No abstract is provided. / Thesis / Master of Engineering (MEngr) / Scope and contents: In this report, a method for calculating the longitudinal shear capacity of the slab of simply-supported steel-concrete composite beams is presented. The method is based on analysing the stresses at failure of the concrete elements located at the slab shear surface. In this analysis, the slab width and the shear span are found to be two main parameters that have been neglected in the empirical solutions previously adopted.

The present research is conducted to investigate the structural behaviour of continuously supported deep beams made with SCC. A series of tests on eight reinforced two-span continuous deep beams made with SCC was performed. The main parameters investigated were the shear span-to-depth ratio, the amount and configuration of web reinforcement and the main longitudinal reinforcement ratio. All beams failed due to a major diagonal crack formed between the applied mid-span load and the intermediate support separating the beam into two blocks: the first one rotated around the end support leaving the rest of the beam fixed on the other two supports. The amount and configuration of web reinforcement had a major effect in controlling the shear capacity of SCC continuous deep beams. The shear provisions of the ACI 318M-11 reasonably predicted the load capacity of SCC continuous deep beams. The strut-and-tie model recommended by different design codes showed conservative results for all SCC continuous deep beams. The ACI Building Code (ACI 318M-11) predictions were more accurate than those of the EC2 and Canadian Code (CSA23.3-04). The proposed effectiveness factor equations for the strut-and-tie model showed accurate predictions compared to the experimental results. The different equations of the effectiveness factor used in upper-bound analysis can reasonably be applied to the prediction of the load capacity of continuously supported SCC deep beams although they were proposed for normal concrete (NC). The proposed three dimensional FE model accurately predicted the failure modes, the load capacity and the load-deflection response of the beams tested.

No description available.

The present research is conducted to investigate the structural behaviour of continuously supported deep beams made with SCC. A series of tests on eight reinforced two-span continuous deep beams made with SCC was performed. The main parameters investigated were the shear span-to-depth ratio, the amount and configuration of web reinforcement and the main longitudinal reinforcement ratio. All beams failed due to a major diagonal crack formed between the applied mid-span load and the intermediate support separating the beam into two blocks: the first one rotated around the end support leaving the rest of the beam fixed on the other two supports. The amount and configuration of web reinforcement had a major effect in controlling the shear capacity of SCC continuous deep beams. The shear provisions of the ACI 318M-11 reasonably predicted the load capacity of SCC continuous deep beams. The strut-and-tie model recommended by different design codes showed conservative results for all SCC continuous deep beams. The ACI Building Code (ACI 318M-11) predictions were more accurate than those of the EC2 and Canadian Code (CSA23.3-04). The proposed effectiveness factor equations for the strut-and-tie model showed accurate predictions compared to the experimental results. The different equations of the effectiveness factor used in upper-bound analysis can reasonably be applied to the prediction of the load capacity of continuously supported SCC deep beams although they were proposed for normal concrete (NC). The proposed three dimensional FE model accurately predicted the failure modes, the load capacity and the load-deflection response of the beams tested. / Higher Education Institute in the Libyan Government

Concrete deep beams with small shear span-to-depth (a/d) ratios are common elements in structures. However, there are few experimental results on the behaviour of FRP reinforced concrete deep beams and no specific modelling techniques exist in design codes for such members. The objectives of this study were to examine the shear behaviour of FRP reinforced concrete deep beams containing no web reinforcement and to develop a modelling technique. Test results of 12 large-scale specimens are reported where the primary variables included the a/d ratio, reinforcement ratio, member height, and concrete strength. The results showed that an arch mechanism was able to form in FRP reinforced concrete beams having a/d 2.1. A strut and tie modelling procedure adapted from CSA A23.3-04 was capable of accurately predicting the capacity of FRP reinforced concrete deep beams containing no web reinforcement while sectional shear models gave poor, but conservative, predictions. / Structural Engineering

No description available.

The flexural performance of composite systems made of reinforced concrete, Fibre Reinforced Polymers (FRPs) and adhesives was studied during the current research. The experimental investigation was principally concentrated on the potential use of Kevlar® 49 (aramid fibre) for RC beam strengthening. The main aims of research have been; (a) to investigate the relative merits of using Aramids in comparison to other FRPs, (b) strength optimisation of systems to prevent excessive losses of ductility, (c) to examine the failure mode and crack patterns, together with salient strength factors at ultimate limit state and (d) to carry out analytical modelling using a commercial FE package. The experimental investigation comprised of testing 55 simply supported RC beams of either 1.5m or 2.6m length. In addition to the parametric studies included in points (a)-(d) above (to assess the section characteristics), further experimentation was conducted to investigate the beam performance by varying the factors of; (e) beam shear span, (f) FRP anchorage length, (g) concrete surface preparation, (h) FRP end-anchoring, (i) beam precracking, (j) introduction of air-voids within the bond line of FRP/concrete, (k) influence of cyclic loading and, (1) exposure to aggressive environment. The results from current tests confirm elements of reports from other researchers (by thorough review of literature) that all FRPs have great potential for flexural strengthening of RC members. This is valid even in cases where additional environmental degradation and/or cracking (due to serviceability loads), had taken place. Aramid fibres were found to result in favourable outcomes concerning both strength and ductility enhancements. It was determined, both from experiments and non-linear modelling, that the amount of FRP fibre content is an important factor in every strengthening application. Experimentation showed that depending on the existing condition of the structure (concrete strength, internal reinforcement ratio, section dimensions, degradation level and load configuration), there seems to be a unique level of optimum fibre content. The FRP levels in excess of the optimum were seen to lead to premature brittle tearing-off failure modes. It was also found that to prevent premature beam failure (due to incompatibility of stress at concrete and FRP interface), a maximum possible anchorage length should be considered in order to deliver an optimum section performance. The results from the analytical modelling indicated a most satisfactory agreement with the experimental data after the initial mechanical properties were calibrated. It was found that actual representation of material properties (e.g. steel constitutive law) are of great significance, for an accurate modelling of RC element loaded behaviour. The bond developed between the FRP and concrete is one of the key parameters for achieving good performance of the systems. It was determined that concrete surface preparation and priming is beneficial, while the introduction of air-voids due to poor workmanship can reduce the section load bearing capabilities. Cyclic loading on FRP strengthened sections was found to curtail the full rotational capacity utilisation of the beam. However, even the above mentioned curtailed behaviour was more advantageous than cyclically loaded beam performance without FRP strengthening.