Failure of Alloy 600 steam generator tubing in Pressurised Water Reactors (PWRs) has prompted the investigation of alloy 690 as an alternative material. Six commercially produced tubes and ten experimentally produced alloys have been examined with varying amounts of carbon, aluminium and titanium. Alloy compositions have been selected to investigate the individual and combined effects of these elements on the microstructure and corrosion behaviour in the environments of corrosion tests and simulated PWR conditions. Alloys were subjected to simulated mill annealing treatments at varied temperatures. Microstructural characterisation using optical and electron microscopy has demonstrated the effects of composition and thermal treatment in controlling grain size and carbide precipitation together with the interdependence between these structural details. Stress corrosion resistance of selected alloy 690 tubes has been examined with samples in an autoclave at fixed temperatures with environments based on pure water, sodium hydroxide and sodium hydroxide + sodium sulphate solutions. Susceptibility to intergranular attack has been related to aluminium contents of the alloy and to thermal treatments given. Results suggest a decreased resistance to IGA when aluminium is increased. Thermal treatments given to the samples appear not to be very significant to the amounts of IGA. The compositions and heat treatments used in the corrosion study were further examined on a dedicated scanning transmission electron microscope in order to correlate the effects of, chromium depletion, nickel enrichment and impurity segregation at grain boundaries, with corrosion characteristics. These results have shown the effect of varying the special thermal treatment temperature and time on the degree of enrichment / depletion / segregation and the corrosion resistance of the alloy. The mechanism of protection afforded by the special thermal treatment can thus be elucidated.

Os tubos de Geradores de Vapor em Reatores Nucleares do tipo PWR são submetidos a diferentes níveis de tensões e carregamento em altas temperaturas, reduzindo sua vida útil devido o surgimento de defeitos e corrosão. A inspeção por Correntes Parasitas é um ensaio não destrutivo usado para diagnosticar defeitos de corrosão e descontinuidades na superfície externa e interna em tubos de trocadores de calor. Esses tubos estão sujeitos a danos por diferentes mecanismos de degradação mecânica e química, tais como trincas por fadiga e corrosão sob tensão. Os sinais de inspeção por Correntes Parasitas são afetados por diferentes ruídos dificultando sua análise pelo inspetor. Esse trabalho apresenta os resultados da análise dos sinais de Correntes Parasitas usando a Transformada de Hilbert-Huang (THH) funcionando como filtro de ruídos (De-noising), como uma técnica alternativa de processamento e análise de sinais. A Transformada de Hilbert-Huang teve esse nome atribuído pela agência espacial norte-americana (NASA) para o resultado da reunião de dois processos, um método de decomposição empiricamente modal (Empirical Mode Decomposition EMD), seguido da análise espectral de Hilbert (Hilbert Spectral Analysis HSA). Os sinais de inspeção por correntes parasitas possuem características de transiente, não estacionário e não linear. A transformada de Hilbert-Huang aplicada neste trabalho forneceu dois recursos alternativos em processamento de sinais; o pré-processamento que funcionou como filtro de ruídos, e outro de análise de sinais, responsável pela identificação das características tempo-frequência-energia do sinal. / The nuclear power plant steam generator tubes are subjected to different levels of stress and loading at high temperatures, reducing its lifetime due to the development of defects and corrosion. The Eddy Current Testing (ECT) is a nondestructive testing used to diagnose defects of corrosion and discontinuities in the inner and outer surface of heat exchanger tubes. These tubes are subject to failure by different mechanisms of chemical and mechanical degradation such as fatigue and stress corrosion crack. The ECT signals are affected by different noises making the analysis a difficult task to the inspector. This dissertation presents the results of the main characteristics from the ECT signals using the Hilbert-Huang Transform (HHT) as an alternative method for the processing and signal analysis. The Hilbert-Huang Transform has its name given by the American National Aeronautics and Space Administration, NASA, as the result of Empirical Mode Decomposition (EMD) and the Hilbert Spectral Analysis (HSA) methods. The Eddy Current signals are transient, nonstationary and nonlinear. The Hilbert-Huang Transform applied in this work provided two alternative proceedings in signal processing, one in signal pre-processing acting as noise filter (De-noising) and another as signal analysis, which identifies the characteristics of signal time-frequency-energy.

Os tubos de Geradores de Vapor em Reatores Nucleares do tipo PWR são submetidos a diferentes níveis de tensões e carregamento em altas temperaturas, reduzindo sua vida útil devido o surgimento de defeitos e corrosão. A inspeção por Correntes Parasitas é um ensaio não destrutivo usado para diagnosticar defeitos de corrosão e descontinuidades na superfície externa e interna em tubos de trocadores de calor. Esses tubos estão sujeitos a danos por diferentes mecanismos de degradação mecânica e química, tais como trincas por fadiga e corrosão sob tensão. Os sinais de inspeção por Correntes Parasitas são afetados por diferentes ruídos dificultando sua análise pelo inspetor. Esse trabalho apresenta os resultados da análise dos sinais de Correntes Parasitas usando a Transformada de Hilbert-Huang (THH) funcionando como filtro de ruídos (De-noising), como uma técnica alternativa de processamento e análise de sinais. A Transformada de Hilbert-Huang teve esse nome atribuído pela agência espacial norte-americana (NASA) para o resultado da reunião de dois processos, um método de decomposição empiricamente modal (Empirical Mode Decomposition EMD), seguido da análise espectral de Hilbert (Hilbert Spectral Analysis HSA). Os sinais de inspeção por correntes parasitas possuem características de transiente, não estacionário e não linear. A transformada de Hilbert-Huang aplicada neste trabalho forneceu dois recursos alternativos em processamento de sinais; o pré-processamento que funcionou como filtro de ruídos, e outro de análise de sinais, responsável pela identificação das características tempo-frequência-energia do sinal. / The nuclear power plant steam generator tubes are subjected to different levels of stress and loading at high temperatures, reducing its lifetime due to the development of defects and corrosion. The Eddy Current Testing (ECT) is a nondestructive testing used to diagnose defects of corrosion and discontinuities in the inner and outer surface of heat exchanger tubes. These tubes are subject to failure by different mechanisms of chemical and mechanical degradation such as fatigue and stress corrosion crack. The ECT signals are affected by different noises making the analysis a difficult task to the inspector. This dissertation presents the results of the main characteristics from the ECT signals using the Hilbert-Huang Transform (HHT) as an alternative method for the processing and signal analysis. The Hilbert-Huang Transform has its name given by the American National Aeronautics and Space Administration, NASA, as the result of Empirical Mode Decomposition (EMD) and the Hilbert Spectral Analysis (HSA) methods. The Eddy Current signals are transient, nonstationary and nonlinear. The Hilbert-Huang Transform applied in this work provided two alternative proceedings in signal processing, one in signal pre-processing acting as noise filter (De-noising) and another as signal analysis, which identifies the characteristics of signal time-frequency-energy.