and high molecular weight of national petroleum contribute for needs of materials with more resistance to corrosion, to temperature and to pressure. At this way, how part of systematic study, this work pretends to define operational range for adequate ERNiCrMo-3 weld overlay in structural steel with application of GMAW process, and to evaluate microstructural characteristics and mechanical properties in as welded and aging conditions. To realize the objective, were used an industrial robot, an electronic power source and an argon shielding gas for automated welding. To define the operational range, simple deposit welds and evaluation of superficial aspect, geometry and dilution were conducted. This step indicated that the welds in efficient current below 200 A showed high convexity and the variation of current for the calc of heat input is more significant for convexity and dilution of the weld than the variation of welding speed for the calc of same heat input. It was selected 290 A as welding current in two heat inputs (10 and 14 kJ/cm). The overlay at ASTM A 516 g60 steel was in simple layer, had overlap up to 40 pct between passes and had about 15 pct of dilution at the two heat inputs. The aging temperature employed was 600 oC for times of 100 and 300 hours. To metallurgical characterization was used: microhardness measures, optical microscope, scanning electron microscope, composition variations (EDAX), x-ray diffraction, electron backscatter diffraction and shear tests according ASTM A 265-03 standard specification. The microhardness and structures observed were, approximately, the same for the two heat inputs. Post aging HAZ showed absence of carbides. The dendritic structure had MC and Laves micro-phases in as welded condition and the aging provoked formation of secondary carbides, dissolution of primary carbides and formation of gama’’. As welded overlay microhardness was 240 HV and as welded HAZ was 190 HV. Aging HAZ was 120 HV and aging overlay was 290 HV for 100 h and 310 HV for 300 h. Only for aging conditions, were observed hard zones (800 HV) in interface of overlay, due to carbide concentration and aging of partially dilution zone, where the Fe favored the formation of gama’’. Despite the hardness differences of overlay, base metal and interface, were identified no cracks in metallographic analyses. The maximum shear strength was above of the specification requirement (140 MPa) in all conditions employed, the penetration shape (like finger) favored this result, and the aging provoked a gradual grow up in shear resistance. / O uso de componentes revestidos por ligas de níquel do sistema Ni-Cr-Mo em equipamentos da indústria do petróleo pode vir a ser mais freqüente, pois os aumentos no índice de acidez naftênica e no peso molecular do petróleo nacional requerem materiais mais resistentes à corrosão, temperatura e pressão. Desta forma, como parte de um estudo sistemático, este trabalho pretende definir faixas operacionais para revestir de forma adequada aço estrutural com o eletrodo ERNiCrMo-3, através da soldagem MIG/MAG, e avaliar características microestruturais e propriedades mecânicas de revestimentos na condição como soldados e envelhecidos. Para atingir o objetivo, foram realizadas soldagens automáticas com utilização de robô industrial, fonte eletrônica e argônio puro como gás de proteção. Para definição das faixas operacionais, as soldagens foram em simples deposição, com avaliação de aspecto superficial, geometria e diluição da solda. Nesta etapa, foi constatado que a solda apresenta alta convexidade em corrente eficaz abaixo de 200 A e a variação da corrente, para o cálculo da energia, influencia de forma mais significativa na convexidade e na diluição da solda, em comparação com a variação da velocidade de soldagem, para o cálculo das mesmas energias. Através dos testes preliminares, foi selecionada a corrente de 290 A em duas energias de soldagem (10 e 14 kJ/cm). O revestimento foi em única camada aplicada em aço ASTM A516 g60 de 12,7 mm de espessura, com sobreposição acima de 40 % e temperatura de interpasse abaixo de 100 oC. A diluição em ambas as energias ficou em torno de 15 %. O envelhecimento foi na temperatura de 600 oC por tempos de 100 e 300 horas. Para caracterização metalúrgica foram utilizados: perfis de microdureza, microscopia ótica (MO) e eletrônica de varredura (MEV), energia dispersiva de raio X (EDX), difração de raio X, energia de elétrons retro-espalhados (EBSD) e ensaio de arrancamento, segundo norma ASTM A 265-03. Os perfis de microdureza e estruturas observadas foram semelhantes para ambas as energias de soldagem utilizadas. Após envelhecimento foi observado uma descarbonetação da ZAC-GG onde as ferritas passaram a não possuir segundas fases (carbonetos). A estrutura dendrítica do revestimento apresentou microfases do tipo MC e Laves na condição como soldada. Após o envelhecimento, houve formação de carbonetos secundários, dissolução de carbonetos primários e formação de fase gama’’. Os perfis de dureza indicaram que na condição como soldada a dureza do revestimento foi de 240 HV e da ZAC-GG de 190 HV, com o envelhecimento a dureza na ZAC-GG caiu para 120 HV, e a do revestimento cresceu para 290 HV em 100 h e 310 HV em 300 h. Na interface foram observadas, somente após o envelhecimento, regiões duras da ordem de 800 HV, devido a grande concentração de carbonetos e envelhecimento da zona parcialmente diluída, com teor elevado de ferro, que atua na formação de gama’’. Apesar das elevadas diferenças de dureza entre o revestimento, metal base e interface não foram identificadas trincas nas análises metalográficas. A carga máxima no ensaio de arrancamento foi superior a da norma (140 MPa) nas condições analisadas. O perfil de penetração dos cordões (tipo taça) favoreceu esse resultado, e o envelhecimento provocou um aumento gradativo de resistência ao cisalhamento.

