abstract: Nitride semiconductors have wide applications in electronics and optoelectronics technologies. Understanding the nature of the optical recombination process and its effects on luminescence efficiency is important for the development of novel devices. This dissertation deals with the optical properties of nitride semiconductors, including GaN epitaxial layers and more complex heterostructures. The emission characteristics are examined by cathodoluminescence spectroscopy and imaging, and are correlated with the structural and electrical properties studied by transmission electron microscopy and electron holography. Four major areas are covered in this dissertation, which are described next. The effect of strain on the emission characteristics in wurtzite GaN has been studied. The values of the residual strain in GaN epilayers with different dislocation densities are determined by x-ray diffraction, and the relationship between exciton emission energy and the in-plane residual strain is demonstrated. It shows that the emission energy increases withthe magnitude of the in-plane compressive strain. The temperature dependence of the emission characteristics in cubic GaN has been studied. It is observed that the exciton emission and donor-acceptor pair recombination behave differently with temperature. The donor-bound exciton binding energy has been measured to be 13 meV from the temperature dependence of the emission spectrum. It is also found that the ionization energies for both acceptors and donors are smaller in cubic compared with hexagonal structures, which should contribute to higher doping efficiencies. A comprehensive study on the structural and optical properties is presented for InGaN/GaN quantum wells emitting in the blue, green, and yellow regions of the electromagnetic spectrum. Transmission electron microscopy images indicate the presence of indium inhomogeneties which should be responsible for carrier localization. The temperature dependence of emission luminescence shows that the carrier localization effects become more significant with increasing emission wavelength. On the other hand, the effect of non-radiative recombination on luminescence efficiency also varies with the emission wavelength. The fast increase of the non-radiative recombination rate with temperature in the green emitting QWs contributes to the lower efficiency compared with the blue emitting QWs. The possible saturation of non-radiative recombination above 100 K may explain the unexpected high emission efficiency for the yellow emitting QWs Finally, the effects of InGaN underlayers on the electronic and optical properties of InGaN/GaN quantum wells emitting in visible spectral regions have been studied. A significant improvement of the emission efficiency is observed, which is associated with a blue shift in the emission energy, a reduced recombination lifetime, an increased spatial homogeneity in the luminescence, and a weaker internal field across the quantum wells. These are explained by a partial strain relaxation introduced by the InGaN underlayer, which is measured by reciprocal space mapping of the x-ray diffraction intensity. / Dissertation/Thesis / Ph.D. Physics 2012

In this thesis I present and discuss the results of optical spectroscopy performed on InGaN/GaN single and multiple quantum well (QW) structures. I report on the optical properties of InGaN/GaN single and multiple QW structures, measured at high excitation power densities. I show a correlation exists between the reduction in PL efficiency at high excitation power densities, the phenomenon so-called ``efficiency-droop'', and a broadening of the PL spectra. I also show a distinct change in recombination dynamics, measured by time-resolved photoluminescence (PL), which occurs at the excitation power densities for which efficiency droop is measured. The broadening of the PL spectra at high excitation power densities is shown to occur due to a rapidly redshifting, short-lived high energy emission band. The high energy emission band is proposed to be due to the recombination of weakly localised/delocalised carriers occurring as a consequence of the progressive saturation of the local potential fluctuations responsible for carrier localisation, at high excitation power densities. I report on the effects of varying threading dislocation (TD) density on the optical properties of InGaN/GaN multiple QW structures. No systematic relationship exists between the room temperature internal quantum efficiency (IQE) and the TD density, in a series of nominally identical InGaN/GaN multiple QWs deposited on GaN templates of varying TD density. I also show the excitation power density dependence of the PL efficiency, at room temperatures, is unaffected for variation in the TD density between 2 x107 and 5 x109 cm-2. The independence of the optical properties to TD density is proposed to be a consequence of the strong carrier localisation, and hence short carrier diffusion lengths. I report on the effects of including an InGaN underlayer on the optical and microstructural properties of InGaN/GaN multiple QW structures. I show an increase in the room temperature IQE occurs for the structure containing the InGaN underlayer, compared to the reference. I show using PL excitation spectroscopy that an additional carrier transfer and recombination process occurs on the high energy side of the PL spectrum associated with the InGaN underlayer. Using PL decay time measurements I show the additional recombination process for carriers excited in the underlayer occurs on a faster timescale than the recombination at the peak of the PL spectrum. The additional contribution to the spectrum from the faster recombination process is proposed as responsible for the increase in room temperature IQE.