Corrosion of reinforcing bars is the major cause of deterioration of reinforced concrete (RC) structures in North America, Europe, the Middle East, and many coastal regions around the world. This deterioration leads to a loss of serviceability and functionality and ultimately affects the structural safety. The objective of this research is to formulate and implement a general stochastic finite element analysis (SFEA) framework for the time-dependent reliability analysis of RC beams with corroding flexural reinforcement. The framework is based on the integration of nonlinear finite element and reliability analyses through an iterative response surface methodology (RSM). Corrosion-induced damage is modelled through the combined effects of gradual loss of the cross-sectional area of the steel reinforcement and the reduction bond between steel and concrete for increasing levels of corrosion. Uncertainties in corrosion rate, material properties, and imposed actions are modelled as random variables. Effective implementation of the framework is achieved by the coupling of commercial finite element and reliability software. Application of the software is demonstrated through a case study of a simply-supported RC girder with tension reinforcement subjected to the effects of uniform (general) corrosion, in which two limit states are considered: (i) a deflection serviceability limit state and (ii) flexural strength ultimate limit state. The results of the case study show that general corrosion leads to a very significant decrease in the reliability of the RC beam both in terms of flexural strength and maximum deflections. The loss of strength and serviceability was shown to be predominantly caused by the loss of bond strength, whereas the gradual reduction of the cross-sectional area of tension reinforcement was found to be insignificant. The load-deflection response is also significantly affected by the deterioration of bond strength (flexural strength and stiffness). The probability of failure at the end of service life, due to the effects of uniform corrosion-induced degradation, is observed to be approximately an order of magnitude higher than in the absence of corrosion. Furthermore, the results suggest that flexural resistance of corroded RC beams is controlled by the anchorage (bond) of the bars and not by the yielding of fully bonded tensile reinforcement at failure. This is significant since the end regions can be severely corroded due to chloride, moisture, and oxygen access at connections and expansion joints. The research strongly suggests that bond damage must be considered in the assessment of the time-dependent reliability of RC beams subjected to general corrosion.

Reliability based life cycle cost analysis is becoming an important consideration for decision-making in relation to bridge design, maintenance and rehabilitation. An optimal solution should ensure reliability during service life while minimizing the life cycle cost. Risk of failure is an important component in whole of life cycle cost for both new and existing structures. Research work presented here aimed to develop a methodology for evaluation of the risk of failure of reinforced concrete bridges to assist in decision making on rehabilitation. Methodology proposed here combines fault tree analysis and probabilistic time-dependent reliability analysis to achieve qualitative and quantitative assessment of the risk of failure. Various uncertainties are considered including the degradation of resistance due to initiation of a particular distress mechanism, increasing load effects, changes in resistance as a result of rehabilitation, environmental variables, material properties and model errors. It was shown that the proposed methodology has the ability to provide users two alternative approaches for qualitative or quantitative assessment of the risk of failure depending on availability of detailed data. This work will assist the managers of bridge infrastructures in making decisions in relation to optimization of rehabilitation options for aging bridges.

Corrosion of reinforcing bars is the major cause of deterioration of reinforced concrete (RC) structures in North America, Europe, the Middle East, and many coastal regions around the world. This deterioration leads to a loss of serviceability and functionality and ultimately affects the structural safety. The objective of this research is to formulate and implement a general stochastic finite element analysis (SFEA) framework for the time-dependent reliability analysis of RC beams with corroding flexural reinforcement. The framework is based on the integration of nonlinear finite element and reliability analyses through an iterative response surface methodology (RSM). Corrosion-induced damage is modelled through the combined effects of gradual loss of the cross-sectional area of the steel reinforcement and the reduction bond between steel and concrete for increasing levels of corrosion. Uncertainties in corrosion rate, material properties, and imposed actions are modelled as random variables. Effective implementation of the framework is achieved by the coupling of commercial finite element and reliability software. Application of the software is demonstrated through a case study of a simply-supported RC girder with tension reinforcement subjected to the effects of uniform (general) corrosion, in which two limit states are considered: (i) a deflection serviceability limit state and (ii) flexural strength ultimate limit state. The results of the case study show that general corrosion leads to a very significant decrease in the reliability of the RC beam both in terms of flexural strength and maximum deflections. The loss of strength and serviceability was shown to be predominantly caused by the loss of bond strength, whereas the gradual reduction of the cross-sectional area of tension reinforcement was found to be insignificant. The load-deflection response is also significantly affected by the deterioration of bond strength (flexural strength and stiffness). The probability of failure at the end of service life, due to the effects of uniform corrosion-induced degradation, is observed to be approximately an order of magnitude higher than in the absence of corrosion. Furthermore, the results suggest that flexural resistance of corroded RC beams is controlled by the anchorage (bond) of the bars and not by the yielding of fully bonded tensile reinforcement at failure. This is significant since the end regions can be severely corroded due to chloride, moisture, and oxygen access at connections and expansion joints. The research strongly suggests that bond damage must be considered in the assessment of the time-dependent reliability of RC beams subjected to general corrosion.

Corrosion of reinforcing bars is the major cause of deterioration of reinforced concrete (RC) structures in North America, Europe, the Middle East, and many coastal regions around the world. This deterioration leads to a loss of serviceability and functionality and ultimately affects the structural safety. The objective of this research is to formulate and implement a general stochastic finite element analysis (SFEA) framework for the time-dependent reliability analysis of RC beams with corroding flexural reinforcement. The framework is based on the integration of nonlinear finite element and reliability analyses through an iterative response surface methodology (RSM). Corrosion-induced damage is modelled through the combined effects of gradual loss of the cross-sectional area of the steel reinforcement and the reduction bond between steel and concrete for increasing levels of corrosion. Uncertainties in corrosion rate, material properties, and imposed actions are modelled as random variables. Effective implementation of the framework is achieved by the coupling of commercial finite element and reliability software. Application of the software is demonstrated through a case study of a simply-supported RC girder with tension reinforcement subjected to the effects of uniform (general) corrosion, in which two limit states are considered: (i) a deflection serviceability limit state and (ii) flexural strength ultimate limit state. The results of the case study show that general corrosion leads to a very significant decrease in the reliability of the RC beam both in terms of flexural strength and maximum deflections. The loss of strength and serviceability was shown to be predominantly caused by the loss of bond strength, whereas the gradual reduction of the cross-sectional area of tension reinforcement was found to be insignificant. The load-deflection response is also significantly affected by the deterioration of bond strength (flexural strength and stiffness). The probability of failure at the end of service life, due to the effects of uniform corrosion-induced degradation, is observed to be approximately an order of magnitude higher than in the absence of corrosion. Furthermore, the results suggest that flexural resistance of corroded RC beams is controlled by the anchorage (bond) of the bars and not by the yielding of fully bonded tensile reinforcement at failure. This is significant since the end regions can be severely corroded due to chloride, moisture, and oxygen access at connections and expansion joints. The research strongly suggests that bond damage must be considered in the assessment of the time-dependent reliability of RC beams subjected to general corrosion.