Measurements of the thermodynamic activities of chromium  and vanadium oxides in CaO-MgO-Al2O3-SiO2 slags

Dong, Pengli January 2009 (has links)
<p>In the present work, the thermodynamic activities of chromium and vanadium oxide in CaO-SiO2-MgO-Al2O3 slags were measured using gas-slag equilibration technique. The slag was equilibrated with a gas mixture of CO, CO2 and Ar gases enabling well-defined oxygen partial pressures in the gas mixture (PO2=10-3,10-4,10-5 Pa) at temperatures 1803, 1823K, 1873, 1923 K. The slags were kept in Pt crucibles during the equilibration and the duration of which was 20 h. From a knowledge of the thermodynamic activity of chromium and vanadium in Cr or V in Pt alloy, obtained from literature, and the oxygen partial pressure in the gas stream calculated by Thermo Calc software, the thermodynamic activity of chromium, vanadium oxide in the slags could be observed.An assessment of the experimental studies in earlier works reveal that, the activities of chromium at low chromium contents and vanadium in their respective alloys in platinum exhibits a strong negative deviation from ideality, the logarithms of activity coefficient of these elements were found to increase with increasing mole fractions of these metals in the Pt-alloys.Regarding the slag phase, all the chromium in the slags was assumed to be present in the divalent state in view of the low Cr contents and the low oxygen potentials employed in the present studies. Analogously, vanadium in the slag was assumed to be in the trivalent state in view of the low vanadium contents in the slag and the low oxygen partial pressure in the gas phase. Activity of chromium oxide, CrO decreases with increasing temperature and decreasing content of chromium oxide in slag and oxygen partial pressure in the gas phase. Activity of vanadium oxide, VO1.5 in slag phase shows a negative deviation from ideality. Activity coefficient of vanadium oxide shows a decrease with basicity of slag and the “break point” occurs at about slag basicity of 1 under the oxygen partial pressure of 10-3 Pa and temperature of 1873 K.A relationship for estimating the actual content of chromium, vanadium in slag as a function of activities of chromium or vanadium, temperature, oxygen partial pressure and slag basicity were developed from the present results, the agreement between the estimated and experimental values is satisfactory, especially at lower oxygen partial pressure.</p>
2

Measurements of the thermodynamic activities of chromium  and vanadium oxides in CaO-MgO-Al2O3-SiO2 slags

Dong, Pengli January 2009 (has links)
In the present work, the thermodynamic activities of chromium and vanadium oxide in CaO-SiO2-MgO-Al2O3 slags were measured using gas-slag equilibration technique. The slag was equilibrated with a gas mixture of CO, CO2 and Ar gases enabling well-defined oxygen partial pressures in the gas mixture (PO2=10-3,10-4,10-5 Pa) at temperatures 1803, 1823K, 1873, 1923 K. The slags were kept in Pt crucibles during the equilibration and the duration of which was 20 h. From a knowledge of the thermodynamic activity of chromium and vanadium in Cr or V in Pt alloy, obtained from literature, and the oxygen partial pressure in the gas stream calculated by Thermo Calc software, the thermodynamic activity of chromium, vanadium oxide in the slags could be observed.An assessment of the experimental studies in earlier works reveal that, the activities of chromium at low chromium contents and vanadium in their respective alloys in platinum exhibits a strong negative deviation from ideality, the logarithms of activity coefficient of these elements were found to increase with increasing mole fractions of these metals in the Pt-alloys.Regarding the slag phase, all the chromium in the slags was assumed to be present in the divalent state in view of the low Cr contents and the low oxygen potentials employed in the present studies. Analogously, vanadium in the slag was assumed to be in the trivalent state in view of the low vanadium contents in the slag and the low oxygen partial pressure in the gas phase. Activity of chromium oxide, CrO decreases with increasing temperature and decreasing content of chromium oxide in slag and oxygen partial pressure in the gas phase. Activity of vanadium oxide, VO1.5 in slag phase shows a negative deviation from ideality. Activity coefficient of vanadium oxide shows a decrease with basicity of slag and the “break point” occurs at about slag basicity of 1 under the oxygen partial pressure of 10-3 Pa and temperature of 1873 K.A relationship for estimating the actual content of chromium, vanadium in slag as a function of activities of chromium or vanadium, temperature, oxygen partial pressure and slag basicity were developed from the present results, the agreement between the estimated and experimental values is satisfactory, especially at lower oxygen partial pressure.
3

Abatement of Chromium Emissions from Steelmaking Slags - Cr Stabilization by Phase Separation

Albertsson, Galina January 2013 (has links)
Chromium is an important alloying element in stainless steel but also environmentally harmful element. A number of mineralogical phases present in the slag matrix can contain chromium and lead to chromium leaching. Chromium in slag if not stabilized, could oxidize to the cancerogenic hexavalent state, and leach out if exposed to acidic and oxygen rich environment. Other environmental concerns are slag dusting and chromium escape to the atmosphere. Despite the fact that there is a certain risk of Cr-emission from slags at operating conditions, still very little is known regarding the emission of the oxides of chromium during the slag tapping. Spinel phase is known to be important for controlling the leaching properties of chromium from the slag. The objective of the present study was to get an understanding of the phase relationships and chromium partition in the chromium-containing industrial slags and synthetic slags with a view to control the chromium stabilization in spinel phase. The impact of slag basicity, heat treatment, oxygen partial pressure and Al2O3 addition, on the phase relationships and chromium partition has been determined. The experimental results were compared with the phase equilibrium calculations. It was found that the oxygen partial pressure in the gas phase had a strong impact on chromium partition. The experimental results show that the impact of the slag basicity on chromium partition at lower oxygen partial pressures was negligible in contrast to that in air. The amount of spinel phase was found to increase with increased Al2O3 content. Slow cooling of slag and soaking at low oxygen partial pressure would improve the spinel phase precipitation. This treatment will also lead to less Cr dissolved in the unstable matrix phases. Chromium oxide was found to be emitted when chromium containing slags were exposed to oxidizing atmosphere. The results indicate that chromium oxide evaporation increases with increase in temperature and oxygen partial pressure, but decreases with slag basicity and sample thickness. / <p>QC 20131114</p> / Steel Eco-Cycle