Submitted by FERNANDO SANTOS DA SILVA null (fernandoquimicauems@hotmail.com) on 2017-09-28T02:21:06Z No. of bitstreams: 1 Tese_Fernando_Santos_da_Silva_IQ_UNESP.pdf: 19317124 bytes, checksum: b4f79b295bc22505ca8f3f01bd3db519 (MD5) / Approved for entry into archive by Monique Sasaki (sayumi_sasaki@hotmail.com) on 2017-09-28T14:59:57Z (GMT) No. of bitstreams: 1 silva_fs_dr_araiq.pdf: 19317124 bytes, checksum: b4f79b295bc22505ca8f3f01bd3db519 (MD5) / Made available in DSpace on 2017-09-28T14:59:57Z (GMT). No. of bitstreams: 1 silva_fs_dr_araiq.pdf: 19317124 bytes, checksum: b4f79b295bc22505ca8f3f01bd3db519 (MD5) Previous issue date: 2017-09-15 / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Este trabalho teve como objetivo investigar a microestrutura, resistência à corrosão e propriedades mecânicas de revestimentos produzidos por Aspersão Fria (AF) a base de: (I) pó de alumínio (Al), com ou sem alumina (Al2O3), depositados sobre aço comum; (II) revestimentos metálico-cerâmicos de WC-12Co e WC-25Co depositados sobre a liga Al7075-T6 e (III) revestimentos de cobre depositados sobre aço e obtidos a partir de pós submetidos a diferentes tratamentos. A análise dos materiais de partida e dos revestimentos, antes e após os ensaios de corrosão, foi realizada por difração a laser (DL), microscopia óptica (OM), microscopia eletrônica de varredura (SEM) acoplado a um sistema de espectroscopia de dispersão de energia de raios X (EDS) e difração de raios X (DRX). Foram realizadas medidas de dureza e ensaios de resistência ao desgaste por abrasão (Rubber Wheel) e por deslizamento (Ball on disk). A resistência à corrosão dos revestimentos foi avaliada por medidas eletroquímicas em meio de NaCl 3,5% e testes de névoa salina. Foram realizadas medidas de potencial em circuito aberto (ECA), espectroscopia de impedância eletroquímica (EIS) e curvas de polarização linear e cíclica. As imagens de SEM da secção transversal mostram que os revestimentos são densos, não possuem porosidade interconectada e nem trincas. Os resultados eletroquímicos e de névoa salina mostram que todos os revestimentos investigados protegem o substrato por longos tempos de imersão por serem compactos quando obtidos pela tecnologia de AF. Para os revestimentos a base de alumínio, os estudos mostram que o eletrólito atinge o substrato em alguns pontos somente após 2000 h de imersão e os ensaios de desgaste indicam que o revestimento compósito Al-Al2O3 apresenta melhores propriedades mecânicas. Quanto aos revestimentos metálicocerâmicos, o revestimento de WC-25Co apresentou maior espessura e também maior proteção contra corrosão até tempos maiores do que 2000 h. A caracterização dos revestimentos de cobre mostra claramente que os diferentes tratamentos dos materiais de partida exercem influência na eficiência de deposição, formação dos revestimentos e principalmente na sua resistência à corrosão. / The purpose of this work was to investigate the microstructure, corrosion resistance and mechanical properties of coatings prepared by Cold Gas Spray (CGS) based on: (I) aluminum (Al) powder with or without alumina (Al2O3), deposited on common steel; (II) WC-12Co and WC-25Co metallic-ceramic coatings deposited onto Al7075- T6 alloy and (III) copper coatings deposited onto common steel and obtained from powders submitted to different treatments. The analysis of the feedstock materials and the coatings before and after the corrosion tests were performed by laser diffraction (LD), optical microscopy (OM), scanning electron microscopy (SEM) with energy dispersive X-ray spectroscopy system (EDS) and X-ray diffraction (XRD). Hardness measurements, abrasion testing (Rubber Wheel) and sliding wear test (Ball on disk) were performed. The corrosion resistance of the coatings was evaluated by electrochemical measurements in 3.5% NaCl medium, and salt fog tests. Open circuit potential (EOC), electrochemical impedance spectroscopy (EIS), linear and cyclic polarization measurements were performed. SEM images of the cross section showed that coatings are dense, without interconnected porosity and cracks. Electrochemical and salt fog results show that all investigated coatings protect the substrate during long immersion times because they are compact when obtained by CGS technology. For the aluminum based coatings, the studies show that the electrolyte reaches the substrate at some points only after 2000 h of immersion and the wear tests show that the Al-Al2O3 composite coating has better mechanical properties. For the metal-ceramic coatings, the WC-25Co coating show higher thickness and corrosion protection up to 2000 h of immersion when compared to WC-12Co. Copper coatings characterization clearly shows that the different treatments of the feedstock materials exert influence on the deposition efficiency, coating formation and especially on their corrosion resistance. / CNPq: 153177/2014-4